CN107345437A - A kind of construction method of water-based uncured coating and coiled material composite waterproof system - Google Patents
A kind of construction method of water-based uncured coating and coiled material composite waterproof system Download PDFInfo
- Publication number
- CN107345437A CN107345437A CN201710295419.8A CN201710295419A CN107345437A CN 107345437 A CN107345437 A CN 107345437A CN 201710295419 A CN201710295419 A CN 201710295419A CN 107345437 A CN107345437 A CN 107345437A
- Authority
- CN
- China
- Prior art keywords
- water
- uncured coating
- parts
- based uncured
- coiled material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the construction method of a kind of water-based uncured coating and coiled material composite waterproof system, comprise the following steps:S1:Water-based uncured coating is sprayed on substrate layer;S2:Waterproof roll layer is pasted in S1 coating surfaces.The construction method of the water-based uncured coating coiled material composite waterproof system of the present invention sprays water-based uncured coating in substrate surface first, the waterproof layer of integral seamless is formed in substrate surface, then the adhesive property of the water-based uncured coating is utilized, waterproof roll is directly bonded in the upper end of water-based uncured coating, to increase the rigidity of waterproof system, compared with prior art, work progress is without heating, dry and wet degree no requirement (NR) to construction surface, cold construction and rainy day construction can be achieved.
Description
Technical field
The present invention relates to waterproof construction technology field, and in particular to a kind of water-based uncured coating and coiled material composite water-proof system
The construction method of system.
Background technology
The water-based uncured coating of uncured rubber asphalt and coating have good adhesion, extensibility, self-healing property, low temperature
It is flexible, jointless construction can be realized in waterproof construction, is a kind of new asphalt waterproofing material.In existing roofing, underground
Waterproof material, buildings waterproof construction in the related specifications of waterproofing work, code to more than, construction method, the acceptance of work have
Relatively clearly provide.The construction of a kind of uncured rubber-asphalt coating and coiled material complex waterproof layer is disclosed in CN103465540A
Method, its content are included after uncured rubber-asphalt coating is heated into set point of temperature, are existed by the method construction for scratching, spraying
The surface of basic unit, in the waterproof roll layer that surface mount and the uncured rubber-asphalt coating of hot coating mix.This document is said
Referred in bright book, technical problem to be solved is self-adhesive coiled material waterproof layer and basic unit in wet-laying engineering method of the prior art
The channeling water and drainage gone between (or structure sheaf) into " Sandwich biscuit type ", moreover it is possible to which solution is led because worker's constructing operation is lack of standardization
The waterproof layer hollowing phenomenon of cause.Uncured rubber-asphalt coating in such scheme needs to be coated with after heating, in construction environment
Solvent volatile quantity is larger, to fire-fighting requirements height;Substrate surface must be dried, and can not be constructed under wet condition.
Improved technical scheme also includes connecing waterproof roll using melt viscosity in the prior art, but the use of PUR is same
Sample needs to heat, and clean-up performance to waterproof construction face and degree of drying require higher, and working procedure is cumbersome.
In addition, although coiled material seam crossing passes through much time using, seam crossing easily seeps water through water-proofing treatment
Phenomenon, so as to further influence the bonding stability between coiled material and base material.
The content of the invention
It is an object of the invention to overcome defect present in prior art, there is provided a kind of to construction substrate and environmental requirement
The construction method of low water-based uncured coating and coiled material composite waterproof system.
To realize above-mentioned technique effect, the technical scheme is that:A kind of water-based uncured coating is compound anti-with coiled material
The construction method of water system, it is characterised in that comprise the following steps:
S1:Water-based uncured coating is sprayed on substrate layer;
S2:Waterproof roll layer is pasted in S1 coating surfaces.
In order to optimize the compatibility of water-based uncured coating and coiled material, preferable technical scheme is that waterproof roll layer is certainly
The polymer modified waterproof roll of adhesive aggregation, SBS/APP modified asphalt waterproof coiled materials and the non-bituminous base waterproof roll of macromolecule.
Further preferred technical scheme is that the material of the non-bituminous base waterproof roll of macromolecule is TPO, HDPE, PVC, three
First EP rubbers.
