CN107522997A - A kind of electronic material with good dielectric properties - Google Patents

A kind of electronic material with good dielectric properties Download PDF

Info

Publication number
CN107522997A
CN107522997A CN201710752985.7A CN201710752985A CN107522997A CN 107522997 A CN107522997 A CN 107522997A CN 201710752985 A CN201710752985 A CN 201710752985A CN 107522997 A CN107522997 A CN 107522997A
Authority
CN
China
Prior art keywords
parts
lime glass
electronic material
dielectric properties
calcium soda
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710752985.7A
Other languages
Chinese (zh)
Inventor
陶彩英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Tianrun New Mstar Technology Ltd
Original Assignee
Taicang Tianrun New Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Tianrun New Mstar Technology Ltd filed Critical Taicang Tianrun New Mstar Technology Ltd
Priority to CN201710752985.7A priority Critical patent/CN107522997A/en
Publication of CN107522997A publication Critical patent/CN107522997A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of electronic material with good dielectric properties, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon stone, polybutadiene, steatite ceramic, polyethylene, the content of each component of the electronic material with good dielectric properties are：In parts by weight, 20 30 parts of calcium soda-lime glass, 10 15 parts of polyvinyl chloride, 8 13 parts of melting silicon stone, 21 27 parts of polybutadiene, 14 20 parts of steatite ceramic, 27 parts of polyethylene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1018‑1021.By the above-mentioned means, the electronic material with good dielectric properties of the present invention, can realize electronic device in the effect electrically to be insulated, reach the material for preventing electric current from passing through, there is very high resistivity, do not leak electricity, climb electric or the accident such as puncture.

Description

A kind of electronic material with good dielectric properties
Technical field
The present invention relates to field of electronic materials, more particularly to a kind of electronic material with good dielectric properties.
Background technology
Electronic material refers to the material used in electronic technology and microelectric technique, including dielectric material, semiconductor material Material, piezoelectricity and ferroelectric material, conducting metal and its alloy material, magnetic material, photoelectron material, electromagnetic shielding material and Other associated materials.Electronic material is the material base of modern electronics industry and scientific technological advance, while is sciemtifec and technical sphere again Middle technology-intensive subject.It is related to the multi-subject knowledges such as electronic technology, physical chemistry, solid state physics and Process ba- sis. According to the chemical property of material, can be divided into metal electron material, electronic ceramics, macromolecule electronics, glass dielectric, mica, Gas-insulated medium material, inductor, insulating materials, magnetic material, electronics handware, electrotechnical ceramics material, shielding material, pressure Crystal material, fine Electronic chemical materials, electronics gently build woven material, electronics tin solder material, PCB making materials and other electricity Sub- material.Existing electronic material dielectric properties are bad, and using effect is bad.
The content of the invention
The present invention solves the technical problem of provide a kind of electronic material with good dielectric properties, using effect It is good.
In order to solve the above technical problems, one aspect of the present invention is：There is provided one kind has good dielectricity Can electronic material, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon stone, polybutadiene, steatite ceramic, polyethylene, The content of each component of the electronic material with good dielectric properties is：In parts by weight, calcium soda-lime glass 20-30 parts, poly- Vinyl chloride 10-15 parts, melting silicon stone 8-13 parts, polybutadiene 21-27 parts, steatite ceramic 14-20 parts, polyethylene 2-7 parts, Wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1018-1021。
In a preferred embodiment of the present invention, the content of each component of the electronic material with good dielectric properties For：In parts by weight, 20 parts of calcium soda-lime glass, 15 parts of polyvinyl chloride, 8 parts of melting silicon stone, 27 parts of polybutadiene, steatite ceramic 14 parts, 7 parts of polyethylene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1018。
In a preferred embodiment of the present invention, the content of each component of the electronic material with good dielectric properties For：In parts by weight, 30 parts of calcium soda-lime glass, 10 parts of polyvinyl chloride, 13 parts of melting silicon stone, 21 parts of polybutadiene, steatite ceramic 20 parts, 2 parts of polyethylene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1021。
In a preferred embodiment of the present invention, the content of each component of the electronic material with good dielectric properties For：In parts by weight, 22 parts of calcium soda-lime glass, 14 parts of polyvinyl chloride, 9 parts of melting silicon stone, 26 parts of polybutadiene, steatite ceramic 15 parts, 6 parts of polyethylene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1019。
In a preferred embodiment of the present invention, the content of each component of the electronic material with good dielectric properties For：In parts by weight, 28 parts of calcium soda-lime glass, 11 parts of polyvinyl chloride, 12 parts of melting silicon stone, 22 parts of polybutadiene, steatite ceramic 19 parts, 3 parts of polyethylene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1020。
In a preferred embodiment of the present invention, the content of each component of the electronic material with good dielectric properties For：In parts by weight, 25 parts of calcium soda-lime glass, 13 parts of polyvinyl chloride, 11 parts of melting silicon stone, 24 parts of polybutadiene, steatite ceramic 17 parts, 4 parts of polyethylene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1020。
The beneficial effects of the invention are as follows：The electronic material with good dielectric properties of the present invention, can realize electronics device Part reaches the material for preventing electric current from passing through, has very high resistivity in the effect electrically to be insulated, do not occur to leak electricity, Climb the accident such as electricity or breakdown.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area All other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects Enclose.
Embodiment one：
A kind of electronic material with good dielectric properties is provided, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon Stone, polybutadiene, steatite ceramic, polyethylene.The content of each component of the electronic material with good dielectric properties is：With weight Measure part meter, it is 20 parts of calcium soda-lime glass, 15 parts of polyvinyl chloride, 8 parts of melting silicon stone, 27 parts of polybutadiene, 14 parts of steatite ceramic, poly- 7 parts of ethene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1018。
Embodiment two：
A kind of electronic material with good dielectric properties is provided, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon Stone, polybutadiene, steatite ceramic, polyethylene.The content of each component of the electronic material with good dielectric properties is：With weight Measure part meter, it is 30 parts of calcium soda-lime glass, 10 parts of polyvinyl chloride, 13 parts of melting silicon stone, 21 parts of polybutadiene, 20 parts of steatite ceramic, poly- 2 parts of ethene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1021。
Embodiment three：
A kind of electronic material with good dielectric properties is provided, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon Stone, polybutadiene, steatite ceramic, polyethylene.The content of each component of the electronic material with good dielectric properties is：With weight Measure part meter, it is 22 parts of calcium soda-lime glass, 14 parts of polyvinyl chloride, 9 parts of melting silicon stone, 26 parts of polybutadiene, 15 parts of steatite ceramic, poly- 6 parts of ethene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1019。
Example IV：
A kind of electronic material with good dielectric properties is provided, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon Stone, polybutadiene, steatite ceramic, polyethylene.The content of each component of the electronic material with good dielectric properties is：With weight Measure part meter, it is 28 parts of calcium soda-lime glass, 11 parts of polyvinyl chloride, 12 parts of melting silicon stone, 22 parts of polybutadiene, 19 parts of steatite ceramic, poly- 3 parts of ethene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1020。
Embodiment five：
A kind of electronic material with good dielectric properties is provided, including component have：Calcium soda-lime glass, polyvinyl chloride, melting silicon Stone, polybutadiene, steatite ceramic, polyethylene.The content of each component of the electronic material with good dielectric properties is：With weight Measure part meter, it is 25 parts of calcium soda-lime glass, 13 parts of polyvinyl chloride, 11 parts of melting silicon stone, 24 parts of polybutadiene, 17 parts of steatite ceramic, poly- 4 parts of ethene, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1020。
The beneficial effects of the invention are as follows：
First, the electronic material with good dielectric properties can realize electronic device in the effect electrically to be insulated, Reach the material for preventing electric current from passing through；
2nd, the electronic material with good dielectric properties does not leak electricity with very high resistivity, climbs electricity or breakdown etc. Accident.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks Domain, it is included within the scope of the present invention.

