CN107574003A - A kind of lathe lubricant oil composite - Google Patents
A kind of lathe lubricant oil composite Download PDFInfo
- Publication number
- CN107574003A CN107574003A CN201710924571.8A CN201710924571A CN107574003A CN 107574003 A CN107574003 A CN 107574003A CN 201710924571 A CN201710924571 A CN 201710924571A CN 107574003 A CN107574003 A CN 107574003A
- Authority
- CN
- China
- Prior art keywords
- parts
- lathe
- lubricant oil
- compound additive
- oil composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of lathe lubricant oil composite, including base oil, compound additive, inorganic salts, pH adjusting agent, base oil, compound additive, the weight ratio of inorganic salts and pH adjusting agent are 65 78：23‑29：12‑25：13, the compound additive is made up of 20 25 parts of 28 parts of 12 18 parts of 25 48 parts of oleic acid, glycerin oleyl monoether, alkaline-earth metal alkylsalicylate, the flavones and 10 15 parts of water counted in parts by weight；The base oil is 2.5 3.5mPas in 100 DEG C of down cut viscosity.Compared with prior art, lathe lubricant oil composite of the present invention is oily based on vegetable fat, and in the presence of compound addition, greasy property is improved, and the wear-resistant number in interface handled with this lubricant oil composite is high, and ageing resistance is strong.
Description
Technical field
The present invention relates to the lubricating oil field used on hydraulic means on lathe, and in particular to a kind of lathe lubricating oil group
Compound.
Background technology
With the improvement of living standards, the application of lathe is increasingly popularized, the service life of lathe how is improved, reduces event
Barrier occurs, it has also become important research topic.Lubricating oil is as the indispensable material of mechanical movement, the operation to maintaining mechanism
And improve mechanical life and play very crucial effect.With the continuous progress of modern industry, the requirement to mechanism service life
More and more higher, while running environment is also increasingly harsher, lubricating oil has more excellent synthesis used by these are required to
Performance.Mineral based lubricating oil has been difficult in temperature tolerance, lubricity, inoxidizability, viscosity-temperature characteristics energy etc. used by early stage
Meet requirement, it is therefore desirable to using synthetic lubricant fluid.Because artificial oil is by the way of artificial synthesized, its combination property is remote
Higher than plain mineral oil, but artificial oil species is more at present, and different types of lubricating oil has different performance and requirement.
CN104204166B discloses a kind of lathe lubricant oil composite, and it contains：Lube base oil, with composition
Total amount benchmark meter, 0.05~5 mass % (R1O)3Phosphate [R shown in P=O1Represent carbon number be 6~15 aryl and
Carbon number is any number of, the R of 1~20 saturated hydrocarbyl1Between optionally it is identical or different.], 0.01~2 mass % (R2O)nP (=O) (OH)(3-n)Shown phosphate ester acid [R2It is the alkyl that carbon number is 4~20, n is 1 or 2, R2Between optional phase
It is same or different.], the mass % of 0.5 mass %~5 sulfide.Although the anti-wear performance of the lubricant oil composite is excellent, the group
Polymer component is complicated, and it is too high to use price.
The content of the invention
For prior art, it is an object of the invention to provide a kind of lathe lubricant oil composite, the lubricating oil composition
Thing composition is natural, effectively meets outside machine working condition requirement, moreover it is possible to avoids impacting ecological environment.
To solve prior art problem, the technical scheme that the present invention takes is：
A kind of lathe lubricant oil composite, including base oil, compound additive, inorganic salts, pH adjusting agent are base oil, compound
The weight ratio of additive, inorganic salts and pH adjusting agent is 65-78：23-29：12-25：1-3, the compound additive is by by weight
Oleic acid 25-48 parts, glycerin oleyl monoether 12-18 parts, alkaline-earth metal alkylsalicylate 2-8 parts, flavones 20-25 part of number meter
Formed with water 10-15 parts；The base oil is 2.5-3.5mPas in 100 DEG C of down cut viscosity.
Preferably, the compound additive is golden by 15 parts of 35 parts of oleic acid, glycerin oleyl monoether, the alkaline earth counted in parts by weight
Belong to 12 parts of 6 parts of alkylsalicylate, 22 parts of flavones and water compositions.
Specifically, alkaline-earth metal alkylsalicylate and water are mixed, add glycerin oleyl monoether and flavones,
After 1200-1800rpm magnetic agitation is uniform, it is 10-15% to be concentrated into moisture content, you can.
Preferably, the base oil is one or more combinations of rilanit special, sesame oil or rapeseed oil.
Preferably, the inorganic salts are made up of nano boric acid copper, Nanometer Copper, foam copper and deionized water, wherein nanometer boron
Sour copper, Nanometer Copper, the mol ratio of foam copper and deionized water are 2-3：1-2：2-3：1.
Preferably, the pH adjusting agent is the sodium acid carbonate that molar concentration is 1mol/L.
Compared with prior art, lathe lubricant oil composite of the present invention is oily based on vegetable fat, in compound addition
In the presence of, greasy property is improved, and the wear-resistant number in interface handled with this lubricant oil composite is high, and ageing resistance is strong.
Embodiment
The present invention is further described in detail below by specific embodiment.
The component and equipment being related in embodiment are that in the market is easily purchased, and each component is by weight.
