CN107571555A - It is a kind of to make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in - Google Patents
It is a kind of to make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in Download PDFInfo
- Publication number
- CN107571555A CN107571555A CN201710693213.0A CN201710693213A CN107571555A CN 107571555 A CN107571555 A CN 107571555A CN 201710693213 A CN201710693213 A CN 201710693213A CN 107571555 A CN107571555 A CN 107571555A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- lost
- manufacture craft
- fibre
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite material manufacture craft for making bacteriostasis antibiosis active principle not be lost in, including bamboo raw material, bamboo raw material use then bamboo wood be processed, classified according to selection and blocked respectively, bamboo chip is put into boiling-off in boiling water and carries out first of softening, digested bamboo chip taking-up is cleaned with water after completing technique, it is put into soak, bamboo chip is processed by machinery, carry out decompositing crude fibre by moulding draw-wire machine, degumming is rinsed with water, bamboo fibre is put into progress second softening among digester again, bamboo fibre cleaning after enzyme is decomposed, bleaching, oil, it is soft, shredding combs the bamboo fiber that can obtain weaving.The present invention maintains fabric strength, ensures the dye-uptake of fabric, reduces the washing shrinkage of fabric and improves fabric feeling, improve the temperature tolerance and adsorption strength of bamboo fibre, reach the effect not easily runed off, lift the resistant to elevated temperatures characteristic of bamboo fibre, be affected by temperature fabric small.
Description
Technical field
The present invention relates to a kind of manufacture craft, more particularly to a kind of composite material for making bacteriostasis antibiosis active principle not be lost in
Manufacture craft.
Background technology
Bamboo fibre fabric is that bamboo fibre is made through special process for raw material in bamboo, the novel fabric through being formed by weaving, is had：
The features such as soft and smooth soft warm, bacteriostasis antibiosis, moisture absorption are ventilative, green, uvioresistant, natural health, Comfortable attractive, expert refers to
Go out, bamboo fibre is a kind of natural environmental-protective type green fiber truly, and bamboo fibre fabric replicates bamboo fibre completely because of it
The inherent characteristic of dimension, and it is popular with consumers again, and product consumption rises year by year, has antibacterial bacteriostatic function, same amount of
Bacterium is observed under the microscope, and bacterium can largely multiply in cotton, wood-fibred product, and the bacterium on bamboo fiber products is 24
75% or so is killed after hour, its raw material bamboo can grow tall 3 feet overnight, quickly can grow and update, and
Sustainable use, can largely alleviate timber, the shortage of resources of cotton, and bamboo fibre fabric is using can biology
The material of degraded, it can be degradable by microorganism and sunlight in soil, and this process decomposed will not cause any
Environmental pollution.
In the manufacture craft of existing bamboo fibre fabric, bamboo fibre is highly susceptible to destroy the situation hair being lost in
It is raw, processing quality is reduced, is easy to make the sterilization rate of bamboo fibre to decline in manufacture craft, the situation of highly basic kiering easily occurs,
It cannot be guaranteed that the dye-uptake of fabric, while during use, the toughness after bamboo fibre water suction can be attenuated to the 60- before water suction
70%, firmly pull reduction service life, it is impossible to high temperature soaks, and should not rob quarter immersion forever, can not dry during machine washing, after cleaning
Dried at ventilation lucifugal, it is impossible to exposure, while use range is limited and all reduces easily the effect of antibacterial sterilizing.
The content of the invention
The technical problem to be solved in the present invention is the defects of overcoming prior art, there is provided one kind makes bacteriostasis antibiosis active principle
The composite material manufacture craft not being lost in, maintains fabric strength, ensures the dye-uptake of fabric, by the expansion for rationally controlling fabric
Width amount and overfeed ratio, reduce the washing shrinkage of fabric and improve fabric feeling, improve temperature tolerance and the suction of bamboo fibre
Attached intensity, reach the effect not easily runed off, lift the high temperature resistant of bamboo fibre, the characteristic of high water pressure resistant, be affected by temperature fabric
It is small.
In order to solve the above-mentioned technical problem, the invention provides following technical scheme：
The present invention is a kind of to make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, including bamboo raw material, bamboo original
Material use then bamboo wood be processed, classified according to selection and blocked respectively, bamboo chip is put into boiling-off in boiling water enters
Row softens for first, and digested bamboo chip taking-up is cleaned with water after completing technique, is put into soak, by machinery by bamboo chip
It is processed, carries out decompositing crude fibre by moulding draw-wire machine, rinses degumming with water, then bamboo fibre is put among digester and carried out
Second softens, and the bamboo fibre after enzyme is decomposed is cleaned, bleached, oiling, soft, shredding combs the bamboo original that can obtain weaving
Fiber, by processing produced with combination into textile fiber, add expanded microporous polytetra fluoroethylene-EPTEE in produced with combination process and carry out feature
Overlay film, in terms of rinsing, using the hydrogen peroxide of medium quantity on the upper side during bleaching, chelated using new stabilizer SOF liquid and ZUN
Agent, 1g/L soda ash dosage is first added in reactive dyeing.
