CN107418188A - A kind of multifunctional polyurethane bubble silk floss and preparation method thereof - Google Patents
A kind of multifunctional polyurethane bubble silk floss and preparation method thereof Download PDFInfo
- Publication number
- CN107418188A CN107418188A CN201710330583.8A CN201710330583A CN107418188A CN 107418188 A CN107418188 A CN 107418188A CN 201710330583 A CN201710330583 A CN 201710330583A CN 107418188 A CN107418188 A CN 107418188A
- Authority
- CN
- China
- Prior art keywords
- continuous
- parts
- bubble
- polyurethane
- steeping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to make up to steep continuous technical field, more particularly to a kind of multifunctional polyurethane bubble silk floss and preparation method thereof, multifunctional polyurethane bubble is continuous to be included steeping continuous body, the continuous body of bubble includes steeping continuous top and steeps continuous bottom, the edge convex for steeping continuous top is provided with upper flange, the edge convex for steeping continuous bottom is provided with lower flange, steeps continuous top and the continuous bottom of bubble passes through upper flange and lower flange hot pressing is bonded;At least one side of the continuous body of bubble is fitted with TPU membrane.The present invention at least one side for steeping continuous body by being fitted with TPU membrane, with preferable gas permeability, and effectively block external world water it can be entered by supporting plane in the continuous body of bubble, play a part of water proof, waterproof, and then reduce growth and breeding of the bacterium on continuous body is steeped, and it is avoided that extraneous water influences the continuous using effect of bubble, moreover it is possible to avoid the germ contamination bubble using bubble when continuous on hand continuous, extend the service life of bubble silk floss.
Description
Technical field
The present invention relates to make up to steep continuous technical field, and in particular to a kind of multifunctional polyurethane bubble silk floss and preparation method thereof.
Background technology
Polyurethane is a kind of emerging high-molecular organic material, is described as " the fifth-largest plastics ", wide because of its premium properties
It is general to be applied to the department such as automobile making, civil construction, petrochemical industry, electromechanics, ship, medical treatment, agricultural, and flexible polyurethane foaming material
Material is widely used in making various " bubble is continuous " products.
But the bubble silk floss of cosmetic, powder puff etc. at present, lack with waterproof, are easily accessible bubble every the separation layer of liquid, extraneous water
In silk floss, bacterium is caused to grow and breed in bubble is continuous, and extraneous water also reduces the continuous absorption to cosmetic foundation of bubble, very greatly
Using effect is reduced to degree, and then causes the continuous service life of bubble very short;In addition, current cosmetic bubble is continuous, powder puff, skin care
Effect is poor, mostly bubble it is continuous itself not skin care the effect of act on.
The content of the invention
In order to overcome shortcoming and defect present in prior art, it is an object of the invention to provide a kind of multi-functional poly- ammonia
Ester bubble is continuous, and multifunctional polyurethane bubble is continuous by being fitted with TPU membrane at least one side for steeping continuous body, has preferably ventilative
Property, play a part of water proof, waterproof, reduce growth and breeding of the bacterium on continuous body is steeped, improve the continuous using effect of bubble,
Extend service life.
Another object of the present invention is to provide a kind of multifunctional polyurethane bubble continuous preparation method, preparation method operation
Simple and convenient, steady quality, production efficiency is high, and production cost is low, can large-scale industrial production.
The purpose of the present invention is achieved through the following technical solutions:A kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, institute
Stating the continuous body of bubble includes steeping continuous top and steeps continuous bottom, and the edge convex for steeping continuous top is provided with upper flange, steeps the side of continuous bottom
Edge convex is provided with lower flange, steeps continuous top and the continuous bottom of bubble passes through upper flange and lower flange hot pressing is bonded;The continuous body of bubble
At least one side be fitted with TPU membrane.
The present invention has preferable gas permeability, plays water proof, prevents by being fitted with TPU membrane at least one side for steeping continuous body
The effect of water, growth and breeding of the bacterium on continuous body is steeped are reduced, improve the continuous using effect of bubble, extend service life.
Preferably, the layer of polyurethane includes the raw material of following parts by weight:
Polyurethane prepolymer 60-70 parts
Surfactant 5-15 parts
Hardening agent 5-10 parts
Function composition 15-25 parts
Foaming agent 2-8 parts
Water 25-35 parts.
The bubble silk floss body of the present invention strictly controls the dosage of each raw material by using above-mentioned raw materials, phase between each raw material
Mutual concerted reaction, the overall obtained continuous body of bubble have preferable hydrophily, skin-friendly and pliability;By using foaming agent,
Make the abscess of the obtained continuous body of bubble fine and closely woven uniformly, improve the continuous close mealiness of bubble;By using hardening agent, make obtained bubble continuous
Body has preferable constancy and resilience, is unlikely to deform;By using functional component, make bubble is continuous itself to there is skin care work(
Effect, enrich the continuous using effect of bubble.
