CN107400277A - A kind of PE of resistance to mould feed pipes - Google Patents
A kind of PE of resistance to mould feed pipes Download PDFInfo
- Publication number
- CN107400277A CN107400277A CN201710658278.1A CN201710658278A CN107400277A CN 107400277 A CN107400277 A CN 107400277A CN 201710658278 A CN201710658278 A CN 201710658278A CN 107400277 A CN107400277 A CN 107400277A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial agent
- raw material
- feed pipes
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PE of resistance to mould feed pipes, it by following weight than raw material form:Including:PE100 levels raw material, regenerated polythene raw material, polyvinyl chloride resin, organic antibacterial agent and inorganic antibacterial agent composition, methylvinyldimethoxysilane, silane coupling A 172, black and white color masterbatch, the mass fraction of each component are:8 20 parts of 60 80 parts of PE100 levels raw material, 20 30 parts of regenerated polythene raw material, 5 12 parts of polyvinyl chloride resin, organic antibacterial agent and inorganic antibacterial agent composition, 15 parts of methylvinyldimethoxysilane, 172 2 10 parts of silane coupling A, 58 parts of black and white color masterbatch.By the above-mentioned means, a kind of PE of resistance to mould feed pipes of the present invention, anti-aging, toughness are very good, can the effective antibacterial and antibacterial cycle is long, requirement of the people to PE feed pipes can be met.
Description
Technical field
The present invention relates to molecular material field, more particularly to a kind of PE of resistance to mould feed pipes.
Background technology
In recent years, PE pipeline materials and product quality have rapid progress, are used widely in feedwater field, PE pipes
Excellent properties and chemical resistance, it is set to occupy very big market segment, at the conveying of municipal reclaimed water, acid waste water conveying, waste water
Manage pipeline etc..But existing PE pipes conveniently also have the defects of very big in high antibacterial, it is impossible to meet people to the high antibacterial of domestic water
Requirement.
The content of the invention
To solve the above problems, a kind of PE of resistance to mould feed pipes of the present invention, anti-aging, toughness are very good, can effective antibacterial
And the antibacterial cycle is long, requirement of the people to the high antibacterial of PE feed pipes can be met.
In order to solve the above technical problems, one aspect of the present invention is:PE100 levels raw material, the poly- second of regeneration
It is alkene raw material, polyvinyl chloride resin, organic antibacterial agent and inorganic antibacterial agent composition, methylvinyldimethoxysilane, silane coupled
Agent A-172, black and white color masterbatch, the mass fraction of each component are:PE100 level raw material 60-80 parts, regenerated polythene raw material 20-
30 parts, polyvinyl chloride resin 5-12 parts, organic antibacterial agent and inorganic antibacterial agent composition 8-20 parts, methylvinyldimethoxysilane
1-5 parts, the 2-10 parts of silane coupling A -172, black and white color masterbatch 5-8 parts.
In a preferred embodiments of the invention, organic antibacterial agent and the inorganic antibacterial agent composition is 3 by mass ratio:2
Organic antibacterial agent and inorganic antiseptic composition.
In a preferred embodiments of the invention, the organic antibacterial agent is vanillic aldehyde or ethyl vanillin aldehydes compound.
Inorganic antiseptic described in a preferred embodiments of the invention is by zinc oxide, cupric oxide, ammonium dihydrogen phosphate, carbonic acid
Lithium forms.
In a preferred embodiments of the invention, the mass fraction of the antimicrobial PE tube each component is:PE100 levels raw material 65
Part, 25 parts of regenerated polythene raw material, 6 parts of polyvinyl chloride resin, organic antibacterial agent and 10 parts of inorganic antibacterial agent composition, ethylene methacrylic
2 parts of base dimethoxysilane, 03 part of silane coupling A -172,5 parts of black and white color masterbatch.
In a preferred embodiments of the invention, the mass fraction of the antimicrobial PE tube each component is:PE100 levels raw material 70
Part, 30 parts of regenerated polythene raw material, 12 parts of polyvinyl chloride resin, organic antibacterial agent and 16 parts of inorganic antibacterial agent composition, ethylene methacrylic
4 parts of base dimethoxysilane, 10 parts of silane coupling A -172,8 parts of black and white color masterbatch.
