CN107488382A - A kind of electric wire fireproof coating based on the manganese of phenodiazine three - Google Patents
A kind of electric wire fireproof coating based on the manganese of phenodiazine three Download PDFInfo
- Publication number
- CN107488382A CN107488382A CN201610403101.2A CN201610403101A CN107488382A CN 107488382 A CN107488382 A CN 107488382A CN 201610403101 A CN201610403101 A CN 201610403101A CN 107488382 A CN107488382 A CN 107488382A
- Authority
- CN
- China
- Prior art keywords
- parts
- phenodiazine
- manganese
- fireproof coating
- electric wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of electric wire fireproof coating based on the manganese of phenodiazine three, the key component of following mass parts is included in its raw material：15 25 parts of ethylene acrylic acid co polymer, 15 30 parts of metal hydroxides, 12 18 parts of three manganese of phenodiazine, 5 12 parts of ethanol, 7 10 parts of calcium carbonate, 15 25 parts of talcum powder, 6 12 parts of silane, 6 12 parts of siloxanes, 58 parts of glass sand, 58 parts of resin.The present invention as being combined in complex, and adds the manganese of phenodiazine three using ethylene acrylic acid co polymer and metal hydroxides, makes fireproof coating in addition to fire retardant property, additionally it is possible to maintains resistance to combustion, flame proof and the fire resistance property such as fire-retardant, can effectively protect surrounding combustible material.
Description
Technical field
The present invention relates to a kind of fireproof coating, and in particular to a kind of fire prevention of poly-organic acid system of fire prevention indoors applies
Material.
Background technology
At present, fire prevention measure both domestic and external from principle for be divided into Dredging Method and blocking cut-off process, and blocking cut-off process be divided into it is outer
Envelope, screen method, spraying process.Fire proofing material is coated in body surface as one kind, has heat-insulated, anti-flaming, anti-flaming function
Material is used widely, and using the development that can effectively delay the intensity of a fire in construction material, prevents propagation of flame.
Application publication number CN103923545A patent application discloses a kind of fireproof coating, fireproof coating proportioning, double cyanogen
Amine, silicate, pentaerythrite, titanium dioxide, chlorinated paraffin, APP, acrylic emulsion, remaining is auxiliary agent, the fireproof coating
Nontoxic, nonirritant, in coating, caking property is good, attractive in appearance and good flame retardation effect.Existing fireproof coating exists anti-toward contact
The shortcomings of fiery time is short, and protection domain limits to.The fire-proof and thermal-insulation effect for further improving fireproof coating is still art technology
The direction that personnel make great efforts.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of electric wire based on the manganese of phenodiazine three for above-mentioned prior art
Cable fire-refractory coating, it has good fireproofing flame-resistant characteristic.
Technical scheme is used by the present invention solves the above problems：A kind of electric wire fire prevention based on the manganese of phenodiazine three applies
Expect, the key component of following mass parts is included in its raw material：
Ethylene acrylic acid co polymer 15-25 parts,
The manganese 12-18 parts of phenodiazine three,
Metal hydroxides 15-30 parts,
Ethanol 5-12 parts,
Calcium carbonate 7-10 parts,
Talcum powder 15-25 parts,
Silane 6-12 parts,
Siloxanes 6-12 parts,
Glass sand 5-8 parts,
Resin 5-8 parts.
Metal hydroxides of the present invention is magnesium hydroxide, aluminium hydroxide.
The particle diameter of talcum powder of the present invention is 100~350nm.
Glass sand of the present invention can be replaced with glass fibre.
Electric wire fireproof coating of the present invention also includes pigment, water, thickener, defoamer.
Electric wire fireproof coating of the present invention also includes levelling agent, curing agent.
Compared with prior art, the advantage of the invention is that：The present invention is with ethylene acrylic acid co polymer and metal hydroxide
Thing is homogeneously dispersed in ethylene acrylic acid co polymer and reacted as complex composition, metal hydroxides, reinforcement ethene
The performance of acrylic copolymer, and the manganese of phenodiazine three is added, make final fireproof coating in addition to fire retardant property, additionally it is possible to tie up
Resistance to combustion, flame proof and the fire resistance property such as fire-retardant are held, can be used, can effectively protect inflammable around as the fire prevention on electric wire surface
Material.
Embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
Based on the electric wire fireproof coating of the manganese of phenodiazine three, the component of following mass parts is included in its raw material：
20 parts of ethylene acrylic acid co polymer,
15 parts of magnesium hydroxide,
15 parts of three manganese of phenodiazine,
10 parts of ethanol,
10 parts of calcium carbonate,
15 parts of talcum powder,
10 parts of silane,
12 parts of siloxanes,
5 parts of glass sand,
5 parts of resin.
Ethylene acrylic acid co polymer and magnesium hydroxide are first mixed, and are heated to 75-125 DEG C, is incubated 30-240min, so
The manganese of phenodiazine three is added afterwards, and ethanol, calcium carbonate, talcum powder, silane, siloxanes, glass sand, resin are added, and temperature is adjusted into 60-85
DEG C, 50-120min is incubated, produces fireproof coating.
Embodiment 2
Based on the electric wire fireproof coating of the manganese of phenodiazine three, the component of following mass parts is included in its raw material：
25 parts of ethylene acrylic acid co polymer,
30 parts of magnesium hydroxide,
16 parts of three manganese of phenodiazine,
5 parts of ethanol,
10 parts of calcium carbonate,
15 parts of talcum powder,
10 parts of silane,
8 parts of siloxanes,
8 parts of glass fibre,
6 parts of resin,
3 parts of levelling agent,
2 parts of defoamer.
Ethylene acrylic acid co polymer and magnesium hydroxide are first mixed, and are heated to 75-125 DEG C, is incubated 30-240min, so
The manganese of phenodiazine three, ethanol, calcium carbonate, talcum powder, silane, siloxanes, glass fibre, resin, levelling agent and defoamer is added afterwards to add
Enter, temperature is adjusted to 60-85 DEG C, 50-120min is incubated, produces fireproof coating.
Embodiment 3
Based on the electric wire fireproof coating of the manganese of phenodiazine three, the component of following mass parts is included in its raw material：
15 parts of ethylene acrylic acid co polymer,
25 parts of aluminium hydroxide,
17 parts of three manganese of phenodiazine,
5 parts of ethanol,
7 parts of calcium carbonate,
25 parts of talcum powder,
6 parts of silane,
12 parts of siloxanes,
5 parts of glass sand,
8 parts of resin,
8 parts of water,
2 parts of thickener.
Ethylene acrylic acid co polymer and aluminium hydroxide and water are first mixed, and are heated to 75-125 DEG C, is incubated 30-
240min, then add the manganese of phenodiazine three, ethanol, calcium carbonate, talcum powder, silane, siloxanes, glass sand, resin and thickener and add
Enter, temperature is adjusted to 60-85 DEG C, 50-120min is incubated, produces fireproof coating.
Claims (6)
- A kind of 1. electric wire fireproof coating based on the manganese of phenodiazine three, it is characterised in that：Comprising following mass parts in its raw material Key component：Ethylene acrylic acid co polymer 15-25 parts,The manganese 12-18 parts of phenodiazine three,Metal hydroxides 15-30 parts,Ethanol 5-12 parts,Calcium carbonate 7-10 parts,Talcum powder 15-25 parts,Silane 6-12 parts,Siloxanes 6-12 parts,Glass sand 5-8 parts,Resin 5-8 parts.
- 2. the electric wire fireproof coating according to claim 1 based on the manganese of phenodiazine three, it is characterised in that：The metallic hydrogen Oxide is magnesium hydroxide, aluminium hydroxide.
- 3. the electric wire fireproof coating according to claim 1 based on the manganese of phenodiazine three, it is characterised in that：The talcum powder Particle diameter be 100~350nm.
- 4. the electric wire fireproof coating according to claim 1 based on the manganese of phenodiazine three, it is characterised in that：The glass sand It can be replaced with glass fibre.
- 5. the electric wire fireproof coating according to claim 1 based on the manganese of phenodiazine three, it is characterised in that：Also include face Material, water, thickener, defoamer.
- 6. the electric wire fireproof coating according to claim 1 based on the manganese of phenodiazine three, it is characterised in that：Also include levelling Agent, curing agent.