As a preferred technical solution of the present invention, bamboo, which blocks, to be removed ring and cuts open into bamboo chip, wherein a width of 2 lis
Rice, depending on the length of bamboo chip is as needed, bamboo wood burst, wherein tabasheer are carried out at twice according to tabasheer and bamboo are blue or green.
As a preferred technical solution of the present invention, bamboo green grass or young crops, tabasheer are individually placed to heat boiling progress in bating liquor
First of softening, wherein bating liquor must flood bamboo chip completely, and bamboo green grass or young crops is heated to 80 degree to 150 degree, while is internally added
3kg/cm2-5kg/cm2 is pressed, digestion time is 3 to 5 hours, carries out desugar, degreasing, degumming and sterilization.
As a preferred technical solution of the present invention, wherein second softening adds soak, is heated to 120 degree, adds
Press 4kg/cm2,4 hours of boiling.
As a preferred technical solution of the present invention, wherein second softening removes part pectin, hemicellulose, wooden
Element, the bamboo silk of discharging is immersed in the solution containing biology enzyme and handled, allow biology enzyme further decompose the lignin in bamboo silk,
Hemicellulose, pectin, also can be while lignin, hemicellulose, pectin is decomposed to obtain the cellulose fibre in bamboo
Added in treatment fluid it is a certain amount of can be with the enzyme of decomposition of cellulose, to obtain thinner bamboo fiber.
As a preferred technical solution of the present invention, wherein carrying out kiering and bleaching to blank cloth during rinsing, find
Hydrogen peroxide is added while soda ash kiering and completes bleaching.
As a preferred technical solution of the present invention, the new technology of 1g/L soda ash dosage is first added in reactive dyeing
First add 2/1 to three/3rds soda ash dosage than tradition.
Compared with prior art, beneficial effects of the present invention are as follows：
1：Fabrication processing of the invention by changing traditional bamboo fibre, first add 1g/L in reactive dyeing
The new technology of soda ash dosage, first add the technique of 2/1 to three/3rds soda ash dosage is more efficiently ensure that than tradition
The equalization of bamboo fibre, highly basic kiering is avoided, strengthen washing, maintain fabric strength, ensure the dye-uptake of fabric, by reasonable
The expanding amount and overfeed ratio of fabric are controlled, the washing shrinkage of fabric is reduced and improves fabric feeling.
2：The present invention improves the temperature tolerance and adsorption strength of bamboo fibre in bamboo fibre fabrication processing, reaches not
The effect being easy to run off, improve the use range of bamboo fibre composite material.
3：The present invention carries out feature overlay film in the flow of bamboo fibre manufacture craft, lifts the high temperature resistant of bamboo fibre, resistance to
The characteristic of high hydraulic pressure, it is affected by temperature fabric small, breathes freely comfortable.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
Present invention offer is a kind of to make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, including bamboo raw material,
Bamboo raw material use then bamboo wood be processed, classified according to selection and blocked respectively, bamboo chip is put into boiling water and boiled
Refining carries out first of softening, and digested bamboo chip taking-up is cleaned with water after completing technique, is put into soak, will by machinery
Bamboo chip is processed, and carries out decompositing crude fibre by moulding draw-wire machine, rinses degumming with water, then bamboo fibre is put among digester
Second softening is carried out, the bamboo fibre after enzyme is decomposed, which is cleaned, bleached, oiling, soft, shredding combs can obtain weaving
Bamboo fiber, by processing produced with combination into textile fiber, add expanded microporous polytetra fluoroethylene-EPTEE in produced with combination process and carry out work(
Can property overlay film, in terms of rinsing, using the hydrogen peroxide of medium quantity on the upper side during bleaching, using new stabilizer SOF liquid and ZUN chelas
Mixture, 1g/L soda ash dosage is first added in reactive dyeing.
Bamboo, which blocks, to be removed ring and cuts open into bamboo chip, wherein a width of 2 centimetres, depending on the length of bamboo chip is as needed, according to
Tabasheer and the blue or green progress bamboo wood burst of bamboo, wherein tabasheer at twice, conveniently carry out classification processing.
