CN107419357A - The preparation method of white bamboo charcoal negative ion fiber - Google Patents
The preparation method of white bamboo charcoal negative ion fiber Download PDFInfo
- Publication number
- CN107419357A CN107419357A CN201710815592.6A CN201710815592A CN107419357A CN 107419357 A CN107419357 A CN 107419357A CN 201710815592 A CN201710815592 A CN 201710815592A CN 107419357 A CN107419357 A CN 107419357A
- Authority
- CN
- China
- Prior art keywords
- bamboo charcoal
- negative ion
- white bamboo
- charcoal negative
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of preparation method of white bamboo charcoal negative ion fiber, described white bamboo charcoal negative ion fiber includes following two compositions according to percentage by weight：The white bamboo charcoal negative ion master batch 5 10% of nanometer；Slices of caprone 90 95%；Described preparation method is to carry out spinning by melt spinning process, is mainly included the following steps that:（1）Dry；（2）Prepare spin fluid；（3）Spinning；（4）Post-processing, finally give white bamboo charcoal negative ion fiber.Fabric made of the white bamboo charcoal negative ion fiber that the preparation method of the present invention is produced, due to being mixed with white bamboo charcoal and negative-ion fiber, and has following technique effect：（1）The degerming effect of smelly eliminating；（2）Negative ion health effect；（3）Far infrared heating heat-preserving function.
Description
Technical field
The present invention relates to a kind of preparation method of white bamboo charcoal negative ion fiber, belong to chemical fibre field.
Background technology
Negative-ion fiber, is a kind of fiber with negative ion releasing function, discharges caused anion by the fiber
To improving air quality, environment with obvious effect, particularly for anion to the health-care effect of human body, more and more is people
Received.The English of anion is ANION, is negatively charged oxygen molecule.At present, negative-ion fiber be made it is main
It is by the production process of fiber, adding a kind of nano-scaled electric stone powder with negative ion releasing function, making these
Tourmaline powder is embedded in the surface of fiber, the electronics launched by these tourmaline, hits the oxygen molecule of fiber peripheral, is allowed to
As electrically charged negative oxygen ion（Normally referred to as anion）.At present, negative-ion fiber on the market mainly have viscose glue bear from
Subbundle, terylene negative-ion fiber, polypropylene fibre negative-ion fiber, acrylic fibers negative-ion fiber etc..
Bamboo charcoal can send clear and melodious metallic sound when tapping, the manufactured bamboo charcoal under 750 DEG C of high temperature above, also have well
Electric conductivity.And the white one kind of bamboo charcoal as bamboo charcoal, it is using the Japanese Meng Zongzhu grown as raw material, in 800 DEG C~1000 DEG C of height
The bamboo charcoal formed under warm destructive distillation, also referred to as " binchotan "；It is different from general bamboo charcoal, the white bamboo charcoal that just system is formed, is also in
Black, but general silver-colored light, therefore referred to as white bamboo charcoal, are a kind of advanced bamboo charcoals.Bamboo vinegar about contains 200 species compounds, and it is led
Function is wanted to have fungi-proofing, mould proof, desinsection, deodorization, promote plant growth, the activity for keeping plant and the effect such as freshness, improved soil.
At present there has been no correlation white bamboo charcoal to be mixed with anion material, prepare polyamide fibre functional fiber product and
Its preparation method.
The content of the invention
It is an object of the invention to provide a kind of polyamide fibre functional fiber containing white bamboo charcoal and anion material, make white bamboo charcoal
Brought together with the advantages of anion material.
The present invention white bamboo charcoal negative ion fiber preparation method, described raw materials for production according to percentage by weight include with
Lower two kinds of compositions：
The white bamboo charcoal negative ion master batch 5-10% of nanometer
Slices of caprone 90-95%；
The preparation method of described white bamboo charcoal negative ion fiber is to carry out spinning by melt spinning process, mainly including following step
Suddenly:
（1）Dry：The white bamboo charcoal negative ion master batch of nanometer is dried；
（2）Prepare spin fluid：According to certain ratio, using master batch export note color pump accurately add the white bamboo charcoal of nanometer bear from
Primary and secondary grain, with slices of caprone mixed melting；
（3）Spinning：Melting is extruded into fine high poly- melt from the spinneret orifice of spinning head, cooled down in surrounding air or water solidifying
Gu into silk, in process of production, stable temperature, humidity and pressure are kept, the temperature in spinning process is 260~262 DEG C；
（4）Winding：Manufactured fiber is carried out to oil cooling antistatic treatment, pre- network, stretching heat-shaping, pre- net successively
Network, winding, balance, inspection, packaging and inspection process, finally give white bamboo charcoal negative ion fiber.