Preferably, the polyurethane prepolymer includes the raw material of following parts by weight:Toluene di-isocyanate(TDI) polyalcohol pre-polymerization
Thing 25-40 parts, poly methylene poly phenyl poly isocyanate polyol prepolymer 20-30 parts, stearyl ether 2-8 parts, good blue red 1-3
Part and calcium carbonate 1-3 parts.
The polyurethane prepolymer of the present invention strictly controls the dosage of each raw material by using above-mentioned raw materials, can make to be made
Polyurethane prepolymer there is preferable stability and antibiotic property, the stearyl ether of use is as nonionic alcohol ether emulsifying agent, tool
Have an excellent emulsifying ability, splendid skin compatibility, the Jia Landan of use is nontoxic as antiseptic, to human body skin without
Injury, and the antibacterial action of prepolymer is improved, obtained bubble silk floss is not easy breed bacteria or bacterial growth;And above-mentioned prepolymer
Raw material can cooperate with other continuous raw materials of bubble, concerted reaction, make obtained bubble is continuous to have preferable close mealiness and skin-friendly.
Preferably, the surfactant is nonionic surface active agent, and the nonionic surface active agent is the moon
Cinnamic alcohol APEO, alkylolamides APEO, fatty acid methyl ester ethoxylate, polyoxyethylene carboxylate and embedding
At least one of section polyoxyethylene polyoxypropylene ether;The foaming agent is by azodicarbonamide, azo isobutyronitrile, azo
At least one of two diisopropyl carbonates, unifor and sodium acid carbonate;The hardening agent be by BDO and
Diglycol is using parts by weight as 1.5-2.5:The mixture of 1 composition.
The present invention by using above-mentioned raw materials be used as surfactant, stability is good, easily with other raw materials interaction, and
Side effect is not produced, makes the obtained continuous body of bubble that there is preferable flexibility and close mealiness, resilience by mutual concerted reaction
Height, it is unlikely to deform;Wherein, the Block polyoxyethylene-polyethenoxy ether includes propane diols polyoxyethylene poly-oxygen propylene aether, third
Triol polyoxyethylene poly-oxygen propylene aether, glycerine polyoxyethylene polyoxypropylene blocked copolymer, ethylenediamine polyoxyethylene polyoxy
Polypropylene block formula polyethers, polysiloxane polyether copolymer etc..It is more highly preferred to, the surfactant is lived for non-ionic surface
Property agent, the nonionic surface active agent is by alkylolamides APEO, polyoxyethylene carboxylate and block polyoxy
Ethene-polyethenoxy ether compares 2.5-3.5 with weight:1.2-1.8:The mixture of 1 composition.
For the present invention by using above-mentioned raw materials as foaming agent, foaming capacity is strong, and stability is good, easily mutual with other raw materials
Effect, and side effect is not produced, make the obtained continuous body of bubble that there is preferable flexibility and close mealiness by mutual concerted reaction,
Resilience is high, is unlikely to deform, can make the expansion density of bubble silk floss body in 0.01-0.05g/cm3, and unifor and carbonic acid
Hydrogen sodium need to share in the lump.It is more highly preferred to, the foaming agent is with weight by nitrogen diformamide, unifor and sodium acid carbonate
Measure ratio 1:1.5-2.5:1.0-1.5 the mixture of composition.
For the present invention by using above-mentioned raw materials as hardening agent, stability is good, is easily interacted with other raw materials, and do not produce pair
Effect, make the obtained continuous body of bubble that there is preferable flexibility and close mealiness by mutual concerted reaction, resilience is high, is unlikely to deform.
Preferably, the function composition is to compare 1.5-2.5 by plant extracts and essential oil with weight:The mixture of 1 composition.
Preferably, the plant extracts includes the raw material of following parts by weight:Marine algae extract 0.1-1.0 parts, aloe carry
Take thing 0.5-1.5 parts, Honegsukle flower P.E 0.8-1.2 parts, Chinese torreya extract 0.5-1.0 parts;The essential oil includes following weight
The raw material of part:Tea tree ethereal oil 1.2-1.8 parts, Lavender 0.8-1.2 parts, sandalwood essential oil 0.3-0.8 parts.
The present invention, as functional component, and strictly controls plant extract by using the mixture of plant extracts and essential oil
The dosage of the mixed proportion and each material composition of thing and essential oil, the continuous effect with skin care of obtained bubble, and the feelings that can releive can be made
Thread, alleviate pressure, enrich the use function and using effect of polyurethane foam.
Preferably, the TPU membrane includes the raw material of following parts by weight:
'-diphenylmethane diisocyanate 15-30 parts
Toluene di-isocyanate(TDI) 20-35 parts
2,2- dihydromethyl propionic acid 10-15 parts
Chain extender 8-16 parts
Sorbierite 3-7 parts
Expoxy propane 1-3 parts
Laurate 2-8 parts.
