CN107497140A - A kind of high efficiency defoamer and preparation method thereof - Google Patents
A kind of high efficiency defoamer and preparation method thereof Download PDFInfo
- Publication number
- CN107497140A CN107497140A CN201710799347.0A CN201710799347A CN107497140A CN 107497140 A CN107497140 A CN 107497140A CN 201710799347 A CN201710799347 A CN 201710799347A CN 107497140 A CN107497140 A CN 107497140A
- Authority
- CN
- China
- Prior art keywords
- parts
- high efficiency
- preparation
- weight
- inorganic salts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to chemical industry preparation technique field, especially a kind of high efficiency defoamer and preparation method thereof, solve the problems, such as that defoaming effectiveness is low in the prior art, Preparation equipment is harsh, preparation process has potential safety hazard, the high effective antifoaming agent includes following raw material:Organosiloxane, dimethicone, hexenyl double stearoylketene amine, glyceryl monostearate, molybdenum disulfide, montmorillonite powder, metal oxide, charcoal powder, inorganic salts, surfactant and polyvinylethers;Its preparation method comprises the following steps:S1, the mixing of dimethicone and polyvinylether and the addition of organosiloxane;S2, reduction of speed add hexenyl double stearoylketene amine, glyceryl monostearate and surfactants, then raising speed to add montmorillonite powder, molybdenum disulfide, charcoal powder and inorganic salts, then add 4A molecular sieves and metal oxide, produce.Defoamer proposed by the present invention, property is stable, and defoaming effect is good, and usage amount is small, and preparation method is simple, and device requirement is low, production process safety.
Description
Technical field
The present invention relates to chemical industry preparation technique field, more particularly to a kind of high efficiency defoamer and preparation method thereof.
Background technology
Foam may be defined as the gas being stabilized in liquid medium.In latex, textile sizing, food fermentation, biology doctor
Many unwanted bubbles can be produced in the commercial process of the industries such as medicine, agricultural chemicals, coating, petrochemical industry, papermaking, and then are influenceed
Plant capacity, the waste of raw material is caused, extend reaction time, influence product quality etc., therefore often need to add defoaming
Purpose caused by bubble is reduced or avoided to reach in agent.
Defoamer can be divided into two kinds of approach of suds and brokenly bubble from intreractive theory, and suds refer to suppress bubble as its name suggests
The generation of foam, that is to say, that favorable factor caused by foam is eliminated from source, and brokenly bubble refers to abolish caused foam,
To have the function that to reduce foam.Two kinds of defoaming modes of defoamer can all play a part of effectively controlling bubble amt, therefore
Important function is respectively provided with actual production.
The species of defoamer on the market is various at present, mainly there is mineral matter oils, organic silicon and polyethers.It is Chinese special
Profit CN103263789A discloses a kind of high effective antifoaming agent and preparation method thereof, and the defoamer is mainly by fluorosilicon oil, triphen first
The compositions such as alkane, NPE, emulsifying agent, deionized water, thickener form.China Patent No. CN104225965B is public
A kind of organic silicon defoamer and preparation method thereof is opened, the preparing raw material weight percent composition of the defoamer is:Dimethicone
(201) 10~40%, high boiling point silicon oil 10~25%, thickener 1~5%, water 40~60%, emulsifying agent 5~25%, gas phase hard charcoal
Black 1~5%, total component is 100%.The composition for the defoamer that above-mentioned two patent proposes is close, contains silicon on composition composition
Oil component, emulsifying agent, thickener and water, and the content of the composition reclaimed water in raw material is occupied an leading position, the presence of substantial amounts of water
Although act as carrier to silicone oil raw material, reducing silicone oil material proportion when in use causes such defoamer
Addition is larger, and suds and brokenly bubble efficiency are relatively low, and in the preparation method of the defoamer proposed in above-mentioned two patent, is required to
Add the raw material into reactor, and reaction a few hours are carried out with higher temperature in a kettle, make the preparation of defoamer
Journey is more harsh, and the requirement of reactor is higher, potential safety hazard be present using process, is unfavorable for industrialized production.
Based on above statement, the present invention proposes a kind of high efficiency defoamer and preparation method thereof.
The content of the invention
The invention aims to solve, defoaming effectiveness is low present in prior art, Preparation equipment is harsh, prepared
There is the shortcomings that potential safety hazard in journey, and a kind of high efficiency defoamer proposed and preparation method thereof.
