CN107323032A - A kind of environmental-protection decorative warming plate and preparation method thereof - Google Patents

A kind of environmental-protection decorative warming plate and preparation method thereof Download PDF

Info

Publication number
CN107323032A
CN107323032A CN201710566174.8A CN201710566174A CN107323032A CN 107323032 A CN107323032 A CN 107323032A CN 201710566174 A CN201710566174 A CN 201710566174A CN 107323032 A CN107323032 A CN 107323032A
Authority
CN
China
Prior art keywords
parts
environmental
warming plate
protection decorative
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710566174.8A
Other languages
Chinese (zh)
Inventor
张玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Xinyada Intelligent Technology Co Ltd
Original Assignee
Hefei Xinyada Intelligent Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Xinyada Intelligent Technology Co Ltd filed Critical Hefei Xinyada Intelligent Technology Co Ltd
Priority to CN201710566174.8A priority Critical patent/CN107323032A/en
Publication of CN107323032A publication Critical patent/CN107323032A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of environmental-protection decorative warming plate, include following raw material according to parts by weight：20 ~ 55 parts of polyester staple fiber, 20 ~ 45 parts of Fypro, 3 ~ 15 parts of aramid fiber, 10 ~ 15 parts of ore, 2 ~ 7 parts of flyash, 5 ~ 15 parts of coating perlite, 3 ~ 9 parts of calcium carbonate part, 5 ~ 10 parts of aluminum oxide, 3 ~ 7 parts of oxidized paraffin wax, 2 ~ 9 parts of polyacrylamide, 5 ~ 10 parts of terephthalic acid (TPA), 5 ~ 10 parts of mine tailing, 5 ~ 7 parts of polymer dispersion powder, 1.5 ~ 3.5 parts of waterproofing agent.The present invention provides a kind of environmental-protection decorative warming plate and preparation method thereof, polyester staple fiber is employed as insulation material, it can be by together with itself bond vitrified with other raw material, adhesive is not needed fiber can just to be adhered to each other, and without harmful substance, formaldehydeless, free from extraneous odour, environmental protection, will not produce condensed water.

