CN107345007A - A kind of big bottom of high abrasion post-cure transparent rubber footwear and its formula - Google Patents
A kind of big bottom of high abrasion post-cure transparent rubber footwear and its formula Download PDFInfo
- Publication number
- CN107345007A CN107345007A CN201610288182.6A CN201610288182A CN107345007A CN 107345007 A CN107345007 A CN 107345007A CN 201610288182 A CN201610288182 A CN 201610288182A CN 107345007 A CN107345007 A CN 107345007A
- Authority
- CN
- China
- Prior art keywords
- big
- transparent rubber
- big bottom
- formula
- footwear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of big bottom of post-cure transparent rubber footwear and its formula, the formula is calculated in parts by weight, including:Cis-butadiene cement 80 90, isoprene rubber 10 20, stearic acid 13, white carbon 30 40, altax 1.4 1.5, accelerator TT 0.1 0.3, Urotropinum 79, zinc carbonate 24, sulphur 1.4 1.6, transformer oil 13 17, the resins 35 of RX 80, calcium carbonate 30.It is major ingredient through being kneaded that this big bottom, which uses mixed milling type cis-butadiene cement, is suppressed by mould, vulcanize transparent rubber is made, transparency is high, color inhibition 3~4, and arkron is wear-resisting typically below 0.15 under equal conditions, is amenable to wear away for a long time, anti-wear performance height;It is adapted for use as the big bottom of tennis shoes and other footwear big bottoms higher to anti-wear performance requirement, adaptive surface is wider.
Description
Technical field
The present invention relates to field of rubber technology, is related to transparent rubber formula, and particularly a kind of high abrasion post-cure is transparent
The big bottom of rubber boots and its formula.
Background technology
The existing big bottom of footwear transparent rubber, is typically made up with butadiene-styrene rubber of major ingredient, this big bottom poor transparency of footwear,
Transparency is less than 50%;Ultraviolet resistance xanthochromia poor-performing, its anti-wear performance are poor;Under general styrene-butadiene transparent rubber equal conditions
Arkron is wear-resisting can to accomplish less than 0.3, be only applicable to be used as basketball shoes and the big bottom of city shoe, be not particularly suited for the big bottom of tennis shoes
And other footwear big bottoms higher to anti-wear performance requirement, adaptive surface are narrower.
The content of the invention
The purpose of the present invention is that in view of the shortcomings of the prior art, and it is big to provide a kind of high abrasion post-cure transparent rubber footwear
Bottom and its formula, this big bottom transparency of transparent rubber footwear is high, ultraviolet resistance xanthochromia performance is good and anti-wear performance is good, suitable for use
Make the big bottom of tennis shoes and other footwear big bottoms higher to anti-wear performance requirement, adaptive surface are wider.
Realize that the technical scheme of above-mentioned purpose is as follows:
A kind of high abrasion post-cure transparent rubber footwear big-sole formula, is calculated in parts by weight, including:
Cis-butadiene cement 80-90, isoprene rubber 10-20, stearic acid 1-3, white carbon 30-40, altax 1.4-1.5, accelerator
TT 0.1-0.3, Urotropinum 7-9, zinc carbonate 2-4, sulphur 1.4-1.6, transformer oil 13-17, RX-80 resin 3-5, carbonic acid
Calcium 30.
A kind of big bottom of high abrasion post-cure transparent rubber footwear, is made of above-mentioned formula.
Beneficial effects of the present invention:
It is major ingredient through being kneaded to use mixed milling type cis-butadiene cement, is suppressed by mould, vulcanize transparent rubber is made, transparency height, resistance to Huang
Become 3~4, arkron is wear-resisting typically below 0.15 under equal conditions, is amenable to wear away for a long time, and anti-wear performance is high;It is applicable
In wider as the big bottom of tennis shoes and other footwear big bottoms higher to anti-wear performance requirement, adaptive surface.
Embodiment
Present invention is described further below by embodiment, but is not limitation of the invention.
Embodiment:
A kind of high abrasion post-cure transparent rubber footwear big-sole formula, is calculated in parts by weight, including:
Cis-butadiene cement 85, isoprene rubber 15, stearic acid 2, white carbon 35, altax 1.45, accelerator TT 0.2, Urotropinum
8th, zinc carbonate 3, sulphur 1.5, transformer oil 15, RX-80 resins 4, calcium carbonate 30.
It is put into after above raw material is kneaded by said ratio in big bed die tool, compacting, sulfidization molding in vulcanizer, vulcanization
145~155 DEG C of temperature, cure time 5~10 minutes.
Material property performance is as follows after tested:
Tension intensity(Mpa) 19.7;
Elongation(%) 500;
90 degree of tears(kg/cm)68.5N/mm;
Hardness(A types) 71;
Color inhibition 3-4;
Arkron(Akron)Abrasion(gr/cc) 0.14.
Claims (3)
- A kind of 1. high abrasion post-cure transparent rubber footwear big-sole formula, it is characterised in that calculate in parts by weight, including:Cis-butadiene cement 80-90, isoprene rubber 10-20, stearic acid 1-3, white carbon 30-40, altax 1.4-1.5, accelerator TT 0.1-0.3, Urotropinum 7-9, zinc carbonate 2-4, sulphur 1.4-1.6, transformer oil 13-17, RX-80 resin 3-5, carbonic acid Calcium 30.
- 2. high abrasion post-cure transparent rubber footwear big-sole formula according to claim 1, it is characterised in that according to weight Part calculates, including:Cis-butadiene cement 85, isoprene rubber 15, stearic acid 2, white carbon 35, altax 1.45, accelerator TT 0.2, Urotropinum 8th, zinc carbonate 3, sulphur 1.5, transformer oil 15, RX-80 resins 4, calcium carbonate 30.
- 3. a kind of big bottom of high abrasion post-cure transparent rubber footwear, it is characterised in that the big bottom will by claim 1 or right The high abrasion post-cure transparent rubber footwear big-sole formula described in 2 is asked to be made.