CN107503153A - A kind of use for synthetic leather corium skin light processing agent and preparation method thereof - Google Patents
A kind of use for synthetic leather corium skin light processing agent and preparation method thereof Download PDFInfo
- Publication number
- CN107503153A CN107503153A CN201710710813.3A CN201710710813A CN107503153A CN 107503153 A CN107503153 A CN 107503153A CN 201710710813 A CN201710710813 A CN 201710710813A CN 107503153 A CN107503153 A CN 107503153A
- Authority
- CN
- China
- Prior art keywords
- parts
- processing agent
- light processing
- synthetic leather
- corium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of use for synthetic leather corium skin light processing agent, in terms of mass parts, wherein including 25~27 parts of modified polyurethane resin, 15~17 parts of acrylic resin, 14~16 parts of butyl ether, 14~16 parts of ethyl ester, 14~16 parts of butyl ester, 5~8 parts of silica flatting silica, 2~4 parts of corium wax, 1~3 part of erucyl amide, 1~2 part of dispersant, 1~3 part of polymethylphenyl siloxane fluid.A kind of preparation method of use for synthetic leather corium skin light processing agent is also disclosed, including：It will grind and filter after partially modified polyurethane resin, acrylic resin, butyl ether, ethyl ester, butyl ester, silica flatting silica, dispersant stirring by formula；Special corium wax, erucyl amide, polymethylphenyl siloxane fluid is added afterwards to stir；Remaining modified polyurethane resin is added afterwards to stir to obtain use for synthetic leather corium skin light processing agent.It is good to form corium skin light processing agent temperature tolerance, can be embossed, available for high solid processing, leather surface leather effect is good after polishing, and feel is unique, and gloss is naturally, color clarification, and waxy luster sense is good, and resultant effect is excellent.
Description
Technical field
The present invention relates to a kind of use for synthetic leather corium skin light processing agent, the more particularly to conjunction applied to synthetic leather rear section technique
Finished leather corium skin light processing agent, belongs to innovative back segment material.The invention further relates to a kind of use for synthetic leather corium skin light processing
The preparation method of agent.
Background technology
Synthetic leather surface conditioning agent can according to the classification of product carry out top finishing, so as to improve the brightness of synthetic leather,
Color and luster and feel.The raising required however as consumer leather surface color and luster, feel, will not only increase synthetic leather
Sense of touch, also to ensure brightness and the color on synthetic leather surface etc..
After leather surface is sprayed to, leather effect is bad for existing skin light processing agent, puckery, the synthetic leather surface colour of feel
Pool is not clear enough, natural, vivid, and therefore, existing epidermis light processing agent can not meet consumer to synthetic leather surface
The increasingly increased requirement of corium feel, brightness and color and luster, so synthetic leather sense of touch can both be improved by being badly in need of one kind, and can improves synthesis
Remove from office feel, color and luster and the skin light processing agent of brightness.
The content of the invention
In order to solve the above problems, it is an object of the invention to provide a kind of use for synthetic leather corium skin light processing agent and preparation side
Method.
The invention particularly discloses a kind of use for synthetic leather corium skin light processing agent, in terms of mass parts, wherein comprising modified poly-
25~27 parts of urethane resin, 15~17 parts of acrylic resin, 14~16 parts of butyl ether, 14~16 parts of ethyl ester, 14~16 parts of butyl ester, two
5~8 parts of silica flatting silica, special 2~4 parts of corium wax, 1~3 part of erucyl amide, 1~2 part of dispersant, polymethylphenyl siloxane fluid 1~
3 parts.
Further, in terms of mass parts, wherein including 25 parts of modified polyurethane resin, 16 parts of acrylic resin, butyl ether 15
Part, 15 parts of ethyl ester, 15 parts of butyl ester, 7 parts of silica flatting silica, 3 parts of corium wax, 2 parts of erucyl amide, 1 part of dispersant, benzyl
1 part of silicone oil.