Description

A kind of environmental-protection decorative warming plate and preparation method thereof
Technical field
The invention belongs to decoration material field, and in particular to a kind of environmental-protection decorative warming plate and preparation method thereof.
Background technology
Decorative panel is a kind of artificial board, and plate body is mainly made up of lime, gypsum, cement and perlite, and plate body two sides has Fibrous mesh cloth or non-woven fabrics.Crushed crude pearlite therein can also be substituted with wood saw end.Above-mentioned raw materials grind through batch mixing, stirring cream processed Molded and drying process is made.
Existing indoor heat insulating material uses benzene plate, but it has the disadvantage that pernicious gas, not ageing-resistant, deformation coefficient can be discharged Greatly, stability is poor, security is poor, easy firing, eco-environmental prote is poor, difficulty of construction is big, engineering cost is higher, its resource-constrained and It is difficult to recycle.For the angle of environmental protection, cork high insulating effect, but cost is too high.
In addition, heat insulating inner wall material is in use, condensed water is easily produced, the generation of condensed water will great shadow Ring the heat insulation effect of material.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of environmental-protection decorative warming plate and its preparation side Method.
To achieve the above object, the technical scheme is that：A kind of environmental-protection decorative warming plate, according to parts by weight include with Lower raw material：20 ~ 55 parts of polyester staple fiber, 20 ~ 45 parts of Fypro, 3 ~ 15 parts of aramid fiber, 10 ~ 15 parts of ore, flyash 2 ~ 7 parts, 5 ~ 15 parts of coating perlite, calcium carbonate parts 3 ~ 9 parts, 5 ~ 10 parts of aluminum oxide, 3 ~ 7 parts of oxidized paraffin wax, polyacrylamide 2 ~ 9 Part, 5 ~ 10 parts of terephthalic acid (TPA), 5 ~ 10 parts of mine tailing, 5 ~ 7 parts of polymer dispersion powder, 1.5 ~ 3.5 parts of waterproofing agent.
Further, 20 parts of polyester staple fiber, 20 parts of Fypro, 3 parts of aramid fiber, 10 parts of ore, flyash 2 Part, 3 parts of 5 parts of coating perlite, calcium carbonate part, 5 parts of aluminum oxide, 3 parts of oxidized paraffin wax, 2 parts of polyacrylamide, terephthalic acid (TPA) 5 Part, 5 parts of mine tailing, 5 parts of polymer dispersion powder, 1.5 parts of waterproofing agent.
Further, the mine tailing be molybdic tailing, phosphorus mine tailing, iron tailings, copper tailing, the one or more of manganese mine tailing, The ore is galena, and pyrite is quartzy, sericite, the one or more in chlorite.
Further, the dispersible rubber powder is polyacrylate rubber powder, ethylene-vinyl acetate copolymer rubber powder and gathered One or more in sbr powder.
Further, the coating expanded perlite is made in the following manner：The expanded perlite of 100 mesh is taken, is added 200 ~ 250 DEG C are heated into seed-coating machine, and adds calcium carbonate powder, is stirred, wherein expanded perlite and Paris white The mass ratio at end is 20：1；Then one end sprinkling distilled water of seed-coating machine soaks expanded perlite, one end sprinkling epoxy resin Powder, and 20 ~ 40min is stirred continuously, produce coating expanded perlite.
A kind of preparation method of environmental-protection decorative warming plate, is mainly included the following steps that：
Step 1：Ester chopped fiber, Fypro, aramid fiber, ore are well mixed, water is then added, and be put into mixer In 10 ~ 50min is stirred with 200 ~ 300r/min rotating speed, obtain slurry；
Step 2：The slurry that step 1 is obtained carries out shredding, combed, and forms web；
Step 3：By remaining raw material add water uniform stirring mix, obtained mixed material, then by mixed material using sealing spray The web surface that rifle even application is obtained in step 2, do not got wet natural curing 1 ~ 2 day；
Step 4：Web of the step 3 after treated is obtained being incubated plate body, the pin of the acupuncture by acupuncture, first time roll-in Thorn density is 1.0~1.5 pins/cm2；
Step 5：The upper and lower surface for the warming plate body that step 4 is obtained sticks aluminium-foil paper or aluminium foil cloth, through second of roll-in After obtain environmental-protection decorative warming plate.
Further, the rolling pressure during first time roll-in is 2.5 ~ 3.5Mpa, roll-in pressure during second of roll-in Power is 3.5 ~ 4.5Mpa.
Further, uniformly punched on the aluminium-foil paper or aluminium foil cloth, aperture is 2 ~ 3mm.
The beneficial effects of the present invention are：The present invention provides a kind of environmental-protection decorative warming plate and preparation method thereof, employs Polyester staple fiber is as insulation material, and it can be by together with itself bond vitrified with other raw material, it is not necessary to adhesive Fiber can just be adhered to each other, and without harmful substance, formaldehydeless, free from extraneous odour, environmental protection will not produce condensed water.This hair It is bright that aluminium-foil paper or aluminium foil cloth fit together with warming plate body, preferably serve insulation, protection against the tide and do not absorb water Effect.
By being punched on aluminium-foil paper or aluminium foil cloth, it is also possible that warming plate plays a part of sqouynd absorption lowering noise.This hair The bright polyester staple fiber used is all the fiber of the polyester material spinning reclaimed, and the material can recycle, and price is low It is honest and clean, can also recycle again.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention It is described in further detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, do not limit The fixed present invention.
Embodiment 1
A kind of environmental-protection decorative warming plate, includes following raw material according to parts by weight：20 parts of polyester staple fiber, 20 parts of Fypro, 3 parts of aramid fiber, 10 parts of ore, 2 parts of flyash, 5 parts of coating perlite, 3 parts of calcium carbonate part, 5 parts of aluminum oxide, oxidized paraffin wax 3 Part, 2 parts of polyacrylamide, 5 parts of terephthalic acid (TPA), 5 parts of mine tailing, 5 parts of polymer dispersion powder, 1.5 parts of waterproofing agent.
The mine tailing is molybdic tailing, phosphorus mine tailing, iron tailings, copper tailing, the one or more of manganese mine tailing, and the ore is One or more in galena, pyrite, quartz, sericite, chlorite.
The dispersible rubber powder is polyacrylate rubber powder, ethylene-vinyl acetate copolymer rubber powder and poly- sbr powder In one or more.
