CN107419813A - A kind of building panel - Google Patents
A kind of building panel Download PDFInfo
- Publication number
- CN107419813A CN107419813A CN201710803057.9A CN201710803057A CN107419813A CN 107419813 A CN107419813 A CN 107419813A CN 201710803057 A CN201710803057 A CN 201710803057A CN 107419813 A CN107419813 A CN 107419813A
- Authority
- CN
- China
- Prior art keywords
- parts
- standby
- sent
- building panel
- forming machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of building panel, and the building panel is made up of 22 28 parts of 16 20 parts of 14 18 parts of 12 18 parts of 10 16 parts of 24 28 parts of 20 30 parts of 12 16 parts of 69 parts of 8 10 parts of 6 12 parts of 10 12 parts of 58 parts of 22 28 parts of stalk, hydrogen peroxide, phenolphthalein resin, dichloroethanes, sodium alkyl sulfonate, m-phenylene diamine (MPD), string, lime stone, glass waste, sodium carbonate, graphite, iron oxide, iron powder, the timber and 10 16 parts of sodium carbonate matching in parts by weight;The building panel intensity is high, soundproof effect is good and shielding property is high.
Description
Technical field
The present invention relates to a kind of building panel.
Background technology
With the construction and development in city, the noise that traffic, industry and building are brought is increasingly severe, greatly interferes with
Work, study and the sleep of people, therefore, employing the acoustic isolation facility of many in many house decoration, architectural engineering.Typically
Object all there is soundproof effect, sound is a kind of wavy energy, it is necessary to which medium could be propagated, in same middle Propagation
When, the density of medium is bigger, and spread speed is faster.When being propagated in different medium, i.e., pass through two media from a kind of medium
Critical contact face enters another medium, and now, the transmission essence of acoustic energy is the transmission of Oscillation Amplitude, therefore acoustic energy can produce damage
Consumption, when the density difference of two media is bigger, then the loss of acoustic energy is bigger.Because the material for differing bigger with atmospheric density is general
For highdensity material, density is higher, and soundproof effect is better.The life of vehicle and the noise of building site production to people in life
Living and work brings very big influence, or even is endangered to the health care belt of people, is this many house decoration, architectural engineering
On employ many acoustic isolation facility, sound panel on the market is all to use single layer designs at present, and cost is higher, this sound panel
Sound-absorbing and soundproof effect it is all less preferable, much time using can be shortened service life by corrosion impact.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of intensity height, the building that soundproof effect is good and shielding property is high
Plate.
In order to solve the above technical problems, the present invention adopts the following technical scheme that:
A kind of building panel by match in parts by weight stalk 22-28 parts, hydrogen peroxide 5-8 parts, phenolphthalein resin 10-12 parts,
Dichloroethanes 6-12 parts, sodium alkyl sulfonate 8-10 parts, m-phenylene diamine (MPD) 6-9 parts, string 12-16 parts, lime stone 20-30 parts,
Glass waste 24-28 parts, sodium carbonate 10-16 parts, graphite 12-18 parts, iron oxide 14-18 parts, iron powder 16-20 parts, timber 22-28
Part and sodium carbonate 10-16 parts are made, and the manufacture method of building panel, comprise the following steps:
1) stalk 22-28 parts are put into airslide disintegrating mill and particle is made, then particle is put into cauldron, add hydrogen peroxide 5-
8 parts, 85-90 DEG C is heated to, continues 2-3 hours, it is standby;
2) material in step 1) is sent into forming machine and sound-insulating layer is made, then will be made inside sound-insulating layer true
Dead level, it is standby;
3) phenolphthalein resin 10-12 parts, dichloroethanes 6-12 parts, sodium alkyl sulfonate 8-10 parts and m-phenylene diamine (MPD) 6-9 parts are sent
Enter in casting machine, cystosepiment is made, it is standby;
4) string 12-16 parts are sent into grind into powder in grinder, are re-fed into cauldron, heat 90-100 DEG C,
Continue 1-2 hours, be cooked into slurries, be re-fed into forming machine and resonance ball is made, it is standby;
5) the resonance ball in step 4) is embedded in cystosepiment, it is standby;
6) lime stone 20-30 parts, glass waste 24-28 parts and sodium carbonate 10-16 parts are sent into melting furnace, melting is made
Thing, stir, be sent into forming machine and the first glass fibre cotton layer and the second mineral wool layer is made, it is standby;
7) graphite 12-18 parts, iron oxide 14-18 parts and iron powder 16-20 parts are sent into melting furnace, fused mass is made, stirs
Mix uniformly, be sent into forming machine and radiation protective layer is made, it is standby;
8) timber 22-28 parts are sent into airslide disintegrating mill and are ground into powder, then powder and sodium carbonate 10-16 parts are mixed
Close, be put into melting furnace and merge, be finally sent into forming machine and wood plies are made, it is standby;
9) material made of step 2), step 3), step 5), step 6), step 7) and step 8) is bonded, you can
Building panel is made.