Preferable technical scheme is that the main composition of water-based uncured coating is:Anion rubber elastomer modified emulsifying
Pitch, modified resin emulsion, filler, auxiliary agent, wherein auxiliary agent be selected from defoamer, dispersant, stabilizer, vulcanizing agent, age resistor,
Combination more than one or both of wetting agent and antifreezing agent, water-based uncured coating is using exterior mixing two-component spray gun with promoting
Solidifying agent solution sprays simultaneously.Coagulant and water-based uncured coating are sprayed simultaneously, it is ensured that two kinds of solution are dropping down onto spraying
Mix in front, promote demulsification to accelerate de-emulsification speed by inside dope layer, it is above-mentioned anti-under rainy day or cryogenic conditions
Water construction can be also normally carried out, in addition, the phenomenon for being applied directly to cause in coating shower nozzle to block coagulant can be avoided.
Preferable technical scheme is that the key component of water-based uncured coating is:Anion rubber elastomer modified emulsifying
70~80 parts of pitch, 8~13 parts of the modified resin emulsion that solid content is 42~70%, 5~20 parts of filler, auxiliary agent 0.005~12
Part.With cationic emulsified bitumen de-emulsification speed soon compared with, anionic emulsified bitumen is relatively slow, but has stronger bonding force,
The demulsification process of coating can realize the wetting and infiltration with waterproof roll, and waterproof roll can directly be bonded in water-based uncured coating
Surface, Quick cross-linking occurs between two layers, so as to ensure larger adhesive strength between two layers of waterproof system.
Preferable technical scheme is that the composition and parts by weight of anion rubber elastomer modified emulsifying asphalt are:Matrix
40~60 parts of pitch, 2~5 parts of SBS rubber grains, 1~4 part of SBR rubber powder, 3~7 parts of NBR rubber powder, polythene wax emulsion 2
~10 parts, 1~5 part of modified siloxane, 10~20 parts of deionized water, 1~3 part of anion emulsifier, nonionic surfactant
0.5~2 part, 1~3 part of at least one of aromatic naphtha and naphthenic oil.NBR rubber powder is added into anionic emulsified bitumen, is had
Help improve the heat resistance of emulsified asphalt, in addition, one kind in aromatic naphtha and naphthenic oil can be miscible with matrix pitch, emulsifying
Emulsification forms homogeneous and stable emulsified asphalt system in the presence of agent and nonionic surfactant.
In order to further speed up the de-emulsification speed of anion rubber elastomer modified emulsifying asphalt, preferable technical scheme
For, sprayed simultaneously with water-based uncured coating and in outer mixed accelerator solution coagulant combined by alum and calcium chloride and
Into the percentage by weight of calcium chloride is 10~50% in coagulant, and water-based uncured coating spray volume coagulates with promoting in the unit interval
The mass ratio of coagulant is (5~10) in agent solution spray volume:1.
Preferable technical scheme is that water-based uncured coating surface spraying water swelling rubber is additionally included between S1 and S2
The step of, the material of the water accepting layer is bentonite/acrylamide graft natural rubber, and quantity for spray is 20~30g/m2.Swelling
Soil/acrylamide graft natural rubber has excellent repetition water imbibition and water-retaining property, and the moisture part for being demulsified to obtain is penetrated into
In base material, another part volatilization, residual fraction is absorbed through water swelling rubber, and bentonite/acrylamide graft natural rubber is not
The elasticity of the forming coating between base material and coiled material can only be increased, moreover it is possible to via waterproof roll seam or split preventing moisture
Stitch and spread to substrate surface.
Preferable technical scheme is that vulcanizing agent is made up of alkyl phenol disulfide and dibenzoyl paraquinonedioxime, vulcanization
The percentage by weight of alkyl phenol disulfide is 15~25% in agent.The combination of vulcanizing agent can be to rubber asphalt and rubber powder in two
Between and the crosslinking between rubber asphalt and waterproof roll play a part of Synergistic, further shorten coating shaping when
Between, improve the crosslink density that water-based uncured coating shapes the space multistory network structure to be formed.In addition, the vulcanizing agent can promote
Crosslinking between water swelling rubber and waterproof roll.
