CN107459343A - A kind of ceramic for being beneficial to human liver and preparation method thereof - Google Patents

A kind of ceramic for being beneficial to human liver and preparation method thereof Download PDF

Info

Publication number
CN107459343A
CN107459343A CN201710711737.8A CN201710711737A CN107459343A CN 107459343 A CN107459343 A CN 107459343A CN 201710711737 A CN201710711737 A CN 201710711737A CN 107459343 A CN107459343 A CN 107459343A
Authority
CN
China
Prior art keywords
parts
ceramic
sand
beneficial
human liver
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710711737.8A
Other languages
Chinese (zh)
Inventor
程燕文
周永富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Kangshitai New Material Technology Co Ltd
Original Assignee
Guangdong Kangshitai New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Kangshitai New Material Technology Co Ltd filed Critical Guangdong Kangshitai New Material Technology Co Ltd
Priority to CN201710711737.8A priority Critical patent/CN107459343A/en
Publication of CN107459343A publication Critical patent/CN107459343A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of ceramic for being beneficial to human liver and preparation method thereof, and in parts by weight, ceramic component includes：40 50 parts of Dongxing sand, 41 50 parts of pure white sand, 9 16 parts of the bright sand of good fortune, 13 20 parts of water milling powder, 5 10 parts of ultrawhite ball clay, 5 15 parts of Huidong original mud, 5 15 parts of silica flour, 48 parts of bentonite, 0.4 1 parts of adjuvant, 30 40 parts of sea-buckthorn, 20 30 parts of matrimony vine, 10 25 parts of hawthorn；The ceramic of the present invention effectively improves human body function, is beneficial to the function of human liver, wide market.

Description

A kind of ceramic for being beneficial to human liver and preparation method thereof
Technical field
The present invention relates to the technical field of ceramic, and in particular to a kind of ceramic for being beneficial to human liver and its Preparation method.
Background technology
Ceramic can not realize the effect need for transmitting bio-energy for a long time to people, lifting itself holistic health at present Ask, the ceramic for being beneficial to human liver is in vacancy in ceramic industry.
The content of the invention
It is an object of the invention to for weak point of the prior art, propose a kind of ceramics for being beneficial to human liver Product and preparation method thereof, the ceramic are beneficial to the function of human liver.
To use following technical scheme up to this purpose, the present invention：
A kind of ceramic for being beneficial to human liver, in parts by weight, ceramic component includes：Dongxing sand 40-50 Part, pure white sand 41-50 parts, the bright sand 9-16 parts of good fortune, water milling powder 13-20 parts, ultrawhite ball clay 5-10 parts, Huidong original mud 5-15 parts, stone English powder 5-15 parts, bentonite 4-8 parts, adjuvant 0.4-1 parts, sea-buckthorn 30-40 parts, matrimony vine 20-30 parts, hawthorn 10-25 parts.
Further, in parts by weight, ceramic component includes：45 parts of Dongxing sand, 45 parts of pure white sand, good fortune are bright 10 parts of sand, 15 parts of water milling powder, 9 parts of ultrawhite ball clay, 10 parts of Huidong original mud, 10 parts of silica flour, burn 8 parts of talcum, be 6 parts of bentonite, auxiliary 0.5 part of auxiliary agent, 35 parts of sea-buckthorn, 25 parts of matrimony vine, 15 parts of hawthorn.
A kind of method for preparing the above-mentioned ceramic for being beneficial to human liver, including step are as follows：
A, raw material preparation；Dongxing sand 40-50 parts, pure white sand 41-50 parts, the bright sand 9-16 parts of good fortune, water milling powder 13-20 parts, ultrawhite Ball clay 5-10 parts, Huidong original mud 5-15 parts, silica flour 5-15 parts, bentonite 4-8 parts, adjuvant 0.4-1 parts carry out mixing outfit, Obtain resulting mixture A1；B, ball milling；The mixture A1 and water（By weight 2：1）Mixing is carried out in addition ball mill to grind Mill, form slurry B1；C, mist projection granulating；Slurry B1 injections are dried to it in the spray drying tower, are granulated, are formed Powder C1；D, punch forming；The powder C1 is added stamping machine and carries out cloth, punch forming, obtains ceramic tile blank D1；E, forge Burn；The ceramic tile blank D1 is put into kiln and calcined, obtains Ceramic Tiles E1；F, sea-buckthorn 30-40 parts, matrimony vine 20-30 Part, hawthorn 10-25 parts are prepared into solution, solution are repeatedly coated in step E on Ceramic Tiles E1, dry masking liquid again and dry again.
Beneficial effects of the present invention：1. the ceramic that the present invention realizes has the regulation function such as body metabolism, toxin expelling, can To improve body metabolism function, accelerate metabolism, be beneficial to the function of human liver, meet the market demand.
Embodiment
Technical scheme is further illustrated below by embodiment.
Embodiment 1：
A kind of method for preparing the described ceramic for being beneficial to human liver, including step are as follows：
A, raw material preparation；In parts by weight, ceramic component includes：40 parts of Dongxing sand, 41 parts of pure white sand, the bright sand of good fortune 9 parts, 13 parts of water milling powder, 5 parts of ultrawhite ball clay, 5 parts of Huidong original mud, 5 parts of silica flour, burn 5 parts of talcum, 4 parts of bentonite, adjuvant 0.4 part carries out mixing outfit, obtains resulting mixture A1；B, ball milling；The mixture A1 and water（By weight 2：1）Add ball Mixed grinding is carried out in grinding machine, forms slurry B1；C, mist projection granulating；Slurry B1 injections are entered to it in the spray drying tower Row drying, it is granulated, forms powder C1；D, punch forming；The powder C1 is added stamping machine and carries out cloth, punch forming, is obtained To ceramic tile blank D1；E, calcine；The ceramic tile blank D1 is put into kiln and calcined, obtains Ceramic Tiles E1；F, sea-buckthorn 30 parts, 20 parts of matrimony vine, 10 parts of hawthorn be prepared into solution, solution is repeatedly coated in step E on Ceramic Tiles E1, dries again masking liquid again Dry.
Embodiment 2：
A kind of method for preparing the described ceramic for being beneficial to human liver, including step are as follows：
A, raw material preparation；50 parts of Dongxing sand, 50 parts of pure white sand, 16 parts of the bright sand of good fortune, 20 parts of water milling powder, 10 parts of ultrawhite ball clay, favour Former 15 parts of the mud in east, 15 parts of silica flour, 10 parts of talcum of burning, 8 parts of bentonite, 1 part of adjuvant carry out mixing outfit, obtain resulting mixture A1；B, ball milling；The mixture A1 and water（By weight 2：1）Add and mixed grinding is carried out in ball mill, form slurry B1； C, mist projection granulating；Slurry B1 injections are dried to it in the spray drying tower, are granulated, form powder C1；D, punching press Shaping；The powder C1 is added stamping machine and carries out cloth, punch forming, obtains ceramic tile blank D1；E, calcine；The ceramic tile Base substrate D1, which is put into kiln, to be calcined, and obtains Ceramic Tiles E1；F, 40 parts of sea-buckthorn, 30 parts of matrimony vine, 25 parts of hawthorn are prepared into molten Liquid, solution is repeatedly coated in step E on Ceramic Tiles E1, dries masking liquid again and dry again.
Embodiment 3：
A kind of method for preparing the described ceramic for being beneficial to human liver, including step are as follows：
A, raw material preparation；45 parts of Dongxing sand, 45 parts of pure white sand, 10 parts of the bright sand of good fortune, 15 parts of water milling powder, 9 parts of ultrawhite ball clay, Huidong Former 10 parts of mud, 10 parts of silica flour, 8 parts of talcum of burning, 6 parts of bentonite, 0.5 part of adjuvant carry out mixing outfit, obtain resulting mixture A1；B, ball milling；The mixture A1 and water（By weight 2：1）Add and mixed grinding is carried out in ball mill, form slurry B1； C, mist projection granulating；Slurry B1 injections are dried to it in the spray drying tower, are granulated, form powder C1；D, punching press Shaping；The powder C1 is added stamping machine and carries out cloth, punch forming, obtains ceramic tile blank D1；E, calcine；The ceramic tile Base substrate D1, which is put into kiln, to be calcined, and obtains Ceramic Tiles E1；F, 35 parts of sea-buckthorn, 25 parts of matrimony vine, 15 parts of hawthorn are prepared into molten Liquid, solution is repeatedly coated in step E on Ceramic Tiles E1, dries masking liquid again and dry again.
The technical principle of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's Principle, and limiting the scope of the invention can not be construed in any way.Based on explanation herein, the technology of this area Personnel would not require any inventive effort the other embodiments that can associate the present invention, and these modes are fallen within Within protection scope of the present invention.

