CN107364209A - A kind of warming combination process of looped fabric and looped fabric - Google Patents
A kind of warming combination process of looped fabric and looped fabric Download PDFInfo
- Publication number
- CN107364209A CN107364209A CN201710578113.3A CN201710578113A CN107364209A CN 107364209 A CN107364209 A CN 107364209A CN 201710578113 A CN201710578113 A CN 201710578113A CN 107364209 A CN107364209 A CN 107364209A
- Authority
- CN
- China
- Prior art keywords
- looped fabric
- fabric
- dye
- looped
- knitting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of looped fabric and the warming combination process of looped fabric, comprise the following steps：A, the preparation of material；B, pre-treatment；C, dye is taken off；D, dye：The knitting fabric for taking off dye is handled with refining agent, dried, dye liquor is heated to 60 DEG C, then knitting fabric is put into the dye liquor of heating, then by dye liquor continuous heating to 90 110 DEG C, stops heating, stands 60 90 min, finally dry stand-by；E, PU moisture permeable membranes are compound：PUR is smeared to the one side of looped fabric, at this time raised pressing plate temperature, it is by pressing machine that PU moisture permeable membranes and knitting cloth progress is compound；F, looped fabric is compound with looped fabric again：PUR is smeared to the another side of looped fabric, then raised pressing plate temperature, it is by pressing machine that looped fabric and looped fabric progress is compound.The product more waterproof and breathable of the warming combination process of the looped fabric and looped fabric production, and good warmth retention effect.
Description
Technical field
The invention belongs to cloth production technical field, and in particular to a kind of warming combination process of looped fabric and looped fabric.
Background technology
PU leathers are exactly the epidermis of polyurethane composition.It is widely used in makeing case and bag, clothes, footwear, vehicle and furniture now
Decoration, it has increasingly obtained the affirmative in market, and its application is wide, and quantity is big, as many as kind, is traditional natural leather
It can not meet.Its quality of PU leathers also has quality, and good PU skins are even also more expensive than corium price, and fixed effect is good, surface
Light, PU are applied to the in the market that fabric face comes across the 1950s earliest, and by 1964, du pont company developed
A kind of PU synthetic leather as upper of a shoe is gone out.After Japanese firm establishes a set of production line for producing 600000 square metres per year, pass through
The continuous research and development of more than 20 years, no matter PU synthetic leather is obtained in product quality, kind, or yield rapidly increases
It is long.Its performance becomes closer to natural leather, and some performances are even more than natural leather, has reached with natural leather true and false difficult point
Degree, in occupation of highly important status in the daily life of the mankind.So typically now increase face using PU is compound
The gas permeability and warmth retention property of material, but existing looped fabric mostly warming effect is bad, and also gas permeability is poor, so we need
The warming combination process of a new looped fabric and looped fabric is wanted to solve the above problems, meets the needs of people.
The content of the invention
It is an object of the invention to provide a kind of looped fabric and the warming combination process of looped fabric, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme：A kind of warming compound work of looped fabric and looped fabric
Skill, comprise the following steps：
A, the preparation of material：Knitting fabric is chosen, then carries out the steps such as fabric inspection, turn-over material and margin to seam；
B, pre-treatment：The knitting fabric of selection deoil decontamination, singe, the simple treatment process such as desizing and kiering；
C, dye is taken off：Above-mentioned treated knitting fabric is carried out using bleaching agent to take off dye processing, the knitted side after dye processing will be taken off
Material preserve stand-by；
D, dye：The knitting fabric for taking off dye is handled with refining agent, dried, dye liquor is heated to 60 DEG C, then will knitting
Fabric is put into the dye liquor of heating, then by dye liquor continuous heating to 90-110 DEG C, is stopped heating, is stood 60-90 min, most
After dry it is stand-by；
E, PU moisture permeable membranes are compound：：PUR is smeared to the one side of looped fabric, at this time pressing plate temperature is raised, passes through pressing
Machine carries out PU moisture permeable membranes with knitting cloth compound；
F, looped fabric is compound with looped fabric again：PUR is smeared to the another side of looped fabric, then pressing plate temperature is raised, led to
Cross pressing machine looped fabric and looped fabric progress is compound.
Preferably, sodium hypochlorite, hydrogen peroxide or sodium chlorite can be used in the bleaching agent in the step C.
Preferably, the processing of singing in the step B is or the red heat of nuzzling up quickly through thermal-flame by looped fabric open width
Metal surface, at this moment fine hair present on looped fabric heats up quickly, and burns, and looped fabric is relatively close in itself, rises
Temperature is slower, when not being raised to ignition point, that is, the metal surface of flame or red heat has been have left, so as to reach the mesh of burning-off fine hair
's.