Bamboo green grass or young crops, tabasheer are individually placed to heat first of softening of boiling progress in bating liquor, wherein bating liquor must be by bamboo
Piece floods completely, and bamboo green grass or young crops is heated to 80 degree to 150 degree, while internally carries out pressurization 3kg/cm2-5kg/cm2, digestion time 3
To 5 hours, desugar, degreasing, degumming and sterilization are carried out, is effectively accomplished the effect of desugar, degreasing, degumming and sterilization.
Wherein second softening adds soak, is heated to 120 degree, and pressurize 4kg/cm2, and 4 hours of boiling, second is soft
Change for extracting bamboo fibre, make the bamboo fibre effect of extraction and processing quality more preferable.
Wherein second softening removes part pectin, hemicellulose, lignin, and the bamboo silk of discharging is immersed in containing biology
Handled in the solution of enzyme, allow biology enzyme further to decompose lignin, hemicellulose, pectin in bamboo silk, to obtain in bamboo
Cellulose fibre, can also be added while lignin, hemicellulose, pectin is decomposed in treatment fluid a certain amount of can decompose
The enzyme of cellulose, to obtain thinner bamboo fiber.
Kiering and bleaching are carried out to blank cloth when wherein rinsing, it is found that hydrogen peroxide is added while soda ash kiering completes drift
In vain, to improving production efficiency, reduce production cost and to reduce waste water favourable, using the new technology of decomposing hydrogen dioxide solution enzyme, effectively
The slightly yellow element for eliminating bamboo fibre surface and containing, improve product whiteness and coloured light.
The new technology of 1g/L soda ash dosage is first added first to add 2/1 to three/3rds than tradition in reactive dyeing
Soda ash dosage the more efficiently equalization that ensure that bamboo fibre of technique, avoid highly basic kiering, strengthen washing, maintain and knit
Thing strength, ensures the dye-uptake of fabric, by rationally controlling the expanding amount and overfeed ratio of fabric, reduces the washing shrinkage of fabric
With improve fabric feeling.
Specifically, in manufacturing process, bamboo wood is processed first, is classified according to selection and is blocked respectively,
Bamboo, which blocks, to be removed ring and cuts open into bamboo chip, wherein a width of 2 centimetres, depending on the length of bamboo chip is as needed, according to tabasheer and bamboo
Green grass or young crops carries out bamboo wood burst, and bamboo chip at twice, is put into boiling-off in boiling water and carries out first of softening, by bamboo green grass or young crops, tabasheer by wherein tabasheer
It is individually placed to heat boiling in bating liquor, wherein bating liquor must flood bamboo chip completely, and bamboo green grass or young crops is heated to 80 degree to 150 degree,
Pressurization 3kg/cm2-5kg/cm2 is internally carried out simultaneously, digestion time is 3 to 5 hours, carries out desugar, degreasing, degumming and disappears
Bacterium, digested bamboo chip taking-up is cleaned with water after completing technique, is put into soak, is processed bamboo chip by machinery,
Carry out decompositing crude fibre by moulding draw-wire machine, with water rinse degumming, then by bamboo fibre be put among digester carry out second it is soft
Change.
Wherein second softening adds soak, is heated to 120 degree, and pressurize 4kg/cm2,4 hours of boiling, wherein second
Road softening removes part pectin, hemicellulose, lignin, and the bamboo silk of discharging is immersed in the solution containing biology enzyme and handled,
Allow biology enzyme further to decompose lignin, hemicellulose, pectin in bamboo silk, to obtain the cellulose fibre in bamboo, dividing
Solution lignin, hemicellulose, pectin while can also be added in treatment fluid it is a certain amount of can be with the enzyme of decomposition of cellulose, to obtain
Thinner bamboo fiber is obtained, the bamboo fibre after enzyme is decomposed, which is cleaned, bleached, oiling, soft, shredding combs can obtain weaving use
Bamboo fiber.
