CN107572775A - Suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor - Google Patents
Suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor Download PDFInfo
- Publication number
- CN107572775A CN107572775A CN201710889078.7A CN201710889078A CN107572775A CN 107572775 A CN107572775 A CN 107572775A CN 201710889078 A CN201710889078 A CN 201710889078A CN 107572775 A CN107572775 A CN 107572775A
- Authority
- CN
- China
- Prior art keywords
- silicate glasses
- boroalumino silicate
- alkali metal
- flat
- metal containing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to Boroalumino silicate glasses technical field, and in particular to suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor, it includes 50~70%SiO of molar percentage2, 15~25%Al2O3, 5~15%B2O3, 2~10%MgO, 0~10%SrO, 0~8%CaO and 0~8%BaO, wherein, 65%≤SiO2+Al2O3≤ 85%, liquidus viscosity >=100,000 of Boroalumino silicate glasses are moored, and the strain point of Boroalumino silicate glasses is more than 600 DEG C.Compared with prior art, the Boroalumino silicate glasses of not alkali metal containing of the invention realize good dimensional stability, and larger compression is formed on alumina silicate glass surface, improve the intensity of glass.
Description
Technical field
The present invention relates to Boroalumino silicate glasses technical field, and in particular to suitable for the not alkali metal containing of flat-panel monitor
Boroalumino silicate glasses.
Background technology
Flat-panel monitor refers to that the ratio between length and complete machine thickness of display screen diagonal are more than 4:1 display device, including
Liquid crystal display, plasma scope, electroluminescent display and light emitting diode etc..In recent years, flat-panel monitor is in
Reveal slimming, lightweight and high-resolution development trend.Being thinned a problem can bringing is, the intensity of glass can be with
The reduction of thickness and decline, therefore the property of substrate glass is particularly important.In order to meet the requirement used, it is necessary to make to show
The glass shown still has higher intensity under small thickness.At present, in the composition of alumina silicate glass used, in order to protect
It is higher to demonstrate,prove factor, the alkali metal content such as ion-exchange capacity and meltbility, formability, devitrification resistance in view of glass baseplate.
, it is necessary to which glass baseplate to be maintained to 350 DEG C~450 DEG C for the treatment of temperature in the manufacturing process of flat-panel monitor
Under, at these temperatures, most of glass baseplates experienced to be handled by compression, so as to cause the change of heat endurance and size,
This is due to the irreversible change in size of glass baseplate caused by the fictive temperature of glass changes.The degree of compression depends on system
Make the process of glass and the viscoplasticity of glass.Because alkali-free glass has high strain-point, therefore there is good dimensional stability,
But due in raw material alkali metal be very difficult to remove completely.If alkali metal Li2O、Na2O and K2O total concentration is less than
About 0.1 mole of %), then it is assumed that these glass of the invention are substantially free of alkali metal.
The content of the invention
Above-mentioned technical problem be present for prior art, it is an object of the invention to provide suitable for flat-panel monitor not
The Boroalumino silicate glasses of alkali metal containing, the Boroalumino silicate glasses have good dimensional stability and higher intensity concurrently.
To achieve the above object, the present invention provides following technical scheme:
The Boroalumino silicate glasses of not alkali metal containing suitable for flat-panel monitor, the Boroalumino silicate glasses bag are provided
Include the following component with molar percent:
Wherein, 65%≤SiO2+Al2O3≤ 85%, liquidus viscosity >=100,000 of the Boroalumino silicate glasses are moored, institute
The strain point for stating Boroalumino silicate glasses is more than 600 DEG C.
Preferably, the Boroalumino silicate glasses are included below with the component of molar percent:
Preferably, the Young's modulus of the Boroalumino silicate glasses is more than 80GPa.
Preferably, the density of the Boroalumino silicate glasses is 2.51~2.55g/cm3。
Preferably, described MgO, CaO, BaO and SrO molar percentage sum are 10~25%.
Preferably, the annealing point of the Boroalumino silicate glasses is more than 750 DEG C.
Preferably, the liquidus viscosity of the Boroalumino silicate glasses >=160,000 are moored.
Beneficial effects of the present invention:
The Boroalumino silicate glasses of the not alkali metal containing suitable for flat-panel monitor of the present invention, including molar percentage
50~70%SiO2, 15~25%Al2O3, 5~15%B2O3, 2~10%MgO, 0~10%SrO, 0~8%CaO and 0~8%
BaO, wherein, 65%≤SiO2+Al2O3≤ 85%, liquidus viscosity >=100,000 of Boroalumino silicate glasses are moored, boroaluminosilicate
The strain point of glass is more than 600 DEG C.Compared with prior art, Boroalumino silicate glasses of the invention are not due to containing alkali metal,
Control SiO2And Al2O3Total content it is higher, can significantly improve the strain point and shaking property of heat resistanceheat resistant of alumina silicate glass, reduce
The thermal coefficient of expansion of glass, suitable for High temperature tempered, Al2O3Glass is also provided with low liquidus temperature and high viscosity, is improved
The annealing point and modulus of glass;Control B2O3Amount increase the liquidus viscosity of glass;MgO, 0~10%SrO, 0~8%CaO
Can be played with 0~8%BaO, tetra- kinds of metal oxides makes liquid phase for crystalchecked and then reduces liquidus temperature, simultaneously
High annealing point is kept, and then keeps low pressure contracting.Therefore, the Boroalumino silicate glasses of not alkali metal containing of the invention realize well
Dimensional stability, and larger compression is formed on alumina silicate glass surface, improves the intensity of glass.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1:
Suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor, including molar percentage with the following group
Point:55.2%SiO2, 17.8%Al2O3, 7.6%B2O3, 5.4%MgO, 7.2%SrO, 2.8%CaO and 4.0%BaO.