Preferable technical scheme is that wetting agent is formed by alkylnaphthalene sulfonate and tween compounding, wherein the weight hundred of tween
Divide than being 5~30%.Using anion surfactant alkylnaphthalene sulfonate and non-ionic surfactant polyoxyethylene sorb
Sugar alcohol acid anhydride fatty acid ester is compounded, and the advantages of two kinds of surfactants of mixed system spacing, coating interfacial tension is low, accelerates to apply
Expect the wetting rate on base material and waterproof roll surface, optimize osmotic effect, so as to increase the adhesive force of waterproof system and interlayer
Adhesive strength.
The advantages of the present invention are:
The construction method of the water-based uncured coating of the present invention and coiled material composite waterproof system sprays water in substrate surface first
Property uncured coating, substrate surface formed integral seamless waterproof layer, then utilize the bonding of the water-based uncured coating
Performance, waterproof roll is directly bonded in the upper end of water-based uncured coating, to increase the rigidity of waterproof system and impact resistance
Can, compared with prior art, work progress is without heating, the dry and wet degree no requirement (NR) to construction surface, and cold construction can be achieved
Constructed with the rainy day;
Compared with coiled material of the prior art, the water-based uncured coating of bottom covers for integral type, is connect in the absence of bonding
Seam, therefore can avoid using seam crossing infiltration phenomenon caused by aging for a long time.
Embodiment
With reference to embodiment, the embodiment of the present invention is further described.Following examples are only used for more
Add and clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
Embodiment 1
The water-based uncured coating of embodiment 1 and the construction method of coiled material composite waterproof system, comprise the following steps:
S1:Water-based uncured coating is sprayed on substrate layer;
S2:Waterproof roll layer is pasted in S1 coating surfaces.
The water-based uncured rubber-asphalt coating of cation emulsified asphalt is used in embodiment 1, by component A and B component
Form in proportion, wherein component A by 75 parts of cation modified rubber emulsified asphalts, 10 parts of tackifier resin emulsions, 5 parts of monooctyl esters, 2 parts
Interfacial agents, 2 parts of antifreezing agents and 2 parts of age resistor compositions;Component B is made up of 10 parts of inorganic salts, 15 parts of buffers and 60 parts of water;Component
A and component B mass ratio is 30:1.Above-mentioned tackifying resin is C5 Petropols, and tackifier resin emulsion is terpene resin emulsion, boundary
Face agent is polyether modified siloxane, and antifreezing agent is ethylene glycol, and age resistor is antioxidant 264, and inorganic salts are that magnesium chloride is solidifying as promoting
Agent uses, and buffer is glycerine.
Cation modified rubber emulsified asphalt is by matrix pitch, mixed rubber, vulcanizing agent, stabilizer, deionized water and sun
Ionic emulsifying agent forms, and matrix pitch, mixed rubber, vulcanizing agent, the mass ratio of deionized water and cationic emulsifier are 100:
11:0.1:0.1:40:6.Vulcanizing agent is sulphur, and mixed rubber is that SBR rubber, SBS rubber and SIS building rubber compounds form, and is combined
Ratio is 3:3:5.
Waterproof roll in embodiment 1 is modified waterproof roll, specially PVC waterproof rolls for self-adhering polymer.
Embodiment 2
The difference of embodiment 2 and embodiment 1 is:Waterproof roll is the type of self-adhered polymer modified bitumen waterproofing membrane I;
Embodiment 3
The difference of embodiment 3 and embodiment 1 is that waterproof roll is SBS/APP modified asphalt waterproof coiled materials;
Embodiment 4
The difference of embodiment 4 and embodiment 3 is that waterproof roll is TPO waterproof rolls.TPO waterproof rolls can also be adopted
Replaced with HDPE, PVC, ethylene propylene diene rubber material waterproof roll.
Embodiment 5
The difference of embodiment 5 and embodiment 3 is:The water-based uncured coating of bottom is the painting containing anionic emulsified bitumen
Material, the key component of water-based uncured coating are:60 parts of anion rubber elastomer modified emulsifying asphalt, solid content are 70%
8 parts of modified resin emulsion, 20 parts of filler, 0.005 part of auxiliary agent.
