CN107383885A - A kind of Milan watt and its production method - Google Patents
A kind of Milan watt and its production method Download PDFInfo
- Publication number
- CN107383885A CN107383885A CN201710645554.0A CN201710645554A CN107383885A CN 107383885 A CN107383885 A CN 107383885A CN 201710645554 A CN201710645554 A CN 201710645554A CN 107383885 A CN107383885 A CN 107383885A
- Authority
- CN
- China
- Prior art keywords
- watt
- milan
- production method
- substrate
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of Milan watt and its production method belong to structural metal watt technical field, relate generally to a kind of watt and its production method;The present invention is in order to solve the problems, such as that the composite construction stability on metal tile-base surface of the prior art is poor, durability is low, service life is low;Al-Zn coated steel is struck out substrate by the present invention using punching press grinding tool;Substrate is placed in mould, silicon rubber coloured silk sand is mixed in injection mould, and then mixed layer is formed in the upper surface of substrate;By the substrate support mould in step 2, and solidified;Tile both sides spraying protective layer after the solidification is complete;Technique is simple, and what is contacted between color sand particle and silicon rubber has good uniformity, and color sand is evenly distributed, and tile thickness is uniform, and stress dispersive property is high, has good economic benefit.
Description
Technical field
One kind watt and its production method belong to structural metal watt technical field, relate generally to a kind of Milan watt and its producer
Method.
Background technology
At present, colored stone metal tile on the market is a kind of new type roof Building wood to grow up on the basis of color steel tile
Material, it is using high corrosion resistant Al-Zn coated steel as base material, with special process by high durable natural colorful basalt particle spray coating in base material
Top layer, then the first-generation metal roofing being processed into by treatment technique.Colored stone metal tile is except with color steel
It is also more excellent with heat-proof quality outside the advantages that watt original attractive in appearance, light, fire prevention, waterproof, wind resistance, antidetonation, install convenient
It is good.Due to the good heat conductivity of metal, the heat-proof quality of common color steel tile is very poor.And colored stone metal tile is due to the surface spraying Black Warrior
Rock particle, improve the heat-proof quality of whole metal tile;Anti-acoustic capability is excellent.When raindrop or other articles drop to common color steel tile
Surface can send very big noise, and colored stone metal tile works as raindrop because surface spraying layer belongs to rock particles and adhesive
Or other articles fall on surface, this composite bed can sponge external impulsive force, the noiseproof feature improved watt;Rotproofness and
Crushing resistance is more excellent.
Composite construction stability on metal tile-base surface of the prior art is poor, durability is low, service life is low.
The content of the invention
In order to solve the above problems, the invention discloses a kind of Milan watt and its production method, the product durability of production
By force, concise production process.
The object of the present invention is achieved like this:
A kind of Milan watt, including watt body, both sides are provided with the saddle and flanging being arranged in parallel to watt body up and down, and watt body is included from top to bottom
Up-protective layer, silicon rubber coloured silk sand mixed layer, aluminum-zinc alloy substrate and the lower protective layer set gradually.
A kind of production method in Milan watt, comprises the following steps:
Step 1:Al-Zn coated steel is struck out into substrate using punching press grinding tool;
Step 2:Substrate is placed in mould, silicon rubber coloured silk sand is mixed in injection mould, and then is formed in the upper surface of substrate
Mixed layer;
Step 3:By the substrate support mould in step 2, and solidified;
Step 4:Tile both sides spraying protective layer after the solidification is complete.
The mould includes injection molding and shake table, and injection molding includes the upper die and lower die of front and rear pairing, and inlet is located at injection molding
Upper end, the injection molding is vertically inserted on shake table.
The average particle size range of the color sand is 1-3mm.
The up-protective layer and lower protective layer are transparent silicon dioxide coating, and stability is good, and weatherability is strong, prevents tile
Face checking.
Silicon rubber described in step 2 is made due to the composition of following portion rate:Straight chain type vinyl silicone oil 10-20 parts, MQ
Vinyl polysiloxane 8-12 parts, containing hydrogen silicone oil 7-20 parts, cassette catalyst 0.01-0.05 parts, cyclohexyl alkynol 0.01-0.02
Part.
The composition for preparing silicon rubber includes aerosil 0.5-5 parts.
The present invention has the advantages that metallic tile durability of the invention is high, traditional compared with prior art
The processing of metallic tile in technique needs first to spray glue-line, is dispensing color sand particle, and process is cumbersome, the present invention by silicon rubber and
Color sand particle is stirred in advance, by die perfusion, color sand thin layer is directly formed on tile, compared to prior art, work
Skill is simple, and what is contacted between color sand particle and silicon rubber has good uniformity, and color sand is evenly distributed, and tile thickness is uniform, should
Power dispersive property is high, has good economic benefit.
