CN107526127A - One kind strengthens tempering filter - Google Patents
One kind strengthens tempering filter Download PDFInfo
- Publication number
- CN107526127A CN107526127A CN201710841567.5A CN201710841567A CN107526127A CN 107526127 A CN107526127 A CN 107526127A CN 201710841567 A CN201710841567 A CN 201710841567A CN 107526127 A CN107526127 A CN 107526127A
- Authority
- CN
- China
- Prior art keywords
- layer
- thickness
- substrate
- film layer
- filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to strengthen tempering filter, and the gradual change ash filter includes substrate and film layer, and the position form that the film layer is attached to substrate is divided into one side and is coated with and double coated, in addition, the film layer of the reinforcement tempering filter uses Al2O3With Ti materials, in the past conventional SiO instead of2With Cr materials, the hardness of filter can either be strengthened, while can also reduce the pollution to environment;In addition, the substrate of filter uses chemically toughened glass, can strengthen when filter falls resistance to falls physical strength.
Description
Technical field
It is particularly a kind of to strengthen tempering filter the present invention relates to a kind of filter being made by new material.
Background technology
The usually said filter arrived, refers to optical physics filter, is a kind of photographic part with light filter effect.
In landscape photography, general most commonly used filter be exactly in grey filter (ND) and middle grey the Graduated Filter (GND).The middle grey filter
(ND) whole eyeglass is grey black, and major function is filtering light, reduces thang-kng amount, the increase time for exposure, is usually used in shooting
Innervation virtualization scene;The top half of middle grey the Graduated Filter (GND) eyeglass is grey black, and the latter half is Transparent color, main
Be used to balance light ratio, the dark portion in picture is rationally exposed with high light portion, suitable for big light than environment, such as clapping
Take the photograph the scene at sunrise and dusk.The filter is made up of substrate and film layer, the material used due to the substrate in common filter
It is all common glass and resin that material is most of, and the resistance to physical strength that falls has been short of, in addition, the film layer of attachment over the substrate surface
It is all SiO that the material of use is most of2With Cr materials, the physical hardness that frequently can lead to filter is relatively low and cause one to environment
Fixed pollution.
The content of the invention
To solve the above problems, it is an object of the invention to provide one kind strengthen tempering filter, it is possible to increase filter it is hard
The pollution of degree and reduction to environment.
Technical scheme is used by the present invention solves its problem:
One kind strengthens tempering filter, it is characterised in that:Including substrate and film layer, the film layer is by Al2O3Electricity Jie of composition
Matter layer and by TiThe metallic diaphragm of composition by being alternately stacked to form, the film layer be attached only to substrate single side surface or
Person is attached to the both side surface of substrate simultaneously.The material of film layer uses Al2O3And TiForm, substitute in the past conventional SiO2And Cr
Material, the hardness and the feature of environmental protection of filter can be improved in the case where meeting to filter light, in addition, being coated with the position mode of film layer
There are two kinds, one kind is that one side is coated with, and another kind is double coated.
Further, the material that the substrate uses is chemically toughened glass.The hardness and intensity of chemically toughened glass are all
Conventional simple glass and resin material are big than ever, and substrate is made using chemically toughened glass material, it is possible to increase filter
The hardness of mirror, improve the resistance to of filter and fall physical strength.
Further, total number of plies of the dielectric layer and metallic diaphragm includes 5-15 layers.Dielectric layer in film layer and
Metallic diaphragm alternates stacking, and total number of plies of dielectric layer and metallic diaphragm is by 5-15 layers.
Further, the first layer in film layer is dielectric layer, and the first layer is attached to the surface of substrate.It is attached to base
The first layer on piece surface is Al2O3The dielectric layer of composition, the second layer are TiThe metallic diaphragm of composition, according to dielectric layer metal
Alternately laminated form of film layer and so on goes out the material composition of other numbers of plies.