The composition and parts by weight of anion rubber elastomer modified emulsifying asphalt be:60 parts of matrix pitch, SBS rubber
Grain 2 parts, 4 parts of SBR rubber powder, 3 parts of NBR rubber powder, 10 parts of polythene wax emulsion, 1 part of modified siloxane, 40 parts of deionized water,
1 part of anion emulsifier, 2 parts of nonionic surfactant, 3 parts of aromatic naphtha.Wherein anion emulsifier is selected from sulfuric acid, non-
Ionic surface active agent APES;Modified resin emulsion is terpene resin emulsion;Filler is bentonite.
Auxiliary agent is wetting agent, and water-based uncured coating uses exterior mixing two-component spray gun spraying, and wherein coagulant is chlorination
Calcium.The spraying of coating and calcium chloride is compared for 20:1.
Embodiment 6
Embodiment 6 differs only in embodiment 5, and the key component of water-based uncured coating is:Anion rubber bullet
Property modifies 70 parts of emulsified asphalt, solid content be 70% 8 parts of modified resin emulsion, 20 parts of filler, 0.005 part of auxiliary agent.Coating
Spraying with alum is compared for 10:1.
Embodiment 7
The difference of embodiment 7 and embodiment 6 is:The key component of water-based uncured coating is:Anion caoutchouc elasticity
Modifies 80 parts of emulsified asphalt, 13 parts of the modified resin emulsion that solid content is 42%, 5 parts of filler, 12 parts of auxiliary agent.Auxiliary agent, which includes, to disappear
2 parts of 1 part of infusion, 1 part of dispersant, 1 part of stabilizer, 3 parts of vulcanizing agent, 2 parts of age resistor, 2 parts of wetting agent and antifreezing agent.Defoamer is
Mineral oil antifoam agent;Dispersant is amido sulfoacid series water paint dispersant, and stabilizer is Colloidal microcrystalline cellulose.Vulcanizing agent is
Sulphur, age resistor DLTP, wetting agent are silanol class nonionic surfactant, and antifreezing agent is propane diols.
The composition and parts by weight of anion rubber elastomer modified emulsifying asphalt be:40 parts of matrix pitch, SBS rubber
5 parts of grain, 1 part of SBR rubber powder, 7 parts of NBR rubber powder, 2 parts of polythene wax emulsion, 5 parts of modified siloxane, 10 parts of deionized water, the moon
3 parts of ionic emulsifying agent, 0.5 part of nonionic surfactant, 1 part of naphthenic oil.
With coagulant in the ejection simultaneously of water-based uncured coating and outer mixed accelerator solution by alum and calcium chloride
Combine, the percentage by weight of calcium chloride is 10% in coagulant, and water-based uncured coating spray volume is with promoting in the unit interval
The mass ratio of coagulant is 5 in solidifying agent solution spray volume:1.
Embodiment 8
The difference of embodiment 8 and embodiment 7 is:The key component of water-based uncured coating is:Anion caoutchouc elasticity
Modifies 75 parts of emulsified asphalt, 10 parts of the modified resin emulsion that solid content is 70%, 12 parts of filler, 6 parts of auxiliary agent.Auxiliary agent, which includes, to disappear
1 part of 0.5 part of infusion, 0.5 part of dispersant, 0.5 part of stabilizer, 1.5 parts of vulcanizing agent, 1 part of age resistor, 1 part of wetting agent and antifreezing agent.
The composition and parts by weight of anion rubber elastomer modified emulsifying asphalt be:50 parts of matrix pitch, SBS rubber
3.5 parts of grain, 2.5 parts of SBR rubber powder, 5 parts of NBR rubber powder, 6 parts of polythene wax emulsion, 3 parts of modified siloxane, deionized water 25
Part, 2 parts of anion emulsifier, 1.2 parts of nonionic surfactant, aromatic naphtha and each 1 part of naphthenic oil.
The percentage by weight of calcium chloride is 50% in coagulant, and water-based uncured coating spray volume coagulates with promoting in the unit interval
The mass ratio of coagulant is 10 in agent solution spray volume:1.
