CN107383681A - A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant - Google Patents

A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant Download PDF

Info

Publication number
CN107383681A
CN107383681A CN201710635483.6A CN201710635483A CN107383681A CN 107383681 A CN107383681 A CN 107383681A CN 201710635483 A CN201710635483 A CN 201710635483A CN 107383681 A CN107383681 A CN 107383681A
Authority
CN
China
Prior art keywords
parts
environment
resistant
friendlycorrosion
cable materials
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710635483.6A
Other languages
Chinese (zh)
Inventor
刘佳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710635483.6A priority Critical patent/CN107383681A/en
Publication of CN107383681A publication Critical patent/CN107383681A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, it is prepared from the following raw materials in parts by weight：15 20 parts of ethylene-vinyl acetate copolymer, 10 15 parts of haloflex, 15 20 parts of ferrocene; 10 14 parts of chloroplatinic acid, 20 22 parts of polyvinyl chloride resin, 10 14 parts of methyl hydroxybenzoate; 10 12 parts of magnesia, 20 25 parts of fluor-apatite, 8 10 parts of tetramethoxymethylglycoluril; 68 parts of Environment-friendlycalcium calcium zinc stabilizer; 6 14 parts of polyphenylene oxide resin, 5 10 parts of epoxyoleic acid butyl ester, 68 parts of citroflex A-4; 38 parts of zinc stearate, 27 parts of polybenzimidazoles.The present invention has the ability of good acid-alkali-corrosive-resisting, while anti-flammability and high-temperature resistant result are good, and good combination property is environment friendly and pollution-free.

Description

A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant
Technical field
The present invention relates to CABLE MATERIALS technical field, more particularly to a kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant.
Background technology
With developing rapidly for economic construction, the continuous improvement of people's standard of living, all kinds of infrastructure in town and country it is quick Development, it is increasing to all kinds of cabling requirements amounts.Both with good fire resistance while with environmental-protecting performance, good machine Tool processability, the CABLE MATERIALS material of preferable insulating properties turn into the direction of CABLE MATERIALS development, it can be ensured that the protection to cable Effect.
The content of the invention
Goal of the invention：In order to overcome the deficiencies in the prior art, there is provided a kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, have The ability of good acid-alkali-corrosive-resisting, while anti-flammability and high-temperature resistant result are good, good combination property.
Technical scheme：To achieve the above object, the present invention provides a kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, and it is by following weight The raw material of number is made：
Ethene-acetate ethylene copolymer 15-20 parts, haloflex 10-15 parts, ferrocene 15-20 parts, chloroplatinic acid 10-14 parts, PVC resin 20-22 parts, methyl hydroxybenzoate 10-14 parts, magnesia 10-12 parts, fluor-apatite 20-25 parts, four Methoxymethyl glycoluril 8-10 parts, Environment-friendlycalcium calcium zinc stabilizer 6-8 parts, polyphenylene oxide resin 6-14 parts, epoxyoleic acid butyl ester 5-10 Part, citroflex A-4 6-8 parts, zinc stearate 3-8 parts, polybenzimidazoles 2-7 parts.
Further, a kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, it is prepared from the following raw materials in parts by weight：
17.5 parts of ethene-acetate ethylene copolymer, 12.5 parts of haloflex, 17.5 parts of ferrocene, 12 parts of chloroplatinic acid, 21 parts of PVC resins, 12 parts of methyl hydroxybenzoate, 11 parts of magnesia, 22.5 parts of fluor-apatite, 9 parts of tetramethoxymethylglycoluril, 7 parts of Environment-friendlycalcium calcium zinc stabilizer, 10 parts of polyphenylene oxide resin, 7.5 parts of epoxyoleic acid butyl ester, 7 parts of citroflex A-4, firmly 5.5 parts of resin acid zinc, polybenzimidazoles 4.5-7 parts.Further, the stabilizer is Environment-friendlycalcium calcium zinc stabilizer.
Beneficial effect：The present invention compared with prior art, has the ability of good acid-alkali-corrosive-resisting, while anti-flammability Good, good combination property, environment friendly and pollution-free with high-temperature resistant result.
Embodiment
The present invention is further described with reference to embodiment.
Embodiment one：
A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, it is prepared from the following raw materials in parts by weight：
15 parts of ethene-acetate ethylene copolymer, 10 parts of haloflex, 15 parts of ferrocene, 10 parts of chloroplatinic acid, PVC trees 20 parts of fat, 10 parts of methyl hydroxybenzoate, 10 parts of magnesia, 20 parts of fluor-apatite, 8 parts of tetramethoxymethylglycoluril, environmentally friendly calcium zinc are steady Determine 6 parts of agent, 6 parts of polyphenylene oxide resin, 5 parts of epoxyoleic acid butyl ester, 6 parts of citroflex A-4,3 parts of zinc stearate, gather 2 parts of benzimidazole.
Embodiment two：
A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, it is prepared from the following raw materials in parts by weight：
17.5 parts of ethene-acetate ethylene copolymer, 12.5 parts of haloflex, 17.5 parts of ferrocene, 12 parts of chloroplatinic acid, 21 parts of PVC resins, 12 parts of methyl hydroxybenzoate, 11 parts of magnesia, 22.5 parts of fluor-apatite, 9 parts of tetramethoxymethylglycoluril, 7 parts of Environment-friendlycalcium calcium zinc stabilizer, 10 parts of polyphenylene oxide resin, 7.5 parts of epoxyoleic acid butyl ester, 7 parts of citroflex A-4, firmly 5.5 parts of resin acid zinc, polybenzimidazoles 4.5-7 parts.
Embodiment three：
A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, it is prepared from the following raw materials in parts by weight：
20 parts of ethene-acetate ethylene copolymer, 15 parts of haloflex, 20 parts of ferrocene, 14 parts of chloroplatinic acid, PVC 22 parts of resin, 14 parts of methyl hydroxybenzoate, 12 parts of magnesia, 25 parts of fluor-apatite, 10 parts of tetramethoxymethylglycoluril, environmental protection 8 parts of calcium zinc stabilizer, 14 parts of polyphenylene oxide resin, 10 parts of epoxyoleic acid butyl ester, 8 parts of citroflex A-4 are stearic Sour 8 parts of zinc, 7 parts of polybenzimidazoles.
Described above is only the preferred embodiment of the present invention, it should be pointed out that：Come for those skilled in the art Say, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should be regarded as Protection scope of the present invention.

