CN107446389A - A kind of fire-resistant coating for steel structure based on halloysite - Google Patents
A kind of fire-resistant coating for steel structure based on halloysite Download PDFInfo
- Publication number
- CN107446389A CN107446389A CN201610361366.0A CN201610361366A CN107446389A CN 107446389 A CN107446389 A CN 107446389A CN 201610361366 A CN201610361366 A CN 201610361366A CN 107446389 A CN107446389 A CN 107446389A
- Authority
- CN
- China
- Prior art keywords
- parts
- halloysite
- fire
- steel structure
- resistant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fire-resistant coating for steel structure based on halloysite, the key component of following mass parts is included in its raw material：15 25 parts of halloysite, 15 30 parts of metal hydroxides, 5 12 parts of ethanol, 7 10 parts of calcium carbonate, 15 25 parts of talcum powder, 6 12 parts of silane, 6 12 parts of siloxanes, 58 parts of glass sand, 58 parts of resin.The present invention, as being combined in complex, makes fireproof coating in addition to fire retardant property using halloysite and metal hydroxides, additionally it is possible to maintains resistance to combustion, flame proof and the fire resistance property such as fire-retardant, can effectively protect surrounding combustible material.
Description
Technical field
The present invention relates to a kind of fireproof coating, and in particular to a kind of fire prevention of poly-organic acid system in steel structure fireproofing applies
Material.
Background technology
At present, fire prevention measure both domestic and external from principle for be divided into Dredging Method and blocking cut-off process, and blocking cut-off process be divided into it is outer
Envelope, screen method, spraying process.Fire proofing material is coated in body surface as one kind, has heat-insulated, anti-flaming, anti-flaming function
Material is used widely, and using the development that can effectively delay the intensity of a fire in construction material, prevents propagation of flame.
Application publication number CN103923545A patent application discloses a kind of fireproof coating, fireproof coating proportioning, double cyanogen
Amine, silicate, pentaerythrite, titanium dioxide, chlorinated paraffin, APP, acrylic emulsion, remaining is auxiliary agent, the fireproof coating
Nontoxic, nonirritant, in coating, caking property is good, attractive in appearance and good flame retardation effect.Existing fireproof coating exists anti-toward contact
The shortcomings of fiery time is short, and protection domain limits to.The fire-proof and thermal-insulation effect for further improving fireproof coating is still art technology
The direction that personnel make great efforts.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of steel based on halloysite for above-mentioned prior art
Structure fire coating, it has good fireproofing flame-resistant characteristic.
Technical scheme is used by the present invention solves the above problems：A kind of steel structure fireproofing based on halloysite applies
Expect, the key component of following mass parts is included in its raw material：
Halloysite 15-25 parts,
Metal hydroxides 15-30 parts,
Ethanol 5-12 parts,
Calcium carbonate 7-10 parts,
Talcum powder 15-25 parts,
Silane 6-12 parts,
Siloxanes 6-12 parts,
Glass sand 5-8 parts,
Resin 5-8 parts.
Metal hydroxides of the present invention is magnesium hydroxide, aluminium hydroxide.
The particle diameter of talcum powder of the present invention is 100~350nm.
Glass sand of the present invention can be replaced with glass fibre.
Fire-resistant coating for steel structure of the present invention also includes pigment, water, thickener, defoamer.
Fire-resistant coating for steel structure of the present invention also includes levelling agent, curing agent.
Compared with prior art, the advantage of the invention is that：The present invention using halloysite and metal hydroxides as
Complex composition, metal hydroxides are homogeneously dispersed in halloysite and reacted, the performance of reinforcement halloysite,
Fireproof coating is in addition to fire retardant property, additionally it is possible to maintains resistance to combustion, flame proof and the fire resistance property such as fire-retardant, can effectively protect
Surrounding combustible material.
Embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
Fire-resistant coating for steel structure based on halloysite, the component of following mass parts is included in its raw material：
20 parts of halloysite,
15 parts of magnesium hydroxide,
10 parts of ethanol,
10 parts of calcium carbonate,
15 parts of talcum powder,
10 parts of silane,
12 parts of siloxanes,
5 parts of glass sand,
5 parts of resin.
Halloysite and magnesium hydroxide are first mixed, and are heated to 75-125 DEG C, 30-240min is incubated, then adds
Ethanol, calcium carbonate, talcum powder, silane, siloxanes, glass sand, resin are added, and temperature is adjusted into 60-85 DEG C, is incubated 50-
120min, produce fireproof coating.
Embodiment 2
Fire-resistant coating for steel structure based on halloysite, the component of following mass parts is included in its raw material：
25 parts of halloysite,
30 parts of magnesium hydroxide,
5 parts of ethanol,
10 parts of calcium carbonate,
15 parts of talcum powder,
10 parts of silane,
8 parts of siloxanes,
8 parts of glass fibre,
6 parts of resin,
3 parts of levelling agent,
2 parts of defoamer.
Halloysite and magnesium hydroxide are first mixed, and are heated to 75-125 DEG C, 30-240min is incubated, then adds
Ethanol, calcium carbonate, talcum powder, silane, siloxanes, glass fibre, resin, levelling agent and defoamer are added, and temperature is adjusted into 60-
85 DEG C, 50-120min is incubated, produces fireproof coating.
Embodiment 3
Fire-resistant coating for steel structure based on halloysite, the component of following mass parts is included in its raw material：
15 parts of halloysite,
25 parts of aluminium hydroxide,
5 parts of ethanol,
7 parts of calcium carbonate,
25 parts of talcum powder,
6 parts of silane,
12 parts of siloxanes,
5 parts of glass sand,
8 parts of resin,
8 parts of water,
2 parts of thickener.
Halloysite and aluminium hydroxide and water are first mixed, and are heated to 75-125 DEG C, is incubated 30-240min, then
Add ethanol, calcium carbonate, talcum powder, silane, siloxanes, glass sand, resin and thickener to add, temperature be adjusted to 60-85 DEG C,
50-120min is incubated, produces fireproof coating.
Claims (6)
- A kind of 1. fire-resistant coating for steel structure based on halloysite, it is characterised in that：Comprising following mass parts in its raw material Key component：Halloysite 15-25 parts,Metal hydroxides 15-30 parts,Ethanol 5-12 parts,Calcium carbonate 7-10 parts,Talcum powder 15-25 parts,Silane 6-12 parts,Siloxanes 6-12 parts,Glass sand 5-8 parts,Resin 5-8 parts.
- 2. the fire-resistant coating for steel structure according to claim 1 based on halloysite, it is characterised in that：The metallic hydrogen Oxide is magnesium hydroxide, aluminium hydroxide.
- 3. the fire-resistant coating for steel structure according to claim 1 based on halloysite, it is characterised in that：The talcum powder Particle diameter be 100~350nm.
- 4. the fire-resistant coating for steel structure according to claim 1 based on halloysite, it is characterised in that：The glass sand It can be replaced with glass fibre.
- 5. the fire-resistant coating for steel structure according to claim 1 based on halloysite, it is characterised in that：Also include face Material, water, thickener, defoamer.
- 6. the fire-resistant coating for steel structure according to claim 1 based on halloysite, it is characterised in that：Also include levelling Agent, curing agent.