Vulcanizing agent is made up of alkyl phenol disulfide and dibenzoyl paraquinonedioxime, alkylphenol curing in vulcanizing agent
The percentage by weight of thing is 15%.
Wetting agent is formed by alkylnaphthalene sulfonate and tween compounding, and wherein the percentage by weight of tween is 5%.
Embodiment 9
The difference of embodiment 9 and embodiment 8 is:The difference of embodiment 8 and embodiment 7 is, calcium chloride in coagulant
Percentage by weight be 30%, water-based uncured coating spray volume and coagulant in accelerator solution spray volume in the unit interval
Mass ratio is 15:2.
Vulcanizing agent is made up of alkyl phenol disulfide and dibenzoyl paraquinonedioxime, alkylphenol curing in vulcanizing agent
The percentage by weight of thing is 25%.
Wetting agent is formed by alkylnaphthalene sulfonate and tween compounding, and wherein the percentage by weight of tween is 30%.
Embodiment 10
The difference of embodiment 10 and embodiment 9 is:Difference is to spray bentonite/acryloyl on S1 sprayed coatings surface
Amine grafted natural rubber, quantity for spray 20g/m2.Quantity for spray can suitably increase to 30g/m2, it is excessive based on cost consideration, fountain height
Unhelpful to soaking effect, bentonite/acrylamide graft natural rubber thickness, which crosses conference, influences the layers cementing effect of waterproof system
Fruit, bentonitic addition, which is crossed, to be needed suitably to increase water volatilization time, the shortening unobvious for speed of application at least.
Vulcanizing agent is made up of alkyl phenol disulfide and dibenzoyl paraquinonedioxime, alkylphenol curing in vulcanizing agent
The percentage by weight of thing is 20%.
Wetting agent is formed by alkylnaphthalene sulfonate and tween compounding, and wherein the percentage by weight of tween is 17%.
Comparative example
Comparative example uses two panels waterproof roll, and uses S1 water-based uncured coating processing seam, at coiled material and waterproof
It is bonded between reason face using PUR.
Coagulant is directly appended in coating in embodiment 1-4, in embodiment 5-9 coagulant using it is outer it is mixed by the way of and painting
Material mixing.
Adhesive property detection method:Water-based uncured coating is sprayed into cement mortar surface, coated area 100*
50mm, thickness are 2 ± 0.2mm, are then bonded waterproof roll and form composite waterproof system, are adhered to after maintenance using waterproof coating
Force tester detects to the adhesive strength between waterproof system and cement mortar.
Heat aging property detection method:The water-based uncured coating of embodiment is sprayed into surface of aluminum plate, coated area is
100*50mm, thickness are 2 ± 0.2mm, then be bonded waterproof roll formed composite waterproof system, be placed in after maintenance constant temperature 70 ±
In 2 DEG C of baking oven keep 168 ± 2h, to after heat treatment sample carry out low temperature flexibility (- 20 DEG C) and water penetration (0.3Mpa,
30min) test.In addition, comparative example waterproof roll is fitted into surface of aluminum plate by the way of to hot melt glue surface heating, using S1
Water-based uncured coating processing seam, and tested through same heat aging property, after contrasting heat-proof aging with embodiment
Low temperature flexibility and water penetration.
Survey the waterproof system engineering time.
The performance test results of water-based uncured coating and coiled material composite waterproof system are as follows:
Embodiment 1 and embodiment the 2-4 material for differing only in waterproof roll, the material of waterproof roll is also largely
On determine the deformabilities such as tensile strength and the elasticity of waterproof system.
Embodiment 5, embodiment 6 and implementation 7 are contrasted, and embodiment 5 is adopted using calcium chloride as the solidifying agent of group, embodiment 6
By the use of alum as coagulant, embodiment 6 is by the way of both combinations, from the rate of set of water-based uncured coating
See, the reason for embodiment 7 is substantially better than embodiment 5 and embodiment 6, and the rate of set of embodiment 5 is more than embodiment 6 is to promote solidifying
Agent and the large percentage of coating.
In addition, embodiment 7 is contrasted with embodiment 8-9, vulcanizing agent and the further preferred of wetting agent increase waterproof
System and the adhesive strength in waterproof construction face.