Further, the thickness of each layer of different parts is consistent or each layer of thickness is from one end to another
End shows the trend of linear decrease.When the thickness of each layer of different parts in film layer is consistent, the filter
For middle grey filter, major function is filtering light, reduces thang-kng amount, the increase time for exposure, is usually used in shooting dynamic virtualization feelings
Scape;When each layer of thickness in film layer shows the trend of linear decrease from one end to the other end, the filter is middle ash
The Graduated Filter, there is fade effect, be mainly used in balancing light ratio, the dark portion in picture is rationally exposed with high light portion, be applicable
Yu great Guang than environment, such as shooting the scene at sunrise and dusk.
Further, the thickness of the thickest part of the first layer in film layer is 15nm or 20nm.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 5
During layer, the thickness of first layer thickest part is 20nm, and the thickness of second layer thickest part is 2.5nm, third layer thickest part
Thickness is 105.43nm, and the thickness of the 4th layer of thickest part is 5.79nm, and the thickness of layer 5 thickest part is 101.44nm.On
The filter for stating thickness distribution is 0.3 rank, corresponding 1 grade of dim light.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 7
During layer, the thickness of first layer thickest part is 20nm, and the thickness of second layer thickest part is 3.85nm, third layer thickest part
Thickness is 88.27nm, and the thickness of the 4th layer of thickest part is 3.9nm, and the thickness of layer 5 thickest part is 79.04nm, the 6th
The thickness of layer thickest part is 7.6nm, and the thickness of layer 7 thickest part is 77.19nm.The filter of above-mentioned thickness distribution is 0.6
Rank, corresponding 2 grades of dim light.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 7
During layer, the thickness of first layer thickest part is 15nm, and the thickness of second layer thickest part is 3.5nm, third layer thickest part
Thickness is 88.38nm, and the thickness of the 4th layer of thickest part is 2.23nm, and the thickness of layer 5 thickest part is 81.48nm, the 6th
The thickness of layer thickest part is 4.93nm, and the thickness of layer 7 thickest part is 76.46nm.The filter of above-mentioned thickness distribution is
0.9 rank, corresponding 3 grades of dim light.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 7
During layer, the thickness of first layer thickest part is 20nm, and the thickness of second layer thickest part is 5.3nm, third layer thickest part
Thickness is 83.28nm, and the thickness of the 4th layer of thickest part is 12.4nm, and the thickness of layer 5 thickest part is 65.96nm, the 6th
The thickness of layer thickest part is 8.5nm, and the thickness of layer 7 thickest part is 76.65nm.The filter of above-mentioned thickness distribution is 1.2
Rank, corresponding 4 grades of dim light.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 7
During layer, the thickness of first layer thickest part is 20nm, and the thickness of second layer thickest part is 12nm, the thickness of third layer thickest part
Degree is 63.27nm, and the thickness of the 4th layer of thickest part is 16nm, and the thickness of layer 5 thickest part is 81.68nm, and layer 6 is most
The thickness at thick position is 7.85nm, and the thickness of layer 7 thickest part is 77.54nm.The filter of above-mentioned thickness distribution is 1.5 grades
Not, corresponding 5 grades of dim light.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 9
During layer, the thickness of first layer thickest part is 20nm, and the thickness of second layer thickest part is 5.72nm, third layer thickest part
Thickness is 62.65nm, and the thickness of the 4th layer of thickest part is 13.24nm, and the thickness of layer 5 thickest part is 85.82nm, the
The thickness of six layers of thickest part is 12.2nm, and the thickness of layer 7 thickest part is 54.11nm, the thickness of the 8th layer of thickest part
It is 15.44nm, the thickness of the 9th layer of thickest part is 55.07nm.The filter of above-mentioned thickness distribution is 1.8 ranks, corresponding to subtract
6 grades of light.