The TPU membrane of the present invention strictly controls the dosage of each raw material by using above-mentioned raw materials, is mutually assisted between each raw material
With reaction, TPU membrane made from entirety has gas permeability, water proofing property, heat resistance and processing characteristics, the isocyanide of diphenyl-methane two of use
Acid esters and toluene di-isocyanate(TDI) carry out prepolymerization reaction as primary raw material, the 2- hydrocarbon methylpropanoic acid of use as hydrophilic monomer,
Promote the reaction process of reaction system, the chain extender of use makes the further prepolymerization reaction of reaction system, sorbierite, the epoxy of use
Propane, laurate play anti-corrosion, antibacterial effect in TPU membrane system, and then continuous realize of bubble is suppressed bacteria breed, breeding
Effect.
Preferably, the chain extender is trimethylolpropane, α-allylin, methyl diethanolamine and diethyl first
At least one of phenylenediamine.The present invention as chain extender, effectively facilitates TPU reaction system by using above-mentioned raw materials, and
Raw material components viscosity can be reduced, improves the intermiscibility of feed components, is easy to act on other raw material mutual cooperations, is made obtained
PTU films have preferable gas permeability, water proofing property, heat resistance and processing characteristics.It is more highly preferred to, the chain extender is by α-glycerine
Allyl ether and methyl diethanolamine are using weight ratio as 1:1.5-2.5 the mixture of composition.
Another object of the present invention is achieved through the following technical solutions:A kind of continuous preparation of above-mentioned multifunctional polyurethane bubble
Method, comprise the following steps:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 50-60s with 6000-9000r/min speed, then adds stearyl ether, with
5000-8000r/min speed stirring 25-35s, adds Jia Landan and calcium carbonate, with 10000-13000r/min speed
60-80s is stirred, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 4000-5000r/min
Speed stirring 5-6min, then add the mixing of 2- hydrocarbon methylpropanoic acid, 1-2min stirred with 4500-5500r/min speed, then
Sorbierite, expoxy propane and laurate are added, 5000-6000r/min speed stirring 3-5min, chain extender is eventually adding, mixes
Stirring is closed, shaping, TPU membrane is made;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
The step(3)In, the speed of agitator of mixing is 8000-12000r/min, mixing time 5-10min;
The hot pressing laminate pressure for steeping continuous top and the continuous bottom of bubble is 80-100Kg/cm2, the thermal-adhering temperature of TPU membrane is 90-130 DEG C,
The heat posted resultant pressure of TPU membrane is 60-80Kg/cm2。
The present invention prepares multifunctional polyurethane bubble silk floss by using above-mentioned steps, and strictly controls the addition of each raw material suitable
Sequence, addition, and the state modulator of each reaction condition, the stability of whole reaction system can be improved, and simple to operate be easy to
Control, steady quality, production efficiency are high, and production cost is low, can large-scale industrial production, and can have obtained TPU membrane
Preferable gas permeability and water proofing property, and then growth and breeding of the bacterium on continuous body is steeped are reduced, and it is avoided that extraneous water influences
Continuous using effect is steeped, the using effect of polyurethane foam is improved, extends service life.
The beneficial effects of the present invention are:The present invention by being fitted with TPU membrane at least one side for steeping continuous body, have compared with
Good gas permeability, and effectively block external world water can be entered by supporting plane in the continuous body of bubble, play a part of water proof, waterproof,
And then growth and breeding of the bacterium on continuous body is steeped are reduced, and it is avoided that extraneous water influences the continuous using effect of bubble, moreover it is possible to keep away
Exempt from, using germ contamination bubble silk floss when steeping continuous on hand, to extend the continuous service life of bubble, health, safe cosmetic are provided for user
Experience.
The continuous preparation method of multifunctional polyurethane bubble of the present invention is simple to operate, and steady quality, production efficiency is high, production
Cost is low, can large-scale industrial production.
Embodiment
For the ease of the understanding of those skilled in the art, with reference to embodiment, the present invention is further illustrated, real
The content that the mode of applying refers to not is limitation of the invention.
Embodiment 1
A kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, and the continuous body of bubble includes steeping continuous top and steeps continuous bottom, and bubble is continuous
The edge convex on top is provided with upper flange, and the edge convex for steeping continuous bottom is provided with lower flange, steeps continuous top and steeps continuous bottom
It is bonded by upper flange and lower flange hot pressing;At least one side of the continuous body of bubble is fitted with TPU membrane.
Wherein, the layer of polyurethane includes the raw material of following parts by weight:
60 parts of polyurethane prepolymer
5 parts of surfactant
5 parts of hardening agent
15 parts of function composition
2 parts of foaming agent
25 parts of water.
