CN107471505A - A kind of housing of mobile terminal and preparation method thereof, mobile terminal - Google Patents
A kind of housing of mobile terminal and preparation method thereof, mobile terminal Download PDFInfo
- Publication number
- CN107471505A CN107471505A CN201710512204.7A CN201710512204A CN107471505A CN 107471505 A CN107471505 A CN 107471505A CN 201710512204 A CN201710512204 A CN 201710512204A CN 107471505 A CN107471505 A CN 107471505A
- Authority
- CN
- China
- Prior art keywords
- area
- mobile terminal
- carried out
- matrix
- housing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of housing of mobile terminal and preparation method thereof, mobile terminal, this method includes providing a mould, and first time surface treatment is carried out to an inner surface of mould, to cause inner surface that there is smooth first area surface and the second area surface of spark line;Mold injection molding after being surface-treated by first time is to obtain the matrix with corresponding smooth domain surface and spark line region surface;Second of surface treatment is carried out to the surface of matrix, to cause smooth domain surface and spark line region surface that there is the first metal-like and the second metal-like respectively.By this method, on the premise of causing the surface of shell of mobile terminal while there are two kinds of metal-likes, simplify technique, improve production efficiency, reduce cost.
Description
Technical field
The present invention relates to field of terminal technology, more particularly to a kind of housing of mobile terminal and preparation method thereof, movement
Terminal.
Background technology
With the development of life, people can only realize a kind of end of texture effect to the appearance requirement more and more higher of terminal
End housing can not meet the needs of people.
In the prior art, generally use 3D laser carvings technique is to realize double texture effects of terminal enclosure to meet the need of people
Ask, but found in the studying for a long period of time of present inventor, this comparison of processes is complicated, and cost is higher.
The content of the invention
Present invention generally provides a kind of housing of mobile terminal and preparation method thereof, mobile terminal, it is intended to solves to realize eventually
The problem of processes of the double texture effects of end housing is complicated, cost is high.
In order to solve the above technical problems, one aspect of the present invention is:A kind of housing of mobile terminal is provided
Preparation method, methods described includes:One mould is provided, and first time surface treatment is carried out to an inner surface of the mould,
To cause the inner surface that there is smooth first area surface and the second area surface of spark line;Pass through the first time table
Mold injection molding after the processing of face is to obtain the matrix with corresponding smooth domain surface and spark line region surface;To institute
The surface for stating matrix carries out second of surface treatment, to cause the smooth domain surface and the spark line region surface to distinguish
With the first metal-like and the second metal-like.
Wherein, the inner surface includes first area and second area, and the inner surface to the mould carries out the
One-time surface processing, to cause the inner surface that there is smooth first area surface and the second area surface of spark line to wrap
Include:Mirror surface treatment is carried out to the first area to cause the surface of the first area that there is mirror effect;Pass through electrode fire
Flower electric discharge forms spark line on the surface of second area.
Wherein, the quantity of the first area and the second area is multiple, multiple first areas and multiple institutes
Second area is stated to be arranged alternately.
Wherein, the surface to described matrix carries out second and is surface-treated, with cause the smooth domain surface and
The spark line region surface respectively there is the first metal-like and the second metal-like to include:The surface of described matrix is carried out
Decontamination processing;Matrix surface after decontamination processing is carried out successively in UV basecoat paints, non-conductive vacuum plated film, UV paint spraying and
UV finish paints are sprayed to form prime coat, film plating layer, middle enamelled coating and top coat layer respectively.
Wherein, the thickness of the prime coat is 2~3 μm.
Wherein, the thickness of the film plating layer is 20~25nm.
Wherein, the thickness of the middle enamelled coating is 6~7 μm.
Wherein, the thickness of the top coat layer is 20~25 μm.
In order to solve the above technical problems, another technical solution used in the present invention is:A kind of shell of mobile terminal is provided
Body, the housing is adopted to be prepared with the aforedescribed process.
In order to solve the above technical problems, another technical scheme that the present invention uses is:A kind of mobile terminal is provided, it is described
Mobile terminal includes above-mentioned housing.
The beneficial effects of the invention are as follows:The situation of prior art is different from, the present invention to an inner surface of mould by entering
Surface treatment causes the inner surface to have smooth first area surface and the second area surface of spark line to row for the first time, and then
So that the matrix of injection molding has corresponding smooth domain surface and a spark line region surface, then the is carried out to the surface of matrix
Secondary surface treatment causes smooth domain surface and spark line region surface to have the first metal-like and the second metallic respectively
The method of sense, on the premise of causing the surface of shell of mobile terminal while there are two kinds of metal-likes, simplify technique, improve
Production efficiency, reduce cost.