The invention further particularly discloses a kind of preparation method of use for synthetic leather corium skin light processing agent, it is characterised in that bag
Include following steps：
Step 1：It is formulated more than by partially modified polyurethane resin, acrylic resin, butyl ether, ethyl ester, butyl ester, titanium dioxide
Mixture is filtered to obtain in grinding after silicon flatting silica, dispersant stirring；
Step 2：Special corium wax, erucyl amide, polymethylphenyl siloxane fluid are added to the mixture obtained by step 1 to stir
Mixture；
Step 3：To the mixture obtained by step 2 add remaining modified polyurethane resin stir use for synthetic leather is true
Skin skin light processing agent.
Further, raw material proportioning is calculated as with mass parts in step 1：18~25 parts of the partially modified polyurethane resin,
15~17 parts of the acrylic resin, 14~16 parts of the butyl ether, 14~16 parts of the ethyl ester, 14~16 parts of the butyl ester, institute
State 5~8 parts of silica flatting silica, 1~2 part of the dispersant.
Further, raw material proportioning is calculated as with mass parts in step 2：2~4 parts of the special corium wax, the erucic acid acyl
1~3 part of amine, 1~3 part of the polymethylphenyl siloxane fluid.
Further, remaining modified polyurethane resin described in step 3 is 2~9 parts, and partially modified described in step 1
The overall control of remaining modified polyurethane resin is at 25~27 parts described in polyurethane and step 2.
Further, raw material proportioning is calculated as with mass parts in step 1：19 parts of the partially modified polyurethane resin, it is described
16 parts of acrylic resin, 15 parts of the butyl ether, 15 parts of the ethyl ester, 15 parts of the butyl ester, 7 parts of the silica flatting silica,
1 part of the dispersant.
Further, raw material proportioning is calculated as with mass parts in step 2：3 parts of the corium wax, 2 parts of the erucyl amide, institute
State 1 part of polymethylphenyl siloxane fluid.
Further, remaining modified polyurethane resin described in step 3 is 6 parts.
Compared with prior art, the advantages of the present invention：
1st, form corium skin light processing agent each component is mutually coordinated, collective effect, temperature tolerance is good, can be embossed, it is also possible to
In high solid processing, leather surface leather effect is good after polishing, and feel is unique, and the leather gloss made with such a inorganic agent is naturally, color and luster is clear
Clear, waxy luster sense is good, and leather effect is strong, and resultant effect is excellent；
2nd, the corium skin light processing agent is applied on existing synthetic leather production line, technique is simple, is the one of back segment printing
Kind new material need not change production equipment increase cost.
Brief description of the drawings
Fig. 1 is the schematic flow sheet of the preparation method of use for synthetic leather corium skin light processing agent of the present invention.
Embodiment
Below by embodiment, the present invention is described in further detail：
Embodiment 1：
Use for synthetic leather corium skin light processing agent is made up of the following raw material component：On the basis of the gross weight of resin, it, which is included, changes
25 parts of polyurethane resin of property, 16 parts of acrylic resin, 15 parts of butyl ether, 15 parts of ethyl ester, 15 parts of butyl ester, 7 parts of silica flatting silica,
Special 3 parts of corium wax, 2 parts of erucyl amide, 1 part of dispersant, 1 part of polymethylphenyl siloxane fluid.
The use for synthetic leather corium skin light processing agent is waxy luster polishing agent.
The production technology of the smooth polishing agent of polyurethane of the present invention is as follows：
Step 1：By formula by partially modified 19 parts of polyurethane resin, 16 parts of acrylic resin, 15 parts of butyl ether, ethyl ester 15
Mixture is filtered to obtain in grinding after 1 part of part, 15 parts of butyl ester, 7 parts of silica flatting silica, dispersant stirring；
Step 2：Mixture obtained by step 1 is added into 1 part of 3 parts of corium wax, 2 parts of erucyl amide, polymethylphenyl siloxane fluid stirring
It is uniform to obtain mixture；
Step 3：Mixture obtained by step 2 is added into remaining 6 parts of modified polyurethane resin to stir to obtain synthetic leather
With corium skin light processing agent.