Further, when film layer is attached only to the single side surface of substrate and total number of plies of dielectric layer and metallic diaphragm is 11
During layer, the thickness of first layer thickest part is 15nm, and the thickness of second layer thickest part is 11.62nm, third layer thickest part
Thickness be 72.49nm, the thickness of the 4th layer of thickest part is 31.84nm, and the thickness of layer 5 thickest part is 76.49nm,
The thickness of layer 6 thickest part is 26.38nm, and the thickness of layer 7 thickest part is 133.54nm, the 8th layer of thickest part
Thickness is 80.22nm, and the thickness of the 9th layer of thickest part is 69.26nm, and the thickness of the tenth layer of thickest part is 19.31nm, the
The thickness of eleventh floor thickest part is 53.17nm.The filter of above-mentioned thickness distribution is 3.0 ranks, corresponding 10 grades of dim light.
Further, when film layer is attached to the both side surface of substrate simultaneously, the thickness of the metallic diaphragm in the film layer of both sides
The half of the corresponding thickness when film layer is attached only to the single side surface of substrate, the thickness of the dielectric layer in the film layer of both sides with
Corresponding consistency of thickness when film layer is attached only to the single side surface of substrate.When double coated, by Ti metal materials in film layer
The half of thickness when the thickness of the metallic diaphragm of composition is coated with for one side, by Al2O3The thickness and list for the dielectric layer that material is formed
It is consistent when face is coated with.
Further, when film layer is attached to the both side surface of substrate simultaneously, the thickness of substrate both sides film layer using substrate as
Center shows symmetrical structure distribution.When double coated, the structure and thickness of the film layer of substrate both sides using substrate as
It is centrally formed symmetrical.
The beneficial effects of the invention are as follows:A kind of reinforcement tempering filter that the present invention uses, film layer is by Al2O3The electricity of composition
Dielectric layer and by TiThe metallic diaphragm of composition is coated with the mode of film layer and is coated with including one side and double by what is be alternately stacked to form
Face is coated with, and the dielectric layer in filter film layer uses Al2O3The conventional SiO of material substitution2Material, due to Al2O3Hardness SiO2
Hardness it is big, so the hardness of filter can be strengthened, in addition, the metallic diaphragm in filter film layer uses TiMaterial substitution Cr materials
Material, due to TiThe feature of environmental protection it is better than Cr, so the pollution to environment can be reduced, improve the feature of environmental protection of filter.
Brief description of the drawings
The invention will be further described with example below in conjunction with the accompanying drawings.
Fig. 1 is a kind of overall construction drawing for the first embodiment for strengthening tempering filter of the present invention;
Fig. 2 is a kind of overall construction drawing for the second embodiment for strengthening tempering filter of the present invention;
Fig. 3 is a kind of film layer structure figure for the first embodiment for strengthening tempering filter of the present invention;
Fig. 4 is a kind of film layer structure figure for the second embodiment for strengthening tempering filter of the present invention.
Embodiment
One kind strengthens tempering filter, including substrate 110 and film layer 120, and the film layer 120 is by Al2O3The dielectric of composition
Layer and by TiFor the metallic diaphragm of composition by what is be alternately stacked to form, the film layer 120 is attached to the surface of substrate 110;Institute
Film layer 120 is stated to be attached only to the single side surface of substrate 110 or be attached to the both side surface of substrate 110 simultaneously;The substrate 110
It is to be made using chemically toughened glass.
Referring to Figures 1 and 2, a kind of overall construction drawing for two kinds of different embodiments for strengthening tempering filter of the present invention.Full
In the case of sufficient filter filtering light, the position form that the film layer 120 is attached to substrate 110 has two kinds, one of which such as Fig. 1
Shown, the film layer 120 is attached only to the single side surface of substrate 110, is coated with for one side;Another is as shown in Fig. 2 the film
Layer 120 is attached to the both side surface of substrate 110 simultaneously, is double coated.The substrate 110 is made using chemically toughened glass
Form, hardness is strong, so that the resistance to physical strength that falls of filter is improved, is different from resin film, resin plate and simple glass
Thin plate.