Wherein, the polyurethane prepolymer includes the raw material of following parts by weight:Toluene di-isocyanate(TDI) polyol prepolymer
25 parts, 20 parts of poly methylene poly phenyl poly isocyanate polyol prepolymer, 2 parts of stearyl ether, good blue red 1 part and calcium carbonate 1
Part.
Wherein, the surfactant is nonionic surface active agent, and the nonionic surface active agent is bay
Alcohol APEO;The foaming agent is by azodicarbonamide;The hardening agent is by BDO and a contracting diethyl two
Alcohol is using parts by weight as 1.5:The mixture of 1 composition.
Wherein, the function composition is with weight ratio 1.5 by plant extracts and essential oil:The mixture of 1 composition.
Wherein, the plant extracts includes the raw material of following parts by weight:0.1 part of marine algae extract, aloe extract 1.5
Part, 0.8 part of Honegsukle flower P.E, 1.0 parts of Chinese torreya extract;The essential oil includes the raw material of following parts by weight:Tea tree ethereal oil 1.2
Part, 1.2 parts of Lavender, 0.3 part of sandalwood essential oil.
Wherein, the TPU membrane includes the raw material of following parts by weight:
15 parts of '-diphenylmethane diisocyanate
20 parts of toluene di-isocyanate(TDI)
10 parts of 2,2- dihydromethyl propionic acids
8 parts of chain extender
3 parts of sorbierite
1 part of expoxy propane
2 parts of laurate.
Wherein, the chain extender is trimethylolpropane.
A kind of continuous preparation method of above-mentioned multifunctional polyurethane bubble, comprises the following steps:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 60s with 6000r/min speed, stearyl ether is then added, with 5000r/min's
Speed stirs 35s, adds Jia Landan and calcium carbonate, stirs 80s with 10000r/min speed, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 5000r/min speed
5min is stirred, then adds the mixing of 2- hydrocarbon methylpropanoic acid, 1min is stirred with 5500r/min speed, adds sorbierite, epoxy
Propane and laurate, 5min is stirred with 5000r/min speed, is eventually adding chain extender, is mixed, shaping, TPU is made
Film;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
Wherein, the step(3)In, the speed of agitator of mixing is 8000r/min, mixing time 10min;Bubble is continuous
Top and the hot pressing laminate pressure for steeping continuous bottom are 80Kg/cm2, the thermal-adhering temperature of TPU membrane is 130 DEG C, the thermal-adhering of TPU membrane
Pressure is 60Kg/cm2。
Embodiment 2
A kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, and the continuous body of bubble includes steeping continuous top and steeps continuous bottom, and bubble is continuous
The edge convex on top is provided with upper flange, and the edge convex for steeping continuous bottom is provided with lower flange, steeps continuous top and steeps continuous bottom
It is bonded by upper flange and lower flange hot pressing;At least one side of the continuous body of bubble is fitted with TPU membrane.
Wherein, the layer of polyurethane includes the raw material of following parts by weight:
63 parts of polyurethane prepolymer
8 parts of surfactant
6 parts of hardening agent
18 parts of function composition
4 parts of foaming agent
28 parts of water.
Wherein, the hydrophilic polyurethane prepolymers include the raw material of following parts by weight:Toluene di-isocyanate(TDI) polyalcohol
28 parts of prepolymer, 23 parts of poly methylene poly phenyl poly isocyanate polyol prepolymer, 4 parts of stearyl ether, it is good blue red 1.5 parts and
1.5 parts of calcium carbonate.
Wherein, the surfactant is nonionic surface active agent, and the nonionic surface active agent is alkyl
Alkylolamides APEO;The foaming agent is azo isobutyronitrile;The hardening agent is by BDO and a contracting diethyl two
Alcohol is using parts by weight as 1.8:The mixture of 1 composition.
Wherein, the function composition is with weight ratio 1.8 by plant extracts and essential oil:The mixture of 1 composition.
Wherein, the plant extracts includes the raw material of following parts by weight:0.3 part of marine algae extract, aloe extract 1.3
Part, 0.9 part of Honegsukle flower P.E, 0.8 part of Chinese torreya extract;The essential oil includes the raw material of following parts by weight:Tea tree ethereal oil 1.4
Part, 1.1 parts of Lavender, 0.4 part of sandalwood essential oil.
Wherein, the TPU membrane includes the raw material of following parts by weight:
18 parts of '-diphenylmethane diisocyanate
24 parts of toluene di-isocyanate(TDI)
1 part of 2,2- dihydromethyl propionic acids
10 parts of chain extender
4 parts of sorbierite
1.5 parts of expoxy propane
4 parts of laurate.
Wherein, the chain extender is α-allylin.