Embodiment 2：
Use for synthetic leather corium skin light processing agent is made up of the following raw material component：On the basis of the gross weight of resin, it, which is included, changes
25 parts of polyurethane resin of property, 17 parts of acrylic resin, 16 parts of butyl ether, 16 parts of ethyl ester, 16 parts of butyl ester, 8 parts of silica flatting silica,
4 parts of corium wax, 3 parts of erucyl amide, 2 parts of dispersant, 3 parts of polymethylphenyl siloxane fluid.
The use for synthetic leather corium skin light processing agent is waxy luster polishing agent.
The production technology of use for synthetic leather corium skin light processing agent of the present invention is as follows：
Step 1：By formula by partially modified 19 parts of polyurethane resin, 17 parts of acrylic resin, 16 parts of butyl ether, ethyl ester 16
Mixture is filtered to obtain in grinding after 2 parts of part, 16 parts of butyl ester, 8 parts of silica flatting silica, dispersant stirrings；
Step 2：Mixture obtained by step 1 is added into 3 parts of 4 parts of corium wax, 3 parts of erucyl amide, polymethylphenyl siloxane fluid stirrings
It is uniform to obtain mixture；
Step 3：Mixture obtained by step 2 is added into remaining 6 parts of modified polyurethane resin to stir to obtain synthetic leather
With corium skin light processing agent.
Embodiment 3：
Use for synthetic leather corium skin light processing agent is made up of the following raw material component：On the basis of the gross weight of resin, it, which is included, changes
27 parts of polyurethane resin of property, 15 parts of acrylic resin, 14 parts of butyl ether, 14 parts of ethyl ester, 14 parts of butyl ester, 5 parts of silica flatting silica,
2 parts of corium wax, 1 part of erucyl amide, 1 part of dispersant, 1 part of polymethylphenyl siloxane fluid.
The use for synthetic leather corium skin light processing agent is waxy luster polishing agent.
The production technology of use for synthetic leather corium skin light processing agent of the present invention is as follows：
Step 1：By formula by partially modified 25 parts of polyurethane resin, 15 parts of acrylic resin, 14 parts of butyl ether, ethyl ester 14
Mixture is filtered to obtain in grinding after 1 part of part, 14 parts of butyl ester, 5 parts of silica flatting silica, dispersant stirring；
Step 2：Mixture obtained by step 1 is added into 1 part of 2 parts of corium wax, 1 part of erucyl amide, polymethylphenyl siloxane fluid stirring
It is uniform to obtain mixture；
Step 3：Mixture obtained by step 2 is added into remaining 2 parts of modified polyurethane resin to stir to obtain synthetic leather
With corium skin light processing agent.
Embodiment 4：
Use for synthetic leather corium skin light processing agent is made up of the following raw material component：On the basis of the gross weight of resin, it, which is included, changes
26 parts of polyurethane resin of property, 17 parts of acrylic resin, 14 parts of butyl ether, 16 parts of ethyl ester, 14 parts of butyl ester, 8 parts of silica flatting silica,
1 part of corium wax, 3 parts of erucyl amide, 1 part of dispersant, 3 parts of polymethylphenyl siloxane fluid.
The use for synthetic leather corium skin light processing agent is waxy luster polishing agent.
The production technology of use for synthetic leather corium skin light processing agent of the present invention is as follows：
Step 1：By formula by partially modified 18 parts of polyurethane resin, 17 parts of acrylic resin, 14 parts of butyl ether, ethyl ester 16
Mixture is filtered to obtain in grinding after 1 part of part, 14 parts of butyl ester, 8 parts of silica flatting silica, dispersant stirring；
Step 2：Mixture obtained by step 1 is added into 3 parts of 1 part of corium wax, 3 parts of erucyl amide, polymethylphenyl siloxane fluid stirrings
It is uniform to obtain mixture；
Step 3：Mixture obtained by step 2 is added into remaining 8 parts of modified polyurethane resin to stir to obtain synthetic leather
With corium skin light processing agent.
The technical performance index of above-mentioned polishing agent is shown in Table 1, and wherein embodiment 1 is most preferred embodiment, its obtained conjunction
Finished leather is substantially better than other embodiment with each performance indications of corium skin light processing agent, and compared with other embodiment, it makes
There is more preferable gloss, color and luster, cured light sensation and stability etc. during.