Brief description of the drawings
Fig. 1 is a kind of structural representation of building panel of the present invention.
Embodiment
Embodiment one:
Shown in reference picture 1, a kind of building panel includes plate body 1, and the plate body 1 is internally provided with sound-insulating layer 2, institute
State sound-insulating layer 2 and be internally provided with vacuum layer 3, the upper surface of sound-insulating layer 2 is provided with cystosepiment 4, the cystosepiment 4
More than one resonance ball 5 is internally provided with, the upper surface of cystosepiment 4 is provided with the first glass fibre cotton layer 6, the sound insulation
The lower surface of heat-insulation layer 2 is provided with the second glass fibre cotton layer 7, and the upper surface of the first glass fibre cotton layer 6 is provided with radiation proof
Layer 8, the upper surface of radiation protective layer 8 are provided with the first wood plies 9, and the lower surface of the second glass fiber cotton layer 7 is provided with the
Two wood plies 10.
The plate body 1 is internally provided with diatom ooze (not shown), can absorb sound wave, improves the soundproof effect of building panel.
The plate body 1 is internally provided with the reinforcing bar (not shown) of one or more, improves the intensity of building panel.
Spring (not shown) is provided between the resonance ball 5 and cystosepiment 4, preventing from resonating when ball 5 shakes makes a noise.
The upper surface of first wood plies 9 and the lower surface of the second wood plies 10 are provided with anti-slip veins (not shown), profit
In the carrying of building panel.
The manufacture method of plate body:
1) 22 parts of stalk is put into airslide disintegrating mill and particle is made, then particle is put into cauldron, add 5 parts of hydrogen peroxide,
85 DEG C are heated to, continues 2 hours, it is standby;
2) material in step 1) is sent into forming machine and sound-insulating layer 2 is made, then will be made inside sound-insulating layer 2
Vacuum layer 3, it is standby;
3) by 6 parts of 10 parts of phenolphthalein resin, 6 parts of dichloroethanes, 8 parts of sodium alkyl sulfonate and m-phenylene diamine (MPD) feeding casting machines,
Cystosepiment 4 is made, it is standby;
4) by grind into powder in 12 parts of feeding grinders of string, it is re-fed into cauldron, heats 90 DEG C, it is small to continue 1
When, slurries are cooked into, is re-fed into forming machine and resonance ball 5 is made, it is standby;
5) the resonance ball 5 in step 4) is embedded in cystosepiment 4, it is standby;
6) 10 parts of 20 parts of lime stone, 24 parts of glass waste and sodium carbonate are sent into melting furnace, fused mass is made, stirring is equal
It is even, it is sent into forming machine and the first glass fibre cotton layer 6 and the second mineral wool layer 7 is made, it is standby;
7) 16 parts of 12 parts of graphite, 14 parts of iron oxide and iron powder are sent into melting furnace, fused mass is made, stirs, send
Enter to be made radiation protective layer 8 in forming machine, it is standby;
8) powder will be ground into 22 parts of feeding airslide disintegrating mills of timber, then powder is mixed for 10 parts with sodium carbonate, be put into
Merged in melting furnace, be finally sent into forming machine and the first wood plies 9 and the second wood plies 10 are made, it is standby;
9) material made of step 2), step 3), step 5), step 6), step 7) and step 8) is bonded, you can
Building panel is made.
Embodiment two:
Shown in reference picture 1, a kind of building panel includes plate body 1, and the plate body 1 is internally provided with sound-insulating layer 2, institute
State sound-insulating layer 2 and be internally provided with vacuum layer 3, the upper surface of sound-insulating layer 2 is provided with cystosepiment 4, the cystosepiment 4
More than one resonance ball 5 is internally provided with, the upper surface of cystosepiment 4 is provided with the first glass fibre cotton layer 6, the sound insulation
The lower surface of heat-insulation layer 2 is provided with the second glass fibre cotton layer 7, and the upper surface of the first glass fibre cotton layer 6 is provided with radiation proof
Layer 8, the upper surface of radiation protective layer 8 are provided with the first wood plies 9, and the lower surface of the second glass fiber cotton layer 7 is provided with the
Two wood plies 10.
