CN107344830A - 一种利用废弃泥浆配制盾构注浆的方法 - Google Patents

一种利用废弃泥浆配制盾构注浆的方法 Download PDF

Info

Publication number
CN107344830A
CN107344830A CN201710672989.4A CN201710672989A CN107344830A CN 107344830 A CN107344830 A CN 107344830A CN 201710672989 A CN201710672989 A CN 201710672989A CN 107344830 A CN107344830 A CN 107344830A
Authority
CN
China
Prior art keywords
kilograms
sand
bentonite
discarded slurry
shield
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710672989.4A
Other languages
English (en)
Inventor
许维青
翟志国
李英
邓亨义
杨振朋
崔信为
莫松
王百泉
杨志永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Railway Tunnel Group Erchu Co Ltd
Original Assignee
China Railway Tunnel Group Erchu Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Railway Tunnel Group Erchu Co Ltd filed Critical China Railway Tunnel Group Erchu Co Ltd
Priority to CN201710672989.4A priority Critical patent/CN107344830A/zh
Publication of CN107344830A publication Critical patent/CN107344830A/zh
Pending legal-status Critical Current

Abstract

一种利用废弃泥浆配制盾构注浆的方法，使用到废弃泥浆、水泥、粉煤灰、砂、水、膨润土，膨胀剂、絮凝剂，当废弃泥浆的比重在1.10～1.17g/cm3和粘度在20～24秒之时，每立方的盾构注浆中含有：水泥120～180千克、砂625～700千克、粉煤灰450～550千克、膨润土0～40千克、膨胀剂1.2～15千克、絮凝剂1～12千克、水575～850千克，根据上述配比即可配制出盾构注浆，本发明盾构注浆具有较好的流动性、稳定性、不易分层且泌水小等特点，为达到填充和控制管片上浮，需要有凝结时间的控制，并具有一定的早期强度，同时固结收缩率、浆液倾析率都小于5％，减少环境污染，节约施工成本。