Table 1
| Project | Index |
| PH value | 5~7 |
| Outward appearance | Micro- yellow thick liquid |
| Viscosity (cps/25 DEG C) | 1500~2500 |
| Stability | Without precipitation, it is non-discolouring |
| Dicyandiamide solution | Esters |
| Solid content (%) | 35±1 |
Embodiment described above only expresses embodiments of the present invention, and its description is more specific and detailed, but can not
Therefore it is interpreted as the limitation to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art,
Without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection model of the present invention
Enclose.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (9)
- A kind of 1. use for synthetic leather corium skin light processing agent, it is characterised in that：In terms of mass parts, wherein including modified polyurethane resin 25~27 parts, 15~17 parts of acrylic resin, 14~16 parts of butyl ether, 14~16 parts of ethyl ester, 14~16 parts of butyl ester, silica disappears 5~8 parts of light powder, 2~4 parts of corium wax, 1~3 part of erucyl amide, 1~2 part of dispersant, 1~3 part of polymethylphenyl siloxane fluid.
- 2. use for synthetic leather corium skin light processing agent as claimed in claim 1, it is characterised in that in terms of mass parts, wherein including 25 parts of modified polyurethane resin, 16 parts of acrylic resin, 15 parts of butyl ether, 15 parts of ethyl ester, 15 parts of butyl ester, silica flatting silica 7 Part, 3 parts of corium wax, 2 parts of erucyl amide, 1 part of dispersant, 1 part of polymethylphenyl siloxane fluid.
- 3. a kind of preparation method of use for synthetic leather corium skin light processing agent, it is characterised in that comprise the following steps：Step 1：By claim 1 or 2 formula by partially modified polyurethane resin, acrylic resin, butyl ether, ethyl ester, butyl ester, Mixture is filtered to obtain in grinding after silica flatting silica, dispersant stirring；Step 2：Corium wax, erucyl amide, polymethylphenyl siloxane fluid are added to the mixture obtained by step 1 to stir to obtain mixture；Step 3：Remaining modified polyurethane resin is added to the mixture obtained by step 2 to stir to obtain use for synthetic leather corium skin Light processing agent.
- 4. the preparation method of use for synthetic leather corium skin light processing agent as claimed in claim 3, it is characterised in that step 1 Central Plains Material proportioning is calculated as with mass parts：18~25 parts of the partially modified polyurethane resin, 15~17 parts of the acrylic resin are described 14~16 parts of butyl ether, 14~16 parts of the ethyl ester, 14~16 parts of the butyl ester, 5~8 parts of the silica flatting silica are described 1~2 part of dispersant.
- 5. the preparation method of use for synthetic leather corium skin light processing agent as claimed in claim 4, it is characterised in that step 2 Central Plains Material proportioning is calculated as with mass parts：2~4 parts of the corium wax, 1~3 part of the erucyl amide, 1~3 part of the polymethylphenyl siloxane fluid.
- 6. the preparation method of use for synthetic leather corium skin light processing agent as claimed in claim 5, it is characterised in that institute in step 3 Remaining modified polyurethane resin is stated as 2~9 parts, and it is remaining modified described in partially modified polyurethane described in step 1 and step 2 The overall control of polyurethane resin is at 25~27 parts.
- 7. the preparation method of use for synthetic leather corium skin light processing agent as claimed in claim 3, it is characterised in that step 1 Central Plains Material proportioning is calculated as with mass parts：19 parts of the partially modified polyurethane resin, 16 parts of the acrylic resin, the butyl ether 15 Part, 15 parts of the ethyl ester, 15 parts of the butyl ester, 7 parts of the silica flatting silica, 1 part of the dispersant.
- 8. the preparation method of use for synthetic leather corium skin light processing agent as claimed in claim 7, it is characterised in that step 2 Central Plains Material proportioning is calculated as with mass parts：3 parts of the corium wax, 2 parts of the erucyl amide, 1 part of the polymethylphenyl siloxane fluid.
- 9. the preparation method of use for synthetic leather corium skin light processing agent as claimed in claim 8, it is characterised in that institute in step 3 Remaining modified polyurethane resin is stated as 6 parts.