Preferably, the process of decontamination of being deoiled in the step B is completed using degreaser.
Preferably, the knitting fabric that the step C is taken off after contaminating is placed in dustless environment of divulging information and carries out drying preservation.
The technique effect and advantage of the present invention：The product of the warming combination process of the looped fabric and looped fabric production is more
Waterproof and breathable, and good warmth retention effect so that people put on clothes made of the looped fabric can be more comfortable.
Embodiment
It is clearly and completely described below in conjunction with the technical scheme in the embodiment of the present invention, it is clear that described reality
It is only part of the embodiment of the present invention to apply example, rather than whole embodiments.It is general based on the embodiment in the present invention, this area
The every other embodiment that logical technical staff is obtained under the premise of creative work is not made, belong to what the present invention protected
Scope.
Embodiment 1
To achieve the above object, the present invention provides following technical scheme：A kind of warming combination process of looped fabric and looped fabric, bag
Include following steps：
A, the preparation of material：Knitting fabric is chosen, then carries out the steps such as fabric inspection, turn-over material and margin to seam；
B, pre-treatment：The knitting fabric of selection deoil decontamination, singe, the simple treatment process such as desizing and kiering；
C, dye is taken off：Above-mentioned treated knitting fabric is carried out using bleaching agent to take off dye processing, the knitted side after dye processing will be taken off
Material preserve stand-by；
D, dye：The knitting fabric for taking off dye is handled with refining agent, dried, dye liquor is heated to 60 DEG C, then will knitting
Fabric is put into the dye liquor of heating, then by dye liquor continuous heating to 90-110 DEG C, is stopped heating, is stood 60 min, finally
Dry stand-by；
E, PU moisture permeable membranes are compound：：PUR is smeared to the one side of looped fabric, at this time pressing plate temperature is raised, passes through pressing
Machine carries out PU moisture permeable membranes with knitting cloth compound；
F, looped fabric is compound with looped fabric again：PUR is smeared to the another side of looped fabric, then pressing plate temperature is raised, led to
Cross pressing machine looped fabric and looped fabric progress is compound.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, hypochlorous acid can be used in the bleaching agent in the step C
Sodium, hydrogen peroxide or sodium chlorite.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the processing of singing in the step B is by pin
Open width weave cotton cloth quickly through thermal-flame, or nuzzle up red heat metal surface, at this moment fine hair present on looped fabric heat up quickly,
And burn, and looped fabric is relatively closer in itself, heating is slower, when not being raised to ignition point, that is, have left flame or red
The metal surface of heat, so as to reach the purpose of burning-off fine hair.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the process for decontamination of being deoiled in the step B makes
Completed with degreaser.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the step C takes off the knitting fabric after dye
It is placed in dustless environment of divulging information and carries out drying preservation.
Embodiment 2
A kind of warming combination process of looped fabric and looped fabric, comprises the following steps：
A, the preparation of material：Knitting fabric is chosen, then carries out the steps such as fabric inspection, turn-over material and margin to seam；
B, pre-treatment：The knitting fabric of selection deoil decontamination, singe, the simple treatment process such as desizing and kiering；
C, dye is taken off：Above-mentioned treated knitting fabric is carried out using bleaching agent to take off dye processing, the knitted side after dye processing will be taken off
Material preserve stand-by；
D, dye：The knitting fabric for taking off dye is handled with refining agent, dried, dye liquor is heated to 60 DEG C, then will knitting
Fabric is put into the dye liquor of heating, then by dye liquor continuous heating to 90-110 DEG C, is stopped heating, is stood 75 min, finally
Dry stand-by；
E, PU moisture permeable membranes are compound：：PUR is smeared to the one side of looped fabric, at this time pressing plate temperature is raised, passes through pressing
Machine carries out PU moisture permeable membranes with knitting cloth compound；
F, looped fabric is compound with looped fabric again：PUR is smeared to the another side of looped fabric, then pressing plate temperature is raised, led to
Cross pressing machine looped fabric and looped fabric progress is compound.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, hypochlorous acid can be used in the bleaching agent in the step C
Sodium, hydrogen peroxide or sodium chlorite.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the processing of singing in the step B is by pin
Open width weave cotton cloth quickly through thermal-flame, or nuzzle up red heat metal surface, at this moment fine hair present on looped fabric heat up quickly,
And burn, and looped fabric is relatively closer in itself, heating is slower, when not being raised to ignition point, that is, have left flame or red
The metal surface of heat, so as to reach the purpose of burning-off fine hair.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the process for decontamination of being deoiled in the step B makes
Completed with degreaser.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the step C takes off the knitting fabric after dye
It is placed in dustless environment of divulging information and carries out drying preservation.