The coating expanded perlite is made in the following manner：The expanded perlite of 100 mesh is taken, is added in seed-coating machine 200 DEG C are heated to, and adds calcium carbonate powder, is stirred, wherein the mass ratio of expanded perlite and calcium carbonate powder is 20： 1；Then one end sprinkling distilled water of seed-coating machine soaks expanded perlite, one end sprinkling epoxy resin powder, and is stirred continuously 20min, produces coating expanded perlite.
A kind of preparation method of environmental-protection decorative warming plate, is mainly included the following steps that：
Step 1：Ester chopped fiber, Fypro, aramid fiber, ore are well mixed, water is then added, and be put into mixer In 10min is stirred with 200r/min rotating speed, obtain slurry；
Step 2：The slurry that step 1 is obtained carries out shredding, combed, and forms web；
Step 3：By remaining raw material add water uniform stirring mix, obtained mixed material, then by mixed material using sealing spray The web surface that rifle even application is obtained in step 2, do not got wet natural curing 1 day；
Step 4：Web of the step 3 after treated is obtained being incubated plate body, the pin of the acupuncture by acupuncture, first time roll-in Thorn density is 1.0 pins/cm2。
Step 5：The upper and lower surface for the warming plate body that step 4 is obtained sticks aluminium-foil paper or aluminium foil cloth, through second Environmental-protection decorative warming plate is obtained after roll-in.
Rolling pressure during the first time roll-in is 2.5Mpa, and rolling pressure during second of roll-in is 3.5Mpa.
Uniformly punched on the aluminium-foil paper or aluminium foil cloth, aperture is 2mm.
Embodiment 2
A kind of environmental-protection decorative warming plate, includes following raw material according to parts by weight：40 parts of polyester staple fiber, 35 parts of Fypro, 10 parts of aramid fiber, 12 parts of ore, 4 parts of flyash, 10 parts of coating perlite, 6 parts of calcium carbonate part, 8 parts of aluminum oxide, oxidized paraffin wax 5 parts, 6 parts of polyacrylamide, 7 parts of terephthalic acid (TPA), 7 parts of mine tailing, 6 parts of polymer dispersion powder, 2.5 parts of waterproofing agent.
The mine tailing is molybdic tailing, phosphorus mine tailing, iron tailings, copper tailing, the one or more of manganese mine tailing, and the ore is One or more in galena, pyrite, quartz, sericite, chlorite.
The dispersible rubber powder is polyacrylate rubber powder, ethylene-vinyl acetate copolymer rubber powder and poly- sbr powder In one or more.
The coating expanded perlite is made in the following manner：The expanded perlite of 100 mesh is taken, is added in seed-coating machine 230 DEG C are heated to, and adds calcium carbonate powder, is stirred, wherein the mass ratio of expanded perlite and calcium carbonate powder is 20： 1；Then one end sprinkling distilled water of seed-coating machine soaks expanded perlite, one end sprinkling epoxy resin powder, and is stirred continuously 30min, produces coating expanded perlite.
A kind of preparation method of environmental-protection decorative warming plate, is mainly included the following steps that：
Step 1：Ester chopped fiber, Fypro, aramid fiber, ore are well mixed, water is then added, and be put into mixer In 40min is stirred with 250r/min rotating speed, obtain slurry；
Step 2：The slurry that step 1 is obtained carries out shredding, combed, and forms web；
Step 3：By remaining raw material add water uniform stirring mix, obtained mixed material, then by mixed material using sealing spray The web surface that rifle even application is obtained in step 2, do not got wet natural curing 1 day；
Step 4：Web of the step 3 after treated is obtained being incubated plate body, the pin of the acupuncture by acupuncture, first time roll-in Thorn density is 1.2 pins/cm2。
Step 5：The upper and lower surface for the warming plate body that step 4 is obtained sticks aluminium-foil paper or aluminium foil cloth, through second Environmental-protection decorative warming plate is obtained after roll-in.
Rolling pressure during the first time roll-in is 3.5Mpa, and rolling pressure during second of roll-in is 4.0Mpa.
Uniformly punched on the aluminium-foil paper or aluminium foil cloth, aperture is 2.5mm.
Embodiment 3
A kind of environmental-protection decorative warming plate, includes following raw material according to parts by weight：55 parts of polyester staple fiber, 45 parts of Fypro, 15 parts of aramid fiber, 15 parts of ore, 7 parts of flyash, 15 parts of coating perlite, 9 parts of calcium carbonate part, 10 parts of aluminum oxide, oxidation stone 7 parts of wax, 9 parts of polyacrylamide, 10 parts of terephthalic acid (TPA), 10 parts of mine tailing, 7 parts of polymer dispersion powder, 3.5 parts of waterproofing agent.
The mine tailing is molybdic tailing, phosphorus mine tailing, iron tailings, copper tailing, the one or more of manganese mine tailing, and the ore is One or more in galena, pyrite, quartz, sericite, chlorite.
The dispersible rubber powder is polyacrylate rubber powder, ethylene-vinyl acetate copolymer rubber powder and poly- sbr powder In one or more.
The coating expanded perlite is made in the following manner：The expanded perlite of 100 mesh is taken, is added in seed-coating machine 250 DEG C are heated to, and adds calcium carbonate powder, is stirred, wherein the mass ratio of expanded perlite and calcium carbonate powder is 20： 1；Then one end sprinkling distilled water of seed-coating machine soaks expanded perlite, one end sprinkling epoxy resin powder, and is stirred continuously 40min, produces coating expanded perlite.
A kind of preparation method of environmental-protection decorative warming plate, is mainly included the following steps that：
Step 1：Ester chopped fiber, Fypro, aramid fiber, ore are well mixed, water is then added, and be put into mixer In 50min is stirred with 300r/min rotating speed, obtain slurry；
Step 2：The slurry that step 1 is obtained carries out shredding, combed, and forms web；
Step 3：By remaining raw material add water uniform stirring mix, obtained mixed material, then by mixed material using sealing spray The web surface that rifle even application is obtained in step 2, do not got wet natural curing 2 days；
Step 4：Web of the step 3 after treated is obtained being incubated plate body, the pin of the acupuncture by acupuncture, first time roll-in Thorn density is 1.5 pins/cm2；
Step 5：The upper and lower surface for the warming plate body that step 4 is obtained sticks aluminium-foil paper or aluminium foil cloth, through second of roll-in After obtain environmental-protection decorative warming plate.
Rolling pressure during the first time roll-in is 3.5Mpa, and rolling pressure during second of roll-in is 4.5Mpa.
Uniformly punched on the aluminium-foil paper or aluminium foil cloth, aperture is 3mm.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.

