CN107345368A - A kind of self-adhesion grid cloth - Google Patents
A kind of self-adhesion grid cloth Download PDFInfo
- Publication number
- CN107345368A CN107345368A CN201610295552.9A CN201610295552A CN107345368A CN 107345368 A CN107345368 A CN 107345368A CN 201610295552 A CN201610295552 A CN 201610295552A CN 107345368 A CN107345368 A CN 107345368A
- Authority
- CN
- China
- Prior art keywords
- warp
- twisting
- self
- grid cloth
- thin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of self-adhesion grid cloth, and it includes glass fiber substrate, alkaline-resisting emulsion layer, glue layer;The double braid form similar to lace stitch that glass fiber substrate uses, there is higher intensity derived from viscous grid cloth, the life-span is longer, quality is more soft, with preferably performance is pasted, it is set not formed when pasting in polystyrene main body, the hollowing in local areas such as corners;A kind of self-adhesion grid cloth, by the processing of alkaline-resisting emulsion layer, alkali resistant liquid, reinforcing agent, its intensity is further increased, it is not produced the Splitting in local areas such as corners when pasting in polystyrene main body, be advantageous to next step scrapes slurry process;A kind of self-adhesion grid cloth glue layer is by the twisted gap of thin twisting warp, and the twisted gap of thick twisting warp is merged with whole glass fiber substrate, and is covered thereon so that the viscosity of self-adhesion grid cloth is more preferable.
Description
Technical field
The present invention relates to building materials technology field, more particularly to a kind of self-adhesion grid cloth for being used to manufacture EPS.
Background technology
With expanding economy and the raising of living standards of the people, to the more and more higher of aesthetical perception requirement, building trade shows especially prominent for society.The buildings such as house, market, school, office building are not only physically showing different, outstanding characteristics, and on the moulding at the positions such as roof, stringcourse, exterior window trim
Also it is novel, show aesthetic feeling.
Occur a kind of EPS mouldings on the market at present, EPS moulding is a kind of new decoration of exterior wall line and component, and it is main body by being stripped B1 level fireproof polystyrene, pastes alkali resistant glass fibre open weave cloth, is subject to special bonding external protection and is combined.After hardening, the pliability of organic material and the intensity of the base of cement are had concurrently.Not only it had been incubated but also light and handy, the dimensionally stable product, had not been changed by temperature change, had been resisted cold, it is heat-resisting, do not influenceed by humid climate and acid rain.It can substitute traditional cement (GRC) component completely, more it is practically applicable to install on the wall of exterior wall, European classic, graceful decorated style can be embodied, and can ensures that main building exterior wall occurs without hot and cold bridge effect, with advantages such as easy for installation, economy, durability length, can prevent fires will not send noxious material again, be the high-quality decorative building material product of environmental protection.
But, alkali resistant glass fibre open weave cloth in the EPS lines pillars used on the market at present, it is most in itself and not strong without viscosity or viscosity, need artificial spreading glue again, and when grid cloth is pasted onto on polystyrene, dry glue, and local phenomena such as heaving occur once in a while, photoresist coating process needs that there is the worker of related installation experience to be installed, and cost is higher;Simultaneously, currently used alkali resistant glass fibre open weave cloth, weaving is most to use currently used plain weave, with decorative pattern knitting skill, hardness of the grid cloth being made into itself is higher, its intensity also and not up to optimal state, easily forms hollowing, and easily tear when pasting in the local areas such as corner and polystyrene.
The content of the invention
The present invention is directed to above-mentioned the deficiencies in the prior art, provide a kind of self-adhesion grid cloth, the double braid form similar to lace stitch that glass fiber substrate uses, there is higher intensity derived from viscous grid cloth, the life-span is longer, quality is more soft, with preferably pasting performance, and glue layer is merged by the twisted gap of thin twisting warp, the twisted gap of thick twisting warp with whole glass fiber substrate, and cover thereon so that the viscosity of self-adhesion grid cloth is more preferable.
To solve problems of the prior art, the concrete technical scheme of use is:
A kind of self-adhesion grid cloth, it includes glass fiber substrate, alkaline-resisting emulsion layer, glue layer;
Its preparation method includes following a)、b)、c)Step:
a)Compiled with glass fibre woven into glass fiber substrate on cloth machine;
b)Alkaline-resisting emulsion layer and alkali resistant liquid, reinforcing agent are coated on glass fiber substrate;
c)Shaping is baked at a temperature of 190 °C ~ 210 °C, after cooking phase coating glue layer;
The reinforcing agent is made after being mixed by the polymer builder that concentration is 55% ± 1% with the water that concentration is 45% ± 1%;
The glue layer is made up of esters of acrylic acid synthetic latex.