Description

一种利用废弃泥浆配制盾构注浆的方法
技术领域
本发明属于盾构施工技术领域，尤其是一种利用废弃泥浆配制盾构注浆的方法。
背景技术
泥水盾构隧道在施工过程中不可避免产生大量的废弃泥浆，而废弃泥浆处理需要较高的费用，若直接排放会对环境造成严重污染。因此，研究废弃泥浆再利用具有很高的实用价值，但是截止目前并没有废弃泥浆再利用的相关报道。
发明内容
为解决废弃泥浆再利用问题，本发明提供一种利用废弃泥浆配制盾构注浆的方法，该方法废弃泥浆配制盾构注浆，从而达到经济环保、节省盾构施工成本之目的。
为实现上述发明目的，本发明采用如下技术方案：
一种利用废弃泥浆配制盾构注浆的方法，该方法使用到废弃泥浆、水泥、粉煤灰、砂、水、膨润土，膨胀剂、絮凝剂，废弃泥浆主要含有水、砂、膨润土、粘土颗粒和黏稠剂CMC、纯碱，其特征是：
要求水泥达到42.5级、粉煤灰达到二级、膨润土是钠基膨润土、砂子为细砂；
一、当废弃泥浆的比重在1.10～1.17g/cm3和粘度在20～24秒之时，每立方的盾构注浆中含有：水泥120～180千克、砂625～700千克、粉煤灰450～550千克、膨润土0～40千克、膨胀剂1.2～15千克、絮凝剂1～12千克、水575～850千克，根据上述配比即可配制出盾构注浆；
二、当废弃泥浆的比重在1.17-1.28g/cm3和粘度在24-28秒之时，每立方的盾构注浆中含有：水泥110～120千克、砂646～755千克、粉煤灰400～450千克、膨润土0～66千克、膨胀剂2～15千克、絮凝剂1～12千克、水620～1050千克，根据上述配比即可配制出盾构注浆；
按上述两种配方配制出的盾构注浆其性能要求均为：一天强度大于0.2兆帕、二十八天强度大于2.5兆帕、固结收缩率、浆液倾析率都要求小于5％。
由于采用如上所述技术方案，本发明产生如下积极效果：
1、采用废弃泥浆配制盾构注浆具有良好性能，完全满足泥水盾构的施工要求。
2、由于充分利用了废弃泥浆，节省了大量施工成本，环保经济效益非常明显。
3、盾构注浆具有较好的流动性和稠度，并且泌水率方面优于原注浆。
具体实施方式
本发明是一种利用废弃泥浆配制盾构注浆的方法，本发明充分利用了废弃泥浆，减少环境污染，节约施工成本。
本发明的方法使用到废弃泥浆、水泥、粉煤灰、砂、水、膨润土，膨胀剂、絮凝剂，废弃泥浆主要含有水、砂、膨润土、粘土颗粒和黏稠剂CMC、纯碱。
要求水泥达到42.5级、粉煤灰达到二级、膨润土是钠基膨润土、砂子为细砂；
一、当废弃泥浆的比重在1.10～1.17g/cm3和粘度在20～24秒之时，每立方的盾构注浆最佳配比是：
1、水泥120千克、砂700千克、粉煤灰550千克、膨润土36千克、膨胀剂8千克、絮凝剂5千克、水575千克。
2、水泥150千克、砂625千克、粉煤灰450千克、膨润土40千克、膨胀剂10千克、絮凝剂5千克、水700千克。
3、水泥180千克、砂625千克、粉煤灰450千克、膨胀剂15千克、絮凝剂12千克、水850千克。
二、当废弃泥浆的比重在1.17-1.28g/cm3和粘度在24-28秒之时，每立方的盾构注浆最佳配比是：
4、水泥110千克、砂650千克、粉煤灰450千克、膨润土66千克、膨胀剂15千克、絮凝剂10千克、水650千克。
5、水泥120千克、砂700千克、粉煤灰400千克、膨胀剂0～15千克、絮凝剂8千克、水820千克。
6、水泥120千克、砂755千克、粉煤灰400千克、膨润土40千克、膨胀剂15千克、絮凝剂12千克、水1000千克。
上述六种最佳配方配制出的盾构注浆其性能要求均达到：一天强度大于0.2兆帕、二十八天强度大于2.5兆帕、固结收缩率、浆液倾析率都要求小于5％。
本发明盾构注浆具有较好的流动性、稳定性、不易分层且泌水小等特点，为达到填充和控制管片上浮，需要有凝结时间的控制，并具有一定的早期强度，同时固结收缩率、浆液倾析率都小于5％。

Claims (1)

1.一种利用废弃泥浆配制盾构注浆的方法，该方法使用到废弃泥浆、水泥、粉煤灰、砂、水、膨润土，膨胀剂、絮凝剂，废弃泥浆主要含有水、砂、膨润土、粘土颗粒和黏稠剂CMC、纯碱，其特征是：
要求水泥达到42.5级、粉煤灰达到二级、膨润土是钠基膨润土、砂子为细砂；
(1)当废弃泥浆的比重在1.10～1.17g/cm3和粘度在20～24秒之时，每立方的盾构注浆中含有：水泥120～180千克、砂625～700千克、粉煤灰450～550千克、膨润土0～40千克、膨胀剂1.2～15千克、絮凝剂1～12千克、水575～850千克，根据上述配比即可配制出盾构注浆；
(2)当废弃泥浆的比重在1.17-1.28g/cm3和粘度在24-28秒之时，每立方的盾构注浆中含有：水泥110～120千克、砂646～755千克、粉煤灰400～450千克、膨润土0～66千克、膨胀剂2～15千克、絮凝剂1～12千克、水620～1050千克，根据上述配比即可配制出盾构注浆；
按上述两种配方配制出的盾构注浆其性能要求均为：一天强度大于0.2兆帕、二十八天强度大于2.5兆帕、固结收缩率、浆液倾析率都要求小于5％。
CN201710672989.4A 2017-08-09 2017-08-09 一种利用废弃泥浆配制盾构注浆的方法 Pending CN107344830A (zh)