Specifically, the Young's modulus of Boroalumino silicate glasses is 80.13GPa, the liquidus viscosity of Boroalumino silicate glasses
For 170,000 pools.
Specifically, the density of Boroalumino silicate glasses is 2.523g/cm3。
Specifically, the strain point of Boroalumino silicate glasses is 675 DEG C, 752 DEG C of the annealing point of Boroalumino silicate glasses.
Embodiment 2:
Suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor, including molar percentage with the following group
Point:59.5%SiO2, 25.5%Al2O3, 5.3%B2O3, 7.6%MgO and 2.1%SrO,
Specifically, the Young's modulus of Boroalumino silicate glasses is 81.35GPa, the liquidus viscosity of Boroalumino silicate glasses
For 180,000 pools.
Specifically, the density of Boroalumino silicate glasses is 2.531g/cm3。
Specifically, the strain point of Boroalumino silicate glasses is 682 DEG C, 756 DEG C of the annealing point of Boroalumino silicate glasses.
Embodiment 3:
Suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor, including molar percentage with the following group
Point:64.1%SiO2, 15.9%Al2O3, 5.3%B2O3, 2.7%MgO, 6.2%CaO and 5.8%BaO.
Specifically, the Young's modulus of Boroalumino silicate glasses is 81.26GPa, the liquidus viscosity of Boroalumino silicate glasses
For 170,000 pools.
Specifically, the density of Boroalumino silicate glasses is 2.525g/cm3。
Specifically, the strain point of Boroalumino silicate glasses is 679 DEG C, 755 DEG C of the annealing point of Boroalumino silicate glasses.
Embodiment 4:
Suitable for the Boroalumino silicate glasses of the not alkali metal containing of flat-panel monitor, including molar percentage with the following group
Point:50.0%SiO2, 14.6%Al2O3, 15.4%B2O3, 9.2%MgO, 4.8%SrO, 3.1%CaO and 2.9%BaO.
Specifically, the Young's modulus of Boroalumino silicate glasses is 80.57GPa, the liquidus viscosity of Boroalumino silicate glasses
For 190,000 pools.
Specifically, the density of Boroalumino silicate glasses is 2.536g/cm3。
Specifically, the strain point of Boroalumino silicate glasses is 685 DEG C, 753 DEG C of the annealing point of Boroalumino silicate glasses.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of scope is protected, although being explained with reference to preferred embodiment to the present invention, one of ordinary skill in the art should
Work as understanding, technical scheme can be modified or equivalent substitution, without departing from the reality of technical solution of the present invention
Matter and scope.
Claims (7)
1. the Boroalumino silicate glasses of the not alkali metal containing suitable for flat-panel monitor, it is characterised in that:The boroaluminosilicate
Glass is included below with the component of molar percent:
Wherein, 65%≤SiO2+Al2O3≤ 85%, liquidus viscosity >=100,000 of the Boroalumino silicate glasses are moored, the boron
The strain point of alumina silicate glass is more than 600 DEG C.
2. the Boroalumino silicate glasses of the not alkali metal containing according to claim 1 suitable for flat-panel monitor, its feature
It is:The Boroalumino silicate glasses are included below with the component of molar percent:
3. the Boroalumino silicate glasses of the not alkali metal containing according to claim 1 suitable for flat-panel monitor, its feature
It is:The Young's modulus of the Boroalumino silicate glasses is more than 80GPa.
4. the Boroalumino silicate glasses of the not alkali metal containing according to claim 1 suitable for flat-panel monitor, its feature
It is:The density of the Boroalumino silicate glasses is 2.51~2.55g/cm3。
5. the Boroalumino silicate glasses of the not alkali metal containing according to claim 1 suitable for flat-panel monitor, its feature
It is:Described MgO, CaO, BaO and SrO molar percentage sum are 10~25%.
6. the Boroalumino silicate glasses of the not alkali metal containing according to claim 1 suitable for flat-panel monitor, its feature
It is:The annealing point of the Boroalumino silicate glasses is more than 750 DEG C.
7. the Boroalumino silicate glasses of the not alkali metal containing according to claim 1 suitable for flat-panel monitor, its feature
It is:Moor the liquidus viscosity of the Boroalumino silicate glasses >=160,000.