A kind of continuous preparation method of above-mentioned multifunctional polyurethane bubble, comprises the following steps:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 58s with 6500r/min speed, stearyl ether is then added, with 6000r/min's
Speed stirs 32s, adds Jia Landan and calcium carbonate, stirs 75s with 10700r/min speed, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 4800r/min speed
Stir 5.3min, then add the mixing of 2- hydrocarbon methylpropanoic acid, 1.3min is stirred with 5300r/min speed, add sorbierite,
Expoxy propane and laurate, 4.5min is stirred with 5300r/min speed, is eventually adding chain extender, is mixed, is molded, system
Obtain TPU membrane;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
Wherein, the step(3)In, the speed of agitator of mixing is 9000r/min, mixing time 9min;Bubble is continuous
Top and the hot pressing laminate pressure for steeping continuous bottom are 85Kg/cm2, the thermal-adhering temperature of TPU membrane is 120 DEG C, the thermal-adhering of TPU membrane
Pressure is 65Kg/cm2。
Embodiment 3
A kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, and the continuous body of bubble includes steeping continuous top and steeps continuous bottom, and bubble is continuous
The edge convex on top is provided with upper flange, and the edge convex for steeping continuous bottom is provided with lower flange, steeps continuous top and steeps continuous bottom
It is bonded by upper flange and lower flange hot pressing;At least one side of the continuous body of bubble is fitted with TPU membrane.
Wherein, the layer of polyurethane includes the raw material of following parts by weight:
65 parts of polyurethane prepolymer
10 parts of surfactant
7 parts of hardening agent
20 parts of function composition
5 parts of foaming agent
30 parts of water.
Wherein, the hydrophilic polyurethane prepolymers include the raw material of following parts by weight:Toluene di-isocyanate(TDI) polyalcohol
32 parts of prepolymer, 25 parts of poly methylene poly phenyl poly isocyanate polyol prepolymer, 8 parts of stearyl ether, good blue red 2 parts and carbon
Sour 2 parts of calcium.
Wherein, the surfactant is nonionic surface active agent, and the nonionic surface active agent is fat
Sour FMEE;The foaming agent is the diisopropyl carbonate of azo two;The hardening agent is by BDO and one
Diglycol ethylene is using parts by weight as 2:The mixture of 1 composition.
Wherein, the function composition is with weight ratio 2 by plant extracts and essential oil:The mixture of 1 composition.
Wherein, the plant extracts includes the raw material of following parts by weight:0.5 part of marine algae extract, aloe extract 1.0
Part, 1.0 parts of Honegsukle flower P.E, 0.7 part of Chinese torreya extract;The essential oil includes the raw material of following parts by weight:Tea tree ethereal oil 1.5
Part, 1.0 parts of Lavender, 0.5 part of sandalwood essential oil.
Wherein, the TPU membrane includes the raw material of following parts by weight:
23 parts of '-diphenylmethane diisocyanate
28 parts of toluene di-isocyanate(TDI)
12 parts of 2,2- dihydromethyl propionic acids
12 parts of chain extender
5 parts of sorbierite
2 parts of expoxy propane
5 parts of laurate.
Wherein, the chain extender is methyl diethanolamine.
A kind of continuous preparation method of above-mentioned multifunctional polyurethane bubble, comprises the following steps:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 55s with 7500r/min speed, stearyl ether is then added, with 6500r/min's
Speed stirs 30s, adds Jia Landan and calcium carbonate, stirs 70s with 11500r/min speed, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 4500r/min speed
Stir 5.5min, then add the mixing of 2- hydrocarbon methylpropanoic acid, 1.5min is stirred with 5000r/min speed, add sorbierite,
Expoxy propane and laurate, 4min is stirred with 5500r/min speed, is eventually adding chain extender, is mixed, is molded, is made
TPU membrane;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
Wherein, the step(3)In, the speed of agitator of mixing is 10000r/min, mixing time 8min;Bubble is continuous
Top and the hot pressing laminate pressure for steeping continuous bottom are 90Kg/cm2, the thermal-adhering temperature of TPU membrane is 110 DEG C, the thermal-adhering of TPU membrane
Pressure is 70Kg/cm2。
Embodiment 4
A kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, and the continuous body of bubble includes steeping continuous top and steeps continuous bottom, and bubble is continuous
The edge convex on top is provided with upper flange, and the edge convex for steeping continuous bottom is provided with lower flange, steeps continuous top and steeps continuous bottom
It is bonded by upper flange and lower flange hot pressing;At least one side of the continuous body of bubble is fitted with TPU membrane.
Wherein, the layer of polyurethane includes the raw material of following parts by weight:
68 parts of polyurethane prepolymer
13 parts of surfactant
8 parts of hardening agent
23 parts of function composition
6 parts of foaming agent
32 parts of water.
Wherein, the hydrophilic polyurethane prepolymers include the raw material of following parts by weight:Toluene di-isocyanate(TDI) polyalcohol
36 parts of prepolymer, 28 parts of poly methylene poly phenyl poly isocyanate polyol prepolymer, 6 parts of stearyl ether, it is good blue red 2.5 parts and
2.5 parts of calcium carbonate.