A kind of high efficiency defoamer, include the raw material of following parts by weight:2~4 parts of organosiloxane, dimethicone 10~
20 parts, double 4~8 parts of the stearoylketene amine of hexenyl, 2~4 parts of glyceryl monostearate, 1~3 part of molybdenum disulfide, montmorillonite powder 1~3
Part, 2~4 parts of metal oxide, 3~6 parts of charcoal powder, 2~6 parts of inorganic salts, 1~3 part of surfactant, polyvinylether 20~30
Part.
Preferably, described a kind of high efficiency defoamer, the raw material of following parts by weight is included:2~4 parts of organosiloxane,
12~18 parts of dimethicone, double 5~8 parts of the stearoylketene amine of hexenyl, 2~4 parts of glyceryl monostearate, molybdenum disulfide 1~3
Part, 1~3 part of montmorillonite powder, 2~4 parts of metal oxide, 3~5 parts of charcoal powder, 2~5 parts of inorganic salts, surfactant 1~3
Part, 22~28 parts of polyvinylether.
Preferably, described a kind of high efficiency defoamer, the raw material of following parts by weight is included:3 parts of organosiloxane, diformazan
15 parts of base silicone oil, double 6 parts of the stearoylketene amine of hexenyl, 3 parts of glyceryl monostearate, 2 parts of molybdenum disulfide, 2 parts of montmorillonite powder, metal
3 parts of oxide, 4 parts of charcoal powder, 4 parts of inorganic salts, 2 parts of surfactant, 25 parts of polyvinylether.
Preferably, the double stearoylketene amine of the hexenyl and glyceryl monostearate mass ratio are 1~4:1.
Preferably, the metal oxide is the mixture of calcium oxide and barium monoxide, and the quality of calcium oxide and barium monoxide
Than for 1.2~3:1, and calcium oxide and barium monoxide before use in 105 DEG C of baking oven dry 0.5~1.5h, calcium to be oxidized and
Barium monoxide be cooled to after room temperature be transferred to it is standby in drier.
Preferably, the inorganic salts are the mixing of any one in sodium chloride and potassium chloride or barium chloride, if inorganic salts
Sodium chloride and potassium chloride are combined as, then the amount ratio of the material of sodium chloride and potassium chloride is 1.4~2.8:1, if the combination of inorganic salts
For sodium chloride and barium chloride, then the ratio of the amount of the material of sodium chloride and barium chloride is 1.6~3.2:1.
Preferably, the particle diameter of the molybdenum disulfide is 500~1250 mesh, and the granularity of the charcoal powder is 250~800 mesh,
The particle diameter of the montmorillonite powder is 180~500 mesh.
The invention also provides a kind of preparation method of high efficiency defoamer, comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, will accordingly be weighed
The organosiloxane of amount part is encased in dropping funel, and side is stirred liquid A with 500~1000r/min speed, simultaneously will
Organosiloxane in dropping funel is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 10~20min/L, is treated
Organosiloxane continues 5~10min of stirring after being added dropwise, obtain mixture B;
S2, mixing speed is down to 200~300r/min, then the hexenyl pair of corresponding parts by weight is added into mixture B
Stearoylketene amine, glyceryl monostearate and surfactant, continue 5~10min of mixing, mixing speed is then risen to 400~
800r/min, add montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight, continue stirring 10~
20min, mixture C is obtained, then 4A molecular sieves are added into mixture C, continued 5~10min of stirring, add corresponding parts by weight
Metal oxide, produce high effective antifoaming agent.
Preferably, for 4A molecular sieves using preceding being activated, activation method is 350~450 DEG C of horse in the S2 steps
Any one under 8h, 150 DEG C of vacuumized conditions in activation 5h is not activated in stove.
Preferably, the relative humidity of the production environment of the high effective antifoaming agent is less than 60%.
Defoamer proposed by the present invention, property is stable, and defoaming effect is good, and usage amount is small, and preparation method is simple, and equipment needs
Ask low, production process safety;Defoamer with the double stearoylketene amine of the organosiloxane, dimethicone, hexenyl of rational proportion and
Glyceryl monostearate is the main component of defoamer, compared to China Patent No. CN103263789A and China Patent No.