One kind strengthens tempering filter, and total number of plies of the dielectric layer and metallic diaphragm includes 5-15 layers, and in film layer 120
First layer be dielectric layer, first layer is attached to the surface of substrate 110.In addition, the thickness of each layer of different parts is protected
Hold the trend that consistent or each layer of thickness shows linear decrease from one end to the other end.When dielectric layer and metallic diaphragm
The total number of plies difference when, each layer of thickness in film layer 120 can change, when double coated, in both sides film layer 120
The thickness of metallic diaphragm is the half that thickness is corresponded to when one side is coated with, the thickness and one side of the dielectric layer in both sides film layer 120
Corresponding consistency of thickness when being coated with.Meanwhile when double coated, film layer 120 is attached to the both side surface of substrate 110, base simultaneously
The thickness of the both sides film layer 120 of piece 110 shows symmetrical structure distribution centered on substrate 110.
Reference picture 3 and Fig. 4, a kind of two kinds of differences for strengthening tempering filter of the present invention apply the structure chart of film layer 120 of example;It is described
Film layer 120 is by Al2O3The dielectric layer of composition and by TiThe metallic diaphragm of composition is by being alternately stacked to form, the electricity
Total number of plies of dielectric layer and metallic diaphragm includes 5-15 layers.Dielectric layer in the film layer 120 of the present invention is using Al2O3Material
Material, instead of conventional SiO2Material, due to Al2O3Hardness than SiO2It is big so that the hardness of filter is carried
It is high;In addition, the metallic diaphragm 120 in film layer 120 instead of conventional Cr using the high purity Ti metal material of food-grade
Metal material, because the feature of environmental protection of Ti metal materials is better than Cr metal material, so as to reduce the pollution to environment.
Under the effect for meeting the good filtering light of filter, total number of plies of dielectric layer and metallic diaphragm in the film layer 120 can be with
It is 5-15 layers.As shown in Fig. 3 total number of plies of the dielectric layer in film layer 120 and metallic diaphragm is 7 layers of situation, such as
Shown in Fig. 4 be dielectric layer in film layer 120 and metallic diaphragm total number of plies be 11 layers situation.
In order to meet the effect of filter filtering light, dielectric layer and metallic diaphragm in the film layer 120 have necessarily
Thickness.
When the thickness of each layer of different parts in the film layer 120 is consistent, the filter is middle grey filter
(ND), major function is filtering light, reduces thang-kng amount, the increase time for exposure, is usually used in shooting dynamic virtualization scene;
When the thickness of each layer of the film layer 120 shows the trend of linear decrease from one end to the other end, the filter
Mirror is middle grey the Graduated Filter (GND), has fade effect, is mainly used in balancing light ratio, makes dark portion in picture and high light portion equal
Rationally exposure, suitable for big light than environment, such as shooting the scene at sunrise and dusk.
For middle grey filter (ND) and middle grey the Graduated Filter (GND), the metallic diaphragm and electricity of the middle grey filter (ND) are situated between
The thickness one of the thickest part of corresponding metallic diaphragm and dielectric layer in the thickness of matter layer and middle grey the Graduated Filter (GND)
Cause, shown in list lattice specific as follows, list when one side is coated with film layer 120, total number of plies of dielectric layer and metallic diaphragm is 5
Layer, 7 layers, the thickness distribution situation of 9 layers and 11 layers.The filter be by control gear reach dim light or balance light than effect
Fruit, when each layer of material thickness difference, the rank and gear of filter also accordingly change.The filter typically has 0.3,0.6,
0.9th, 1.2,1.5,1.8,2.4 and 3.0 rank, corresponding dim light 1,2,3,4,5,6,8 and 10 gears, gear difference can cause to expose
The time of light also accordingly changes.
