CN107540955A - Air conditioning for automobiles flabellum of good weatherability and preparation method thereof - Google Patents
Air conditioning for automobiles flabellum of good weatherability and preparation method thereof Download PDFInfo
- Publication number
- CN107540955A CN107540955A CN201710678059.XA CN201710678059A CN107540955A CN 107540955 A CN107540955 A CN 107540955A CN 201710678059 A CN201710678059 A CN 201710678059A CN 107540955 A CN107540955 A CN 107540955A
- Authority
- CN
- China
- Prior art keywords
- parts
- flabellum
- automobiles
- air conditioning
- good weatherability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to auto parts machinery production technical field, and in particular to air conditioning for automobiles flabellum of a kind of good weatherability and preparation method thereof；Include the raw material of following parts by weight：100 parts of polystyrene, 10 25 parts of binding agent, 15 parts of barium carbonate, 13 parts of titanium nitride, 12 parts of neodymia, 10 30 parts of reinforcing fiber, doping 25 parts, 2 10 parts of additive；The present invention passes through polystyrene, binding agent, barium carbonate, titanium nitride, neodymia, reinforcing fiber, the synergy of doping and additive, so as to obtain a kind of air conditioning for automobiles flabellum material, obtained flabellum still has excellent weather resistance under prolonged working condition, and then the service life and performance of flabellum are ensure that, it is favorably improved the quality of flabellum；In addition, preparation method provided by the invention is simple and easy, production efficiency is high, suitable for industrialized production.
Description
Technical field
The invention belongs to auto parts machinery production technical field, and in particular to a kind of air conditioning for automobiles flabellum of good weatherability and its
Preparation method.
Background technology
Air conditioning for automobiles flabellum is the important component of air conditioning for automobiles, its be driven by motor formed it is distinguished and admirable, with to automobile
Indoor offer is cold/warm wind.At present, air conditioning for automobiles flabellum is typically made up of high polymer material.Because air conditioning for automobiles flabellum is in work
There is the larger temperature difference in the temperature during work, under conditions of such big temperature difference, automobile is empty with the temperature after being stopped
Adjust flabellum that deformation and aging phenomenon often occurs, and then have impact on the service life of air conditioning for automobiles flabellum.
The content of the invention
It is an object of the invention to provide a kind of air conditioning for automobiles flabellum and preparation method thereof, the air conditioning for automobiles flabellum has excellent
Different weatherability, and preparation method is efficiently, simply.
To achieve the above object, the technical solution adopted by the present invention is：
A kind of air conditioning for automobiles flabellum of good weatherability, include the raw material of following parts by weight：100 parts of polystyrene, binding agent 10-
25 parts, barium carbonate 1-5 parts, titanium nitride 1-3 parts, neodymia 1-2 parts, reinforcing fiber 10-30 parts, doping 2-5 parts, additive 2-10
Part.
Further, the air conditioning for automobiles flabellum of described good weatherability, the raw material of following parts by weight is included：Polystyrene
100 parts, binding agent 15-20 parts, barium carbonate 2-4 parts, titanium nitride 1-2 parts, neodymia 1-2 parts, reinforcing fiber 15-25 parts, doping
3-4 parts, additive 3-8 parts.
Further, the air conditioning for automobiles flabellum of described good weatherability, the raw material of following parts by weight is included：Polystyrene
100 parts, 16 parts of binding agent, 3 parts of barium carbonate, 2 parts of titanium nitride, 1 part of neodymia, 20 parts of reinforcing fiber, doping 3 parts, additive 4
Part.
Further, described binding agent is Ludox, Alumina gel, silicon-aluminum sol, boehmite, polyacrylamide
The one or more of powder, xanthans.
Further, described reinforcing fiber in glass fibre, carbon fiber, asbestos fibre, aramid fiber wherein
It is a kind of.
Further, it is described be doped to calcium phosphate, aluminum phosphate, magnesium phosphate, one kind in mixed heavy rare earth oxide or
It is a variety of.
Further, described additive is one in magnesium chloride, nano zine oxide, nano tin dioxide, nano-dolomite
Kind is a variety of.
In addition, the present invention also provides a kind of preparation method of the air conditioning for automobiles flabellum of good weatherability as described above, including
Following steps：
（1）Each raw material is measured respectively by formula；
（2）Each raw material is put into high-speed mixer respectively, is uniformly mixed, rotating speed 300-500r/min, incorporation time
For 10-30 minutes；
（3）Above-mentioned compound is calcined, and calcining heat is 220-240 DEG C, and calcination time is 1-2 hours；
（4）Material after calcining is crushed, 100 mesh sieves is crossed, obtains powder；
（5）Powder is uniformly injected into mould, matched moulds curing 1-5 minutes.
Further, the step（5）In mold temperature be 165-170 DEG C, injection pressure 100-120MPa.
Beneficial effect is caused by above-mentioned technical proposal：
The present invention is by polystyrene, binding agent, barium carbonate, titanium nitride, neodymia, reinforcing fiber, the association of doping and additive
Same-action, so as to obtain a kind of air conditioning for automobiles flabellum material, obtained flabellum still has excellent under prolonged working condition
Different weather resistance, and then the service life and performance of flabellum are ensure that, it is favorably improved the quality of flabellum；In addition, this
It is simple and easy to invent the preparation method provided, production efficiency is high, suitable for industrialized production.
