CN107573559A - 一种秸秆塑料薄膜及其制备方法 - Google Patents

一种秸秆塑料薄膜及其制备方法 Download PDF

Info

Publication number
CN107573559A
CN107573559A CN201610516933.5A CN201610516933A CN107573559A CN 107573559 A CN107573559 A CN 107573559A CN 201610516933 A CN201610516933 A CN 201610516933A CN 107573559 A CN107573559 A CN 107573559A
Authority
CN
China
Prior art keywords
parts
plastic film
straw
polyethylene
straw plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610516933.5A
Other languages
English (en)
Inventor
邵锐
崔成杰
谢众
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Heilongjiang Xinda Enterprise Group Co Ltd
Original Assignee
Heilongjiang Xinda Enterprise Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heilongjiang Xinda Enterprise Group Co Ltd filed Critical Heilongjiang Xinda Enterprise Group Co Ltd
Priority to CN201610516933.5A priority Critical patent/CN107573559A/zh
Publication of CN107573559A publication Critical patent/CN107573559A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种秸秆塑料薄膜及其制备方法,涉及生物降解技术领域,由如下原料组成:植物纤维粉末、聚乙烯、添加剂。本发明制备的一种秸秆塑料薄膜具有良好的性能,能够满足各个领域的应用,在购物袋、农用地膜上更有广大的市场,同时具有成本低廉、操作简单、工艺流程短等优点。

Description

一种秸秆塑料薄膜及其制备方法
技术领域
本发明涉及生物降解技术领域,具体涉及一种降解薄膜其制备方法。
背景技术
塑料薄膜用聚氯乙烯、聚乙烯、聚丙烯、聚苯乙烯以及其他树脂制成的薄膜,用于包装以及用作覆膜层。 塑料包装及塑料包装产品在市场上所占的份额越来越大,特别是复合塑料软包装,已经广泛地应用于食品、医药、化工等领域,其中又以食品包装所占比例最大,比如饮料包装、速冻食品包装、蒸煮食品包装、快餐食品包装等,这些产品都给人们生活带来了极大的便利。
生物降解塑料薄膜是指在一定条件下,在能分泌酵素的微生物作用下可完全生物降解的高分子材料,可分为生物破坏性塑料和完全生物降解塑料,其中最有发展前途的是全淀粉塑料薄膜,这类塑料薄膜在使用后能完全被生物降解,产生二氧化碳和水,不污染环境,是近年来国内外淀粉降解塑料薄膜研究的主要方向。而淀粉由于难以铸造成型,产品机械性能差等缺点,使得淀粉的用途受到限制。因此,淀粉必须经过表面物理或化学改性后才能作为材料使用。
发明内容
本发明所要解决的技术问题在于提供一种工艺简单、生产成本低且对环境友好的可降解秸秆塑料薄膜。
一种秸秆塑料薄膜,由如下原料组成:植物纤维粉末、聚乙烯、添加剂。
所述的植物纤维粉末为稻壳粉末、秸秆粉末、玉米芯粉末中的一种;使用的秸秆粉目数为500目以上,使用份数为20-50份。
所述的聚乙烯使用份数为50-80份。
所述的添加试剂和试用份数为木塑偶联剂2份-5份、PE蜡1份-3份、硬酯酸锌1份-2份、乙二醇0.5份-2份、马来酸酐0.5份-3份。
一种秸秆塑料薄膜的制备方法包括如下步骤:
步骤a:将秸秆粉与聚乙烯及添加助剂按上述比例混合,在双螺杆挤出机中挤出,挤出温度为170-200℃,螺杆转速为100-400rpm;
步骤b:将步骤a制得的混合母粒加到吹膜机中经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜,最后得到成品薄膜,吹塑温度为180-210℃,螺杆转速为100-450rpm。
本发明的有益效果是:本发明制备的一种秸秆塑料薄膜具有良好的性能,能够满足各个领域的应用,在购物袋、农用地膜上更有广大的市场,同时具有成本低廉、操作简单、工艺流程短等优点。
具体实施方式
实施例1:秸秆粉40份、聚乙烯60份、木塑偶联剂3份、PE蜡1份、硬酯酸锌1份、乙二醇1.0份、马来酸酐0.5份。
性能测试结果:拉伸强度 (MPa)38,断裂伸长率(%)356,透光率(%)92。
实施例2:秸秆粉30份、聚乙烯70份、木塑偶联剂3份、PE蜡2份、硬酯酸锌1.5份、乙二醇1.5份、马来酸酐1.5份。
性能测试结果:拉伸强度 (MPa)40,断裂伸长率(%)421,透光率(%)94。
实施例3:秸秆粉20份、聚乙烯80份、木塑偶联剂5份、PE蜡3份、硬酯酸锌2份、乙二醇2份、马来酸酐2份。性能测试结果:拉伸强度45,断裂伸长率(%)376,透光率(%)97。
由实施例1-3的原料配方制备可生物降解的可降解秸秆塑料薄膜,包括如下步骤:
步骤a:将秸秆粉与聚乙烯及添加助剂按上述比例混合,在双螺杆挤出机中挤出;
双螺杆机各区温度为:一区150℃、二区160℃、三区160℃、四区170℃、五区170℃、六区175℃、机头180℃;螺杆转速分别为100、150、200rpm。
步骤b:将步骤a制得的混合母粒加到吹膜机中经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜,最后得到成品薄膜。
吹膜机各区温度:一区160℃、二区170℃、三区180℃、三通180℃、模头170℃;螺杆转速分别为160、140、120rpm。

Claims (5)

1.一种秸秆塑料薄膜及其制备方法,涉及薄膜生产技术领域,由如下原料组成:秸秆粉、聚乙烯、添加助剂。
2.根据权利要求1所述的可降解秸秆塑料薄膜,其特征在于:所述的秸秆粉目数为500目以上,使用份数为20-50份。
3.根据权利要求1所述的可降解秸秆塑料薄膜,其特征在于:所述的聚乙烯使用份数为50-80份。
4.根据权利要求1所述的可降解秸秆塑料薄膜,其特征在于:所述的添加试剂和试用份数为木塑偶联剂2份-5份、PE蜡1份-3份、硬酯酸锌1份-2份、乙二醇0.5份-2份、马来酸酐0.5份-3份。
5.一种秸秆塑料薄膜的制备方法,其特征在于,包括如下步骤:
步骤a:将秸秆粉与聚乙烯及添加助剂按上述比例混合,在双螺杆挤出机中挤出,挤出温度为170-200℃,螺杆转速为100-400rpm;
步骤b:将步骤a制得的混合母粒加到吹膜机中经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜,最后得到成品薄膜,吹塑温度为180-210℃,螺杆转速为100-450rpm。
CN201610516933.5A 2016-07-04 2016-07-04 一种秸秆塑料薄膜及其制备方法 Pending CN107573559A (zh)