CN107573493A - 一种新型纳米SiO2改性醇酸树脂 - Google Patents
一种新型纳米SiO2改性醇酸树脂 Download PDFInfo
- Publication number
- CN107573493A CN107573493A CN201710819717.2A CN201710819717A CN107573493A CN 107573493 A CN107573493 A CN 107573493A CN 201710819717 A CN201710819717 A CN 201710819717A CN 107573493 A CN107573493 A CN 107573493A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- modified alkyd
- monoglyceride
- novel nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型纳米SiO2改性醇酸树脂,由以下质量份的原料组成:酯化催化剂8‑10份、脂肪酸1‑3份、有机酸酐1‑3份、间苯二甲酸10‑20份、二元醇1‑3份、三羟甲基丙烷1‑3份、六羟甲基三聚氰0.1‑0.7份、去离子水20‑80份、油酸2‑10份、新戊二醇6‑16份、癸二酸1‑9份、油溶性表面活性剂OSP100‑120份、磺酸钙5‑8份、单酸甘油酯15‑25份。本发明制得的一种纳米SiO2改性醇酸树脂,贮存稳定性好,该纳米复合树脂制成的涂层具有优异的硬度、耐磨性、抗刮伤性、抗紫外线和耐老化性,而不影响树脂的透明性和相容性;广泛应用于木器、金属、塑料等制品的表面涂装与保护。
Description
技术领域
本发明属于化工领域,具体涉及一种新型纳米SiO2改性醇酸树脂。
背景技术
近几年,为了满足不同的性能要求,改性醇酸树脂的品种增多,有松香、苯乙烯、丙烯酸、有机硅等改性的醇酸树脂;由于醇酸树脂存在硬度、耐磨性、耐老化性、干燥速度慢、耐久性、耐水性等诸多缺陷。
而纳米改性的复合树脂涂覆层能提高涂料的耐老化性、抗刮伤性、耐磨性、耐UV性等,但将纳米粒子直接共混添加到树脂中,纳米粒子容易发生团聚与析出,树脂粘度增大,透明性差,无法制备稳定的纳米粒子改性的树脂;若在树脂中加入经过表面改性的纳米粒子,由于有外加助剂存在,影响树脂性能下降。
CN1554689A 公开了一种提高水性醇酸树脂性能的方法,醇酸树脂直接分散在含至少一种无机纳米粒子的含水分散液中制备纳米微粒改性水性醇酸树脂,或聚氨酯改性醇酸树脂直接分散在含至少一种无机纳米粒子的含水分散液中制备纳米微粒改性水性聚氨酯改性醇酸树脂;纳米微粒指金属氧化物、金属盐以及半金属和非金属化合物或它们的复合物。但该发明是直接将纳米粒子或改性后的纳米粒子外添加法直接分散到树脂中,纳米粒子容易发生团聚与析出,造成树脂粘度增大,树脂的贮存稳定性差,透明性下降。
发明内容
本发明的目的在于针对现有技术的不足,现提供一种新型纳米SiO2改性醇酸树脂。
为解决上述技术问题,本发明采用的技术方案为:一种新型纳米SiO2改性醇酸树脂,其创新点在于:由以下质量份的原料组成:酯化催化剂8-10份、脂肪酸1-3份、有机酸酐1-3份、间苯二甲酸10-20份、二元醇1-3份、三羟甲基丙烷1-3份、六羟甲基三聚氰0.1-0.7份、去离子水20-80份、油酸2-10份、新戊二醇6-16份、癸二酸1-9份、油溶性表面活性剂OSP100-120份、磺酸钙5-8份、单酸甘油酯15-25份。
进一步的,由以下质量份的原料组成:酯化催化剂8份、脂肪酸1份、有机酸酐1份、间苯二甲酸10份、二元醇1份、三羟甲基丙烷1份、六羟甲基三聚氰0.1份、去离子水20份、油酸2份、新戊二醇6份、癸二酸1份、油溶性表面活性剂OSP100份、磺酸钙5份、单酸甘油酯15份。
进一步的,由以下质量份的原料组成:酯化催化剂10份、脂肪酸3份、有机酸酐3份、间苯二甲酸20份、二元醇3份、三羟甲基丙烷3份、六羟甲基三聚氰0.7份、去离子水80份、油酸10份、新戊二醇16份、癸二酸9份、油溶性表面活性剂OSP120份、磺酸钙8份、单酸甘油酯25份。