Claims (3)

  1. A kind of 1. ceramic for being beneficial to human liver, it is characterised in that：In parts by weight, ceramic component bag Include：Dongxing sand 40-50 parts, pure white sand 41-50 parts, the bright sand 9-16 parts of good fortune, water milling powder 13-20 parts, ultrawhite ball clay 5-10 parts, Huidong Former mud 5-15 parts, silica flour 5-15 parts, bentonite 4-8 parts, adjuvant 0.4-1 parts, sea-buckthorn 30-40 parts, matrimony vine 20-30 parts, mountain Short, bristly hair or beard 10-25 parts.
  2. 2. the ceramic according to claim 1 for being beneficial to human liver, it is characterised in that：In parts by weight, Ceramic component includes：45 parts of Dongxing sand, 45 parts of pure white sand, 10 parts of the bright sand of good fortune, 15 parts of water milling powder, 9 parts of ultrawhite ball clay, Huidong Former 10 parts of mud, 10 parts of silica flour, burn 8 parts of talcum, 6 parts of bentonite, 0.5 part of adjuvant, 35 parts of sea-buckthorn, 25 parts of matrimony vine, hawthorn 15 Part.
  3. A kind of 3. method for preparing the ceramic for being beneficial to human liver described in claim 1-2, it is characterised in that：Including Step is as follows：A, raw material preparation；Dongxing sand 40-50 parts, pure white sand 41-50 parts, the bright sand 9-16 parts of good fortune, water milling powder 13-20 parts, Ultrawhite ball clay 5-10 parts, Huidong original mud 5-15 parts, silica flour 5-15 parts, bentonite 4-8 parts, adjuvant 0.4-1 parts are mixed It is equipped with, obtains resulting mixture A1；B, ball milling；The mixture A1 and water（By weight 2：1）Add in ball mill and mixed Grinding is closed, forms slurry B1；C, mist projection granulating；Slurry B1 injections are dried to it in the spray drying tower, are granulated, Form powder C1；D, punch forming；The powder C1 is added stamping machine and carries out cloth, punch forming, obtains ceramic tile blank D1； E, calcine；The ceramic tile blank D1 is put into kiln and calcined, obtains Ceramic Tiles E1；F, sea-buckthorn 30-40 parts, matrimony vine 20-30 parts, hawthorn 10-25 parts are prepared into solution, solution are repeatedly coated in step E on Ceramic Tiles E1, dry masking liquid again and dry in the air again It is dry.
CN201710711737.8A 2017-08-18 2017-08-18 A kind of ceramic for being beneficial to human liver and preparation method thereof Withdrawn CN107459343A (en)