CN107386550B - A kind of fire prevention of steel construction exposed parts, anti-corrosion wood grain coating construction method - Google Patents
A kind of fire prevention of steel construction exposed parts, anti-corrosion wood grain coating construction method Download PDFInfo
- Publication number
- CN107386550B CN107386550B CN201710434702.4A CN201710434702A CN107386550B CN 107386550 B CN107386550 B CN 107386550B CN 201710434702 A CN201710434702 A CN 201710434702A CN 107386550 B CN107386550 B CN 107386550B
- Authority
- CN
- China
- Prior art keywords
- wood grain
- exposed parts
- paint
- fire prevention
- aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of steel construction exposed parts fire prevention disclosed by the invention, anti-corrosion wood grain coating construction method, include the following steps: step 1: processing of rust removing carried out to steel construction exposed parts；Step 2: spraying aqueous anticorrosion of steel structure paint；Step 3: spraying thick matter type fireproof coating thickness to 1-3mm；Iron plate is closed flat by hand while spraying；Waterborne Fire Retardant Coatings for Steel is polished after parching；Step 4: then batch anticracking grout is polished；Step 5: then batch exterior wall white smooth surface putty is polished；Step 6: brush and the same color bottom paint of wood grain；Step 7: being used for the color aggregate of wood-grained shape in the homochromy primed surface brushing of wood grain；Step 8: in the aqueous wood grain paint of color aggregate surface brushing；Step 9: wiping color with aqueous wood grain paint on the aqueous wood grain lacquer coat；Step 10: using water-based fluorocarbon clear finish.The present invention makes steel construction achieve the effect that round log, the lumps of wood are the same, makes that steel construction plays the role of fire prevention, anti-corrosion graining is combined into one.
Description
Technical field
The present invention relates to anticorrosion of steel structure, fire prevention processing technology field, in particular to a kind of steel construction exposed parts fire prevention,
The construction method of anti-corrosion wood grain coating.
Background technique
The exposed parts of steel building, it is most of to be handled using steel structure anti-corrosion paint, it is being sprayed after preservative treatment
Apply fireproof coating.Fire-resistant coating for steel structure form of construction work is divided into two kinds at present, and one is thick matter type fireproof coating spraying application sides
Formula；Second is slim fireproof coating spraying and brushing form of construction work.Both modes have that coarse, appearance is inaesthetic asks
Topic,
Summary of the invention
Technical problem to be solved by the present invention lies in for existing anticorrosion of steel structure, present in fire resistant coating it is coarse,
The inaesthetic problem of appearance and the construction method of a kind of fire prevention of steel construction exposed parts, anti-corrosion wood grain coating is provided.
The technical problems to be solved by the invention can be achieved through the following technical solutions:
A kind of fire prevention of steel construction exposed parts, anti-corrosion wood grain coating construction method, include the following steps:
Step 1: processing of rust removing is carried out to steel construction exposed parts；
Step 2: spraying aqueous anticorrosion of steel structure paint；
Step 3: spraying thick matter type fireproof coating thickness to 1-3mm；Iron plate is closed flat by hand while spraying；Aqueous steel knot
Structure fireproof coating is polished after parching；
Step 4: then batch anticracking grout is polished；
Step 5: then batch exterior wall white smooth surface putty is polished；
Step 6: brush and the same color bottom paint of wood grain；
Step 7: being used for the color aggregate of wood-grained shape in the homochromy primed surface brushing of wood grain；
Step 8: in the aqueous wood grain paint of color aggregate surface brushing；
Step 9: wiping color with aqueous wood grain paint on the aqueous wood grain lacquer coat；
Step 10: using water-based fluorocarbon clear finish.
In a preferred embodiment of the invention, in the step 2, aqueous anticorrosion of steel structure paint position is sprayed together.
In a preferred embodiment of the invention, in the step 3, spraying thick matter type fireproof coating is two, is parched
Polishing is primary afterwards.
In a preferred embodiment of the invention, in the step 4, batch anticracking grout together, then carries out polishing one
Road；
In a preferred embodiment of the invention, in the step 5, batch exterior wall white smooth surface putty together, then into
Row polishing is together.
