CN107400466A - A kind of production technology of ultralow medium-temperature reinforced description film - Google Patents
A kind of production technology of ultralow medium-temperature reinforced description film Download PDFInfo
- Publication number
- CN107400466A CN107400466A CN201710857653.5A CN201710857653A CN107400466A CN 107400466 A CN107400466 A CN 107400466A CN 201710857653 A CN201710857653 A CN 201710857653A CN 107400466 A CN107400466 A CN 107400466A
- Authority
- CN
- China
- Prior art keywords
- film
- ultralow
- medium
- eva
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production technology of ultralow medium-temperature reinforced description film.Comprise the following steps, the step of (1) prepares master batch, melt index makees dispersant in 5 40g/10min EVA resin using macromolecule wax when master batch base material uses 190 DEG C;(2) step for being well mixed master batch with EVA resin and coupling agent, EVA resin at 190 DEG C melt index in 5 40g/10min;(3) the step of using casting film-forming Process Production EVA glass films.The invention provides a kind of production technology of ultralow medium-temperature reinforced description film, traditional PVB materials are replaced by using EVA material, employ low temperature moulding technique in process of production, manufactured glass film can at a lower temperature with glass laminating, the influence to glass film under the conditions of high temperature doubling is effectively prevent, while improves the structural strength of description film.
Description
Technical field
The present invention relates to a kind of production technology of ultralow medium-temperature reinforced description film.
Background technology
In fields such as building decorations, doubling glass with its good characteristic such as attractive in appearance, firm obtained it is more and more extensive should
With doubling glass includes the glass film layers positioned at center and the glass positioned at both sides.It is anti-pound/implosion guard is a by glass
Film it is compound enter layer glass among, after HTHP gluing, the new special glass product of integrally formed sandwich.
Existing its structural strength of description film is low, and the peel strength and tensile strength between glass are low.
The content of the invention
The present invention provides a kind of life of ultralow medium-temperature reinforced description film to solve technical problem present in known technology
Production. art, solves problem present in background technology.
The present invention is adopted the technical scheme that to solve technical problem present in known technology:It is a kind of ultralow medium-temperature reinforced
The step of production technology of description film comprises the following steps, and (1) prepares master batch, melt index when master batch base material uses 190 DEG C
In 5-40g/10min EVA resin, dispersant is made using macromolecule wax;(2) master batch is mixed with EVA resin and coupling agent
Even step, EVA resin at 190 DEG C melt index in 5-40g/10min;(3) casting film-forming Process Production EVA glass is used
The step of film.
The advantages and positive effects of the present invention are:The invention provides a kind of production work of ultralow medium-temperature reinforced description film
Skill, replace traditional PVB materials by using EVA material, employ low temperature moulding technique, manufactured glass in process of production
Film can effectively prevent the influence to glass film under the conditions of high temperature doubling at a lower temperature with glass laminating,
The structural strength of description film is improved simultaneously.
Preferably:Macromolecule wax described in step (1) be chosen for Tissuemat E, EVA waxes, copolymerization ester type waxes in one kind or
It is a variety of.
Preferably:Coupling agent described in step (2) is chosen for aminopropyl trimethoxysilane, aminopropyltriethoxy dimethoxy
Base silane, aminopropyl triethoxysilane, aminoethylaminopropyl trimethoxy silane, aminoethylaminopropyl triethoxysilane,
Aminoethylaminopropyl methyl dimethoxysilane, vinyltrimethoxy silane, VTES, methacryl
One or more in epoxide trimethoxy silane.
Preferably:Casting film-forming technique uses single screw extrusion machine in step (3), and extrusion temperature is 90-150 DEG C.
Embodiment
In order to further understand the content, features and effects of the present invention, it is as follows hereby to lift following examples detailed description:
Embodiment 1
(1) the step of preparing master batch, melt index is in 8g/10min EVA resin, use when master batch base material uses 190 DEG C
Macromolecule wax makees dispersant;(2) step for being well mixed master batch with EVA resin and coupling agent, EVA resin melt at 190 DEG C
Melt index in 12g/10min;(3) the step of using casting film-forming Process Production EVA glass films.
Wherein, the macromolecule wax described in step (1) is chosen for Tissuemat E;Coupling agent described in step (2) is chosen
For aminoethylaminopropyl trimethoxy silane;Casting film-forming technique uses single screw extrusion machine in step (3), and extrusion temperature is
100℃。
Embodiment 2
(1) the step of preparing master batch, melt index is adopted in 25g/10min EVA resin when master batch base material uses 190 DEG C
Make dispersant with macromolecule wax;(2) step for being well mixed master batch with EVA resin and coupling agent, EVA resin is at 190 DEG C
Melt index is in 32g/10min;(3) the step of using casting film-forming Process Production EVA glass films.
Wherein, the macromolecule wax described in step (1) is chosen for Tissuemat E;Coupling agent described in step (2) is chosen
For aminopropyl trimethoxysilane;Casting film-forming technique uses single screw extrusion machine in step (3), and extrusion temperature is 110 DEG C.
Embodiment 3
(1) the step of preparing master batch, melt index is adopted in 32g/10min EVA resin when master batch base material uses 190 DEG C
Make dispersant with macromolecule wax;(2) step for being well mixed master batch with EVA resin and coupling agent, EVA resin is at 190 DEG C
Melt index is in 38g/10min;(3) the step of using casting film-forming Process Production EVA glass films.
Wherein, the macromolecule wax described in step (1) is chosen for EVA waxes;Coupling agent described in step (2) is chosen for second
Alkenyl triethoxysilane;Casting film-forming technique uses single screw extrusion machine in step (3), and extrusion temperature is 130 DEG C.
Claims (4)
1. a kind of production technology of ultralow medium-temperature reinforced description film, it is characterized in that:Comprise the following steps,
(1) the step of preparing master batch, melt index is in 5-40g/10min EVA resin, use when master batch base material uses 190 DEG C
Macromolecule wax makees dispersant;
(2) step for being well mixed master batch with EVA resin and coupling agent, EVA resin at 190 DEG C melt index in 5-40g/
10min;
(3) the step of using casting film-forming Process Production EVA glass films.
2. the production technology of ultralow medium-temperature reinforced description film as claimed in claim 1, it is characterised in that:Described in step (1)
Macromolecule wax be chosen for Tissuemat E, EVA waxes, copolymerization ester type waxes in one or more.
3. the production technology of the ultralow medium-temperature reinforced description film of light modulation film as claimed in claim 1, it is characterised in that:Step
(2) coupling agent described in is chosen for aminopropyl trimethoxysilane, aminopropyltriethoxy dimethoxysilane, the ethoxy of aminopropyl three
Base silane, aminoethylaminopropyl trimethoxy silane, aminoethylaminopropyl triethoxysilane, aminoethylaminopropyl methyl dimethoxy
In TMOS, vinyltrimethoxy silane, VTES, methacryloxy trimethoxy silane
It is one or more.
4. the production technology of ultralow medium-temperature reinforced description film as claimed in claim 1, it is characterised in that:It is cast in step (3)
Film-forming process uses single screw extrusion machine, and extrusion temperature is 90-150 DEG C.