CN104225965B, defoamer proposed by the present invention can be defoamed jointly in terms of suds and brokenly bubble two, therefore defoam effect
Rate will be significantly better than two publications, while the present invention coordinates four kinds of main components to also added the charcoal with loose structure
Powder, increase the main component of defoamer and the contact area by defoaming material, while add molybdenum disulfide and surfactant
Cooperation can significantly improve the dispersive property of charcoal powder in defoamer and when in use, and then improve main component to foam
Antifoaming speed, and the cooperation of molybdenum disulfide and surfactant can also reduce the surface tension of foam, promote foam
The defoaming effect of rupture, further auxiliary raising defoamer;And metal oxide can react with water when in use in defoamer
Heat is produced, accelerates the rate of climb of bubble in solution, and then accelerate antifoaming speed;Simultaneously the present invention in dimethicone,
The double stearoylketene amine of hexenyl and glyceryl monostearate auxiliary polyvinylether are used as solvent, reduce the use of water, raising mainly into
The occupation rate divided, significantly reduces the usage amount of defoamer on the premise of defoaming effect is ensured, in addition, proposed by the present invention
Preparation method is used only the equipment commonly used in factory and prepared, compared to China Patent No. CN103263789A and Chinese patent
The reactor used in number CN104225965B, the complexity of equipment substantially reduce, and security performance significantly improves, and avoids producing
During potential safety hazard presence, and preparation method mild condition proposed by the present invention, fidelity factor is high.
Embodiment
The present invention is made with reference to specific embodiment further to explain.
Embodiment one
A kind of high efficiency defoamer proposed by the present invention, include the raw material of following parts by weight:3 parts of organosiloxane, diformazan
15 parts of base silicone oil, double 6 parts of the stearoylketene amine of hexenyl, 3 parts of glyceryl monostearate, 2 parts of molybdenum disulfide, 2 parts of montmorillonite powder, metal
3 parts of oxide, 4 parts of charcoal powder, 4 parts of inorganic salts, 2 parts of surfactant, 25 parts of polyvinylether.
Its preparation method, comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, will accordingly be weighed
The organosiloxane of amount part is encased in dropping funel, and side is stirred liquid A with 800r/min speed, while dropping liquid is leaked
Organosiloxane in bucket is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 15min/L, treats organosiloxane
Continue to stir 8min after being added dropwise, obtain mixture B;
S2, mixing speed is down to 250r/min, then the double stearoylketenes of hexenyl of corresponding parts by weight are added into mixture B
Amine, glyceryl monostearate and surfactant, continue to mix 8min, mixing speed is then risen into 600r/min, added
Montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight, continue to stir 15min, obtain mixture C, then to mixing
4A molecular sieves are added in thing C, continues to stir 8min, adds the metal oxide of corresponding parts by weight, produce high effective antifoaming agent.
In the present invention, the metal oxide is the mixture of calcium oxide and barium monoxide, and the matter of calcium oxide and barium monoxide
Amount is than being 2:1, and calcium oxide and barium monoxide dry 1h, calcium and barium monoxide cooling to be oxidized before use in 105 DEG C of baking oven
It is transferred to after to room temperature standby in drier;The inorganic salts are the mixture of sodium chloride and potassium chloride, and sodium chloride and chlorination
The amount ratio of the material of potassium is 2:1;For 4A molecular sieves using preceding being activated, activation method is 350~450 DEG C in the S2 steps
Muffle furnace in activate 8h.
Embodiment two
A kind of high efficiency defoamer proposed by the present invention, include the raw material of following parts by weight:2 parts of organosiloxane, diformazan
15 parts of base silicone oil, double 5 parts of the stearoylketene amine of hexenyl, 3 parts of glyceryl monostearate, 3 parts of molybdenum disulfide, 2 parts of montmorillonite powder, metal
3 parts of oxide, 3 parts of charcoal powder, 6 parts of inorganic salts, 3 parts of surfactant, 25 parts of polyvinylether.
Its preparation method, comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, will accordingly be weighed
The organosiloxane of amount part is encased in dropping funel, and side is stirred liquid A with 1000r/min speed, while by dropping liquid
Organosiloxane in funnel is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 20min/L, treats organic silica
Alkane continues to stir 10min after being added dropwise, and obtains mixture B;
S2, mixing speed is down to 250r/min, then the double stearoylketenes of hexenyl of corresponding parts by weight are added into mixture B
Amine, glyceryl monostearate and surfactant, continue to mix 10min, mixing speed is then risen into 800r/min, added
Montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight, continue to stir 10min, obtain mixture C, then to mixing
4A molecular sieves are added in thing C, continues to stir 8min, adds the metal oxide of corresponding parts by weight, produce high effective antifoaming agent.