Preferably,
The preparation method of described white bamboo charcoal negative ion fiber, described raw material according to percentage by weight include it is following two into
Point：
The white bamboo charcoal negative ion master batch 8% of nanometer
Slices of caprone 92%.
Fabric made of the white bamboo charcoal negative ion fiber that the preparation method of the white bamboo charcoal negative ion fiber of the present invention is produced,
Due to being mixed with white bamboo charcoal and negative-ion fiber, and there is following technique effect：（1）The degerming effect of smelly eliminating；（2）Negative ion health
Effect；（3）Far infrared heating heat-preserving function.
Embodiment
With reference to embodiment, the present invention is further illustrated, but the scope of protection of present invention is not limited to reality
Apply the scope of example expression.
Embodiment 1
In the present embodiment, the raw material composition and preparation method step of white bamboo charcoal negative ion fiber are as follows：
1st, raw material and weight：
The white bamboo charcoal negative ion master batch 50g of nanometer
Slices of caprone 950g
2nd, method：Spinning is carried out by melt spinning process, mainly included the following steps that:
（1）Dry：The white bamboo charcoal negative ion master batch of nanometer is dried；
（2）Prepare spin fluid：According to certain ratio, using master batch export note color pump accurately add the white bamboo charcoal of nanometer bear from
Primary and secondary grain, with slices of caprone mixed melting；
（3）Spinning：Melting is extruded into fine high poly- melt from the spinneret orifice of spinning head, cooled down in surrounding air or water solidifying
Gu into silk, in process of production, stable temperature, humidity and pressure are kept, the temperature in spinning process is 260~262 DEG C；
（4）Winding：Manufactured fiber is carried out to oil cooling antistatic treatment, pre- network, stretching heat-shaping, pre- net successively
Network, winding, balance, inspection, packaging and inspection process, finally give white bamboo charcoal negative ion fiber.
Embodiment 2
In the present embodiment, the raw material composition and preparation method step of white bamboo charcoal negative ion fiber are as follows：
1st, raw material and weight：
The white bamboo charcoal negative ion master batch 100g of nanometer
Slices of caprone 900g
2nd, method：It is same as Example 1.
Embodiment 3
In the present embodiment, the raw material composition and preparation method step of white bamboo charcoal negative ion fiber are as follows：
1st, raw material and weight：
The white bamboo charcoal negative ion master batch 80g of nanometer
Slices of caprone 920g
2nd, method：It is same as Example 1.
Claims (2)
1. the preparation method of white bamboo charcoal negative ion fiber, it is characterised in that described raw materials for production include according to percentage by weight
Following two compositions：
The white bamboo charcoal negative ion master batch 5-10% of nanometer
Slices of caprone 90-95%；
The preparation method of described white bamboo charcoal negative ion fiber is to carry out spinning by melt spinning process, mainly including following step
Suddenly:
（1）Dry：The white bamboo charcoal negative ion master batch of nanometer is dried；
（2）Prepare spin fluid：According to certain ratio, using master batch export note color pump accurately add the white bamboo charcoal of nanometer bear from
Primary and secondary grain, with slices of caprone mixed melting；
（3）Spinning：Melting is extruded into fine high poly- melt from the spinneret orifice of spinning head, cooled down in surrounding air or water solidifying
Gu into silk, in process of production, stable temperature, humidity and pressure are kept, the temperature in spinning process is 260~262 DEG C；
（4）Winding：Manufactured fiber is carried out to oil cooling antistatic treatment, pre- network, stretching heat-shaping, pre- net successively
Network, winding, balance, inspection, packaging and inspection process, finally give white bamboo charcoal negative ion fiber.
2. the preparation method of white bamboo charcoal negative ion fiber according to claim 1, it is characterised in that described raw material according to
Percentage by weight includes following two compositions：
The white bamboo charcoal negative ion master batch 8% of nanometer
Slices of caprone 92%.