Brief description of the drawings
Fig. 1 is the schematic flow sheet of the preparation method embodiment of the housing of mobile terminal provided by the invention;
Fig. 2 is the inner surface schematic diagram of mould in Fig. 1;
Fig. 3 is the idiographic flow schematic diagram of step S11 in Fig. 1;
Fig. 4 is the idiographic flow schematic diagram of step S13 in Fig. 1.
Embodiment
To make those skilled in the art more fully understand technical scheme, below in conjunction with the accompanying drawings and it is embodied
Mode is described in further detail to a kind of housing of mobile terminal provided by the present invention and preparation method thereof, mobile terminal.
Refering to Fig. 1, the preparation method embodiment of the housing of mobile terminal provided by the invention includes:
S11:One mould is provided, and first time surface treatment is carried out to an inner surface of mould, to cause the inner surface to have
There are smooth first area surface and the second area surface of spark line;
Refering to Fig. 2, an inner surface of the mould includes first area 101 and second area 102, optionally, first area
101 with the quantity of second area 102 be multiple, and multiple first areas 101 and multiple second areas 102 are arranged alternately.
Refering to Fig. 3, step S11 may particularly include:
S111:Mirror surface treatment is carried out to first area 101 to cause the surface of first area 101 that there is mirror effect;
Specifically, mirror finish is carried out to the surface of first area 101, to reduce the surface roughness of first area 101,
Optionally, the surface roughness of the first area 101 after mirror finish is less than 0.8 μm.
Optionally, the mirror finish can use the machining mode for removing material, such as grinding or polishing etc.;Can also
Using the machining without cutting rolling mode of minute surface instrument;The surface of first area 101 after mirror finish is due to thick
Rugosity is relatively low and finish is higher, has mirror effect.
S112:Spark line is formed on the surface of second area 102 by electrode spark discharge.
Optionally, the surface of the high pressure thawing second area 102 of moment, the table of second area 102 are produced using spark machine
Face produces rugged lines in the presence of instantaneous pressure electric shock, you can spark line is formed, to cause second area 102
Surface there is spark line.
Optionally, the scope of the VDI3400 standards of spark line is 18~30.
S12:By first time be surface-treated after mold injection molding with obtain having corresponding smooth domain surface and
The matrix of spark line region surface;
Optionally, makrolon or polymethyl methacrylate material can be selected at the subsurfaces of above-mentioned steps S11 first
To form the matrix of predetermined shape, an inner surface of the mould after being surface-treated due to first time is had for injection in mould after reason
Smooth first area surface and the second area surface of spark line, therefore after moulding, an appearance mask of the matrix
There are smooth domain surface corresponding with the second area surface on smooth first area surface and spark line and fiery pattern area table
Face.
S13:Second of surface treatment is carried out to the surface of matrix, to cause smooth domain surface and spark line region surface
There is the first metal-like and the second metal-like respectively.
Refering to Fig. 4, step S13 may particularly include:
S131:Decontamination processing is carried out to the surface of matrix;
Optionally, supersonic wave decontamination cleaning is carried out to the surface of matrix using supersonic wave cleaning machine, ultrasonic wave is a kind of frequency
Rate exceeds more than human hearing range 20kHz sound wave, and the propagation of ultrasonic wave will rely on elastic fluid, when it is propagated, makes elasticity
Particle oscillation in medium, and energy is transmitted by the direction of propagation of ultrasonic wave by medium, this ripple can be divided into longitudinal wave and horizontal stroke
Xiang Bo, in solid, both it can transmit, and in gas and liquid, only longitudinal wave can transmit.Ultrasonic wave can draw
Play particle vibration, the acceleration of particle vibration and supersonic frequency it is square directly proportional.Therefore, the ultrasonic wave of several KHzs can produce
Great active force, when intense ultrasonic wave is propagated in a liquid, due to nonlinear interaction, acoustic cavitation can be produced.Dashed forward in cavitation bubble
The shock wave so sent during closure can produce thousands of individual atmospheric pressures around it, on the one hand broken to the direct repeated stock of pollution layer
The absorption of bad dirt and cleaning parts surface, on the other hand it can also cause the destruction of crud layer and depart from cleaning parts surface and make them
It is distributed in cleaning fluid, the vibration of bubble can also be cleaned to the surface of solids, and bubble, which " can also pierce " in crack to do, to be vibrated, and is made
Dirt comes off.
After the washing, using dry cloth by the matrix wiped clean after cleaning, and in wiping process, it is impossible to use isopropyl
The chemical agent such as alcohol or tincture ketone is wiped.
S132:Matrix after decontamination processing is carried out successively in UV basecoat paints, non-conductive vacuum plated film, UV paint spraying and
UV finish paints are sprayed to form prime coat, film plating layer, middle enamelled coating and top coat layer respectively.
