CN107557775A - A kind of automobile using surface conditioning agent - Google Patents
A kind of automobile using surface conditioning agent Download PDFInfo
- Publication number
- CN107557775A CN107557775A CN201710737519.1A CN201710737519A CN107557775A CN 107557775 A CN107557775 A CN 107557775A CN 201710737519 A CN201710737519 A CN 201710737519A CN 107557775 A CN107557775 A CN 107557775A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- triethanolamine
- starch
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile using surface conditioning agent, it is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts of each raw material are respectively:30 40 parts of magnesium fluoride, 4 12 parts of hydrochloric acid, 26 parts of dibutyl phthalate, 8 12 parts of Tea Saponin, 15 parts of ammonium molybdate, 10 20 parts of magnesium sulfate, 8 10 parts of natrium nitrosum, 15 parts of triethanolamine, 20 22 parts of sulfosalicylic acid, 10 14 parts of glacial acetic acid, 8 10 parts of starch.After surface treatment of the surface treatment phosphating solution provided by the invention to automobile mechanical part, one layer of evacuation, porous phosphating coat can be formed, good basis has been descended to follow-up coating process pad, has been more beneficial for the processing of painting dressing automobiles.
Description
Technical field
The present invention relates to a kind of automobile using inorganic agent, and in particular to a kind of automobile using surface conditioning agent.
Background technology
Vehicle coating process, it generally can be divided into two large divisions:First, metallic surface is handled before application, pre-treatment skill is also
Art;Second, the construction technology of application.Surface treatment mainly includes removing the greasy dirt of workpiece surface, dust, corrosion and repaiied
Removing of old dope layer etc. when mending operation, to improve the surface state of workpiece.Including according to various concrete conditions to workpiece surface
It is machined and is chemically treated, such as phosphatization, oxidation and Passivation Treatment.Phosphatization is the critical process of pretreatment technology, directly
Affect the quality of painting dressing automobiles.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to now provide a kind of automobile using surface of abrasion and corrosion resistance
Inorganic agent.
In order to solve the above technical problems, the technical solution adopted by the present invention is:A kind of automobile using surface conditioning agent, it is innovated
Point is:It is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, magnesium sulfate, nitrous
Sour sodium, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts of each raw material are respectively:Magnesium fluoride 30-40
Part, hydrochloric acid 4-12 parts, dibutyl phthalate 2-6 parts, Tea Saponin 8-12 parts, ammonium molybdate 1-5 parts, magnesium sulfate 10-20 parts, Asia
Sodium nitrate 8-10 parts, triethanolamine 1-5 parts, sulfosalicylic acid 20-22 parts, glacial acetic acid 10-14 parts, starch 8-10 parts.
Further, it is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, sulphur
Sour magnesium, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts of each raw material are respectively:Fluorine
Change 30 parts of magnesium, 4 parts of hydrochloric acid, 2 parts of dibutyl phthalate, 8 parts of Tea Saponin, 1 part of ammonium molybdate, 10 parts of magnesium sulfate, natrium nitrosum 8
Part, 1 part of triethanolamine, 20 parts of sulfosalicylic acid, 10 parts of glacial acetic acid, 8 parts of starch.
Further, it is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, sulphur
Sour magnesium, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts of each raw material are respectively:Fluorine
Change 40 parts of magnesium, 12 parts of hydrochloric acid, 6 parts of dibutyl phthalate, 12 parts of Tea Saponin, 5 parts of ammonium molybdate, 20 parts of magnesium sulfate, nitrous acid
10 parts of sodium, 5 parts of triethanolamine, 22 parts of sulfosalicylic acid, 14 parts of glacial acetic acid, 10 parts of starch.
Further, it is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, sulphur
Sour magnesium, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts of each raw material are respectively:Fluorine
Change 35 parts of magnesium, 8 parts of hydrochloric acid, 4 parts of dibutyl phthalate, 10 parts of Tea Saponin, 3 parts of ammonium molybdate, 15 parts of magnesium sulfate, natrium nitrosum
9 parts, 3 parts of triethanolamine, 21 parts of sulfosalicylic acid, 12 parts of glacial acetic acid, 9 parts of starch.
Beneficial effects of the present invention are as follows:Surface of the surface treatment phosphating solution provided by the invention to automobile mechanical part
After processing, one layer of evacuation, porous phosphating coat can be formed, good basis has been descended to follow-up coating process pad, has been more beneficial for
The processing of painting dressing automobiles.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
A kind of automobile using surface conditioning agent, is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, tea soap
Element, ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts point of each raw material
It is not:Magnesium fluoride 30-40 parts, hydrochloric acid 4-12 parts, dibutyl phthalate 2-6 parts, Tea Saponin 8-12 parts, ammonium molybdate 1-5 parts,
Magnesium sulfate 10-20 parts, natrium nitrosum 8-10 parts, triethanolamine 1-5 parts, sulfosalicylic acid 20-22 parts, glacial acetic acid 10-14 parts, form sediment
Powder 8-10 parts.