Preferable scheme:The glass fiber substrate is made up of double-decker identical fiber layer and interlayer twisting fiber, and fiber layer includes parallel, thin twisting warp, thick twisting warp, straight warp;Its microcosmic type of weave of fiber layer is:The linearly horizontal direction arrangement of parallel, thin twisting warp, thick twisting warp, straight warp arrange in vertical direction, from left to right put in order as straight warp, thin twisting warp, straight warp, thin twisting warp, straight warp, thick twisting warp, straight warp, thick twisting warp, straight warp, thin twisting warp, straight warp, thin twisting warp, straight warp.
Further preferred scheme:The thin twisting warp, thick twisting warp, straight warp are alternately interspersed between parallel.
Further preferred scheme:The interlayer twisting fiber is alternately interspersed between fiber layer.
Further preferred scheme:The twisted gap of the thin twisting warp is between 0.1mm ~ 0.2mm, and the twisted gap of the thick twisting warp is between 0.4mm ~ 0.6mm.
A kind of self-adhesion grid cloth, its manufacturing process are:Compiled first with glass fibre woven into glass fiber substrate on cloth machine;Secondly, glass fiber substrate is put into coating work platform, and alkaline-resisting emulsion layer and alkali resistant liquid, reinforcing agent are coated thereon;Secondly, after alkaline-resisting emulsion layer and alkali resistant liquid, reinforcing agent are totally immersed in glass fiber substrate, baking production line is put it into;Again, it is baked at a temperature of 190 °C ~ 210 °C, after cooking the phase, coats glue layer, then wait for natural cooling;Finally by monoblock self-adhesion grid cloth, excision forming and a roll is rolled on cutting machine.
The type of weave similar to lace stitch used due to glass fiber substrate, and it has double-decker, warp twisted together causes self-adhesion grid cloth to have higher intensity, and the presence in twisted gap make it that self-adhesion grid cloth quality is more soft, has and preferably pastes performance;Alkaline-resisting emulsion layer, glue layer, alkali resistant liquid, reinforcing agent are coated easily by the twisted gap of thin twisting warp, the twisted gap of thick twisting warp is merged with whole glass fiber substrate, and is covered thereon so that the viscosity of self-adhesion grid cloth is more preferable.
By using such scheme, compared with prior art, it has technical effect that a kind of self-adhesion grid cloth of the invention:
1. the double braid form similar to lace stitch that the glass fiber substrate of the present invention uses, there is higher intensity derived from viscous grid cloth, life-span is longer, quality is more soft, with preferably pasting performance, it is set not formed when pasting in polystyrene main body, the hollowing in local areas such as corners.
2. self-adhesion grid cloth of the present invention, by the processing of alkaline-resisting emulsion layer, alkali resistant liquid, reinforcing agent, its intensity is further increased, it is not produced the Splitting in local areas such as corners when pasting in polystyrene main body, be advantageous to next step scrapes slurry process.
3. self-adhesion grid cloth glue layer of the present invention is merged by the twisted gap of thin twisting warp, the twisted gap of thick twisting warp with whole glass fiber substrate, and is covered thereon so that the viscosity of self-adhesion grid cloth is more preferable.
Brief description of the drawings
Fig. 1 is a kind of overall cross-sectional view of self-adhesion grid cloth of the present invention;
Fig. 2 is a kind of glass fiber substrate structural representation of self-adhesion grid cloth of the present invention;
Fig. 3 is a kind of fiber layer microstructure schematic diagram of the glass fiber substrate of self-adhesion grid cloth of the present invention.
Embodiment
To make the object, technical solutions and advantages of the present invention of greater clarity, with reference to instantiation and referring to the drawings, the present invention is described in more detail.It should be understood that these descriptions are merely illustrative, and it is not intended to limit the scope of the present invention.In addition, in the following description, the description to known features and technology is eliminated, to avoid unnecessarily obscuring idea of the invention.
As shown in Figures 1 and 3:A kind of self-adhesion grid cloth, it includes glass fiber substrate 1, alkaline-resisting emulsion layer 2, glue layer 3;
Its preparation method includes following a)、b)、c)Step:
a)Compiled with glass fibre woven into glass fiber substrate 1 on cloth machine;
b)Alkaline-resisting emulsion layer 2 and alkali resistant liquid, reinforcing agent are coated on glass fiber substrate 1;
c)Shaping is baked at a temperature of 190 °C ~ 210 °C, after cooking phase coating glue layer 3;
The reinforcing agent is made after being mixed by the polymer builder that concentration is 55% ± 1% with the water that concentration is 45% ± 1%;
The glue layer 3 is made up of esters of acrylic acid synthetic latex;
The glass fiber substrate 1 is made up of double-decker identical fiber layer 11 and interlayer twisting fiber 12, and fiber layer 11 includes parallel 111, thin twisting warp 112, thick twisting warp 113, straight warp 114;Its microcosmic type of weave of fiber layer 111 is:111 linearly horizontal direction of parallel arranges, thin twisting warp 112, thick twisting warp 113, straight warp 114 arrange in vertical direction, from left to right put in order as straight warp 114, thin twisting warp 112, straight warp 114, thin twisting warp 112, straight warp 114, thick twisting warp 113, straight warp 114, thick twisting warp 113, straight warp 114, thin twisting warp 112, straight warp 114, thin twisting warp 112, straight warp 114;
The thin twisting warp 112, thick twisting warp 113, straight warp 114 are alternately interspersed between parallel 111;
The interlayer twisting fiber 12 is alternately interspersed between fiber layer 11;
The twisted gap of the thin twisting warp 112 is between 0.1mm ~ 0.2mm, and the twisted gap of the thick twisting warp 113 is between 0.4mm ~ 0.6mm.