进一步的,由以下质量份的原料组成:酯化催化剂9份、脂肪酸2份、有机酸酐2份、间苯二甲酸15份、二元醇2份、三羟甲基丙烷2份、六羟甲基三聚氰0.6份、去离子水50份、油酸6份、新戊二醇11份、癸二酸5份、油溶性表面活性剂OSP110份、磺酸钙7份、单酸甘油酯20份。
本发明的有益效果如下:本发明制得的一种纳米SiO2 改性醇酸树脂,贮存稳定性好,该纳米复合树脂制成的涂层具有优异的硬度、耐磨性、抗刮伤性、抗紫外线和耐老化性,而不影响树脂的透明性和相容性;广泛应用于木器、金属、塑料等制品的表面涂装与保护。
具体实施方式
以下由特定的具体实施例说明本发明的实施方式,熟悉此技术的人士可由本说明书所揭露的内容轻易地了解本发明的其他优点及功效。
一种新型纳米SiO2改性醇酸树脂,由以下质量份的原料组成:酯化催化剂8-10份、脂肪酸1-3份、有机酸酐1-3份、间苯二甲酸10-20份、二元醇1-3份、三羟甲基丙烷1-3份、六羟甲基三聚氰0.1-0.7份、去离子水20-80份、油酸2-10份、新戊二醇6-16份、癸二酸1-9份、油溶性表面活性剂OSP100-120份、磺酸钙5-8份、单酸甘油酯15-25份。
实施例1
一种新型纳米SiO2改性醇酸树脂,由以下质量份的原料组成:酯化催化剂8份、脂肪酸1份、有机酸酐1份、间苯二甲酸10份、二元醇1份、三羟甲基丙烷1份、六羟甲基三聚氰0.1份、去离子水20份、油酸2份、新戊二醇6份、癸二酸1份、油溶性表面活性剂OSP100份、磺酸钙5份、单酸甘油酯15份。
实施例2
一种新型纳米SiO2改性醇酸树脂,由以下质量份的原料组成:酯化催化剂10份、脂肪酸3份、有机酸酐3份、间苯二甲酸20份、二元醇3份、三羟甲基丙烷3份、六羟甲基三聚氰0.7份、去离子水80份、油酸10份、新戊二醇16份、癸二酸9份、油溶性表面活性剂OSP120份、磺酸钙8份、单酸甘油酯25份。
实施例3
一种新型纳米SiO2改性醇酸树脂,由以下质量份的原料组成:酯化催化剂9份、脂肪酸2份、有机酸酐2份、间苯二甲酸15份、二元醇2份、三羟甲基丙烷2份、六羟甲基三聚氰0.6份、去离子水50份、油酸6份、新戊二醇11份、癸二酸5份、油溶性表面活性剂OSP110份、磺酸钙7份、单酸甘油酯20份。
本发明提供的复合二元醇适用于一级乳化工艺的乳化炸药的制备,制得的乳化炸药贮存稳定,爆炸性能优良。
上述实施例只是本发明的较佳实施例,并不是对本发明技术方案的限制,只要是不经过创造性劳动即可在上述实施例的基础上实现的技术方案,均应视为落入本发明专利的权利保护范围内。
Claims (4)
1.一种新型纳米SiO2改性醇酸树脂,其特征在于:由以下质量份的原料组成:酯化催化剂8-10份、脂肪酸1-3份、有机酸酐1-3份、间苯二甲酸10-20份、二元醇1-3份、三羟甲基丙烷1-3份、六羟甲基三聚氰0.1-0.7份、去离子水20-80份、油酸2-10份、新戊二醇6-16份、癸二酸1-9份、油溶性表面活性剂OSP100-120份、磺酸钙5-8份、单酸甘油酯15-25份。
2.根据权利要求1所述的一种新型纳米SiO2改性醇酸树脂,其特征在于:由以下质量份的原料组成:酯化催化剂8份、脂肪酸1份、有机酸酐1份、间苯二甲酸10份、二元醇1份、三羟甲基丙烷1份、六羟甲基三聚氰0.1份、去离子水20份、油酸2份、新戊二醇6份、癸二酸1份、油溶性表面活性剂OSP100份、磺酸钙5份、单酸甘油酯15份。
3.根据权利要求1所述的一种新型纳米SiO2改性醇酸树脂,其特征在于:由以下质量份的原料组成:酯化催化剂10份、脂肪酸3份、有机酸酐3份、间苯二甲酸20份、二元醇3份、三羟甲基丙烷3份、六羟甲基三聚氰0.7份、去离子水80份、油酸10份、新戊二醇16份、癸二酸9份、油溶性表面活性剂OSP120份、磺酸钙8份、单酸甘油酯25份。
4.根据权利要求1所述的一种新型纳米SiO2改性醇酸树脂,其特征在于:由以下质量份的原料组成:酯化催化剂9份、脂肪酸2份、有机酸酐2份、间苯二甲酸15份、二元醇2份、三羟甲基丙烷2份、六羟甲基三聚氰0.6份、去离子水50份、油酸6份、新戊二醇11份、癸二酸5份、油溶性表面活性剂OSP110份、磺酸钙7份、单酸甘油酯20份。