The beneficial effects of the invention are as follows:A kind of PE of resistance to mould feed pipes of the present invention, anti-aging, toughness are very good, can be effective
The antibacterial and antibacterial cycle is long, can meet requirement of the people to the high antibacterial of PE feed pipes.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area
All other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The embodiment of the present invention includes:
A kind of PE of resistance to mould feed pipes, it is characterised in that including:PE100 levels raw material, regenerated polythene raw material, PVC trees
Fat, organic antibacterial agent and inorganic antibacterial agent composition, methylvinyldimethoxysilane, silane coupling A -172, black and white
Color masterbatch, the mass fraction of each component are:PE100 level raw material 60-80 parts, regenerated polythene raw material 20-30 parts, polyvinyl chloride resin
5-12 parts, organic antibacterial agent and inorganic antibacterial agent composition 8-20 parts, methylvinyldimethoxysilane 1-5 parts, silane are even
Join agent A-172 2-10 parts, black and white color masterbatch 5-8 parts.
In above-mentioned, organic antibacterial agent and the inorganic antibacterial agent composition is 3 by mass ratio:2 organic antibacterial agent and nothing
Machine antiseptic forms.
In above-mentioned, the organic antibacterial agent is vanillic aldehyde or ethyl vanillin aldehydes compound.
In above-mentioned, described inorganic antiseptic by zinc oxide, cupric oxide, ammonium dihydrogen phosphate, lithium carbonate group into.
Further, the mass fraction of the antimicrobial PE tube each component is:65 parts of PE100 levels raw material, regenerated polythene
25 parts of raw material, 6 parts of polyvinyl chloride resin, organic antibacterial agent and 10 parts of inorganic antibacterial agent composition, methylvinyldimethoxysilane
2 parts, 03 part of silane coupling A -172,5 parts of black and white color masterbatch.
Further, the mass fraction of the antimicrobial PE tube each component is:70 parts of PE100 levels raw material, regenerated polythene
16 parts of 30 parts of raw material, 12 parts of polyvinyl chloride resin, organic antibacterial agent and inorganic antibacterial agent composition, methyl ethylene dimethoxy silicon
4 parts of alkane, 10 parts of silane coupling A -172,8 parts of black and white color masterbatch.
The beneficial effects of the invention are as follows:A kind of PE of resistance to mould feed pipes, anti-aging, toughness are very good, can effectively antibacterial is simultaneously
And the antibacterial cycle is long, requirement of the people to the high antibacterial of PE feed pipes can be met.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, similarly it is included in the scope of patent protection of the present invention.
Claims (6)
- A kind of 1. PE of resistance to mould feed pipes, it is characterised in that including:PE100 levels raw material, regenerated polythene raw material, PVC trees Fat, organic antibacterial agent and inorganic antibacterial agent composition, methylvinyldimethoxysilane, silane coupling A -172, black and white Color masterbatch, the mass fraction of each component are:PE100 level raw material 60-80 parts, regenerated polythene raw material 20-30 parts, polyvinyl chloride resin 5-12 parts, organic antibacterial agent and inorganic antibacterial agent composition 8-20 parts, methylvinyldimethoxysilane 1-5 parts, silane are even Join agent A-172 2-10 parts, black and white color masterbatch 5-8 parts.
- A kind of 2. PE of resistance to mould feed pipes according to claim 1, it is characterised in that the organic antibacterial agent and inorganic anti- Microbial inoculum mixture is 3 by mass ratio:2 organic antibacterial agent and inorganic antiseptic composition.
- 3. a kind of PE of resistance to mould feed pipes according to claim 2, it is characterised in that the organic antibacterial agent is vanillic aldehyde Or ethyl vanillin aldehydes compound.
- 4. a kind of PE of resistance to mould feed pipes according to claim 2, it is characterised in that described inorganic antiseptic is by aoxidizing Zinc, cupric oxide, ammonium dihydrogen phosphate, lithium carbonate group into.
- A kind of 5. PE of resistance to mould feed pipes according to claim 1, it is characterised in that the matter of the antimicrobial PE tube each component Measuring fraction is:65 parts of PE100 levels raw material, 25 parts of regenerated polythene raw material, 6 parts of polyvinyl chloride resin, organic antibacterial agent and inorganic anti- 10 parts of microbial inoculum mixture, 2 parts of methylvinyldimethoxysilane, 03 part of silane coupling A -172,5 parts of black and white color masterbatch.
- A kind of 6. PE of resistance to mould feed pipes according to claim 1, it is characterised in that the matter of the antimicrobial PE tube each component Measuring fraction is:70 parts of PE100 levels raw material, 30 parts of regenerated polythene raw material, 12 parts of polyvinyl chloride resin, organic antibacterial agent and inorganic 16 parts of antimicrobial mix, 4 parts of methylvinyldimethoxysilane, 10 parts of silane coupling A -172,8 parts of black and white color masterbatch.