Matrix surface first after cleaning carries out UV basecoat paints and forms prime coat to improve follow-up middle vacuum coating
Brightness and adhesive force, optionally, wet shot is carried out using spray gun, UV bakings are carried out after wet shot, baking temperature is 75~85 DEG C, is dried
The roasting time is 6~7min, and UV energy is 700~800mj/cm2。
Optionally, the thickness of prime coat is 2~3 μm.
Then film plating layer is formed using non-conductive vacuum coating process, optionally, the thickness of film plating layer is 20~25nm, plating
Membrane material is indium or indium stannum alloy, plays imitative metal effect.
Enamelled coating to film plating layer to play a protective role during further paint spraying is formed in progress UV, optionally, middle enamelled coating
Thickness is 6~7 μm, and baking temperature is 75~85 DEG C, and baking time is 6~7min, and UV energy is 400~500mj/cm2, spray painting
Material selection light color based material, to improve the mute contrast effect of light.
Finally carry out UV finish paints to spray to form top coat layer to play a protective role and abrasion resistant effect, and different light can be realized
Damp demand, optionally, the thickness of top coat layer is 20~25 μm, and the mute degree of light is more than 8 light splitting, and baking temperature is 75~85 DEG C, baking
Time is 6~7min, and UV energy is 800~1000mj/cm2。。
In decontamination, UV basecoat paints, non-conductive vacuum plated film, UV are carried out on the surface of matrix by step S13
After paint spraying and the spraying of UV finish paints, metal-like can be achieved in the surface of matrix, is wrapped in conjunction with the surface of matrix in step S12
Include smooth domain surface and spark line region surface so that smooth domain surface has the first metal-like, fiery pattern area table
Face has the second metal-like, and then make it that on the surface of matrix two kinds of metal-likes can be realized simultaneously.
The housing embodiments of mobile terminal provided by the invention are prepared using the above method, specifically see above-mentioned reality
Example is applied, will not be repeated here.
Mobile terminal embodiment provided by the invention includes the housing in above-described embodiment.
Prior art is different from, the present invention to an inner surface of mould by carrying out being surface-treated the interior table for the first time
Face has smooth first area surface and the second area surface of spark line, and then the matrix of injection molding is had accordingly
Smooth domain surface and spark line region surface, then second of surface treatment is carried out to the surface of matrix and causes smooth domain table
The method that face and spark line region surface have the first metal-like and the second metal-like respectively, is causing the shell of mobile terminal
Body surface face has two kinds of metal-likes simultaneously on the premise of, simplify technique, improve production efficiency, reduce cost.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright specification and accompanying drawing content are made, or directly or indirectly it is used in other related skills
Art field, is included within the scope of the present invention.
Claims (10)
1. a kind of preparation method of the housing of mobile terminal, it is characterised in that methods described includes:
One mould is provided, and first time surface treatment is carried out to an inner surface of the mould, to cause the inner surface to have
Smooth first area surface and the second area surface of spark line;
Mold injection molding after being surface-treated by the first time is to obtain having corresponding smooth domain surface and spark
The matrix of line region surface;
Second of surface treatment is carried out to the surface of described matrix, to cause the smooth domain surface and the fiery pattern area
Surface has the first metal-like and the second metal-like respectively.
2. according to the method for claim 1, it is characterised in that the inner surface includes first area and second area, institute
State and first time surface treatment is carried out to an inner surface of the mould, to cause the inner surface that there is smooth first area table
Face and the second area surface of spark line include:
Mirror surface treatment is carried out to the first area to cause the surface of the first area that there is mirror effect;
Spark line is formed on the surface of second area by electrode spark discharge.
3. according to the method for claim 2, it is characterised in that the quantity of the first area and the second area is more
Individual, multiple first areas are arranged alternately with multiple second areas.
4. according to the method for claim 1, it is characterised in that the surface to described matrix is carried out at the second subsurface
Reason, to cause the smooth domain surface and the spark line region surface that there is the first metal-like and the second metallic respectively
Sense includes:
Decontamination processing is carried out to the surface of described matrix;
Carry out paint spraying and UV faces in UV basecoat paints, non-conductive vacuum plated film, UV successively to the matrix surface after decontamination processing
Paint is sprayed to form prime coat, film plating layer, middle enamelled coating and top coat layer respectively.
5. according to the method for claim 4, it is characterised in that the thickness of the prime coat is 2~3 μm.
6. according to the method for claim 4, it is characterised in that the thickness of the film plating layer is 20~25nm.
7. according to the method for claim 4, it is characterised in that the thickness of the middle enamelled coating is 6~7 μm.
8. according to the method for claim 4, it is characterised in that the thickness of the top coat layer is 20~25 μm.
9. a kind of housing of mobile terminal, it is characterised in that the housing is using the side as described in any one of claim 1~8
Method is prepared.
10. a kind of mobile terminal, it is characterised in that the mobile terminal includes the housing described in claim 9.