The plate body 1 is internally provided with diatom ooze (not shown), can absorb sound wave, improves the soundproof effect of building panel.
The plate body 1 is internally provided with the reinforcing bar (not shown) of one or more, improves the intensity of building panel.
Spring (not shown) is provided between the resonance ball 5 and cystosepiment 4, preventing from resonating when ball 5 shakes makes a noise.
The upper surface of first wood plies 9 and the lower surface of the second wood plies 10 are provided with anti-slip veins (not shown), profit
In the carrying of building panel.
The manufacture method of plate body:
1) 25 parts of stalk is put into airslide disintegrating mill and particle is made, then particle is put into cauldron, add hydrogen peroxide 6.5
Part, 87.5 DEG C are heated to, continues 2.5 hours, it is standby;
2) material in step 1) is sent into forming machine and sound-insulating layer 2 is made, then will be made inside sound-insulating layer 2
Vacuum layer 3, it is standby;
3) by 7.5 parts of 11 parts of phenolphthalein resin, 9 parts of dichloroethanes, 9 parts of sodium alkyl sulfonate and m-phenylene diamine (MPD) feeding casting machines
In, cystosepiment 4 is made, it is standby;
4) by grind into powder in 14 parts of feeding grinders of string, it is re-fed into cauldron, heats 95 DEG C, continue 1.5
Hour, slurries are cooked into, is re-fed into forming machine and resonance ball 5 is made, it is standby;
5) the resonance ball 5 in step 4) is embedded in cystosepiment, it is standby;
6) 13 parts of 25 parts of lime stone, 26 parts of glass waste and sodium carbonate are sent into melting furnace, fused mass is made, stirring is equal
It is even, it is sent into forming machine and the first glass fibre cotton layer 6 and the second mineral wool layer 7 is made, it is standby;
7) 18 parts of 15 parts of graphite, 16 parts of iron oxide and iron powder are sent into melting furnace, fused mass is made, stirs, send
Enter to be made radiation protective layer 8 in forming machine, it is standby;
8) powder will be ground into 25 parts of feeding airslide disintegrating mills of timber, then powder is mixed for 13 parts with sodium carbonate, be put into
Merged in melting furnace, be finally sent into forming machine and the first wood plies 9 and the second wood plies 10 are made, it is standby;
9) material made of step 2), step 3), step 5), step 6), step 7) and step 8) is bonded, you can
Building panel is made.
Embodiment three:
Shown in reference picture 1, a kind of building panel includes plate body 1, and the plate body 1 is internally provided with sound-insulating layer 2, institute
State sound-insulating layer 2 and be internally provided with vacuum layer 3, the upper surface of sound-insulating layer 2 is provided with cystosepiment 4, the cystosepiment 4
More than one resonance ball 5 is internally provided with, the upper surface of cystosepiment 4 is provided with the first glass fibre cotton layer 6, the sound insulation
The lower surface of heat-insulation layer 2 is provided with the second glass fibre cotton layer 7, and the upper surface of the first glass fibre cotton layer 6 is provided with radiation proof
Layer 8, the upper surface of radiation protective layer 8 are provided with the first wood plies 9, and the lower surface of the second glass fiber cotton layer 7 is provided with the
Two wood plies 10.
The plate body 1 is internally provided with diatom ooze (not shown), can absorb sound wave, improves the soundproof effect of building panel.
The plate body 1 is internally provided with the reinforcing bar (not shown) of one or more, improves the intensity of building panel.
Spring (not shown) is provided between the resonance ball 5 and cystosepiment 4, preventing from resonating when ball 5 shakes makes a noise.
The upper surface of first wood plies 9 and the lower surface of the second wood plies 10 are provided with anti-slip veins (not shown), profit
In the carrying of building panel.