Kiering and bleaching are carried out to blank cloth when wherein rinsing, it is found that hydrogen peroxide is added while soda ash kiering completes drift
In vain, to improving production efficiency, reduce production cost and to reduce waste water favourable, using the new technology of decomposing hydrogen dioxide solution enzyme, effectively
The slightly yellow element for eliminating bamboo fibre surface and containing, improve product whiteness and coloured light, first add 1g/ in reactive dyeing
The new technology of L soda ash dosage first adds the technique of 2/1 to three/3rds soda ash dosage is more efficiently ensure that than tradition
The equalization of bamboo fibre, highly basic kiering is avoided, strengthen washing, maintain fabric strength, ensure the dye-uptake of fabric, by reasonable
The expanding amount and overfeed ratio of fabric are controlled, the washing shrinkage of fabric is reduced and improves fabric feeling, by processing compound system
Textile fiber is made, adding expanded microporous polytetra fluoroethylene-EPTEE in produced with combination process carries out feature overlay film, in terms of rinsing, bleaching
When using medium quantity on the upper side hydrogen peroxide, it is first in reactive dyeing using new stabilizer SOF liquid and ZUN chelating agents
Add 1g/L soda ash dosage.
Fabrication processing of the invention by changing traditional bamboo fibre, first add 1g/L pure in reactive dyeing
The new technology of alkaline agent amount, first add the technique of 2/1 to three/3rds soda ash dosage is more efficiently to ensure that bamboo than tradition
The equalization of fiber, highly basic kiering is avoided, strengthen washing, maintain fabric strength, ensure the dye-uptake of fabric, by rationally controlling
The expanding amount and overfeed ratio of weaving thing, reduce the washing shrinkage of fabric and improve fabric feeling, in bamboo fibre manufacture craft
The temperature tolerance and adsorption strength of bamboo fibre are improved in flow, reaches the effect not easily runed off, improves bamboo fibre composite surface
The use range of material, feature overlay film is carried out in the flow of bamboo fibre manufacture craft, lift the high temperature resistant of bamboo fibre, resistance to Gao Shui
The characteristic of pressure, it is affected by temperature fabric small, breathes freely comfortable.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic.
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in the present invention's
Within protection domain.
Claims (7)
1. a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, including bamboo raw material, it is characterised in that bamboo
Raw material use then bamboo wood be processed, classified according to selection and blocked respectively, bamboo chip is put into boiling-off in boiling water
First of softening is carried out, digested bamboo chip taking-up is cleaned with water after completing technique, is put into soak, by machinery by bamboo
Piece is processed, and carries out decompositing crude fibre by moulding draw-wire machine, rinses degumming with water, then bamboo fibre is put among digester
Row second softens, and the bamboo fibre after enzyme is decomposed is cleaned, bleached, oiling, soft, shredding combs the bamboo that can obtain weaving
Fibrillation, by processing produced with combination into textile fiber, add expanded microporous polytetra fluoroethylene-EPTEE in produced with combination process and carry out function
Property overlay film, in terms of rinsing, using the hydrogen peroxide of medium quantity on the upper side during bleaching, chelated using new stabilizer SOF liquid and ZUN
Agent, 1g/L soda ash dosage is first added in reactive dyeing.
2. it is according to claim 1 it is a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, it is special
Sign is, bamboo, which blocks, to be removed ring and cut open into bamboo chip, wherein a width of 2 centimetres, depending on the length of bamboo chip is as needed, according to bamboo
Yellow and bamboo is blue or green to carry out bamboo wood burst, wherein tabasheer at twice.
3. it is according to claim 1 it is a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, it is special
Sign is, bamboo green grass or young crops, tabasheer is individually placed to heat first of softening of boiling progress in bating liquor, wherein bating liquor must be by bamboo chip
Flood completely, bamboo green grass or young crops is heated to 80 degree to 150 degree, while internally carries out pressurization 3kg/cm2-5kg/cm2, and digestion time is 3 to 5
Individual hour, carry out desugar, degreasing, degumming and sterilization.
4. it is according to claim 1 it is a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, it is special
Sign is that wherein second softening adds soak, is heated to 120 degree, and pressurize 4kg/cm2,4 hours of boiling.
5. it is according to claim 1 it is a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, it is special
Sign is that wherein second softening removes part pectin, hemicellulose, lignin, and the bamboo silk of discharging is immersed in containing biology
Handled in the solution of enzyme, allow biology enzyme further to decompose lignin, hemicellulose, pectin in bamboo silk, to obtain in bamboo
Cellulose fibre, can also be added while lignin, hemicellulose, pectin is decomposed in treatment fluid a certain amount of can decompose
The enzyme of cellulose, to obtain thinner bamboo fiber.
6. it is according to claim 1 it is a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, it is special
Sign is, wherein carrying out kiering and bleaching to blank cloth during rinsing, it is found that hydrogen peroxide is added while soda ash kiering completes drift
In vain.
7. it is according to claim 1 it is a kind of make the composite material manufacture craft that bacteriostasis antibiosis active principle is not lost in, it is special
Sign is, 1g/L soda ash dosage is first added in reactive dyeing.