In the present invention, the metal oxide is the mixture of calcium oxide and barium monoxide, and the matter of calcium oxide and barium monoxide
Amount is than being 3:1, and calcium oxide and barium monoxide dry 1.5h before use in 105 DEG C of baking oven, calcium and barium monoxide to be oxidized are cold
But it is standby in drier to being transferred to after room temperature;The inorganic salts are the mixture of sodium chloride and potassium chloride, and sodium chloride and chlorine
The amount ratio for changing the material of potassium is 2:1;For 4A molecular sieves using preceding being activated, activation method is 350~450 in the S2 steps
DEG C Muffle furnace in activate 8h.
Embodiment three
A kind of high efficiency defoamer proposed by the present invention, include the raw material of following parts by weight:4 parts of organosiloxane, diformazan
20 parts of base silicone oil, double 6 parts of the stearoylketene amine of hexenyl, 3 parts of glyceryl monostearate, 2 parts of molybdenum disulfide, 1 part of montmorillonite powder, metal
4 parts of oxide, 4 parts of charcoal powder, 6 parts of inorganic salts, 1 part of surfactant, 25 parts of polyvinylether.
Its preparation method, comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, will accordingly be weighed
The organosiloxane of amount part is encased in dropping funel, and side is stirred liquid A with 800r/min speed, while dropping liquid is leaked
Organosiloxane in bucket is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 20min/L, treats organosiloxane
Continue to stir 10min after being added dropwise, obtain mixture B;
S2, mixing speed is down to 300r/min, then the double stearoylketenes of hexenyl of corresponding parts by weight are added into mixture B
Amine, glyceryl monostearate and surfactant, continue 5~10min of mixing, mixing speed is then risen into 600r/min, then
Montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight are added, continues to stir 15min, obtains mixture C, then to
4A molecular sieves are added in mixture C, continues to stir 8min, adds the metal oxide of corresponding parts by weight, produce efficient defoaming
Agent.
In the present invention, the metal oxide is the mixture of calcium oxide and barium monoxide, and the matter of calcium oxide and barium monoxide
Amount is than being 3:1, and calcium oxide and barium monoxide dry 1.5h before use in 105 DEG C of baking oven, calcium and barium monoxide to be oxidized are cold
But it is standby in drier to being transferred to after room temperature;The inorganic salts are the mixture of sodium chloride and barium chloride, and sodium chloride and chlorine
The ratio for changing the amount of the material of barium is 3:1;For 4A molecular sieves using preceding being activated, activation method is 150 DEG C in the S2 steps
5h is activated under vacuumized conditions.
Example IV
A kind of high efficiency defoamer proposed by the present invention, include the raw material of following parts by weight:3 parts of organosiloxane, diformazan
10 parts of base silicone oil, double 8 parts of the stearoylketene amine of hexenyl, 4 parts of glyceryl monostearate, 2 parts of molybdenum disulfide, 3 parts of montmorillonite powder, metal
2 parts of oxide, 6 parts of charcoal powder, 4 parts of inorganic salts, 2 parts of surfactant, 30 parts of polyvinylether.
Its preparation method, comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, will accordingly be weighed
The organosiloxane of amount part is encased in dropping funel, and side is stirred liquid A with 500r/min speed, while dropping liquid is leaked
Organosiloxane in bucket is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 10min/L, treats organosiloxane
Continue to stir 10min after being added dropwise, obtain mixture B;
S2, mixing speed is down to 200r/min, then the double stearoylketenes of hexenyl of corresponding parts by weight are added into mixture B
Amine, glyceryl monostearate and surfactant, continue to mix 10min, mixing speed is then risen into 400r/min, added
Montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight, continue to stir 20min, obtain mixture C, then to mixing
4A molecular sieves are added in thing C, continues to stir 5min, adds the metal oxide of corresponding parts by weight, produce high effective antifoaming agent.