When one side is coated with, total number of plies of dielectric layer and metallic diaphragm is 5 layers of thickness distribution situation such as table 1 below institute
Show, corresponding filter is 0.3 rank, and gear is 1 grade:
The number of plies and material | Thickness |
First layer (Al2O3) | 20 |
The second layer (Ti) | 2.5 |
Third layer (Al2O3) | 105.43 |
4th layer (Ti) | 5.79 |
Layer 5 (Al2O3) | 101.44 |
Table 1
When one side is coated with, the first thickness distribution situation that total number of plies of dielectric layer and metallic diaphragm is 7 layers is as follows
Shown in table 2, corresponding filter is 0.6 rank, and gear is 2 grades:
The number of plies and material | Thickness |
First layer (Al2O3) | 20 |
The second layer (Ti) | 3.85 |
Third layer (Al2O3) | 88.27 |
4th layer (Ti) | 3.9 |
Layer 5 (Al2O3) | 79.04 |
Layer 6 (Ti) | 7.6 |
Layer 7 (Al2O3) | 77.19 |
Table 2
When one side is coated with, second of thickness distribution situation that total number of plies of dielectric layer and metallic diaphragm is 7 layers is as follows
Shown in table 3, corresponding filter is 0.9 rank, and gear is 3 grades:
The number of plies and material | Thickness |
First layer (Al2O3) | 15 |
The second layer (Ti) | 3.5 |
Third layer (Al2O3) | 88.38 |
4th layer (Ti) | 2.23 |
Layer 5 (Al2O3) | 81.48 |
Layer 6 (Ti) | 4.93 |
Layer 7 (Al2O3) | 76.46 |
Table 3
When one side is coated with, the third thickness distribution situation that total number of plies of dielectric layer and metallic diaphragm is 7 layers is as follows
Shown in table 4, corresponding filter is 1.2 ranks, and gear is 4 grades:
The number of plies and material | Thickness |
First layer (Al2O3) | 20 |
The second layer (Ti) | 5.3 |
Third layer (Al2O3) | 83.28 |
4th layer (Ti) | 12.4 |
Layer 5 (Al2O3) | 65.96 |
Layer 6 (Ti) | 8.5 |
Layer 7 (Al2O3) | 76.65 |
Table 4
When one side is coated with, the 4th kind of thickness distribution situation that total number of plies of dielectric layer and metallic diaphragm is 7 layers is as follows
Shown in table 5, corresponding filter is 1.5 ranks, and gear is 5 grades:
The number of plies and material | Thickness |
First layer (Al2O3) | 20 |
The second layer (Ti) | 12 |
Third layer (Al2O3) | 63.37 |
4th layer (Ti) | 16 |
Layer 5 (Al2O3) | 81.68 |
Layer 6 (Ti) | 7.85 |
Layer 7 (Al2O3) | 77.54 |
Table 5
When one side is coated with, total number of plies of dielectric layer and metallic diaphragm is 9 layers of thickness distribution situation such as table 6 below institute
Show, corresponding filter is 1.8 ranks, and gear is 6 grades:
Table 6
When one side is coated with, total number of plies of dielectric layer and metallic diaphragm is 11 layers of thickness distribution situation such as table 7 below institute
Show, corresponding filter is 3.0 ranks, and gear is 10 grades:
The number of plies and material | Thickness |
First layer (Al2O3) | 15 |
The second layer (Ti) | 11.62 |
Third layer (Al2O3) | 72.49 |
4th layer (Ti) | 31.84 |
Layer 5 (Al2O3) | 76.49 |
Layer 6 (Ti) | 26.38 |
Layer 7 (Al2O3) | 133.54 |
8th layer (Ti) | 80.22 |
9th layer of (Al2O3) | 69.26 |
Tenth layer (Ti) | 19.31 |
Eleventh floor (Al2O3) | 53.17 |
Table 7
Above-mentioned table 1-7 thickness unit is nanometer (nm).
