CN107556839A - A kind of anti-oxidant nano paint - Google Patents
A kind of anti-oxidant nano paint Download PDFInfo
- Publication number
- CN107556839A CN107556839A CN201710724401.5A CN201710724401A CN107556839A CN 107556839 A CN107556839 A CN 107556839A CN 201710724401 A CN201710724401 A CN 201710724401A CN 107556839 A CN107556839 A CN 107556839A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- resin
- coating
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-oxidant nano paint, it is made up of in parts by weight following component：5 10 parts of nano titanium oxide, 15 25 parts of glass fibre, 30 50 parts of propylene vinegar derivatives resin, 3 10 parts of vinyl organosilicon resin, 58 parts of silane coupler, 10 15 parts of organic silicon adhesive, 20 40 parts of nanometer titanium dioxide, 10 20 parts of nano zinc oxide powder, 13 parts of pH value conditioning agent, 5 10 parts of alumina silicate.The present invention compared with prior art, by adding nano material in the technical recipe of coating, so that the antioxygenic property of coating is significantly enhanced, not only optimizes the using effect of coating, and extend the service life of coating.
Description
Technical field
The present invention relates to a kind of coating, and in particular to a kind of anti-oxidant nano paint.
Background technology
The coating of traditional coating especially exterior wall, due to exposed to the external world, being exposed to wind and rain and intense UV
The test of line, the life-span often used is ofer short duration, and in order to extend the service life of coating, improving the antioxygenic property of coating is
The most key factor, but traditional coating process formula can not break through this difficulty, research and development run into bottleneck.
The content of the invention
Goal of the invention：In order to overcome the deficiencies in the prior art, there is provided a kind of extraordinary nanometer of antioxygenic property
Coating.
Technical scheme：To achieve the above object, the present invention provides a kind of anti-oxidant nano paint, in parts by weight by following
Component forms：
Nano titanium oxide 5-10 parts, glass fibre 15-25 parts, propylene vinegar derivatives resin 30-50 parts, vinyl have
It is machine silicones 3-10 parts, silane coupler 5-8 parts, organic silicon adhesive 10-15 parts, nanometer titanium dioxide 20-40 parts, nano oxidized
Zinc powder 10-20 parts, pH value conditioning agent 1-3 parts, alumina silicate 5-10 parts.
Further, it is made up of in parts by weight following component：
Nano titanium oxide 5-6 parts, glass fibre 15-17 parts, propylene vinegar derivatives resin 30-33 parts, vinyl have
It is machine silicones 3-5 parts, silane coupler 5-6 parts, organic silicon adhesive 10-12 parts, nanometer titanium dioxide 20-22 parts, nano oxidized
Zinc powder 10-12 parts, pH value conditioning agent 1-2 parts, alumina silicate 5-7 parts.
Further, it is made up of in parts by weight following component：
Nano titanium oxide 8-10 parts, glass fibre 22-25 parts, propylene vinegar derivatives resin 45-50 parts, vinyl have
It is machine silicones 8-10 parts, silane coupler 7-8 parts, organic silicon adhesive 13-15 parts, nanometer titanium dioxide 35-40 parts, nano oxidized
Zinc powder 18-20 parts, pH value conditioning agent 2-3 parts, alumina silicate 8-10 parts.
Further, it is made up of in parts by weight following component：
Nano titanium oxide 7-9 parts, glass fibre 18-21 parts, propylene vinegar derivatives resin 35-45 parts, vinyl have
It is machine silicones 5-7 parts, silane coupler 6-7 parts, organic silicon adhesive 12-13 parts, nanometer titanium dioxide 25-35 parts, nano oxidized
Zinc powder 14-16 parts, pH value conditioning agent 1-3 parts, alumina silicate 7-9 parts.
Further, it is made up of in parts by weight following component：
8 parts of nano titanium oxide, 20 parts of glass fibre, 40 parts of propylene vinegar derivatives resin, vinyl organosilicon resin 6
Part, 7 parts of silane coupler, 13 parts of organic silicon adhesive, 30 parts of nanometer titanium dioxide, 15 parts of nano zinc oxide powder, pH value conditioning agent 2
Part, 8 parts of alumina silicate.
Beneficial effect：The present invention compared with prior art, by adding nano material in the technical recipe of coating, so as to
So that the antioxygenic property of coating is significantly enhanced, the using effect of coating is not only optimized, and extends coating
Service life.