In the present invention, the metal oxide is the mixture of calcium oxide and barium monoxide, and the matter of calcium oxide and barium monoxide
Amount is than being 1.2:1, and calcium oxide and barium monoxide dry 1.5h, calcium and barium monoxide to be oxidized before use in 105 DEG C of baking oven
Be cooled to after room temperature be transferred to it is standby in drier;The inorganic salts are sodium chloride and potassium chloride, and sodium chloride and potassium chloride
The amount ratio of material is 1.4:1;Using preceding being activated, activation method is 150 DEG C and vacuumized 4A molecular sieves in the S2 steps
Under the conditions of activate 5h in any one.
Embodiment five
A kind of high efficiency defoamer proposed by the present invention, include the raw material of following parts by weight:2 parts of organosiloxane, diformazan
10 parts of base silicone oil, double 4 parts of the stearoylketene amine of hexenyl, 2 parts of glyceryl monostearate, 1 part of molybdenum disulfide, 2 parts of montmorillonite powder, metal
4 parts of oxide, 3 parts of charcoal powder, 4 parts of inorganic salts, 1 part of surfactant, 25 parts of polyvinylether.
Its preparation method, comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, will accordingly be weighed
The organosiloxane of amount part is encased in dropping funel, and side is stirred liquid A with 500r/min speed, while dropping liquid is leaked
Organosiloxane in bucket is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 15min/L, treats organosiloxane
Continue to stir 10min after being added dropwise, obtain mixture B;
S2, mixing speed is down to 300r/min, then the double stearoylketenes of hexenyl of corresponding parts by weight are added into mixture B
Amine, glyceryl monostearate and surfactant, continue to mix 10min, mixing speed is then risen into 800r/min, added
Montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight, continue to stir 10min, obtain mixture C, then to mixing
4A molecular sieves are added in thing C, continues to stir 10min, adds the metal oxide of corresponding parts by weight, produce high effective antifoaming agent.
In the present invention, the metal oxide is the mixture of calcium oxide and barium monoxide, and the matter of calcium oxide and barium monoxide
Amount is than being 3:1, and calcium oxide and barium monoxide dry 0.5h before use in 105 DEG C of baking oven, calcium and barium monoxide to be oxidized are cold
But it is standby in drier to being transferred to after room temperature;The inorganic salts are the mixture of sodium chloride and potassium chloride, and sodium chloride and chlorine
The amount ratio for changing the material of potassium is 2.8:1;4A molecular sieves are using preceding being activated in the S2 steps, and activation method is 350~
8h is activated in 450 DEG C of Muffle furnace.
The relative humidity for preparing environment of the high effective antifoaming agent of above-described embodiment one~five uses below 60%
The particle diameter of molybdenum disulfide is that 500~1250 mesh, the granularity of charcoal powder are that 250~800 mesh, the particle diameter of montmorillonite powder are
180~500 mesh.
Carry out preparing defoamer according to the China Patent No. CN104225965B defoaming agent prescriptions proposed and preparation method, make
To contrast defoamer, then the defoamer prepared respectively to contrast defoamer and above-described embodiment one~five carries out performance detection, and
The detection numerical value of defoamer prepared by embodiment one~five is as a result as follows compared with contrasting the detection numerical value of defoamer:
Embodiment | One | Two | Three | Four | Five |
Foam time | - 32.3% | - 31.5% | - 35.7% | - 31.2% | - 30.1% |
The suds time | + 38.4% | + 36.7% | + 39.1% | + 35.3% | + 33.1% |
Jitter time | - 23.6% | - 25.4% | - 20.1% | - 24.9% | - 19.6% |
Experimental result shows that the foam time and jitter time needed for the defoamer of the preparation of embodiment one~five compare ratio
The time of defoamer is short, and embodiment one~five prepare defoamer the suds time to be much better than contrast defoamer suds when
Between.The defoaming of embodiment three and suds effect are best in five embodiments, and the jitter time of embodiment two is most fast, and embodiment
One combination property is best.
50%, 70% and 90% according to contrast defoamer dosage takes defoamer prepared by three parts of embodiments one respectively, and
The detection of foam time and dispersive property is carried out with contrast defoamer, testing result is as follows:
Experimental result is shown, i.e. reachable similar to contrast defoamer using the 50%~60% of contrast defoamer dosage
Effect, show that the defoaming effect of defoamer proposed by the present invention is substantially better than contrast defoamer.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (10)
1. a kind of high efficiency defoamer, it is characterised in that include the raw material of following parts by weight:2~4 parts of organosiloxane, diformazan
10~20 parts of base silicone oil, double 4~8 parts of the stearoylketene amine of hexenyl, 2~4 parts of glyceryl monostearate, 1~3 part of molybdenum disulfide, is covered
De- 1~3 part of stone flour, 2~4 parts of metal oxide, 3~6 parts of charcoal powder, 2~6 parts of inorganic salts, 1~3 part of surfactant, poly- second
20~30 parts of alkene ether.