The manufacture method of plate body:
1) 28 parts of stalk is put into airslide disintegrating mill and particle is made, then particle is put into cauldron, add 8 parts of hydrogen peroxide,
90 DEG C are heated to, continues 3 hours, it is standby;
2) material in step 1) is sent into forming machine and sound-insulating layer 2 is made, then will be made inside sound-insulating layer 2
Vacuum layer 3, it is standby;
3) by 9 parts of 12 parts of phenolphthalein resin, 12 parts of dichloroethanes, 10 parts of sodium alkyl sulfonate and m-phenylene diamine (MPD) feeding casting machines
In, cystosepiment 4 is made, it is standby;
4) by grind into powder in 16 parts of feeding grinders of string, it is re-fed into cauldron, heats 100 DEG C, it is small to continue 2
When, slurries are cooked into, is re-fed into forming machine and resonance ball 5 is made, it is standby;
5) the resonance ball 5 in step 4) is embedded in cystosepiment 4, it is standby;
6) 16 parts of 30 parts of lime stone, 28 parts of glass waste and sodium carbonate are sent into melting furnace, fused mass is made, stirring is equal
It is even, it is sent into forming machine and the first glass fibre cotton layer 6 and the second mineral wool layer 7 is made, it is standby;
7) 20 parts of 18 parts of graphite, 18 parts of iron oxide and iron powder are sent into melting furnace, fused mass is made, stirs, send
Enter to be made radiation protective layer 8 in forming machine, it is standby;
8) powder will be ground into 28 parts of feeding airslide disintegrating mills of timber, then powder is mixed for 16 parts with sodium carbonate, be put into
Merged in melting furnace, be finally sent into forming machine and the first wood plies 9 and the second wood plies 10 are made, it is standby;
9) material made of step 2), step 3), step 5), step 6), step 7) and step 8) is bonded, you can
Building panel is made.
Experimental example:
From embodiment one, embodiment two, the sample of embodiment three and common building plate, it is divided into four groups, it is relatively more each to set up
Build the performance of plate.
Comparing result see the table below:
As can be seen here, the building panel performance in embodiment two is best, can reach optimal implementation result.
Beneficial effects of the present invention are:Sound-insulating layer inside the building panel is made of stalk, not only sound-insulating
It is good, and cost is low, and building panel is internally provided with the cystosepiment with resonance ball, is additionally provided with vacuum layer and glass fibre cotton layer,
Further increase soundproof effect;By being provided with radiation protective layer, the incoming of solar radiation can be prevented, improves building panel
Effect of heat insulation.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, it should all cover within the scope of the present invention.
Claims (1)
- A kind of 1. building panel, it is characterised in that:The building panel by match in parts by weight stalk 22-28 parts, hydrogen peroxide 5-8 Part, phenolphthalein resin 10-12 parts, dichloroethanes 6-12 parts, sodium alkyl sulfonate 8-10 parts, m-phenylene diamine (MPD) 6-9 parts, string 12- 16 parts, lime stone 20-30 parts, glass waste 24-28 parts, sodium carbonate 10-16 parts, graphite 12-18 parts, iron oxide 14-18 parts, iron Powder 16-20 parts, timber 22-28 parts and sodium carbonate 10-16 parts are made, and the manufacture method of building panel, comprise the following steps:1) stalk 22-28 parts are put into airslide disintegrating mill and particle are made, then particle is put into cauldron, add hydrogen peroxide 5-8 parts, 85-90 DEG C is heated to, continues 2-3 hours, it is standby;2) material in step 1) is sent into forming machine and sound-insulating layer is made, then vacuum will be made inside sound-insulating layer Layer, it is standby;3) phenolphthalein resin 10-12 parts, dichloroethanes 6-12 parts, sodium alkyl sulfonate 8-10 parts and m-phenylene diamine (MPD) 6-9 parts are sent into and poured In note machine, cystosepiment is made, it is standby;4) string 12-16 parts are sent into grind into powder in grinder, be re-fed into cauldron, heat 90-100 DEG C, continued 1-2 hours, slurries are cooked into, are re-fed into forming machine and resonance ball is made, it is standby;5) the resonance ball in step 4) is embedded in cystosepiment, it is standby;6) lime stone 20-30 parts, glass waste 24-28 parts and sodium carbonate 10-16 parts are sent into melting furnace, fused mass are made, Stir, be sent into forming machine and the first glass fibre cotton layer and the second mineral wool layer is made, it is standby;7) graphite 12-18 parts, iron oxide 14-18 parts and iron powder 16-20 parts are sent into melting furnace, fused mass is made, stirring is equal It is even, it is sent into forming machine and radiation protective layer is made, it is standby;8) timber 22-28 parts are sent into airslide disintegrating mill and are ground into powder, then powder is mixed with sodium carbonate 10-16 parts, put Enter in melting furnace and merge, be finally sent into forming machine and wood plies are made, it is standby;9) material made of step 2), step 3), step 5), step 6), step 7) and step 8) is bonded, you can be made Building panel.