CN107503220A - Desiccant wheel composite fibre paper - Google Patents
Desiccant wheel composite fibre paper Download PDFInfo
- Publication number
- CN107503220A CN107503220A CN201710783784.3A CN201710783784A CN107503220A CN 107503220 A CN107503220 A CN 107503220A CN 201710783784 A CN201710783784 A CN 201710783784A CN 107503220 A CN107503220 A CN 107503220A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite fibre
- paper
- desiccant wheel
- fibre paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses each combination of a kind of desiccant wheel composite fibre paper, including following weight fraction:18 25 parts of alumina silicate fibre;22 31 parts of polyolefine fiber;21 28 parts of vinal;19 30 parts of graphite fibre;25 33 parts of wood pulp;23 30 parts of straw pulp;7 10 parts of sodium hydroxide;57 parts of calcium sulfate;6 12 parts of paraffin.Composite fibre paper of the present invention have high pliability, anti-tortuosity height, high temperature resistant, it is tear-resistant the characteristics of.
Description
Technical field
The present invention relates to desiccant wheel manufacturing field, more particularly to a kind of desiccant wheel composite fibre paper.
Background technology
Fibrous paper is a kind of solid insulating material used in electrician.There are plant fiber paper and synthetic fibre paper, generally warp
It is made after varnished insulation liquid or insulated paint and glue.Density (or tightness) scope of fibrous paper is wide, and air tightness can differ
1000 times;Thickness is as thin as several microns, thick up to 0.5 cm.By the regulation to raw material and papermaking process, can obtain absolutely
The various insulating papers needed in edge technology, such as the dipping paper for manufacturing the laminate of transformer, rod and tube cylinder insulate;With
In manufacture resin-bonded paper condenser type bushing center and the winding paper of general lamination socket;For manufacturing the capacitor of capacitor element
Paper;For manufacturing the cable paper of oil-impregnated paper insulation cable;And for manufacturing the high-temperature fibre paper of motor slot insulation.
Desiccant wheel is the core component of dehumidifier, and its primary raw material is also fibrous paper, still, the fibrous paper of prior art
The problem of single product, poor performance often be present.
The content of the invention
Goal of the invention:In view of the shortcomings of the prior art with defect, the present invention provide a kind of pliability is high, anti-tortuosity is high,
High temperature resistant, tear-resistant desiccant wheel composite fibre paper.
Technical scheme:Desiccant wheel of the present invention composite fibre paper, include each combination of following weight fraction:
Preferably, desiccant wheel composite fibre paper, each combination of following weight fraction is included:
Preferably, desiccant wheel composite fibre paper, each combination of following weight fraction is included:
Wherein, described desiccant wheel composite fibre paper, in addition to rosin 3-6 parts.Preferably include 5 parts of rosin.
Beneficial effect:Compared with prior art, the present invention has following remarkable advantage:The composite fibre paper of the present invention uses
The fibers such as alumina silicate, polyolefin, polyvinyl alcohol, graphite are primary raw material, add wood pulp and straw pulp, increase overall fibrous paper
Pliability and anti-tortuosity.The present invention is using sodium hydroxide, calcium sulfate as auxiliary agent, using paraffin, rosin as sizing agent, increases whole fine
Tie up the heat-resisting ability of paper and tear-resistant intensity.
Embodiment
With reference to embodiment, the present invention will be further described.
Embodiment 1:
The desiccant wheel of the present embodiment composite fibre paper, include each combination of following weight fraction:Alumina silicate fibre 18
Part;22 parts of polyolefine fiber;21 parts of vinal;19 parts of graphite fibre;25 parts of wood pulp;23 parts of straw pulp;Sodium hydroxide 7
Part;5 parts of calcium sulfate;6 parts of paraffin.
Embodiment 2:
The desiccant wheel of the present embodiment composite fibre paper, include each combination of following weight fraction:Alumina silicate fibre 25
Part;31 parts of polyolefine fiber;28 parts of vinal;30 parts of graphite fibre;33 parts of wood pulp;30 parts of straw pulp;Sodium hydroxide 10
Part;7 parts of calcium sulfate;12 parts of paraffin.
Embodiment 3:
The desiccant wheel of the present embodiment composite fibre paper, include each combination of following weight fraction:Alumina silicate fibre 20
Part;25 parts of polyolefine fiber;23 parts of vinal;27 parts of graphite fibre;29 parts of wood pulp;27 parts of straw pulp;Sodium hydroxide 8
Part;6 parts of calcium sulfate;9 parts of paraffin.
Embodiment 4:
The desiccant wheel of the present embodiment composite fibre paper, include each combination of following weight fraction:Alumina silicate fibre 22
Part;27 parts of polyolefine fiber;25 parts of vinal;29 parts of graphite fibre;31 parts of wood pulp;29 parts of straw pulp;Sodium hydroxide 10
Part;7 parts of calcium sulfate;10 parts of paraffin.
Embodiment 5:
Desiccant wheel composite fibre paper, include each combination of following weight fraction:21 parts of alumina silicate fibre;Polyolefin is fine
26 parts of dimension;24 parts of vinal;28 parts of graphite fibre;30 parts of wood pulp;28 parts of straw pulp;9 parts of sodium hydroxide;Calcium sulfate 6.5
Part;9.5 parts of paraffin.
Embodiment 6:
Desiccant wheel composite fibre paper, include each combination of following weight fraction:21 parts of alumina silicate fibre;Polyolefin is fine
26 parts of dimension;24 parts of vinal;28 parts of graphite fibre;30 parts of wood pulp;28 parts of straw pulp;9 parts of sodium hydroxide;Calcium sulfate 6.5
Part;9.5 parts of paraffin;5 parts of rosin.
Claims (5)
1. desiccant wheel composite fibre paper, it is characterised in that:Each combination including following weight fraction:
2. desiccant wheel according to claim 1 composite fibre paper, it is characterised in that:Including each of following weight fraction
Combination:
3. desiccant wheel according to claim 2 composite fibre paper, it is characterised in that:Including each of following weight fraction
Combination:
4. desiccant wheel according to claim 1 composite fibre paper, it is characterised in that:Also include rosin 3-6 parts.
5. desiccant wheel according to claim 4 composite fibre paper, it is characterised in that:Also include 5 parts of rosin.