CN105236812A - 一种混凝土速凝剂 - Google Patents

一种混凝土速凝剂 Download PDF

Info

Publication number
CN105236812A
CN105236812A CN201510577418.3A CN201510577418A CN105236812A CN 105236812 A CN105236812 A CN 105236812A CN 201510577418 A CN201510577418 A CN 201510577418A CN 105236812 A CN105236812 A CN 105236812A
Authority
CN
China
Prior art keywords
parts
aluminum oxide
polyoxyethylene ether
zinc sulfate
naphthalene sulfonic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510577418.3A
Other languages
English (en)
Inventor
王嘉文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510577418.3A priority Critical patent/CN105236812A/zh
Publication of CN105236812A publication Critical patent/CN105236812A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混凝土速凝剂，属于涂料添加剂领域。其包括如下重量份数的原料：脂肪醇聚氧乙烯醚5～15份、脂肪酸甲醇酰胺10～20份、铝氧熟料2～6份、粉煤灰3～9份、对氯间二甲酚5～15份、硫酸锌2～6份、甲酸钙4～12份、萘磺酸甲醛缩合物10～16份、偏铝酸钠5～15份、纤维素2～6份、硫酸铝3～9份、硅粉5～15份。本发明的混凝土速凝剂凝结时间短，强度高，且价格低廉、生产工艺简单、成本低，适合规模化生产。

Description

一种混凝土速凝剂
技术领域
本发明涉及一种混凝土速凝剂，属于涂料添加剂领域。
背景技术
速凝剂是掺入混凝土中使其迅速凝结硬化的一种外加剂，是在进行矿山井巷、铁路隧道、引水涵洞、地下工程等施工时参合在喷射混凝土中不可缺少的添加剂。其作用是加速水泥的水化硬化，在很短的时间内形成足够的强度，以保证特殊施工的要求。
目前，常用的速凝剂通常由铝氧熟料、煅烧明矾石以及石膏配制而成。由于速凝剂容易因风化而影响凝结速度，因此施工中速凝剂的添加量较大；不仅增大了施工成本，而且大量使用速凝剂还会导致混凝土后期强度大幅度下降、以及回弹率高等缺陷，不能满足施工质量要求。
发明内容
本发明的目的是弥补现有技术的不足，提供一种混凝土速凝剂。本发明的高效水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量。
本发明解决上述技术问题的技术方案如下：一种混凝土速凝剂，包括如下重量份数的原料：脂肪醇聚氧乙烯醚5～15份、脂肪酸甲醇酰胺10～20份、铝氧熟料2～6份、粉煤灰3～9份、对氯间二甲酚5～15份、硫酸锌2～6份、甲酸钙4～12份、萘磺酸甲醛缩合物10～16份、偏铝酸钠5～15份、纤维素2～6份、硫酸铝3～9份、硅粉5～15份。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，包括如下重量份数的原料：脂肪醇聚氧乙烯醚10份、脂肪酸甲醇酰胺15份、铝氧熟料4份、粉煤灰6份、对氯间二甲酚10份、硫酸锌4份、甲酸钙8份、萘磺酸甲醛缩合物13份、偏铝酸钠10份、纤维素4份、硫酸铝6份、硅粉10份。
进一步，包括如下重量份数的原料：脂肪醇聚氧乙烯醚5份、脂肪酸甲醇酰胺20份、铝氧熟料2份、粉煤灰9份、对氯间二甲酚5份、硫酸锌6份、甲酸钙4份、萘磺酸甲醛缩合物16份、偏铝酸钠5份、纤维素6份、硫酸铝3份、硅粉15份。
进一步，包括如下重量份数的原料：脂肪醇聚氧乙烯醚15份、脂肪酸甲醇酰胺10份、铝氧熟料6份、粉煤灰3份、对氯间二甲酚15份、硫酸锌2份、甲酸钙12份、萘磺酸甲醛缩合物10份、偏铝酸钠15份、纤维素2份、硫酸铝9份、硅粉5份。
本发明的有益效果是：
(1)本发明的混凝土速凝剂凝结时间短，强度高。
(2)本发明的价格低廉、生产工艺简单、成本低，适合规模化生产。
具体实施方式
以下结合具体实施例对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1：
一种混凝土速凝剂，包括如下重量份数的原料：脂肪醇聚氧乙烯醚5份、脂肪酸甲醇酰胺20份、铝氧熟料2份、粉煤灰9份、对氯间二甲酚5份、硫酸锌6份、甲酸钙4份、萘磺酸甲醛缩合物16份、偏铝酸钠5份、纤维素6份、硫酸铝3份、硅粉15份。
实施例2：
一种混凝土速凝剂，包括如下重量份数的原料：脂肪醇聚氧乙烯醚10份、脂肪酸甲醇酰胺15份、铝氧熟料4份、粉煤灰6份、对氯间二甲酚10份、硫酸锌4份、甲酸钙8份、萘磺酸甲醛缩合物13份、偏铝酸钠10份、纤维素4份、硫酸铝6份、硅粉10份。
实施例3：
一种混凝土速凝剂，包括如下重量份数的原料：脂肪醇聚氧乙烯醚15份、脂肪酸甲醇酰胺10份、铝氧熟料6份、粉煤灰3份、对氯间二甲酚15份、硫酸锌2份、甲酸钙12份、萘磺酸甲醛缩合物10份、偏铝酸钠15份、纤维素2份、硫酸铝9份、硅粉5份。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种混凝土速凝剂，其特征在于，包括如下重量份数的原料：脂肪醇聚氧乙烯醚5～15份、脂肪酸甲醇酰胺10～20份、铝氧熟料2～6份、粉煤灰3～9份、对氯间二甲酚5～15份、硫酸锌2～6份、甲酸钙4～12份、萘磺酸甲醛缩合物10～16份、偏铝酸钠5～15份、纤维素2～6份、硫酸铝3～9份、硅粉5～15份。
2.根据权利要求1所述的一种混凝土速凝剂，其特征在于，包括如下重量份数的原料：脂肪醇聚氧乙烯醚10份、脂肪酸甲醇酰胺15份、铝氧熟料4份、粉煤灰6份、对氯间二甲酚10份、硫酸锌4份、甲酸钙8份、萘磺酸甲醛缩合物13份、偏铝酸钠10份、纤维素4份、硫酸铝6份、硅粉10份。
3.根据权利要求1所述的一种混凝土速凝剂，其特征在于，包括如下重量份数的原料：脂肪醇聚氧乙烯醚5份、脂肪酸甲醇酰胺20份、铝氧熟料2份、粉煤灰9份、对氯间二甲酚5份、硫酸锌6份、甲酸钙4份、萘磺酸甲醛缩合物16份、偏铝酸钠5份、纤维素6份、硫酸铝3份、硅粉15份。
4.根据权利要求1所述的一种混凝土速凝剂，其特征在于，包括如下重量份数的原料：脂肪醇聚氧乙烯醚15份、脂肪酸甲醇酰胺10份、铝氧熟料6份、粉煤灰3份、对氯间二甲酚15份、硫酸锌2份、甲酸钙12份、萘磺酸甲醛缩合物10份、偏铝酸钠15份、纤维素2份、硫酸铝9份、硅粉5份。
CN201510577418.3A 2015-09-11 2015-09-11 一种混凝土速凝剂 Pending CN105236812A (zh)