Claims (6)

  1. A kind of 1. electronic material with good dielectric properties, it is characterised in that including component have：Calcium soda-lime glass, polychlorostyrene second Alkene, melting silicon stone, polybutadiene, steatite ceramic, polyethylene, each component of the electronic material with good dielectric properties contain Measure and be：In parts by weight, calcium soda-lime glass 20-30 parts, polyvinyl chloride 10-15 parts, melting silicon stone 8-13 parts, polybutadiene 21-27 parts, steatite ceramic 14-20 parts, polyethylene 2-7 parts, wherein at 20 degrees celsius, the resistivity of the calcium soda-lime glass is 1018-1021。
  2. 2. the electronic material according to claim 1 with good dielectric properties, it is characterised in that described that there is good be situated between The content of each component of the electronic material of electrical property is：In parts by weight, 20 parts of calcium soda-lime glass, 15 parts of polyvinyl chloride, melting 8 parts of silicon stone, 27 parts of polybutadiene, 14 parts of steatite ceramic, 7 parts of polyethylene, wherein at 20 degrees celsius, the calcium soda-lime glass Resistivity is 1018。
  3. 3. the electronic material according to claim 1 with good dielectric properties, it is characterised in that described that there is good be situated between The content of each component of the electronic material of electrical property is：In parts by weight, 30 parts of calcium soda-lime glass, 10 parts of polyvinyl chloride, melting 13 parts of silicon stone, 21 parts of polybutadiene, 20 parts of steatite ceramic, 2 parts of polyethylene, wherein at 20 degrees celsius, the calcium soda-lime glass Resistivity be 1021。
  4. 4. the electronic material according to claim 1 with good dielectric properties, it is characterised in that described that there is good be situated between The content of each component of the electronic material of electrical property is：In parts by weight, 22 parts of calcium soda-lime glass, 14 parts of polyvinyl chloride, melting 9 parts of silicon stone, 26 parts of polybutadiene, 15 parts of steatite ceramic, 6 parts of polyethylene, wherein at 20 degrees celsius, the calcium soda-lime glass Resistivity is 1019。
  5. 5. the electronic material according to claim 1 with good dielectric properties, it is characterised in that described that there is good be situated between The content of each component of the electronic material of electrical property is：In parts by weight, 28 parts of calcium soda-lime glass, 11 parts of polyvinyl chloride, melting 12 parts of silicon stone, 22 parts of polybutadiene, 19 parts of steatite ceramic, 3 parts of polyethylene, wherein at 20 degrees celsius, the calcium soda-lime glass Resistivity be 1020。
  6. 6. the electronic material according to claim 1 with good dielectric properties, it is characterised in that described that there is good be situated between The content of each component of the electronic material of electrical property is：In parts by weight, 25 parts of calcium soda-lime glass, 13 parts of polyvinyl chloride, melting 11 parts of silicon stone, 24 parts of polybutadiene, 17 parts of steatite ceramic, 4 parts of polyethylene, wherein at 20 degrees celsius, the calcium soda-lime glass Resistivity be 1020。
CN201710752985.7A 2017-08-29 2017-08-29 A kind of electronic material with good dielectric properties Pending CN107522997A (en)