Wherein, the surfactant is nonionic surface active agent, and the nonionic surface active agent is fat
Sour polyoxyethylene ester;The foaming agent is azo isobutyronitrile;The hardening agent be by BDO and diglycol with
Parts by weight are 1.5-2.3:The mixture of 1 composition.
Wherein, the function composition is with weight ratio 2.3 by plant extracts and essential oil:The mixture of 1 composition.
Wherein, the plant extracts includes the raw material of following parts by weight:0.7 part of marine algae extract, aloe extract 0.8
Part, 1.1 parts of Honegsukle flower P.E, 0.6 part of Chinese torreya extract;The essential oil includes the raw material of following parts by weight:Tea tree ethereal oil 1.6
Part, 0.9 part of Lavender, 0.6 part of sandalwood essential oil.
Wherein, the TPU membrane includes the raw material of following parts by weight:
28 parts of '-diphenylmethane diisocyanate
32 parts of toluene di-isocyanate(TDI)
13 parts of 2,2- dihydromethyl propionic acids
14 parts of chain extender
6 parts of sorbierite
2.5 parts of expoxy propane
6 parts of laurate.
Wherein, the diethyl toluene diamine.
A kind of continuous preparation method of above-mentioned multifunctional polyurethane bubble, comprises the following steps:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 53s with 8000r/min speed, stearyl ether is then added, with 7500r/min's
Speed stirs 28s, adds Jia Landan and calcium carbonate, stirs 65s with 12300r/min speed, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 4300r/min speed
Stir 5.8min, then add the mixing of 2- hydrocarbon methylpropanoic acid, 1.8min is stirred with 4800r/min speed, add sorbierite,
Expoxy propane and laurate, 3.5min is stirred with 5800r/min speed, is eventually adding chain extender, is mixed, is molded, system
Obtain TPU membrane;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
Wherein, the step(3)In, the speed of agitator of mixing is 11000r/min, mixing time 7min;Bubble is continuous
Top and the hot pressing laminate pressure for steeping continuous bottom are 95Kg/cm2, the thermal-adhering temperature of TPU membrane is 100 DEG C, the thermal-adhering of TPU membrane
Pressure is 75Kg/cm2。
Embodiment 5
A kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, and the continuous body of bubble includes steeping continuous top and steeps continuous bottom, and bubble is continuous
The edge convex on top is provided with upper flange, and the edge convex for steeping continuous bottom is provided with lower flange, steeps continuous top and steeps continuous bottom
It is bonded by upper flange and lower flange hot pressing;At least one side of the continuous body of bubble is fitted with TPU membrane.
Wherein, the layer of polyurethane includes the raw material of following parts by weight:
70 parts of polyurethane prepolymer
15 parts of surfactant
10 parts of hardening agent
25 parts of function composition
8 parts of foaming agent
35 parts of water.
Wherein, the hydrophilic polyurethane prepolymers include the raw material of following parts by weight:Toluene di-isocyanate(TDI) polyalcohol
40 parts of prepolymer, 30 parts of poly methylene poly phenyl poly isocyanate polyol prepolymer, 8 parts of stearyl ether, good blue red 3 parts and carbon
Sour 3 parts of calcium.
Wherein, the surfactant is nonionic surface active agent, and the nonionic surface active agent is block
Polyoxyethylene polyoxypropylene ether;The foaming agent is azodicarbonamide;The hardening agent is by BDO and a contracting two
Ethylene glycol is using parts by weight as 2.5:The mixture of 1 composition.
Wherein, the function composition is with weight ratio 2.5 by plant extracts and essential oil:The mixture of 1 composition.
Wherein, the plant extracts includes the raw material of following parts by weight:1.0 parts of marine algae extract, aloe extract 0.5
Part, 1.2 parts of Honegsukle flower P.E, 0.5 part of Chinese torreya extract;The essential oil includes the raw material of following parts by weight:Tea tree ethereal oil 1.8
Part, 0.8 part of Lavender, 0.8 part of sandalwood essential oil.
Wherein, the TPU membrane includes the raw material of following parts by weight:
30 parts of '-diphenylmethane diisocyanate
35 parts of toluene di-isocyanate(TDI)
15 parts of 2,2- dihydromethyl propionic acids
16 parts of chain extender
7 parts of sorbierite
3 parts of expoxy propane
8 parts of laurate.
Wherein, the chain extender is diethyl toluene diamine.