A kind of self-adhesion grid cloth, its manufacturing process are:Compiled first with glass fibre woven into glass fiber substrate 1 on cloth machine;Secondly, glass fiber substrate 1 is put into coating work platform, and alkaline-resisting emulsion layer 2 and alkali resistant liquid, reinforcing agent are coated thereon;Secondly, after alkaline-resisting emulsion layer 2 and alkali resistant liquid, reinforcing agent are totally immersed in glass fiber substrate 1, baking production line is put it into;Again, it is baked at a temperature of 190 °C ~ 210 °C, after cooking the phase, coats glue layer 3, then wait for natural cooling;Finally by monoblock self-adhesion grid cloth, excision forming and a roll is rolled on cutting machine.
The type of weave similar to lace stitch used due to glass fiber substrate 1, and it has double-decker, warp twisted together causes self-adhesion grid cloth to have higher intensity, and the presence in twisted gap make it that self-adhesion grid cloth quality is more soft, has and preferably pastes performance;Alkaline-resisting emulsion layer 2, glue layer 3, alkali resistant liquid, reinforcing agent are coated easily by the twisted gap of thin twisting warp 112, the twisted gap of thick twisting warp 113 is merged with whole glass fiber substrate 1, and is covered thereon so that the viscosity of self-adhesion grid cloth is more preferable.
The foregoing is merely illustrative of the preferred embodiments of the present invention, the protection domain being not intended to limit the invention, and within the spirit and principles of the invention, any modification for being made, equivalent substitution, is all contained within protection scope of the present invention.
Claims (7)
- A kind of 1. self-adhesion grid cloth, it is characterised in that:It includes glass fiber substrate(1), alkaline-resisting emulsion layer(2), glue layer(3);Its preparation method includes following a)、b)、c)Step:a)Compiled with glass fibre woven into glass fiber substrate on cloth machine(1);b)In glass fiber substrate(1)The upper alkaline-resisting emulsion layer of coating(2)And alkali resistant liquid, reinforcing agent;c)Glue layer is coated at a temperature of 190 °C ~ 210 °C(3).
- A kind of 2. self-adhesion grid cloth according to claim 1, it is characterised in that:The reinforcing agent is made after being mixed by the polymer builder that concentration is 55% ± 1% with the water that concentration is 45% ± 1%.
- A kind of 3. self-adhesion grid cloth according to claim 1, it is characterised in that:The glue layer(3)It is made up of esters of acrylic acid synthetic latex.
- A kind of 4. self-adhesion grid cloth according to claim 1, it is characterised in that:The glass fiber substrate(1)By double-decker identical fiber layer(11)And interlayer twisting fiber(12)It is made, fiber layer(11)Including parallel(111), thin twisting warp(112), thick twisting warp(113), straight warp(114);Fiber layer(111)Its microcosmic type of weave is:Parallel(111)Linearly horizontal direction arrangement, thin twisting warp(112), thick twisting warp(113), straight warp(114)Arrange, from left to right put in order as straight warp in vertical direction(114), thin twisting warp(112), straight warp(114), thin twisting warp(112), straight warp(114), thick twisting warp(113), straight warp(114), thick twisting warp(113), straight warp(114), thin twisting warp(112), straight warp(114), thin twisting warp(112), straight warp(114).
- A kind of 5. self-adhesion grid cloth according to claim 4, it is characterised in that:The thin twisting warp(112), thick twisting warp(113), straight warp(114)Alternating is interspersed in parallel(111)Between.
- A kind of 6. self-adhesion grid cloth according to claim 4, it is characterised in that:The interlayer twisting fiber(12)Alternating is interspersed in fiber layer(11)Between.
- A kind of 7. self-adhesion grid cloth according to claim 4, it is characterised in that:The thin twisting warp(112)Twisted gap between 0.1mm ~ 0.2mm, the thick twisting warp(113)Twisted gap between 0.4mm ~ 0.6mm.