CN107474436A - A kind of plastic formula for being used to make automotive oil tank - Google Patents
A kind of plastic formula for being used to make automotive oil tank Download PDFInfo
- Publication number
- CN107474436A CN107474436A CN201710767347.2A CN201710767347A CN107474436A CN 107474436 A CN107474436 A CN 107474436A CN 201710767347 A CN201710767347 A CN 201710767347A CN 107474436 A CN107474436 A CN 107474436A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil tank
- automotive oil
- plastic formula
- tank according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plastic formula for being used to make automotive oil tank, it is made up of according to percentage by weight number the following raw material：60 62 parts of polyvinyl chloride resin, 1 2.2 parts of titanium dioxide, 2.5 4 parts of rare-earth stabilizer, 0.2 1 parts of alumina powder, 5 10 parts of carboxyl nitrile rubber, 2.5 4.6 parts of acid polyethylene butyral, 35 parts of citric acid, 2.6 3.4 parts of SA dioctyl ester, 1.8 2.6 parts of dimethyl siloxane, 3 10 parts of carbonic acid ammonium dihydrogen, CrO2 is 0.5 part, SiN is 0.5 part, diamond is 2.5 3.5 parts, 13 parts of bromide fire retardant, 0.5 2 parts of compatilizer, 12 parts of toughener, 0.4 1 parts of antioxidant, 24 parts of glass fibre.Fuel tank prepared by the present invention, light quality, intensity is high, and impact resistance and corrosion resistance are preferable, can apply and replace conventional metals fuel tank in automobile industry.
Description
Technical field
The present invention relates to a kind of automotive oil tank, specifically a kind of plastic automotive fuel tank.
Background technology
Present automotive oil tank, usually metallic oil tank, metallic oil tank weight is big, is unfavorable for the lightweight of automobile, and resistance to
Impact is not strong, in accident easily cracking, seepage situations such as, therefore, design a kind of mailbox of excellent performance and become
Current problem in the urgent need to address.
The content of the invention
In order to solve the above problems, the present invention provides a kind of light weight, impact-resistant plastic fuel tank.
To achieve the above object, the present invention provides a kind of plastic formula for being used to make automotive oil tank, according to weight percent
It is made up of than number the following raw material：Polyvinyl chloride resin 60-62 parts, titanium dioxide 1-2.2 parts, rare-earth stabilizer 2.5-4 parts, alumina powder
0.2-1 parts, carboxyl nitrile rubber 5-10 parts, acid polyethylene butyral 2.5-4.6 parts, citric acid 3-5 parts, SA dioctyl ester
2.6-3.4 parts, dimethyl siloxane 1.8-2.6 parts, carbonic acid ammonium dihydrogen 3-10 parts, CrO2 are 0.5 part, SiN is 0.5 part, artificial
Diamond is 2.5-3.5 parts, bromide fire retardant 1-3 parts, compatilizer 0.5-2 parts, toughener 1-2 parts, antioxidant 0.4-1 parts, glass
Glass fiber 2-4 parts.
Preferably, the plastic material is prepared by the raw material of following weight percentage：
61 parts of polyvinyl chloride resin, 1.5 parts of titanium dioxide, 3 parts of rare-earth stabilizer, 0.5 part of alumina powder, 8 parts of carboxyl nitrile rubber,
3.5 parts of acid polyethylene butyral, 4 parts of citric acid, 3 parts of SA dioctyl ester, 2.5 parts of dimethyl siloxane, carbonic acid ammonium dihydrogen 3
Part, CrO2 is 0.5 part, SiN is 0.5 part, diamond is 3 parts, 1 part of bromide fire retardant, 1.5 parts of compatilizer, toughener 1.5
Part, 0.8 part of antioxidant, 2 parts of glass fibre.
Further, described bromide fire retardant is TDE, is a kind of brominated organic compound；
Further, described compatilizer is propenyl benzene-maleic anhydride multipolymer；
Further, the glass fibre is that a kind of alkali-free length is fine, a diameter of 10 microns.