A kind of continuous preparation method of above-mentioned multifunctional polyurethane bubble, comprises the following steps:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 50s with 9000r/min speed, stearyl ether is then added, with 8000r/min's
Speed stirs 25s, adds Jia Landan and calcium carbonate, stirs 60s with 13000r/min speed, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 4000r/min speed
6min is stirred, then adds the mixing of 2- hydrocarbon methylpropanoic acid, 2min is stirred with 4500r/min speed, adds sorbierite, epoxy
Propane and laurate, 3-5min is stirred with 6000r/min speed, is eventually adding chain extender, is mixed, shaping, TPU is made
Film;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
Wherein, the step(3)In, the speed of agitator of mixing is 12000r/min, mixing time 5min;Bubble is continuous
Top and the hot pressing laminate pressure for steeping continuous bottom are 100Kg/cm2, the thermal-adhering temperature of TPU membrane is 90 DEG C, the thermal-adhering of TPU membrane
Pressure is 80Kg/cm2。
Embodiment 6
The difference of the present embodiment and above-described embodiment 1 is:
In the continuous body of the bubble, the surfactant is nonionic surface active agent, the nonionic surface active agent
By alkylolamides APEO, polyoxyethylene carboxylate and Block polyoxyethylene-polyethenoxy ether with weight ratio 2.5:
1.8:The mixture of 1 composition.
In the continuous body of bubble, the foaming agent is with weight by nitrogen diformamide, unifor and sodium acid carbonate
Than 1:2.5:The mixture of 1.0 compositions.
In the TPU membrane, the chain extender is using weight ratio as 1 by α-allylin and methyl diethanolamine:1.5
The mixture of composition.
Embodiment 7
The difference of the present embodiment and above-described embodiment 2 is:
In the continuous body of the bubble, the surfactant is nonionic surface active agent, the nonionic surface active agent
By alkylolamides APEO, polyoxyethylene carboxylate and Block polyoxyethylene-polyethenoxy ether with weight ratio 2.8:
1.6:The mixture of 1 composition.
In the continuous body of bubble, the foaming agent is with weight by nitrogen diformamide, unifor and sodium acid carbonate
Than 1:2.3:The mixture of 1.1 compositions.
In the TPU membrane, the chain extender is using weight ratio as 1 by α-allylin and methyl diethanolamine:1.8
The mixture of composition.
Embodiment 8
The difference of the present embodiment and above-described embodiment 3 is:
In the continuous body of the bubble, the surfactant is nonionic surface active agent, the nonionic surface active agent
By alkylolamides APEO, polyoxyethylene carboxylate and Block polyoxyethylene-polyethenoxy ether with weight ratio 3:
1.5:The mixture of 1 composition.
In the continuous body of bubble, the foaming agent is with weight by nitrogen diformamide, unifor and sodium acid carbonate
Than 1:2:The mixture of 1.2 compositions.
In the TPU membrane, the chain extender is using weight ratio as 1 by α-allylin and methyl diethanolamine:2 groups
Into mixture.
Embodiment 9
The difference of the present embodiment and above-described embodiment 4 is:
In the continuous body of the bubble, the surfactant is nonionic surface active agent, the nonionic surface active agent
By alkylolamides APEO, polyoxyethylene carboxylate and Block polyoxyethylene-polyethenoxy ether with weight ratio 3.2:
1.4:The mixture of 1 composition.
In the continuous body of bubble, the foaming agent is with weight by nitrogen diformamide, unifor and sodium acid carbonate
Than 1:1.8:The mixture of 1.3 compositions.
In the TPU membrane, the chain extender is using weight ratio as 1 by α-allylin and methyl diethanolamine:2.3
The mixture of composition.
Embodiment 10
The difference of the present embodiment and above-described embodiment 5 is:
In the continuous body of the bubble, the surfactant is nonionic surface active agent, the nonionic surface active agent
By alkylolamides APEO, polyoxyethylene carboxylate and Block polyoxyethylene-polyethenoxy ether with weight ratio 3.5:
1.2:The mixture of 1 composition.
In the continuous body of bubble, the foaming agent is with weight by nitrogen diformamide, unifor and sodium acid carbonate
Than 1:1.5:The mixture of 1.5 compositions.
In the TPU membrane, the chain extender is using weight ratio as 1 by α-allylin and methyl diethanolamine:2.5
The mixture of composition.
Above-described embodiment is the preferable implementation of the present invention, and in addition, the present invention can be realized with other manner,
Do not depart from and any on the premise of present inventive concept obviously replace within protection scope of the present invention.
Claims (10)
1. a kind of multifunctional polyurethane bubble is continuous, including the continuous body of bubble, it is characterised in that:The continuous body of the bubble include steeping continuous top and
Continuous bottom is steeped, the edge convex for steeping continuous top is provided with upper flange, and the edge convex for steeping continuous bottom is provided with lower flange, steeps on silk floss
Portion and the continuous bottom of bubble pass through upper flange and lower flange hot pressing is bonded;At least one side of the continuous body of bubble is fitted with TPU membrane.
2. a kind of multifunctional polyurethane bubble according to claim 1 is continuous, it is characterised in that:The layer of polyurethane includes as follows
The raw material of parts by weight:
Polyurethane prepolymer 60-70 parts
Surfactant 5-15 parts
Hardening agent 5-10 parts
Function composition 15-25 parts
Foaming agent 2-8 parts
Water 25-35 parts.