Embodiment 1
A kind of automobile using surface conditioning agent, is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin,
Ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts difference of each raw material
For:30 parts of magnesium fluoride, 4 parts of hydrochloric acid, 2 parts of dibutyl phthalate, 8 parts of Tea Saponin, 1 part of ammonium molybdate, 10 parts of magnesium sulfate, nitrous
Sour 8 parts of sodium, 1 part of triethanolamine, 20 parts of sulfosalicylic acid, 10 parts of glacial acetic acid, 8 parts of starch.
Embodiment 2
A kind of automobile using surface conditioning agent, is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin,
Ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts difference of each raw material
For:40 parts of magnesium fluoride, 12 parts of hydrochloric acid, 6 parts of dibutyl phthalate, 12 parts of Tea Saponin, 5 parts of ammonium molybdate, 20 parts of magnesium sulfate are sub-
10 parts of sodium nitrate, 5 parts of triethanolamine, 22 parts of sulfosalicylic acid, 14 parts of glacial acetic acid, 10 parts of starch.
Embodiment 3
A kind of automobile using surface conditioning agent, is made up of following raw material:Magnesium fluoride, hydrochloric acid, dibutyl phthalate, Tea Saponin,
Ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, the mass parts difference of each raw material
For:35 parts of magnesium fluoride, 8 parts of hydrochloric acid, 4 parts of dibutyl phthalate, 10 parts of Tea Saponin, 3 parts of ammonium molybdate, 15 parts of magnesium sulfate are sub-
9 parts of sodium nitrate, 3 parts of triethanolamine, 21 parts of sulfosalicylic acid, 12 parts of glacial acetic acid, 9 parts of starch.
After surface treatment of the surface treatment phosphating solution provided by the invention to automobile mechanical part, one layer can be formed and dredged
Dissipate, porous phosphating coat, good basis has been descended to follow-up coating process pad, has been more beneficial for the processing of painting dressing automobiles.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
The technical scheme that can be realized on the basis of above-described embodiment without creative work, it is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (4)
- A kind of 1. automobile using surface conditioning agent, it is characterised in that:It is made up of following raw material:Magnesium fluoride, hydrochloric acid, phthalic acid two Butyl ester, Tea Saponin, ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, glacial acetic acid and starch, it is described each The mass parts of raw material are respectively:Magnesium fluoride 30-40 parts, hydrochloric acid 4-12 parts, dibutyl phthalate 2-6 parts, Tea Saponin 8-12 Part, ammonium molybdate 1-5 parts, magnesium sulfate 10-20 parts, natrium nitrosum 8-10 parts, triethanolamine 1-5 parts, sulfosalicylic acid 20-22 parts, Glacial acetic acid 10-14 parts, starch 8-10 parts.
- A kind of 2. automobile using surface conditioning agent according to claim 1, it is characterised in that:It is made up of following raw material:Fluorination Magnesium, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, ice Acetic acid and starch, the mass parts of each raw material are respectively:30 parts of magnesium fluoride, 4 parts of hydrochloric acid, 2 parts of dibutyl phthalate, 8 parts of Tea Saponin, 1 part of ammonium molybdate, 10 parts of magnesium sulfate, 8 parts of natrium nitrosum, 1 part of triethanolamine, 20 parts of sulfosalicylic acid, glacial acetic acid 10 parts, 8 parts of starch.
- A kind of 3. automobile using surface conditioning agent according to claim 1, it is characterised in that:It is made up of following raw material:Fluorination Magnesium, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, ice Acetic acid and starch, the mass parts of each raw material are respectively:40 parts of magnesium fluoride, 12 parts of hydrochloric acid, dibutyl phthalate 6 Part, 12 parts of Tea Saponin, 5 parts of ammonium molybdate, 20 parts of magnesium sulfate, 10 parts of natrium nitrosum, 5 parts of triethanolamine, 22 parts of sulfosalicylic acid, ice 14 parts of acetic acid, 10 parts of starch.
- A kind of 4. automobile using surface conditioning agent according to claim 1, it is characterised in that:It is made up of following raw material:Fluorination Magnesium, hydrochloric acid, dibutyl phthalate, Tea Saponin, ammonium molybdate, magnesium sulfate, natrium nitrosum, triethanolamine, sulfosalicylic acid, ice Acetic acid and starch, the mass parts of each raw material are respectively:35 parts of magnesium fluoride, 8 parts of hydrochloric acid, 4 parts of dibutyl phthalate, 10 parts of Tea Saponin, 3 parts of ammonium molybdate, 15 parts of magnesium sulfate, 9 parts of natrium nitrosum, 3 parts of triethanolamine, 21 parts of sulfosalicylic acid, glacial acetic acid 12 parts, 9 parts of starch.