Further, the diamond density is 3.5 grams per cubic centimeter.
Further, described toughener is that maleic anhydride is grafted compatilizer.
Fuel tank prepared by the present invention, light quality, intensity is high, and impact resistance and corrosion resistance are preferable, can apply
Automobile industry.
Brief description of the drawings
Embodiment
The present invention provides a kind of plastic formula for being used to make automotive oil tank, according to percentage by weight number by the following raw material
Composition：Polyvinyl chloride resin 60-62 parts, titanium dioxide 1-2.2 parts, rare-earth stabilizer 2.5-4 parts, alumina powder 0.2-1 parts, carboxyl fourth are fine
Rubber 5-10 parts, acid polyethylene butyral 2.5-4.6 parts, citric acid 3-5 parts, SA dioctyl ester 2.6-3.4 parts, dimethyl-silicon
Oxygen alkane 1.8-2.6 parts, carbonic acid ammonium dihydrogen 3-10 parts, CrO2 are 0.5 part, SiN is 0.5 part, diamond be 2.5-3.5 parts,
Bromide fire retardant 1-3 parts, compatilizer 0.5-2 parts, toughener 1-2 parts, antioxidant 0.4-1 parts, glass fibre 2-4 parts.
In addition, the plastic material is prepared by the raw material of following weight percentage：
61 parts of polyvinyl chloride resin, 1.8 parts of titanium dioxide, 3 parts of rare-earth stabilizer, 0.5 part of alumina powder, 8 parts of carboxyl nitrile rubber,
3.5 parts of acid polyethylene butyral, 4 parts of citric acid, 3 parts of SA dioctyl ester, 2.5 parts of dimethyl siloxane, carbonic acid ammonium dihydrogen 3
Part, CrO2 is 0.5 part, SiN is 0.5 part, diamond is 3 parts, 1 part of bromide fire retardant, 1.5 parts of compatilizer, toughener 1.5
Part, 0.8 part of antioxidant, 2 parts of glass fibre.
Described bromide fire retardant is TDE, is a kind of brominated organic compound, and bromide fire retardant uses
It is convenient, it can directly be added in post processing, be nuisanceless tencel fire retardant.
Described compatilizer is propenyl benzene-maleic anhydride multipolymer；
The glass fibre is that a kind of alkali-free length is fine, a diameter of 10 microns, reinforcing material of the glass fibre as reinforced plastics
Maximum to be characterized in that tensile strength is big during material application, heat-resist, temperature does not influence up at 300 DEG C on intensity, there is excellent electricity
Insulating properties, it is advanced electrically insulating material.
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1：
A kind of plastic formula for automotive oil tank, it is made up of according to percentage the following raw material：
60 parts of polyvinyl chloride resin, 1.5 parts of titanium dioxide, 2.8 parts of rare-earth stabilizer, 0.7 part of alumina powder, carboxyl nitrile rubber 7
Part, 4 parts of acid polyethylene butyral, 3 parts of citric acid, 3.2 parts of SA dioctyl ester, 1.8 parts of dimethyl siloxane, carbonic acid ammonium dihydrogen
5 parts, CrO2 is 0.5 part, SiN is 0.5 part, diamond is 2.5 parts, 2 parts of bromide fire retardant, 1.5 parts of compatilizer, toughener
1.5 parts, 0.6 part of antioxidant, 3 parts of glass fibre.
Embodiment 2：
A kind of plastic formula for automotive oil tank, it is made up of according to percentage the following raw material：
62 parts of polyvinyl chloride resin, 1.8 parts of titanium dioxide, 3.8 parts of rare-earth stabilizer, 0.8 part of alumina powder, carboxyl nitrile rubber 8
Part, 4.5 parts of acid polyethylene butyral, 3.8 parts of citric acid, 3 parts of SA dioctyl ester, 2.5 parts of dimethyl siloxane, carbonic acid dihydro
8 parts of ammonium, CrO2 is 0.5 part, SiN is 0.5 part, diamond is 2.8 parts, 2 parts of bromide fire retardant, 1.5 parts of compatilizer, toughness reinforcing
1.5 parts of agent, 0.6 part of antioxidant, 4 parts of glass fibre.