Above-mentioned table 1-7 is the situation that one side is coated with, and the first layer in film layer 120 is dielectric layer, and the first layer is attached
In the surface of substrate 110, the second layer is TiThe metallic diaphragm of composition, according to the alternately laminated form of dielectric layer metallic diaphragm
And so on go out other numbers of plies material composition.
When double coated, when the thickness for the metallic diaphragm being made up of in film layer 120 Ti metal materials is changed into one side and is coated with
The half of thickness, by Al2O3The consistency of thickness when thickness for the dielectric layer that material is formed is coated with one side, in addition, substrate 110
The structure and thickness of both sides film layer 120 show symmetrical distribution centered on substrate 110.
It is described above, simply presently preferred embodiments of the present invention, the invention is not limited in above-mentioned embodiment, as long as
It reaches the technique effect of the present invention with identical means, should all belong to protection scope of the present invention.
Claims (10)
1. one kind strengthens tempering filter, it is characterised in that:Including substrate (110) and film layer (120), the film layer (120) be by
Al2O3The dielectric layer of composition and by TiFor the metallic diaphragm of composition by what is be alternately stacked to form, the film layer (120) is only attached
In substrate (110) single side surface or be attached to the both side surfaces of substrate (110) simultaneously.
A kind of 2. reinforcement tempering filter according to claim 1, it is characterised in that:The material that the substrate (110) uses
It is chemically toughened glass.
A kind of 3. reinforcement tempering filter according to claim 1, it is characterised in that:The dielectric layer and metallic diaphragm
Total number of plies includes 5-15 layers.
A kind of 4. reinforcement tempering filter according to claim 3, it is characterised in that:First layer in film layer (120) is electricity
Dielectric layer, the first layer are attached to the surface of substrate (110).
A kind of 5. reinforcement tempering filter according to claim 3, it is characterised in that:The thickness of each layer of different parts is equal
It is consistent or each layer of thickness shows the trend of linear decrease from one end to the other end.
A kind of 6. reinforcement tempering filter according to claim 5, it is characterised in that:First layer in film layer (120) is most
The thickness at thick position is 15nm or 20nm.
A kind of 7. reinforcement tempering filter according to claim 5, it is characterised in that:When film layer (120) is attached only to substrate
(110) when single side surface and total number of plies of dielectric layer and metallic diaphragm is 5 layers, the thickness of first layer thickest part is
20nm, the thickness of second layer thickest part is 2.5nm, and the thickness of third layer thickest part is 105.43nm, the 4th layer of most thick portion
The thickness of position is 5.79nm, and the thickness of layer 5 thickest part is 101.44nm.
A kind of 8. reinforcement tempering filter according to claim 5, it is characterised in that:When film layer (120) is attached only to substrate
(110) when single side surface and total number of plies of dielectric layer and metallic diaphragm is 7 layers, the thickness of first layer thickest part is
20nm, the thickness of second layer thickest part is 3.85nm, and the thickness of third layer thickest part is 88.27nm, the 4th layer of most thick portion
The thickness of position is 3.9nm, and the thickness of layer 5 thickest part is 79.04nm, and the thickness of layer 6 thickest part is 7.6nm, the
The thickness of seven layers of thickest part is 77.19nm.
A kind of 9. reinforcement tempering filter according to claim 5, it is characterised in that:When film layer (120) while it is attached to base
During the both side surface of piece (110), the thickness of the metallic diaphragm in both sides film layer (120) is when film layer (120) is attached only to substrate
(110) half of corresponding thickness during single side surface, the thickness of dielectric layer is with being attached only to substrate when film layer (120)
(110) corresponding consistency of thickness during single side surface.
A kind of 10. reinforcement tempering filter according to claim 5, it is characterised in that:When film layer (120) while it is attached to base
During the both side surface of piece (110), the thickness of substrate (110) both sides film layer (120) is showed symmetrical centered on substrate (110)
Structure distribution.