CN107502224A - A kind of corrugated board production adhesive - Google Patents
A kind of corrugated board production adhesive Download PDFInfo
- Publication number
- CN107502224A CN107502224A CN201710694854.8A CN201710694854A CN107502224A CN 107502224 A CN107502224 A CN 107502224A CN 201710694854 A CN201710694854 A CN 201710694854A CN 107502224 A CN107502224 A CN 107502224A
- Authority
- CN
- China
- Prior art keywords
- stirred
- corrugated board
- starch
- stirred tanks
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of corrugated board production adhesive, comprise the following steps：(1) 200kg water, 25kg starch, the 6kg of transfer matic special drying agent 4, the 6kg of caustic soda 5 are sequentially added into A stirred tanks, 35 50min are reacted after stirring；(2) 400kg water, 250kg starch, 16kg resins adhesive, the 5kg of borax 3 are sequentially added into B stirred tanks, 15 25min are reacted after stirring；(3) mixed liquor in A stirred tanks is poured slowly into B stirred tanks, stirs 20 40min.The corrugated board production adhesive of the present invention is by using with bonding jail, fast drying, paper board strength height, bonding low cost and other advantages.
Description
Technical field
The present invention relates to corrugated board production technique, specifically a kind of corrugated board production adhesive.
Background technology
The packing case that corrugated board makes is widely used in life, the every field of industry.Corrugated case is by corrugated board
It is made, the quality of corrugated board directly affects corrugated case quality.As corrugated case packaging market develops, to waterproof corrugated paper
Case demand is increasing, and the water proofing property and moisture resistance of common corrugated case are all poor, it is impossible to meet waterproofing packing.
The content of the invention
The invention provides a kind of corrugated board production adhesive, to solve above-mentioned technical problem.
A kind of corrugated board production adhesive, comprises the following steps：
(1) 200kg water, 25kg starch, transfer matic special drying agent 4-6kg, caustic soda 5- are sequentially added into A stirred tanks
6kg, react 35-50min after stirring；
(2) 400kg water, 250kg starch, 16kg resins adhesive, borax 3-5kg are sequentially added into B stirred tanks, is stirred
Reaction 15-25min after uniformly；
(3) mixed liquor in A stirred tanks is poured slowly into B stirred tanks, stirs 20-40min.
Preferably, starch uses wheaten starch or potato starch or sweet potato starch in the step (1).
Preferably, it is stirred in the step (1) with 400 turns/min rotating speed.
Preferably, it is stirred in the step (2) with 450 turns/min rotating speed.
Preferably, it is stirred in the step (3) with 450 turns/min rotating speed.
Beneficial effects of the present invention：
The beneficial effects of the invention are as follows：The corrugated board production adhesive of the present invention is by using firm, dry with bonding
Dry fast, paper board strength height, bonding low cost and other advantages.
Embodiment
Embodiments of the invention are described in detail below, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Below by way of specific embodiment, the present invention will be described in detail.
Corrugated board production provided by the invention with bonding specific implementation technical scheme be：
Embodiment 1
(1) 200kg water, 25kg starch, transfer matic special drying agent 4kg, caustic soda 5kg are sequentially added into A stirred tanks, with
400 turns/min rotating speed reacts 35min after stirring；
(2) 400kg water, 250kg starch, 16kg resins adhesive, borax 3kg are sequentially added into B stirred tanks, with 450
Turn/min rotating speed be stirred uniformly after reaction 15min；
(3) mixed liquor in A stirred tanks is poured slowly into B stirred tanks, 20min is stirred with 400 turns/min rotating speed.
Embodiment 2
(1) 200kg water, 25kg starch, transfer matic special drying agent 5kg, caustic soda 5.5kg are sequentially added into A stirred tanks,
45min is reacted after being stirred with 400 turns/min rotating speed；
(2) 400kg water, 250kg starch, 16kg resins adhesive, borax 4kg are sequentially added into B stirred tanks, with 450
Turn/min rotating speed be stirred uniformly after reaction 20min；
(3) mixed liquor in A stirred tanks is poured slowly into B stirred tanks, 30min is stirred with 400 turns/min rotating speed.
Embodiment 3
(1) 200kg water, 25kg starch, transfer matic special drying agent 6kg, caustic soda 6kg are sequentially added into A stirred tanks, with
400 turns/min rotating speed reacts 50min after stirring；
(2) 400kg water, 250kg starch, 16kg resins adhesive, borax 5kg are sequentially added into B stirred tanks, with 450
Turn/min rotating speed be stirred uniformly after reaction 25min；
(3) mixed liquor in A stirred tanks is poured slowly into B stirred tanks, 40min is stirred with 400 turns/min rotating speed.
The embodiments of the present invention described above are not intended to limit the scope of the present invention, any in the present invention
Spirit and principle within the modifications, equivalent substitutions and improvements made etc., should be included in the claim protection model of the present invention
Within enclosing.
Claims (5)
1. a kind of corrugated board production adhesive, it is characterised in that comprise the following steps：
(1) 200kg water, 25kg starch, transfer matic special drying agent 4-6kg, caustic soda 5-6kg are sequentially added into A stirred tanks, is stirred
Reaction 35-50min after mixing uniformly；
(2) 400kg water, 250kg starch, 16kg resins adhesive, borax 3-5kg are sequentially added into B stirred tanks, is stirred
After react 15-25min；
(3) mixed liquor in A stirred tanks is poured slowly into B stirred tanks, stirs 20-40min.
2. multi-wall corrugated board preparation technology according to claim 1, in the step (1) starch using wheaten starch or
Potato starch or sweet potato starch.
3. multi-wall corrugated board preparation technology according to claim 1, with 400 turns/min rotating speed in the step (1)
It is stirred.
4. multi-wall corrugated board preparation technology according to claim 1, with 450 turns/min rotating speed in the step (2)
It is stirred.
5. multi-wall corrugated board preparation technology according to claim 1, with 450 turns/min rotating speed in the step (3)
It is stirred.