Embodiment 3：
A kind of plastic formula for automotive oil tank, it is made up of according to percentage the following raw material：
61 parts of polyvinyl chloride resin, 1.5 parts of titanium dioxide, 3 parts of rare-earth stabilizer, 0.5 part of alumina powder, 8 parts of carboxyl nitrile rubber,
3.5 parts of acid polyethylene butyral, 4 parts of citric acid, 3 parts of SA dioctyl ester, 2.5 parts of dimethyl siloxane, carbonic acid ammonium dihydrogen 3
Part, CrO2 is 0.5 part, SiN is 0.5 part, diamond is 3 parts, 1 part of bromide fire retardant, 1.5 parts of compatilizer, toughener 1.5
Part, 0.8 part of antioxidant, 2 parts of glass fibre.
Each component ratio in embodiment 3 is best proportion, gained plastic products intensity highest, impact resistance and corrosion-resistant
Property is most strong.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement made within refreshing and principle etc., should be included in the scope of the protection.
Claims (7)
1. a kind of plastic formula for being used to make automotive oil tank, is made up of according to percentage by weight number the following raw material：Polyvinyl chloride resin
It is 60-62 parts, titanium dioxide 1-2.2 parts, rare-earth stabilizer 2.5-4 parts, alumina powder 0.2-1 parts, carboxyl nitrile rubber 5-10 parts, poly-
Hexenoic acid butyral 2.5-4.6 parts, citric acid 3-5 parts, SA dioctyl ester 2.6-3.4 parts, dimethyl siloxane 1.8-2.6
Part, carbonic acid ammonium dihydrogen 3-10 parts, CrO2 are 0.5 part, SiN is 0.5 part, diamond is 2.5-3.5 parts, bromide fire retardant 1-
3 parts, compatilizer 0.5-2 parts, toughener 1-2 parts, antioxidant 0.4-1 parts, glass fibre 2-4 parts.
A kind of 2. plastic formula that can be used for making automotive oil tank according to claim 1, it is characterised in that：The plastics material
Material is prepared by the raw material of following weight percentage：
61 parts of polyvinyl chloride resin, 1.5 parts of titanium dioxide, 3 parts of rare-earth stabilizer, 0.5 part of alumina powder, 8 parts of carboxyl nitrile rubber, poly- second
3.5 parts of olefin(e) acid butyral, 4 parts of citric acid, 3 parts of SA dioctyl ester, 2.5 parts of dimethyl siloxane, 3 parts of carbonic acid ammonium dihydrogen,
CrO2 is 0.5 part, SiN is 0.5 part, diamond is 3 parts, 1 part of bromide fire retardant, 1.5 parts of compatilizer, 1.5 parts of toughener,
0.8 part of antioxidant, 2 parts of glass fibre.
A kind of 3. plastic formula that can be used for making automotive oil tank according to claim 1, it is characterised in that：Described bromine
Flame retardant is TDE.
A kind of 4. plastic formula that can be used for making automotive oil tank according to claim 1, it is characterised in that：Described phase
Appearance agent is propenyl benzene-maleic anhydride multipolymer.
A kind of 5. plastic formula that can be used for making automotive oil tank according to claim 1, it is characterised in that：The glass
Fiber is that a kind of alkali-free length is fine, a diameter of 10 microns.
A kind of 6. plastic formula that can be used for making automotive oil tank according to claim 1, it is characterised in that：It is described artificial
Diamond density is 3.5 grams per cubic centimeter.
A kind of 7. plastic formula that can be used for making automotive oil tank according to claim 1, it is characterised in that：Described increasing
Tough dose is that maleic anhydride is grafted compatilizer.