Lathe provided by the invention is strong with lubricant oil composite lubricating ability, easy cleaning.Compound additive is by oleic acid, glycerine
The condensation reaction products of oleyl monoether, alkaline-earth metal alkylsalicylate, flavones and water composition, oleic acid and flavones, with glycerine oil
Base monoether, alkaline-earth metal alkylsalicylate, water form a network by hydrogen bond each other, and effectively inorganic salts net exists
In network, the anti-wear performance and ageing resistance of lubricating oil are improved.
Embodiment 1
The formula of compound additive
25 parts of oleic acid
12 parts of glycerin oleyl monoether
2 parts of alkaline-earth metal alkylsalicylate
20 parts of flavones
10 parts of water
Compound method：Alkaline-earth metal alkylsalicylate and water are mixed, add glycerin oleyl monoether and flavones,
After 1200-1800rpm magnetic agitation is uniform, it is 10-15% to be concentrated into moisture content, you can.
The formula of lathe lubricant oil composite
65 parts of base oil
23 parts of compound additive
12 parts of inorganic salts
1 part of pH adjusting agent.
Compound method：Compound additive and inorganic salts are mixed, high speed shear obtains reactant a；Base oil is added again anti-
Answer after being stirred in thing a and adding 30-40 DEG C, pH to 6.8-7.2 is adjusted with pH adjusting agent.
Embodiment 2
The formula of compound additive
30 parts of oleic acid
15 parts of glycerin oleyl monoether
5 parts of alkaline-earth metal alkylsalicylate
24 parts of flavones
12 parts of water
Compound method：Alkaline-earth metal alkylsalicylate and water are mixed, add glycerin oleyl monoether and flavones,
After 1200-1800rpm magnetic agitation is uniform, it is 10-15% to be concentrated into moisture content, you can.
The formula of lathe lubricant oil composite
70 parts of base oil
25 parts of compound additive
18 parts of inorganic salts
2 parts of pH adjusting agent.
Compound method：Compound additive and inorganic salts are mixed, high speed shear obtains reactant a；Base oil is added again anti-
Answer after being stirred in thing a and adding 30-40 DEG C, pH to 6.8-7.2 is adjusted with pH adjusting agent.
Embodiment 3
The formula of compound additive
48 parts of oleic acid
18 parts of glycerin oleyl monoether
8 parts of alkaline-earth metal alkylsalicylate
25 parts of flavones
15 parts of water
Compound method：Alkaline-earth metal alkylsalicylate and water are mixed, add glycerin oleyl monoether and flavones,
After 1200-1800rpm magnetic agitation is uniform, it is 10-15% to be concentrated into moisture content, you can.
The formula of lathe lubricant oil composite
78 parts of base oil
29 parts of compound additive
25 parts of inorganic salts
3 parts of pH adjusting agent.
Compound method：Compound additive and inorganic salts are mixed, high speed shear obtains reactant a；Base oil is added again anti-
Answer after being stirred in thing a and adding 30-40 DEG C, pH to 6.8-7.2 is adjusted with pH adjusting agent.
Comparative example 1
In addition to without flavones, remaining is the same as embodiment 2.
Comparative example 2
In addition to without nano boric acid ketone, remaining is the same as embodiment 2.
Performance test is carried out with lubricant oil composite to embodiment 1-3 and comparative example 1-2 lathe, the data obtained is as follows.
It can be seen from the results above that lubricant oil composite lubricity of the present invention is good, it will be apparent that improves processing efficiency, uses in addition
Mechanical surface anti-wear performance after the processing of this lubricant oil composite is high, and the anti-aging time is grown.
In addition, the invention is not restricted to above-mentioned embodiment, as long as in without departing from the scope of the present invention, can take various
Mode implements the present invention.
Claims (5)
1. a kind of lathe lubricant oil composite, it is characterised in that including base oil, compound additive, inorganic salts, pH regulations
Agent, base oil, compound additive, the weight ratio of inorganic salts and pH adjusting agent are 65-78：23-29：12-25：1-3, it is described compound
Additive is by oleic acid 25-48 parts, glycerin oleyl monoether 12-18 parts, alkaline-earth metal alkylsalicylate 2-8 for counting in parts by weight
Part, flavones 20-25 parts and water 10-15 parts composition；The base oil is 2.5-3.5mPas in 100 DEG C of down cut viscosity.
A kind of 2. lathe lubricant oil composite according to claim 1, it is characterised in that the compound additive by by
22 parts of 6 parts of 15 parts of 35 parts of oleic acid, glycerin oleyl monoether, alkaline-earth metal alkylsalicylate, the flavones and water 12 of parts by weight meter
Part composition.
3. a kind of lathe lubricant oil composite according to claim 1, it is characterised in that the base oil is hydrogenation castor
One or more combinations of sesame oil, sesame oil or rapeseed oil.
4. a kind of lathe lubricant oil composite according to claim 1, it is characterised in that the inorganic salts are by nanometer boron
Sour copper, Nanometer Copper, foam copper and deionized water composition, wherein mole of nano boric acid copper, Nanometer Copper, foam copper and deionized water
Than for 2-3：1-2：2-3：1.
5. a kind of lathe lubricant oil composite according to claim 1, it is characterised in that the pH adjusting agent is mole
Concentration is 1mol/L sodium acid carbonate.