Claims (2)

  1. A kind of 1. CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant, it is characterised in that：It is prepared from the following raw materials in parts by weight：
    Ethene-acetate ethylene copolymer 15-20 parts, haloflex 10-15 parts, ferrocene 15-20 parts, chloroplatinic acid 10-14 parts, PVC resin 20-22 parts, methyl hydroxybenzoate 10-14 parts, magnesia 10-12 parts, fluor-apatite 20-25 parts, four Methoxymethyl glycoluril 8-10 parts, Environment-friendlycalcium calcium zinc stabilizer 6-8 parts, polyphenylene oxide resin 6-14 parts, epoxyoleic acid butyl ester 5-10 Part, citroflex A-4 6-8 parts, zinc stearate 3-8 parts, polybenzimidazoles 2-7 parts.
  2. A kind of 2. CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant according to claim 1, it is characterised in that：It is by following parts by weight Raw material be made：
    17.5 parts of ethene-acetate ethylene copolymer, 12.5 parts of haloflex, 17.5 parts of ferrocene, 12 parts of chloroplatinic acid, 21 parts of PVC resins, 12 parts of methyl hydroxybenzoate, 11 parts of magnesia, 22.5 parts of fluor-apatite, 9 parts of tetramethoxymethylglycoluril, 7 parts of Environment-friendlycalcium calcium zinc stabilizer, 10 parts of polyphenylene oxide resin, 7.5 parts of epoxyoleic acid butyl ester, 7 parts of citroflex A-4, firmly 5.5 parts of resin acid zinc, polybenzimidazoles 4.5-7 parts.
CN201710635483.6A 2017-07-31 2017-07-31 A kind of CABLE MATERIALS of Environment-friendlycorrosion-resistant corrosion-resistant Pending CN107383681A (en)