CN107511449A - A kind of casting sand type coating - Google Patents
A kind of casting sand type coating Download PDFInfo
- Publication number
- CN107511449A CN107511449A CN201710779562.4A CN201710779562A CN107511449A CN 107511449 A CN107511449 A CN 107511449A CN 201710779562 A CN201710779562 A CN 201710779562A CN 107511449 A CN107511449 A CN 107511449A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- powder
- type coating
- casting sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of casting sand type coating, by following raw material by weight:The parts by weight of zirconium English powder 55 60, the parts by weight of graphite powder 10 20, the parts by weight of magnesite emery dust 10 20, the parts by weight of organobentonite 25, the parts by weight of isopropanol 23, the parts by weight of polyurethane resin 0.5 1, the parts by weight of waterglass 12, the parts by weight of cryolite powder 0.2 0.8;Magnesite emery dust used, can more effectively avoid the interaction between molten steel/silica sand in casting sand type coating of the present invention, after cooling, be easy to casting stripping, and surface roughness are preferable;Binding agent polyurethane resin used has good heat-resisting quantity, and has certain corrosion resistance, and coating is not easily stripped;Cryolite powder used(Na3AIF6)Active NaF, AIF3 etc. are formed at high temperature, and the carbon decomposited to sand mold produces suction-operated, is allowed to not be deposited in cast(ing) surface, prevents cast(ing) surface carbon distribution or scab from producing.
Description
Technical field
The present invention relates to technical field of coatings, specifically a kind of casting sand type coating.
Background technology
The coating of sand casting, mainly for interpenetrating effect between protection sand mold and metal liquid, in casting temperature
Density fireproof coating is formed under degree, simultaneously because the material of sand mold decomposes generation gas at high temperature, coating can prevent from entering
Molten metal body weight, the surface roughness of casting is influenceed, the binding agent commonly used in cast paint is mainly waterglass, due to waterglass
It is cheap, it is easy to use, but when casting more high-accuracy for temperature, coating easily peels off, and the surface roughness of casting is poor,
And cast(ing) surface adheres to one layer of scab being difficult to clean off, increase process costs.
The content of the invention
It is an object of the invention to provide a kind of casting sand type coating, is asked with solve to propose in above-mentioned background technology
Topic.
To achieve the above object, the present invention provides following technical scheme:
A kind of casting sand type coating, by following raw material by weight:Zirconium English powder 55-60 parts by weight, graphite powder 10-
20 parts by weight, magnesite emery dust 10-20 parts by weight, organobentonite 2-5 parts by weight, isopropanol 2-3 parts by weight, polyurethane resin
0.5-1 parts by weight, waterglass 1-2 parts by weight, cryolite powder 0.2-0.8 parts by weight;
As the further scheme of the present invention:The casting sand type is preferably that following preparation method obtains with coating:
S1, by the parts by weight of zirconium English powder 55, the parts by weight of graphite powder 15, the parts by weight of magnesite emery dust 20, the parts by weight of organobentonite 5,
The parts by weight of cryolite powder 0.5 are ground in grinder;
After S2, grinding, added in grounds travel by material water volume ratio 1:10 water, sequentially add the parts by weight of isopropanol 3, poly- ammonia
The parts by weight of ester resin 0.5, the parts by weight of waterglass 1, carry out centrifugal mixer.
After S3, coating make, uniformly sand mold is brushed, or spraying, coated and dried is carried out in the baker of constant temperature, is followed
Ring is in triplicate.
As the further scheme of the present invention:The centrifugal mixer condition is 1500r/min, time 30min.