In a preferred embodiment of the invention, in the step 6, brush is with wood grain along with color bottom paint.
In a preferred embodiment of the invention, in the step 7, wood grain is used in the homochromy primed surface brushing of wood grain
The color aggregate of moulding is together.
In a preferred embodiment of the present invention, in the step 7, the color aggregate is the quartz sand of 120 mesh.
In a preferred embodiment of the invention, in the step 8, in the aqueous wood grain paint one of color aggregate surface brushing
Road；The aqueous wood grain paint is the aqueous silicon colored varnish after toning.
In a preferred embodiment of the invention, in the step 9, Waterborne wood is used on the aqueous wood grain lacquer coat
Line paint wipes color together.
In a preferred embodiment of the invention, in the step 10, with water-based fluorocarbon clear finish two.
By the present invention in that being made steel construction achieve the effect that round log, the lumps of wood are the same with surface layer wood grain paint Handicraft decorative, being made steel
Structure plays the role of fire prevention, anti-corrosion graining is combined into one.The suitable domestic large-scale synthesis body steel construction of the present invention,
The people are drunk overnight shop, characteristic small town.
Specific embodiment
A kind of fire prevention of steel construction exposed parts, anti-corrosion wood grain coating construction method, include the following steps:
Step 1: processing of rust removing is carried out to steel construction exposed parts；
Step 2: spraying aqueous anticorrosion of steel structure paint together；
Step 3: spraying thick matter type fireproof coating two, thickness to 1-3mm；Iron plate is closed flat by hand while spraying；Water
Property fire-resistant coating for steel structure is polished after parching；
Step 4: batch anticracking grout together, then carries out polishing together；
Step 5: batch exterior wall white smooth surface putty together, then carries out polishing together；
Step 6: brush is with wood grain along with color bottom paint；
Step 7: in one of color aggregate of the homochromy primed surface brushing of wood grain for wood-grained shape, the color aggregate is 120
Purpose quartz sand.
Step 8: at one of the aqueous wood grain paint of color aggregate surface brushing；
Step 9: wiping color together with aqueous wood grain paint on the aqueous wood grain lacquer coat；
Step 10: using water-based fluorocarbon clear finish two.
Claims (9)
1. the construction method of a kind of steel construction exposed parts fire prevention, anti-corrosion wood grain coating, which comprises the steps of:
Step 1: processing of rust removing is carried out to steel construction exposed parts；
Step 2: spraying aqueous anticorrosion of steel structure paint；
Step 3: spraying thick matter type Waterborne Fire Retardant Coatings for Steel thickness to 1-3mm；Iron plate is closed flat by hand while spraying；Water
Property fire-resistant coating for steel structure is polished after parching；
Step 4: then batch anticracking grout is polished；
Step 5: then batch exterior wall white smooth surface putty is polished；
Step 6: brush and the same color bottom paint of wood grain；
Step 7: being used for the color aggregate of wood-grained shape in the homochromy primed surface brushing of wood grain；The color aggregate is the quartz of 120 mesh
Sand；
Step 8: in the aqueous wood grain paint of color aggregate surface brushing；The aqueous wood grain paint is the aqueous silicon colored varnish after toning；
Step 9: wiping color with aqueous wood grain paint on the aqueous wood grain lacquer coat；
Step 10: using water-based fluorocarbon clear finish.
2. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 2, spraying aqueous anticorrosion of steel structure paint is together.
3. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 3, spraying thick matter type fireproof coating is two, is polished after parching primary.
4. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 4, batch anticracking grout together, then carries out polishing together.
5. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 5, batch exterior wall white smooth surface putty together, then carries out polishing together.
6. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 6, brush is with wood grain along with color bottom paint.
7. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 7, in one of color aggregate of the homochromy primed surface brushing of wood grain for wood-grained shape.
8. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 9, on the aqueous wood grain lacquer coat together with aqueous wood grain paint wiping color.
9. the construction method of a kind of steel construction exposed parts fire prevention as described in claim 1, anti-corrosion wood grain coating, feature exist
In in the step 10, with water-based fluorocarbon clear finish two.