CN107446371A - Fire-retardant hollow sheeting and preparation method thereof - Google Patents
Fire-retardant hollow sheeting and preparation method thereof Download PDFInfo
- Publication number
- CN107446371A CN107446371A CN201710858025.9A CN201710858025A CN107446371A CN 107446371 A CN107446371 A CN 107446371A CN 201710858025 A CN201710858025 A CN 201710858025A CN 107446371 A CN107446371 A CN 107446371A
- Authority
- CN
- China
- Prior art keywords
- fire
- retardant
- hollow sheeting
- preparation
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses fire-retardant hollow sheeting and preparation method thereof.The fire-retardant hollow sheeting includes the component remembered with mass percent：Fire retardant 10% 20%, plastic pellet 50% 60%, coupling agent 1.5%, dispersant 0.5%, plasticizer 3%, plastic resin 25%.The fire-retardant hollow sheeting preparation method, including step S1 to step S3.Step S1：Fire retardant, plastic pellet, coupling agent, dispersant, plasticizer are uniformly mixed to form fire-retardant master granule according to preset mass percent.Step S2：Fire-retardant master granule and plastic resin are stirred to form flame retardant plastics in mixer according to preset mass percent.Step S3：By flame retardant plastics by extruder for shaping, fire-retardant hollow sheeting is formed.Fire-retardant hollow sheeting disclosed by the invention and preparation method thereof, effectively lifts fire retardancy, can be widely used in the industries such as building materials, the protection person and property safety, avoid the occurrence of potential safety hazard.
Description
Technical field
The invention belongs to plastic plate technical field, and in particular to fire-retardant hollow sheeting and preparation method thereof.
Background technology
With the continuous progress of economic level, requirement of the public for the field such as building materials and ornaments product is increasingly strict.To meet
Relevant industries flame-retardancy requirements, while consider for the person of the public with property safety, necessary further to improve and optimize plastic plate
The fire retardancy of material, avoid producing potential safety hazard.
The content of the invention
The present invention is directed to the situation of prior art, there is provided a kind of fire-retardant hollow sheeting.
The present invention uses following technical scheme, and the fire-retardant hollow sheeting includes the component remembered with mass percent：Fire retardant
10%-20%, plastic pellet 50%-60%, coupling agent 1.5%, dispersant 0.5%, plasticizer 3%, plastic resin 25%.
The invention also discloses a kind of fire-retardant hollow sheeting preparation method, comprise the following steps：
Step S1：Fire retardant, plastic pellet, coupling agent, dispersant, plasticizer are uniformly mixed according to preset mass percent
Form fire-retardant master granule；
Step S2：Fire-retardant master granule and plastic resin be stirred in mixer according to preset mass percent to be formed it is fire-retardant
Plastics；
Step S3：By flame retardant plastics by extruder for shaping, fire-retardant hollow sheeting is formed.
According to above-mentioned technical proposal, in step sl, preset mass percent is fire retardant 10%-20%, plastic pellet
50%-60%, coupling agent 1.5%, dispersant 0.5%, plasticizer 3%.
According to above-mentioned technical proposal, in step s 2, preset mass percent is plastic resin 25%.
Fire-retardant hollow sheeting disclosed by the invention and preparation method thereof, its advantage is, effectively lifts fire retardancy, can
It is widely used in the industries such as building materials, the protection person and property safety, avoids the occurrence of potential safety hazard.
Embodiment
The invention discloses a kind of fire-retardant hollow sheeting and preparation method thereof, with reference to preferred embodiment, to the present invention's
Embodiment is further described.
Preferably, the fire-retardant hollow sheeting includes the component remembered with mass percent：Fire retardant 10%-20%, plastic pellet
50%-60%, coupling agent 1.5%, dispersant 0.5%, plasticizer 3%, plastic resin 25%.
Preferably, the invention also discloses a kind of fire-retardant hollow sheeting preparation method, comprise the following steps：
Step S1：Fire retardant, plastic pellet, coupling agent, dispersant, plasticizer are uniformly mixed according to preset mass percent
Form fire-retardant master granule；
Step S2：Fire-retardant master granule and plastic resin be stirred in mixer according to preset mass percent to be formed it is fire-retardant
Plastics；
Step S3：By flame retardant plastics by extruder for shaping, fire-retardant hollow sheeting is formed.
Wherein, in step sl, preset mass percent be fire retardant 10%-20%, plastic pellet 50%-60%, coupling
Agent 1.5%, dispersant 0.5%, plasticizer 3%.
Wherein, in step s 2, preset mass percent is plastic resin 25%.
For a person skilled in the art, the technical scheme described in foregoing embodiments can still be repaiied
Change, or equivalent substitution is carried out to which part technical characteristic, within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in protection scope of the present invention.
Claims (4)
1. fire-retardant hollow sheeting, it is characterised in that including the component remembered with mass percent：Fire retardant 10%-20%, plastic pellet
50%-60%, coupling agent 1.5%, dispersant 0.5%, plasticizer 3%, plastic resin 25%.
2. fire-retardant hollow sheeting preparation method, it is characterised in that comprise the following steps：
Step S1：Fire retardant, plastic pellet, coupling agent, dispersant, plasticizer are uniformly mixed according to preset mass percent
Form fire-retardant master granule；
Step S2：Fire-retardant master granule and plastic resin be stirred in mixer according to preset mass percent to be formed it is fire-retardant
Plastics；
Step S3：By flame retardant plastics by extruder for shaping, fire-retardant hollow sheeting is formed.
3. fire-retardant hollow sheeting preparation method according to claim 2, it is characterised in that in step sl, preset quality
Percentage is fire retardant 10%-20%, plastic pellet 50%-60%, coupling agent 1.5%, dispersant 0.5%, plasticizer 3%.
4. fire-retardant hollow sheeting preparation method according to claim 2, it is characterised in that in step s 2, preset quality
Percentage is plastic resin 25%.