3. a kind of multifunctional polyurethane bubble according to claim 2 is continuous, it is characterised in that:The polyurethane prepolymer includes
The raw material of following parts by weight:Toluene di-isocyanate(TDI) polyol prepolymer 25-40 parts, poly methylene poly phenyl poly isocyanate are more
First alcohol prepolymer 20-30 parts, stearyl ether 2-8 parts, good blue red 1-3 parts and calcium carbonate 1-3 parts.
4. a kind of multifunctional polyurethane bubble according to claim 2 is continuous, it is characterised in that:The surfactant for it is non-from
Subtype surfactant, the nonionic surface active agent be ethoxylated dodecyl alcohol, alkylolamides APEO,
At least one of fatty acid methyl ester ethoxylate, polyoxyethylene carboxylate and Block polyoxyethylene-polyethenoxy ether;Institute
It is by azodicarbonamide, azo isobutyronitrile, the diisopropyl carbonate of azo two, unifor and bicarbonate to state foaming agent
At least one of sodium;The hardening agent is using parts by weight as 1.5-2.5 by BDO and diglycol:1 composition
Mixture.
5. a kind of multifunctional polyurethane bubble according to claim 2 is continuous, it is characterised in that:The function composition is by plant
Extract and essential oil compare 1.5-2.5 with weight:The mixture of 1 composition.
6. a kind of multifunctional polyurethane bubble according to claim 5 is continuous, it is characterised in that:The plant extracts is included such as
The raw material of lower parts by weight:Marine algae extract 0.1-1.0 parts, aloe extract 0.5-1.5 parts, Honegsukle flower P.E 0.8-1.2 parts,
Chinese torreya extract 0.5-1.0 parts;The essential oil includes the raw material of following parts by weight:Tea tree ethereal oil 1.2-1.8 parts, Lavender
0.8-1.2 parts, sandalwood essential oil 0.3-0.8 parts.
7. a kind of multifunctional polyurethane bubble according to claim 1 is continuous, it is characterised in that:The TPU membrane includes following weight
Measure the raw material of part:
'-diphenylmethane diisocyanate 15-30 parts
Toluene di-isocyanate(TDI) 20-35 parts
2,2- dihydromethyl propionic acid 10-15 parts
Chain extender 8-16 parts
Sorbierite 3-7 parts
Expoxy propane 1-3 parts
Laurate 2-8 parts.
8. a kind of multifunctional polyurethane bubble according to claim 7 is continuous, it is characterised in that:The chain extender is trihydroxy methyl
At least one of propane, α-allylin, methyl diethanolamine and diethyl toluene diamine.
A kind of 9. continuous preparation method of multifunctional polyurethane bubble according to claim 1-8, it is characterised in that:Including as follows
Step:
(1)The preparation of polyurethane prepolymer:By toluene di-isocyanate(TDI) polyol prepolymer and the more isocyanides of polymethylene polyphenyl
Acid esters polyol prepolymer mixes, and stirs 50-60s with 6000-9000r/min speed, then adds stearyl ether, with
5000-8000r/min speed stirring 25-35s, adds Jia Landan and calcium carbonate, with 10000-13000r/min speed
60-80s is stirred, polyurethane prepolymer is made;
(2)The preparation of TPU membrane:'-diphenylmethane diisocyanate and toluene di-isocyanate(TDI) are mixed, with 4000-5000r/min
Speed stirring 5-6min, then add the mixing of 2- hydrocarbon methylpropanoic acid, 1-2min stirred with 4500-5500r/min speed, then
Sorbierite, expoxy propane and laurate are added, 5000-6000r/min speed stirring 3-5min, chain extender is eventually adding, mixes
Stirring is closed, shaping, TPU membrane is made;
(3)The continuous preparation of multifunctional polyurethane bubble:By surfactant, hardening agent, function composition, foaming agent, water and step(1)
Obtained polyurethane prepolymer mixes, and the continuous top of bubble is made after shaping and steeps continuous bottom, then will steep the upper of continuous top
Flange and the lower flange progress hot pressing fitting for steeping continuous bottom, are made the continuous body of bubble;Again by step(2)Obtained TPU membrane thermal-adhering
In at least surface for steeping continuous body, it is continuous that multifunctional polyurethane bubble is made.
A kind of 10. continuous preparation method of multifunctional polyurethane bubble according to claim 9, it is characterised in that:The step
(3)In, the speed of agitator of mixing is 8000-12000r/min, mixing time 5-10min;Steep under continuous top and bubble silk floss
The hot pressing laminate pressure in portion is 80-100Kg/cm2, the thermal-adhering temperature of TPU membrane is 90-130 DEG C, the heat posted resultant pressure of TPU membrane
For 60-80Kg/cm2。