CN107417152A - 一种速凝剂 - Google Patents
一种速凝剂 Download PDFInfo
- Publication number
- CN107417152A CN107417152A CN201710375874.9A CN201710375874A CN107417152A CN 107417152 A CN107417152 A CN 107417152A CN 201710375874 A CN201710375874 A CN 201710375874A CN 107417152 A CN107417152 A CN 107417152A
- Authority
- CN
- China
- Prior art keywords
- accelerator
- component
- minutes
- flyash
- aluminum sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种速凝剂,其组份按重量百分比为:硫酸铝50~55%、粉煤灰30~40%、氢氧化铝5~10%、柠檬酸5~10%;各组份之和为100%。采用上述组分制备速凝剂的方法为:先将各原料按需要用量称量,混合均匀,用粉碎机粉碎后,再用球磨机粉磨,过180目筛子,即得速凝剂细粉成品。本发明是技术人员在实践操作过程中试制出的一种速凝剂,按照JC477‑2005的要求进行试验,能使普通水泥在2分钟内初凝,5分钟内终凝,各项强度指标满足标准要求。
Description
技术领域
本发明属于建筑材料领域,特别涉及一种能使混凝土快速凝固的速凝剂。
背景技术
速凝剂是能使混凝土迅速凝结硬化的外加剂。速凝剂的主要种类有无机盐类和有机物类。实际使用中常用的速凝剂是无机盐类。无机盐类速凝剂按其主要成分大致可分为三类:以铝酸钠为主要成分的速凝剂;以铝酸钙、氟铝酸钙等为主要成分的速凝剂;以硅酸盐(NaSiO2)为主要成分的速凝剂。不同的速凝剂,其效果不同,初凝和终凝的时间都有区别。特别是在雨天和带水环境下施工,水泥的凝固时间非常重要。
发明内容
本发明的目的是提供一种效果良好且成本低廉的混凝土用速凝剂。
一种速凝剂,其组份按重量百分比为:硫酸铝50~55%、粉煤灰30~40%、氢氧化铝5~10%、柠檬酸5~10%;各组份之和为100%。
采用上述组分制备速凝剂的方法为:先将各原料按需要用量称量,混合均匀,用粉碎机粉碎后,再用球磨机粉磨,过180目筛子,即得速凝剂细粉成品。
进一步,所述速凝剂组分重量百分比为:硫酸铝52%、粉煤灰34%、氢氧化铝7%、柠檬酸7%。
本发明是技术人员在实践操作过程中试制出的一种速凝剂,按照JC477-2005的要求进行试验,能使普通水泥在2分钟内初凝,5分钟内终凝。各项强度指标满足标准要求。
具体实施方式
混凝土速凝剂一般很少采用单一的化合物,多为各种具有速凝作用的化合物复合而成。水泥经过水化作用达到凝结状态是一个机械过程,一定量的水化产物形成网络,产生一定的强度,即为凝结。这一过程中并不需要大量的水化产物,事实上只要少量的连接点即足以搭接成网络,导致凝结。但凝结的时间在施工过程中非常重要,特别是水下施工,因此各种速凝剂应运而生。
实施例1
速凝剂的组份按重量百分比为:硫酸铝50%、粉煤灰30%、氢氧化铝10%、柠檬酸10%。
采用上述组分制备速凝剂的方法为:先将各原料按需要用量称量,混合均匀,然后用粉碎机粉碎,再用球磨机粉磨,过180目筛子,即得速凝剂细粉。
实施例2
速凝剂的组份按重量百分比为:硫酸铝55%、粉煤灰30%、氢氧化铝5%、柠檬酸10%。制备方法与实施例1相同。
实施例3
速凝剂的组份按重量百分比为:硫酸铝50%、粉煤灰40%、氢氧化铝5%、柠檬酸5%。制备方法与实施例1相同。
实施例4
速凝剂的组份按重量百分比为:硫酸铝52%、粉煤灰34%、氢氧化铝7%、柠檬酸7%。制备方法与实施例1相同。但通过试验,采用本组百分比所得速凝剂的效果较为显著。
实施例5
速凝剂的组份按重量百分比为:硫酸铝53%、粉煤灰35%、氢氧化铝6%、柠檬酸6%。制备方法与实施例1相同。
将本发明所制得的速凝剂加入到普通的硅酸盐水泥中,查看其初凝时间和终凝时间,并与未加速凝剂的水泥进行对比,见下表:
水泥种类 | 速凝剂加入量(%) | 初凝时间 | 终凝时间 |
普通425水泥 | 未添加 | 3小时35分钟 | 4小时45分钟 |
普通425水泥 | 3 | 2分20秒 | 4分55秒 |
普通425水泥 | 4 | 1分55秒 | 3分30秒 |
普通425水泥 | 5 | 1分30秒 | 3分钟 |
普通525水泥 | 未添加 | 3小时20分钟 | 4小时25分钟 |
普通525水泥 | 3 | 1分50秒 | 4分50秒 |
普通525水泥 | 4 | 1分30秒 | 3分钟 |
普通525水泥 | 5 | 1分20秒 | 2分30秒 |
通过上表可看出,添加了速凝剂的水泥凝固时间大大缩短,而且随着添加量的增大,凝固效果特别明显。
Claims (3)
1.一种速凝剂,其特征在于:所述速凝剂组份按重量百分比为:硫酸铝50~55%、粉煤灰30~40%、氢氧化铝5~10%、柠檬酸5~10%;各组份之和为100%。
2.采用上述组分制备速凝剂的方法为:先将各原料按需要用量称量,混合均匀,用粉碎机粉碎后,再用球磨机粉磨,过180目筛子,即得速凝剂细粉成品。
3.根据权利要求1所述速凝剂,其特征在于:所述速凝剂组分按重量百分比为:硫酸铝52%、粉煤灰34%、氢氧化铝7%、柠檬酸7%。