As the further scheme of the present invention:The temperature range of the coated and dried constant temperature be 40 DEG C -60 DEG C, preferably 50
℃。
Compared with prior art, the beneficial effects of the invention are as follows:Magnesite used in casting sand type coating of the present invention
Emery dust, the interaction between molten steel/silica sand can be more effectively avoided, after cooling, be easy to casting stripping, and cast(ing) surface is thick
Rugosity is preferable;Binding agent polyurethane resin used has good heat-resisting quantity, and has certain corrosion resistance, and coating is not easy
Peel off;Cryolite powder used(Na3AIF6)Active NaF, AIF3 etc. are formed at high temperature, and the carbon decomposited to sand mold produces absorption
Effect, is allowed to not be deposited in cast(ing) surface, prevents cast(ing) surface carbon distribution or scab from producing.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
Embodiment 1
A kind of casting sand type coating, by following raw material by weight:The parts by weight of zirconium English powder 55, the weight of graphite powder 15
Part, the parts by weight of magnesite emery dust 20, the parts by weight of organobentonite 5, the parts by weight of isopropanol 3, the parts by weight of polyurethane resin 0.5, water
The parts by weight of glass 1, the parts by weight of cryolite powder 0.5;
Preparation method is as follows:
S1, by the parts by weight of zirconium English powder 55, the parts by weight of graphite powder 15, the parts by weight of magnesite emery dust 20, the parts by weight of organobentonite 5,
The parts by weight of cryolite powder 0.5 are ground in grinder;
After S2, grinding, added in grounds travel by material water volume ratio 1:10 water, sequentially add the parts by weight of isopropanol 3, poly- ammonia
The parts by weight of ester resin 0.5, the parts by weight of waterglass 1, carry out centrifugal mixer.
After S3, coating make, uniformly sand mold is brushed, or spraying, coated and dried is carried out in the baker of constant temperature, is followed
Ring is in triplicate.
The centrifugal mixer condition is 1500r/min, time 30min.
The temperature range of the coated and dried constant temperature is 40 DEG C -60 DEG C, preferably 50 DEG C.
Embodiment 2
A kind of casting sand type coating, by following raw material by weight:The parts by weight of zirconium English powder 60, the weight of graphite powder 14
Part, the parts by weight of magnesite emery dust 16, the parts by weight of organobentonite 4.5, the parts by weight of isopropanol 2.5, the weight of polyurethane resin 0.7
Part, the parts by weight of waterglass 1.5, the parts by weight of cryolite powder 0.8;
Preparation method is as follows:
S1, the parts by weight of zirconium English powder 60, the parts by weight of graphite powder 14, the parts by weight of magnesite emery dust 16, the parts by weight of organobentonite 4.5,
The parts by weight of cryolite powder 0.8, grind in grinder;
After S2, grinding, added in grounds travel by material water volume ratio 1:10 water, sequentially add the parts by weight of isopropanol 2.5, gather
The parts by weight of urethane resin 0.7, the parts by weight of waterglass 1.5, carry out centrifugal mixer.
After S3, coating make, uniformly sand mold is brushed, or spraying, coated and dried is carried out in the baker of constant temperature, is followed
Ring is in triplicate.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.Any mark in claim should not be considered as to the involved claim of limitation.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (3)
1. a kind of casting sand type coating, it is characterised in that by following raw material by weight:Zirconium English powder 55-60 weights
Measure part, graphite powder 10-20 parts by weight, magnesite emery dust 10-20 parts by weight, organobentonite 2-5 parts by weight, isopropanol 2-3 weights
Measure part, polyurethane resin 0.5-1 parts by weight, waterglass 1-2 parts by weight, cryolite powder 0.2-0.8 parts by weight;
A kind of casting sand type coating according to claim 1, it is characterised in that be preferably that following preparation method obtains:
S1, by the parts by weight of zirconium English powder 55, the parts by weight of graphite powder 15, the parts by weight of magnesite emery dust 20, the parts by weight of organobentonite 5,
The parts by weight of cryolite powder 0.5 are ground in grinder;
After S2, grinding, added in grounds travel by material water volume ratio 1:10 water, sequentially add the parts by weight of isopropanol 3, poly- ammonia
The parts by weight of ester resin 0.5, the parts by weight of waterglass 1, carry out centrifugal mixer;
After S3, coating make, uniformly sand mold is brushed, or spraying, coated and dried, circulation weight are carried out in the baker of constant temperature
Again three times.
2. a kind of casting sand type coating according to claim 1, it is characterised in that the centrifugal mixer condition is
1500r/min, time 30min.
3. a kind of casting sand type coating according to claim 1 or 2, it is characterised in that the coated and dried constant temperature
Temperature range is 40 DEG C -60 DEG C, preferably 50 DEG C.