Embodiment
Specific embodiment below, the present invention is furture elucidated, it should be understood that these embodiments be merely to illustrate the present invention without
For limiting the scope of the present invention, after the present invention has been read, the various equivalent form of values of the those skilled in the art to the present invention
Modification fall within the application appended claims limited range.
Embodiment 1：
A kind of anti-oxidant nano paint, is made up of following component in parts by weight：
5 parts of nano titanium oxide, 15 parts of glass fibre, 30 parts of propylene vinegar derivatives resin, vinyl organosilicon resin 3
Part, 5 parts of silane coupler, 10 parts of organic silicon adhesive, 20 parts of nanometer titanium dioxide, 10 parts of nano zinc oxide powder, pH value conditioning agent 1
Part, 5 parts of alumina silicate.
Embodiment 2：
A kind of anti-oxidant nano paint, is made up of following component in parts by weight：
10 parts of nano titanium oxide, 25 parts of glass fibre, 50 parts of propylene vinegar derivatives resin, vinyl organosilicon resin
10 parts, 8 parts of silane coupler, 15 parts of organic silicon adhesive, 40 parts of nanometer titanium dioxide, 20 parts of nano zinc oxide powder, pH value regulation
3 parts of agent, 10 parts of alumina silicate.
Embodiment 3：
A kind of anti-oxidant nano paint, is made up of following component in parts by weight：
8 parts of nano titanium oxide, 20 parts of glass fibre, 40 parts of propylene vinegar derivatives resin, vinyl organosilicon resin 6
Part, 7 parts of silane coupler, 13 parts of organic silicon adhesive, 30 parts of nanometer titanium dioxide, 15 parts of nano zinc oxide powder, pH value conditioning agent 2
Part, 8 parts of alumina silicate.
Claims (5)
- A kind of 1. anti-oxidant nano paint, it is characterised in that：It is made up of in parts by weight following component：Nano titanium oxide 5-10 parts, glass fibre 15-25 parts, propylene vinegar derivatives resin 30-50 parts, vinyl organosilicon Resin 3-10 parts, silane coupler 5-8 parts, organic silicon adhesive 10-15 parts, nanometer titanium dioxide 20-40 parts, nano zinc oxide powder 10-20 parts, pH value conditioning agent 1-3 parts, alumina silicate 5-10 parts.
- A kind of 2. anti-oxidant nano paint according to claim 1, it is characterised in that：In parts by weight by following component group Into：Nano titanium oxide 5-6 parts, glass fibre 15-17 parts, propylene vinegar derivatives resin 30-33 parts, vinyl organosilicon Resin 3-5 parts, silane coupler 5-6 parts, organic silicon adhesive 10-12 parts, nanometer titanium dioxide 20-22 parts, nano zinc oxide powder 10-12 parts, pH value conditioning agent 1-2 parts, alumina silicate 5-7 parts.
- A kind of 3. anti-oxidant nano paint according to claim 1, it is characterised in that：In parts by weight by following component group Into：Nano titanium oxide 8-10 parts, glass fibre 22-25 parts, propylene vinegar derivatives resin 45-50 parts, vinyl organosilicon Resin 8-10 parts, silane coupler 7-8 parts, organic silicon adhesive 13-15 parts, nanometer titanium dioxide 35-40 parts, nano zinc oxide powder 18-20 parts, pH value conditioning agent 2-3 parts, alumina silicate 8-10 parts.
- A kind of 4. anti-oxidant nano paint according to claim 1, it is characterised in that：In parts by weight by following component group Into：Nano titanium oxide 7-9 parts, glass fibre 18-21 parts, propylene vinegar derivatives resin 35-45 parts, vinyl organosilicon Resin 5-7 parts, silane coupler 6-7 parts, organic silicon adhesive 12-13 parts, nanometer titanium dioxide 25-35 parts, nano zinc oxide powder 14-16 parts, pH value conditioning agent 1-3 parts, alumina silicate 7-9 parts.
- A kind of 5. anti-oxidant nano paint according to claim 1, it is characterised in that：In parts by weight by following component group Into：8 parts of nano titanium oxide, 20 parts of glass fibre, 40 parts of propylene vinegar derivatives resin, 6 parts of vinyl organosilicon resin, 7 parts of silane coupler, 13 parts of organic silicon adhesive, 30 parts of nanometer titanium dioxide, 15 parts of nano zinc oxide powder, 2 parts of pH value conditioning agent, 8 parts of alumina silicate.