Embodiment 10 with the addition of water swelling rubber due to adding, and during practice of construction, water swelling rubber is same
Step spraying, the duration for waiting water-based non-cured materials moisture evaporation shaping can be shortened, be favorably improved efficiency of construction.System is applied
Work exterior wall class surface drying time≤30min.And the surface drying time of relative embodiment 1~4 is in 60~80min, embodiment 5~6
Surface drying time be 40~50min, the surface drying time of embodiment 7~9 is 30~40min.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (10)
1. the construction method of a kind of water-based uncured coating and coiled material composite waterproof system, it is characterised in that comprise the following steps:
S1:Water-based uncured coating is sprayed on substrate layer;
S2:Waterproof roll layer is pasted in S1 coating surfaces.
2. the construction method of water-based uncured coating according to claim 1 and coiled material composite waterproof system, its feature exist
In waterproof roll layer is that self-adhering polymer is modified waterproof roll, SBS/APP modified asphalt waterproof coiled materials and the non-bituminous base of macromolecule
Waterproof roll.
3. the construction method of water-based uncured coating according to claim 2 and coiled material composite waterproof system, its feature exist
In the material of the non-bituminous base waterproof roll of macromolecule is TPO, HDPE, PVC, ethylene propylene diene rubber.
4. the construction method of water-based uncured coating according to claim 1 and coiled material composite waterproof system, its feature exist
In the main composition of water-based uncured coating is:Anion rubber elastomer modified emulsifying asphalt, modified resin emulsion, filler,
Auxiliary agent, wherein auxiliary agent are one kind in defoamer, dispersant, stabilizer, vulcanizing agent, age resistor, wetting agent and antifreezing agent
Or two or more combinations, water-based uncured coating are sprayed simultaneously using exterior mixing two-component spray gun with accelerator solution.
5. the construction method of water-based uncured coating according to claim 4 and coiled material composite waterproof system, its feature exist
In the key component of water-based uncured coating is:70~80 parts of anion rubber elastomer modified emulsifying asphalt, solid content 42
~70% 8~13 parts of modified resin emulsion, 5~20 parts of filler, 0.005~12 part of auxiliary agent.
6. the construction method of water-based uncured coating according to claim 5 and coiled material composite waterproof system, its feature exist
In the composition and parts by weight of anion rubber elastomer modified emulsifying asphalt are:40~60 parts of matrix pitch, SBS rubber
2~5 parts of grain, 1~4 part of SBR rubber powder, 3~7 parts of NBR rubber powder, 2~10 parts of polythene wax emulsion, modified siloxane 1~5
Part, 10~20 parts of deionized water, 1~3 part of anion emulsifier, 0.5~2 part of nonionic surfactant, aromatic naphtha and cycloalkanes
1~3 part of at least one of oil.
7. the construction method of water-based uncured coating according to claim 4 and coiled material composite waterproof system, its feature exist
In the coagulant in accelerator solution is combined by alum and calcium chloride, the percentage by weight of calcium chloride in coagulant
For 10~50%, the mass ratio of water-based uncured coating spray volume and coagulant in accelerator solution spray volume is in the unit interval
(5~10):1.
8. the construction method of water-based uncured coating according to claim 1 and coiled material composite waterproof system, its feature exist
In, the step of water-based uncured coating surface spraying water swelling rubber is additionally included between S1 and S2, the material of the water accepting layer
Matter is bentonite/acrylamide graft natural rubber, and the material of the water accepting layer is the natural rubber of bentonite/acrylamide graft
Glue, quantity for spray are 20~30g/m2。
9. the construction method of water-based uncured coating according to claim 4 and coiled material composite waterproof system, its feature exist
In vulcanizing agent is made up of alkyl phenol disulfide and dibenzoyl paraquinonedioxime, alkyl phenol disulfide in vulcanizing agent
Percentage by weight is 15~25%.
10. the construction method of the water-based uncured coating and coiled material composite waterproof system according to claim 4 or 8, it is special
Sign is that wetting agent is formed by alkylnaphthalene sulfonate and tween compounding, and wherein the percentage by weight of tween is 5~30%.