2. a kind of high efficiency defoamer according to claim 1, it is characterised in that include the raw material of following parts by weight:Have
2~4 parts of organic siloxane, 12~18 parts of dimethicone, double 5~8 parts of the stearoylketene amine of hexenyl, glyceryl monostearate 2~4
Part, 1~3 part of molybdenum disulfide, 1~3 part of montmorillonite powder, 2~4 parts of metal oxide, 3~5 parts of charcoal powder, 2~5 parts of inorganic salts,
1~3 part of surfactant, 22~28 parts of polyvinylether.
3. a kind of high efficiency defoamer according to claim 1, it is characterised in that include the raw material of following parts by weight:Have
3 parts of organic siloxane, 15 parts of dimethicone, double 6 parts of the stearoylketene amine of hexenyl, 3 parts of glyceryl monostearate, 2 parts of molybdenum disulfide,
2 parts of montmorillonite powder, 3 parts of metal oxide, 4 parts of charcoal powder, 4 parts of inorganic salts, 2 parts of surfactant, 25 parts of polyvinylether.
A kind of 4. high efficiency defoamer according to claim 1, it is characterised in that double stearoylketene amine of the hexenyl and hard
Resin acid monoglyceride mass ratio is 1~4:1.
A kind of 5. high efficiency defoamer according to claim 1, it is characterised in that the metal oxide be calcium oxide and
The mixture of barium monoxide, and the mass ratio of calcium oxide and barium monoxide is 1.2~3:1, and calcium oxide and barium monoxide before use
Dry 0.5~1.5h in 105 DEG C of baking oven, calcium and barium monoxide to be oxidized be cooled to after room temperature be transferred to it is standby in drier.
6. a kind of high efficiency defoamer according to claim 1, it is characterised in that the inorganic salts are sodium chloride and chlorination
The mixing of any one in potassium or barium chloride, if inorganic salts are combined as sodium chloride and potassium chloride, sodium chloride and potassium chloride
The amount ratio of material is 1.4~2.8:1, if the material for being combined as sodium chloride and barium chloride, sodium chloride and barium chloride of inorganic salts
Amount ratio be 1.6~3.2:1.
7. a kind of high efficiency defoamer according to claim 1, it is characterised in that the particle diameter of the molybdenum disulfide is 500
~1250 mesh, the granularity of the charcoal powder is 250~800 mesh, and the particle diameter of the montmorillonite powder is 180~500 mesh.
8. a kind of preparation method of high efficiency defoamer, it is characterised in that comprise the following steps:
S1, the dimethicone and polyvinylether for weighing corresponding parts by weight, after being well mixed, mixed liquor A is obtained, by corresponding parts by weight
Organosiloxane be encased in dropping funel, and side is stirred liquid A with 500~1000r/min speed, while by dropping liquid
Organosiloxane in funnel is added drop-wise in mixed liquor A, and the time for adding of organosiloxane is 10~20min/L, is treated organic
Siloxanes continues 5~10min of stirring after being added dropwise, obtain mixture B;
S2, mixing speed is down to 200~300r/min, then the double hard esters of hexenyl of corresponding parts by weight are added into mixture B
Acid amides, glyceryl monostearate and surfactant, continue 5~10min of mixing, mixing speed is then risen into 400~800r/
Min, montmorillonite powder, molybdenum disulfide, charcoal powder and the inorganic salts of corresponding parts by weight are added, continue 10~20min of stirring, are obtained mixed
Compound C, then 4A molecular sieves are added into mixture C, continue 5~10min of stirring, add the metal oxidation of corresponding parts by weight
Thing, produce high effective antifoaming agent.
A kind of 9. preparation method of high efficiency defoamer according to claim 8, it is characterised in that 4A in the S2 steps
Molecular sieve is activated under 8h, 150 DEG C of vacuumized conditions using preceding being activated in the Muffle furnace that activation method is 350~450 DEG C
Activate any one in 5h.
A kind of 10. preparation method of high efficiency defoamer according to claim 8, it is characterised in that the efficiently defoaming
The relative humidity of the production environment of agent is less than 60%.