CN107584619A - A kind of preparation method of solid wood table trencher - Google Patents
A kind of preparation method of solid wood table trencher Download PDFInfo
- Publication number
- CN107584619A CN107584619A CN201710859360.0A CN201710859360A CN107584619A CN 107584619 A CN107584619 A CN 107584619A CN 201710859360 A CN201710859360 A CN 201710859360A CN 107584619 A CN107584619 A CN 107584619A
- Authority
- CN
- China
- Prior art keywords
- jigsaw
- board body
- carbonization
- chopping board
- health
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of solid wood table trencher, described preparation method comprise the following steps：a）Dry, log be sawn into after through drying process to 8 10 ° of moisture content；b）Carbonization, plank carries out high temperature cabonization at a temperature of being sent into 200-230 DEG C of kiln of carbonization after drying process；c）Rewetting health, rewetting health is carried out after plank carbonization to 68 ° of moisture content；d）Sawing sheet makes, and sawing sheet simultaneously carries out jigsaw, using the glue of EO levels during jigsaw, and makes rectangularity or square or circle or special-shaped chopping board body in jigsaw post-processing；e）Chopping board body after jigsaw completes, polished with 280 mesh fine sands, chopping board body entire area position is embrocated one time except food oil is stained with cotton after dust, gently polished one time with polishing cotton after 24 hours dry, then packed again；It has anti-mildew, anti-deformation, and face value and value are improved in color, the features such as making people's hygiene and health more preferably be ensured.
Description
Technical field
The present invention relates to a kind of preparation method of solid wood table trencher, the manufacturing technology for belonging to wooden kitchen article is led
Domain.
Background technology
Solid wood is originally most environmentally friendly, most has affinity, and solid wood table trencher, the also referred to as chopping block made are that each family kitchen is cut
Dish, the indispensable desirable utensil of anvil meat.But in use, solid wood table trencher needs cleaning daily.Due to no high temperature
The table trencher of carbonization treatment can absorb substantial amounts of moisture content, and these moisture content are absorbed by plank, and plank can be expanded by moisture content, humidity
Arch, deformation, can more seriously grow mould.Have in the timber treated by non-high temperature cabonization nutrition required for bacterium into
Part, humidity hotbed in, cultivated accelerate grow condition, generate large area go mouldy, mottling.Poisonous, harmful bacterium
Very big harm is brought to human body health.Kitchen utensils are the close contacts of immediate access in people's life, and it is defended
The raw health for directly affecting people.
The content of the invention
It is an object of the invention to overcome the shortcomings of the prior art, and a kind of anti-mildew, anti-deformation is provided, in color
Upper raising face value and value, make the preparation method for the solid wood table trencher that people's hygiene and health are more preferably ensured.
The purpose of the present invention is completed by following technical solution, a kind of preparation method of solid wood table trencher, described
Preparation method comprise the following steps：
a）Dry, log be sawn into after through drying process to 8-10 ° of moisture content；
b）Carbonization, plank carries out high temperature cabonization at a temperature of being sent into 200-230 DEG C of kiln of carbonization after drying process；
c）Rewetting health, rewetting health is carried out after plank carbonization to 6-8 ° of moisture content；
d）Sawing sheet makes, and sawing sheet simultaneously carries out jigsaw, using the glue of EO levels during jigsaw, and jigsaw post-processing make rectangularity or
Square circular or special-shaped chopping board body；
e）Chopping board body after jigsaw completes, polished with 280 mesh fine sands, it is except food oil is stained with cotton after dust that chopping board body is complete
Portion is embrocated at area position one time, is gently polished one time with polishing cotton after 24 hours dry, then packed again.
As preferred：Described step d）In, described jigsaw is spelled or with male and female groove jigsaw structure with flat；Made after jigsaw
Into chopping board body specification within length 45cm, between more than width 20cm, 1.8-4cm of thickness；
Described step e）In, food oil used is at least one of sunflower oil, peanut oil.
The present invention is processed into table trencher by more than the 200 DEG C timber being carbonized, bacteria live institute in carbonisation
The nutrition needed is pyrolyzed；Bacterium also just produces, also without the phenomenon of mould and mildew simultaneously without living environment
Improve the deformation of chopping board body, drying shrinkage and wet rise.
Embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail：A kind of preparation method of solid wood table trencher, institute
The preparation method stated comprises the following steps：
a）Dry, log be sawn into after through drying process to 8-10 ° of moisture content；
b）Carbonization, plank carries out high temperature cabonization at a temperature of being sent into 200-230 DEG C of kiln of carbonization after drying process；
c）Rewetting health, rewetting health is carried out after plank carbonization to 6-8 ° of moisture content；
d）Sawing sheet makes, and sawing sheet simultaneously carries out jigsaw, using the glue of EO levels during jigsaw, and jigsaw post-processing make rectangularity or
Square circular or special-shaped chopping board body；
e）Chopping board body after jigsaw completes, polished with 280 mesh fine sands, it is except food oil is stained with cotton after dust that chopping board body is complete
Portion is embrocated at area position one time, is gently polished one time with polishing cotton after 24 hours dry, then packed again.
Described step d）In, described jigsaw is spelled or with male and female groove jigsaw structure with flat；Manufactured chopping board after jigsaw
Body specification is within length 45cm, between more than width 20cm, 1.8-4cm of thickness；
Described step e）In, food oil used is at least one of sunflower oil, peanut oil.
Log is sawn into after plank through drying process to 8-10 ° of moisture content.The kiln that enters to be carbonized carries out 200 DEG C of high temperature above carbonizations.
Color as needed, different temperature and times is set；Temperature is higher, and the time is longer, and discoloration is also deeper；General temperature control
System is within 230 DEG C；Surmount 230 DEG C, risk is larger, if oxygen meeting spontaneous combustion is entered in kiln body gas leakage, the two makes in boarding and used
Property on can be influenceed by fastness.
Rewetting health is wanted to be made to 6-8 ° of moisture content, ability sawing sheet after plank carbonization, the glue that jigsaw uses will get well, and environmental protection must
EO levels must be reached.Waterproof, protection against the tide, fissility will get well.
The present invention makes table trencher from beech carbonization, and also the Wood carbonization including all assortments makes, and its purpose is main
It is anti-mildew, anti-deformation, face value and value is improved in color.
The present invention has following technical characterstic：
First, by more than 200 DEG C of high temperature cabonization, wood color is set to generate the change of color；Can by the difference of design temperature
Teak color, redwood color are controlled into, makes the deep elegance of timber, substantially increases the face value and value of timber.
Second, being handled by high temperature cabonization, cellulose, hemicellulose in timber, there occurs pyrolytic reaction, changes it
Material, its water imbibition, hygroscopicity is weakened significantly.The a quarter of only non-carbonized wood；So its deformation, drying shrinkage,
Wet rise also just improves a lot.
Third, table trencher is processed into by more than the 200 DEG C timber being carbonized, needed for bacteria live in carbonisation
The nutrition wanted is pyrolyzed.Bacterium also just produces without the phenomenon of mould, mildew without living environment, defends people
Raw health gets better protection.
All Spirit Essences according to main technical schemes of the present invention do equivalent transformation or the plank of modification, should all cover
Within protection scope of the present invention.
Claims (2)
1. a kind of preparation method of solid wood table trencher, it is characterised in that described preparation method comprises the following steps：
a）Dry, log be sawn into after through drying process to 8-10 ° of moisture content；
b）Carbonization, plank carries out high temperature cabonization at a temperature of being sent into 200-230 DEG C of kiln of carbonization after drying process；
c）Rewetting health, rewetting health is carried out after plank carbonization to 6-8 ° of moisture content；
d）Sawing sheet makes, and sawing sheet simultaneously carries out jigsaw, using the glue of EO levels during jigsaw, and jigsaw post-processing make rectangularity or
Square circular or special-shaped chopping board body；
e）Chopping board body after jigsaw completes, polished with 280 mesh fine sands, it is except food oil is stained with cotton after dust that chopping board body is complete
Portion is embrocated at area position one time, is gently polished one time with polishing cotton after 24 hours dry, then packed again.
2. the preparation method of solid wood table trencher according to claim 1, it is characterised in that：
Described step d）In, described jigsaw is spelled or with male and female groove jigsaw structure with flat；Manufactured chopping board body rule after jigsaw
Lattice are within length 45cm, between more than width 20cm, 1.8-4cm of thickness；
Described step e）In, food oil used is at least one of sunflower oil, peanut oil.