Embodiment
The specific embodiment of the invention is described in further detail below.
A kind of Milan watt of the present embodiment, including watt body, both sides are provided with the saddle and flanging being arranged in parallel to watt body up and down, watt
Body includes up-protective layer, silicon rubber coloured silk sand mixed layer, aluminum-zinc alloy substrate and the lower protective layer from top to bottom set gradually.
A kind of production method in Milan watt, comprises the following steps:
Step 1:Al-Zn coated steel is struck out into substrate using punching press grinding tool;
Step 2:Substrate is placed in mould, silicon rubber coloured silk sand is mixed in injection mould, and then is formed in the upper surface of substrate
Mixed layer;
Step 3:By the substrate support mould in step 2, and solidified;
Step 4:Tile both sides spraying protective layer after the solidification is complete.
The mould includes injection molding and shake table, and injection molding includes the upper die and lower die of front and rear pairing, and inlet is located at injection molding
Upper end, the injection molding is vertically inserted on shake table.
The average particle size range of the color sand is 1-3mm.
The up-protective layer and lower protective layer are transparent silicon dioxide coating.
Silicon rubber described in step 2 is made due to the composition of following portion rate:3.25 parts of aerosil, straight chain type
13.7 parts of vinyl silicone oil, 9.8 parts of MQ vinyl polysiloxanes, 14.6 parts of containing hydrogen silicone oil, 0.045 part of cassette catalyst, cyclohexyl
0.02 part of alkynol.
The performance parameter of the metallic tile of the present embodiment is as follows:- 5 DEG C of bendings of low temperature are flawless, and the heat-insulated temperature difference is 10 DEG C, warp
After the xenon arc lamp radiation 900h for simulating ultraviolet light and visible ultraviolet light and aging case, properties are unchanged;By -30 DEG C of low temperature colds
Freeze after 5h 90 DEG C of baking oven constant temperature 5 hours immediately, then immerse in 25 DEG C of thermostatted waters the circulation 30 times for soaking 40h, no cracking, without change
Shape, without knockout.
It should be appreciated that although the present specification is described in terms of embodiments, not each embodiment only includes one
Individual independent technical scheme, this narrating mode of specification is only that those skilled in the art will should illustrate for clarity
Book is as an entirety, and the technical solutions in the various embodiments may also be suitably combined, and forming those skilled in the art can manage
The other embodiment of solution.
Claims (7)
1. a kind of Milan watt, including watt body, both sides are provided with the saddle and flanging being arranged in parallel to watt body up and down, it is characterised in that:Watt
Body includes up-protective layer, silicon rubber coloured silk sand mixed layer, aluminum-zinc alloy substrate and the lower protective layer from top to bottom set gradually.
A kind of 2. production method in Milan watt described in claim 1, it is characterised in that:Comprise the following steps:
Step 1:Al-Zn coated steel is struck out into substrate using punching press grinding tool;
Step 2:Substrate is placed in mould, silicon rubber coloured silk sand is mixed in injection mould, and then is formed in the upper surface of substrate
Mixed layer;
Step 3:By the substrate support mould in step 2, and solidified;
Step 4:Tile both sides spraying protective layer after the solidification is complete.
A kind of 3. production method in Milan watt according to claim 2, it is characterised in that:The mould includes injection molding and vibration
Platform, injection molding include the upper die and lower die of front and rear pairing, and inlet is located at the upper end of injection molding, and the injection molding is vertically inserted into shake table
On.
A kind of 4. production method in Milan watt according to claim 2, it is characterised in that:The average particle size range of the color sand
For 1-3mm.
A kind of 5. production method in Milan watt according to claim 2, it is characterised in that:The up-protective layer and lower protective layer
It is transparent silicon dioxide coating.
A kind of 6. production method in Milan watt according to claim 2, it is characterised in that:Silicon rubber described in step 2 due to
The composition of following portion rate is made:Straight chain type vinyl silicone oil 10-20 parts, MQ vinyl polysiloxane 8-12 parts, containing hydrogen silicone oil 7-
20 parts, cassette catalyst 0.01-0.05 parts, cyclohexyl alkynol 0.01-0.02 parts.
A kind of 7. production method in Milan watt according to claim 6, it is characterised in that:It is described prepare silicon rubber into subpackage
Include aerosil 0.5-5 parts.