CN107326675A - 一种纺织面料浆料配方 - Google Patents
一种纺织面料浆料配方 Download PDFInfo
- Publication number
- CN107326675A CN107326675A CN201710473368.3A CN201710473368A CN107326675A CN 107326675 A CN107326675 A CN 107326675A CN 201710473368 A CN201710473368 A CN 201710473368A CN 107326675 A CN107326675 A CN 107326675A
- Authority
- CN
- China
- Prior art keywords
- parts
- rate
- face fabric
- weaving face
- pur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纺织面料浆料配方，包括如下质量份数的组分：PVA28‑32份、接枝淀粉39‑41份、酰胺18‑22份、抗静电剂2.8‑3.2份、甘油2.9‑3.1份、乳化油2.9‑3.2份、2‑奈酚0.25份、蜡片3份，维卡亚麻15‑23份、耐久排水聚合物10‑12份、长绒棉11‑18份、热熔胶4‑8份、涤纶纤维5‑10份、纳米二氧化钛粉末2‑6份、防水性树脂浆料3‑8份、松香3‑8份。通过本发明的配方对纺织面料进行浆纱，可以改善其增强率、减伸率、毛羽降低率和增磨率，提高其可织性，使经纱的断头率达到顺利织造的要求，制成的衣料舒适荣软，保暖防水，制作简便，成本低廉，具有一定的市场价值。
Description
技术领域
本发明属于纺织面料技术领域，具体涉及一种纺织面料浆料配方。
背景技术
随着科学技术的不断发展，面料技术也在不断改进，各种各样的新型功能性面料正在步入人们的日常生活。功能性面料是指具有某种特殊性能和用途的面料，比如防水、防风、透气、透湿、保暖、防油、易去污、防菌除臭、防紫外线、防静电、防辐射、防阻燃、耐高温、耐酸碱等功能。
目前的功能性纺织面料大量应用到服装的制作，用于满足人们日常生活不同时候的各种需求，江南地区的梅雨季节天气经常潮湿或者有雨，导致人们对防水的服装需求很大，但是很多防水面料都不具备保暖的功能，这就限制了人们都防水衣物的使用。
发明内容
发明目的：本发明针对不足，提出一种可以改善其增强率、减伸率、毛羽降低率和增磨率，提高其可织性，使经纱的断头率达到顺利织造的要求的纺织面料浆料配方。
技术方案：本发明所述的一种纺织面料浆料配方，包括如下质量份数的组分：PVA28-32份、接枝淀粉39-41份、 酰胺18-22份、抗静电剂 2.8-3.2 份、甘油 2.9-3.1份、乳化油2.9-3.2 份、2-奈酚 0.25份、蜡片3份，维卡亚麻15-23份、耐久排水聚合物10-12 份、长绒棉11-18 份、热熔胶4-8 份、涤纶纤维5-10 份、纳米二氧化钛粉末2-6 份、防水性树脂浆料 3-8 份、松香3-8份。
进一步的，包括如下质量份数的组分：PVA30-32份、接枝淀粉40-41份、 酰胺20-22份、抗静电剂3-3.2 份、甘油 3-3.1份、乳化油3-3.2 份、2-奈酚 0.25份、蜡片3份，维卡亚麻16-23份、耐久排水聚合物11-12 份、长绒棉12-18 份、热熔胶6-8 份、涤纶纤维7-10 份、纳米二氧化钛粉末4-6 份、防水性树脂浆料4-8 份、松香4-8份。
进一步的，包括如下质量份数的组分：PVA31份、接枝淀粉40.5份、 酰胺21份、抗静电剂3.1份、甘油 3.15份、乳化油3.1 份、2-奈酚 0.25份、蜡片3份，维卡亚麻20份、耐久排水聚合物11.5 份、长绒棉16 份、热熔胶7份、涤纶纤维8份、纳米二氧化钛粉末5份、防水性树脂浆料6份、松香6份。
有益效果：通过本发明的配方对纺织面料进行浆纱，可以改善其增强率、减伸率、毛羽降低率和增磨率，提高其可织性，使经纱的断头率达到顺利织造的要求，制成的衣料舒适荣软，保暖防水，制作简便，成本低廉，具有一定的市场价值。
具体实施方式
下面结合具体实施例对本发明作进一步说明：
实施例1
一种纺织面料浆料配方，包括如下质量份数的组分：PVA28份、接枝淀粉39份、 酰胺18份、抗静电剂 2.8份、甘油 2.9份、乳化油2.9份、2-奈酚 0.25份、蜡片3份，维卡亚麻15份、耐久排水聚合物10份、长绒棉11份、热熔胶4份、涤纶纤维5份、纳米二氧化钛粉末2份、防水性树脂浆料 3份、松香3份。
实施例2
一种纺织面料浆料配方，包括如下质量份数的组分：PVA 32份、接枝淀粉41份、 酰胺22份、抗静电剂 3.2 份、甘油3.1份、乳化油3.2 份、2-奈酚 0.25份、蜡片3份，维卡亚麻23份、耐久排水聚合物12 份、长绒棉18 份、热熔胶8 份、涤纶纤维10 份、纳米二氧化钛粉末6份、防水性树脂浆料8 份、松香8份。
实施例3
一种纺织面料浆料配方，包括如下质量份数的组分：PVA31份、接枝淀粉40.5份、 酰胺21份、抗静电剂3.1份、甘油 3.15份、乳化油3.1 份、2-奈酚 0.25份、蜡片3份，维卡亚麻20份、耐久排水聚合物11.5 份、长绒棉16 份、热熔胶7份、涤纶纤维8份、纳米二氧化钛粉末5份、防水性树脂浆料6份、松香6份。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (3)
1.一种纺织面料浆料配方，其特征在于：包括如下质量份数的组分：PVA28-32份、接枝淀粉39-41份、 酰胺18-22份、抗静电剂 2.8-3.2 份、甘油 2.9-3.1份、乳化油2.9-3.2 份、2-奈酚 0.25份、蜡片3份，维卡亚麻15-23份、耐久排水聚合物10-12 份、长绒棉11-18 份、热熔胶4-8 份、涤纶纤维5-10 份、纳米二氧化钛粉末2-6 份、防水性树脂浆料 3-8 份、松香3-8份。
2.根据权利要求1所述的一种纺织面料浆料配方，其特征在于：包括如下质量份数的组分：PVA30-32份、接枝淀粉40-41份、 酰胺20-22份、抗静电剂3-3.2 份、甘油 3-3.1份、乳化油3-3.2 份、2-奈酚 0.25份、蜡片3份，维卡亚麻16-23份、耐久排水聚合物11-12 份、长绒棉12-18 份、热熔胶6-8 份、涤纶纤维7-10 份、纳米二氧化钛粉末4-6 份、防水性树脂浆料4-8 份、松香4-8份。
3.根据权利要求1所述的一种纺织面料浆料配方，其特征在于：包括如下质量份数的组分：PVA31份、接枝淀粉40.5份、 酰胺21份、抗静电剂3.1份、甘油 3.15份、乳化油3.1 份、2-奈酚 0.25份、蜡片3份，维卡亚麻20份、耐久排水聚合物11.5 份、长绒棉16 份、热熔胶7份、涤纶纤维8份、纳米二氧化钛粉末5份、防水性树脂浆料6份、松香6份。