Embodiment
Below by way of 5 embodiments, the present invention is described in further detail；It is it should be appreciated that described herein
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
Embodiment 1：A kind of air conditioning for automobiles flabellum of good weatherability, include the raw material of following parts by weight：Polystyrene 100
Part, 10 parts of xanthans, 5 parts of Ludox, 1 part of barium carbonate, 3 parts of titanium nitride, 1 part of neodymia, 30 parts of glass fibre, 2 parts of calcium phosphate,
10 parts of magnesium chloride.
Its preparation method, comprise the following steps：
（1）Each raw material is measured respectively by formula；
（2）Each raw material is put into high-speed mixer respectively, is uniformly mixed, rotating speed 300-500r/min, incorporation time
For 10-30 minutes；
（3）Above-mentioned compound is calcined, and calcining heat is 220-240 DEG C, and calcination time is 1-2 hours；
（4）Material after calcining is crushed, 100 mesh sieves is crossed, obtains powder；
（5）Powder is uniformly injected into mould, matched moulds curing 1-5 minutes；Wherein, mold temperature is 165-170 DEG C, injection pressure
Power is 100-120MPa.
Embodiment 2：A kind of air conditioning for automobiles flabellum of good weatherability, include the raw material of following parts by weight：Polystyrene 100
Part, 10 parts of Alumina gel, 5 parts of barium carbonate, 1 part of titanium nitride, 2 parts of neodymia, 10 parts of carbon fiber, 5 parts of aluminum phosphate, nano zine oxide 2
Part.
Its preparation method is the same as embodiment 1.
Embodiment 3：A kind of air conditioning for automobiles flabellum of good weatherability, include the raw material of following parts by weight：Polystyrene 100
Part, 15 parts of silicon-aluminum sol, it is 4 parts of barium carbonate, 1 part of titanium nitride, 2 parts of neodymia, 15 parts of asbestos fibre, 4 parts of magnesium phosphate, nano oxidized
3 parts of tin.
Its preparation method is the same as embodiment 1.
Embodiment 4：A kind of air conditioning for automobiles flabellum of good weatherability, include the raw material of following parts by weight：Polystyrene 100
Part, 20 parts of boehmite, 2 parts of barium carbonate, 2 parts of titanium nitride, 1 part of neodymia, 25 parts of aramid fiber, mixed heavy rare earth oxide
3 parts, 8 parts of nano-dolomite.
Its preparation method is the same as embodiment 1.
Embodiment 5：A kind of air conditioning for automobiles flabellum of good weatherability, include the raw material of following parts by weight：Polystyrene 100
Part, 8 parts of polyacrylamide powder, 8 parts of xanthans, 3 parts of barium carbonate, 2 parts of titanium nitride, 1 part of neodymia, 20 parts of carbon fiber, calcium phosphate 1
Part, 2 parts of mixed heavy rare earth oxide, 4 parts of nano tin dioxide.
Its preparation method is the same as embodiment 1.
Claims (9)
1. the air conditioning for automobiles flabellum of a kind of good weatherability, it is characterised in that include the raw material of following parts by weight：Polystyrene
100 parts, binding agent 10-25 parts, barium carbonate 1-5 parts, titanium nitride 1-3 parts, neodymia 1-2 parts, reinforcing fiber 10-30 parts, doping
2-5 parts, additive 2-10 parts.
2. the air conditioning for automobiles flabellum of good weatherability as claimed in claim 1, it is characterised in that include the original of following parts by weight
Material：100 parts of polystyrene, binding agent 15-20 parts, barium carbonate 2-4 parts, titanium nitride 1-2 parts, neodymia 1-2 parts, reinforcing fiber
15-25 parts, doping 3-4 parts, additive 3-8 parts.
3. the air conditioning for automobiles flabellum of good weatherability as claimed in claim 1, it is characterised in that include the original of following parts by weight
Material：100 parts of polystyrene, 16 parts of binding agent, 3 parts of barium carbonate, 2 parts of titanium nitride, 1 part of neodymia, 20 parts of reinforcing fiber, doping 3
Part, 4 parts of additive.
4. the air conditioning for automobiles flabellum of good weatherability as claimed in claim 1, it is characterised in that described binding agent is that silicon is molten
Glue, Alumina gel, silicon-aluminum sol, boehmite, polyacrylamide powder, the one or more of xanthans.
5. the air conditioning for automobiles flabellum of good weatherability as claimed in claim 1, it is characterised in that described reinforcing fiber is selected from glass
One of which in glass fiber, carbon fiber, asbestos fibre, aramid fiber.
6. the air conditioning for automobiles flabellum of good weatherability as claimed in claim 1, it is characterised in that it is described be doped to calcium phosphate,
One or more in aluminum phosphate, magnesium phosphate, mixed heavy rare earth oxide.
7. the air conditioning for automobiles flabellum of good weatherability as claimed in claim 1, it is characterised in that described additive is chlorination
One or more in magnesium, nano zine oxide, nano tin dioxide, nano-dolomite.
8. a kind of preparation method of the air conditioning for automobiles flabellum of the good weatherability any one of claim 1-7, its feature exist
In comprising the following steps：
（1）Each raw material is measured respectively by formula；
（2）Each raw material is put into high-speed mixer respectively, is uniformly mixed, rotating speed 300-500r/min, incorporation time
For 10-30 minutes；
（3）Above-mentioned compound is calcined, and calcining heat is 220-240 DEG C, and calcination time is 1-2 hours；
（4）Material after calcining is crushed, 100 mesh sieves is crossed, obtains powder；
（5）Powder is uniformly injected into mould, matched moulds curing 1-5 minutes.
9. the preparation method of the air conditioning for automobiles flabellum of good weatherability as claimed in claim 8, it is characterised in that the step
（5）In mold temperature be 165-170 DEG C, injection pressure 100-120MPa.