Embodiment 3
A kind of warming combination process of looped fabric and looped fabric, comprises the following steps：
A, the preparation of material：Knitting fabric is chosen, then carries out the steps such as fabric inspection, turn-over material and margin to seam；
B, pre-treatment：The knitting fabric of selection deoil decontamination, singe, the simple treatment process such as desizing and kiering；
C, dye is taken off：Above-mentioned treated knitting fabric is carried out using bleaching agent to take off dye processing, the knitted side after dye processing will be taken off
Material preserve stand-by；
D, dye：The knitting fabric for taking off dye is handled with refining agent, dried, dye liquor is heated to 60 DEG C, then will knitting
Fabric is put into the dye liquor of heating, then by dye liquor continuous heating to 90-110 DEG C, is stopped heating, is stood 90 min, finally
Dry stand-by；
E, PU moisture permeable membranes are compound：：PUR is smeared to the one side of looped fabric, at this time pressing plate temperature is raised, passes through pressing
Machine carries out PU moisture permeable membranes with knitting cloth compound；
F, looped fabric is compound with looped fabric again：PUR is smeared to the another side of looped fabric, then pressing plate temperature is raised, led to
Cross pressing machine looped fabric and looped fabric progress is compound.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, hypochlorous acid can be used in the bleaching agent in the step C
Sodium, hydrogen peroxide or sodium chlorite.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the processing of singing in the step B is by pin
Open width weave cotton cloth quickly through thermal-flame, or nuzzle up red heat metal surface, at this moment fine hair present on looped fabric heat up quickly,
And burn, and looped fabric is relatively closer in itself, heating is slower, when not being raised to ignition point, that is, have left flame or red
The metal surface of heat, so as to reach the purpose of burning-off fine hair.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the process for decontamination of being deoiled in the step B makes
Completed with degreaser.
The warming combination process of above-mentioned a kind of looped fabric and looped fabric, wherein, the step C takes off the knitting fabric after dye
It is placed in dustless environment of divulging information and carries out drying preservation.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic,
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in the present invention's
Within protection domain.
Claims (5)
- A kind of 1. warming combination process of looped fabric and looped fabric, it is characterised in that：Comprise the following steps：A, the preparation of material：Knitting fabric is chosen, then carries out the steps such as fabric inspection, turn-over material and margin to seam；B, pre-treatment：The knitting fabric of selection deoil decontamination, singe, the simple treatment process such as desizing and kiering；C, dye is taken off：Above-mentioned treated knitting fabric is carried out using bleaching agent to take off dye processing, the knitted side after dye processing will be taken off Material preserve stand-by；D, dye：The knitting fabric for taking off dye is handled with refining agent, dried, dye liquor is heated to 60 DEG C, then will knitting Fabric is put into the dye liquor of heating, then by dye liquor continuous heating to 90-110 DEG C, is stopped heating, is stood 60-90 min, most After dry it is stand-by；E, PU moisture permeable membranes are compound：：PUR is smeared to the one side of looped fabric, at this time pressing plate temperature is raised, passes through pressing Machine carries out PU moisture permeable membranes with knitting cloth compound；F, looped fabric is compound with looped fabric again：PUR is smeared to the another side of looped fabric, then pressing plate temperature is raised, led to Cross pressing machine looped fabric and looped fabric progress is compound.
- 2. the warming combination process of a kind of looped fabric according to claim 1 and looped fabric, it is characterised in that：The step Sodium hypochlorite, hydrogen peroxide or sodium chlorite can be used in bleaching agent in C.
- 3. the warming combination process of a kind of looped fabric according to claim 1 and looped fabric, it is characterised in that：The step Processing of singing in B be by looped fabric open width quickly through thermal-flame, or nuzzle up red heat metal surface, at this moment on looped fabric Existing fine hair heats up quickly, and burns, and looped fabric is relatively closer in itself, and heating is slower, when not being raised to ignition point, The metal surface of flame or red heat is have left, so as to reach the purpose of burning-off fine hair.
- 4. the warming combination process of a kind of looped fabric according to claim 1 and looped fabric, it is characterised in that：The step The process of decontamination of being deoiled in B is completed using degreaser.
- 5. the warming combination process of a kind of looped fabric according to claim 1 and looped fabric, it is characterised in that：The step The knitting fabric that C is taken off after contaminating is placed in dustless environment of divulging information and carries out drying preservation.