Claims (8)

1. a kind of environmental-protection decorative warming plate, it is characterised in that include following raw material according to parts by weight：20 ~ 55 parts of polyester staple fiber, 20 ~ 45 parts of Fypro, 3 ~ 15 parts of aramid fiber, 10 ~ 15 parts of ore, 2 ~ 7 parts of flyash, 5 ~ 15 parts of coating perlite, carbon Sour 3 ~ 9 parts of calcium part, 5 ~ 10 parts of aluminum oxide, 3 ~ 7 parts of oxidized paraffin wax, 2 ~ 9 parts of polyacrylamide, 5 ~ 10 parts of terephthalic acid (TPA), mine tailing 5 ~ 10 parts, 5 ~ 7 parts of polymer dispersion powder, 1.5 ~ 3.5 parts of waterproofing agent.
2. a kind of environmental-protection decorative warming plate according to claim 1, it is characterised in that 20 parts of polyester staple fiber, polyamide 20 parts of fiber, 3 parts of aramid fiber, 10 parts of ore, 2 parts of flyash, 5 parts of coating perlite, calcium carbonate parts 3 parts, 5 parts of aluminum oxide, 3 parts of oxidized paraffin wax, 2 parts of polyacrylamide, 5 parts of terephthalic acid (TPA), 5 parts of mine tailing, 5 parts of polymer dispersion powder, 1.5 parts of waterproofing agent.
3. a kind of environmental-protection decorative warming plate according to claim 1, it is characterised in that the mine tailing is molybdic tailing, phosphorus tail Ore deposit, iron tailings, copper tailing, the one or more of manganese mine tailing, the ore are galena, and pyrite, quartz, sericite is green One or more in mudstone.
4. a kind of environmental-protection decorative warming plate according to claim 1, it is characterised in that the dispersible rubber powder is polypropylene One or more in acid esters rubber powder, ethylene-vinyl acetate copolymer rubber powder and poly- sbr powder.
5. a kind of environmental-protection decorative warming plate according to claim 1, it is characterised in that the coating expanded perlite passes through In the following manner is made：The expanded perlite of 100 mesh is taken, is added in seed-coating machine and is heated to 200 ~ 250 DEG C, and add Paris white End, stirs, and wherein the mass ratio of expanded perlite and calcium carbonate powder is 20：1；Then one end sprinkling distillation of seed-coating machine Water soaks expanded perlite, one end sprinkling epoxy resin powder, and is stirred continuously 20 ~ 40min, produces coating expanded pearlite Rock.
6. a kind of preparation method of environmental-protection decorative warming plate, it is characterised in that mainly include the following steps that：
Step 1：Ester chopped fiber, Fypro, aramid fiber, ore are well mixed, water is then added, and be put into mixer In 10 ~ 50min is stirred with 200 ~ 300r/min rotating speed, obtain slurry；
Step 2：The slurry that step 1 is obtained carries out shredding, combed, and forms web；
Step 3：By remaining raw material add water uniform stirring mix, obtained mixed material, then by mixed material using sealing spray The web surface that rifle even application is obtained in step 2, do not got wet natural curing 1 ~ 2 day；
Step 4：Web of the step 3 after treated is obtained being incubated plate body, the pin of the acupuncture by acupuncture, first time roll-in Thorn density is 1.0~1.5 pins/cm2；
Step 5：The upper and lower surface for the warming plate body that step 4 is obtained sticks aluminium-foil paper or aluminium foil cloth, through second of roll-in After obtain environmental-protection decorative warming plate.
7. a kind of preparation method of environmental-protection decorative warming plate according to claim 6, it is characterised in that the first time roller Rolling pressure during pressure is 2.5 ~ 3.5Mpa, and rolling pressure during second of roll-in is 3.5 ~ 4.5Mpa.
8. a kind of preparation method of environmental-protection decorative warming plate according to claim 6, it is characterised in that the aluminium-foil paper or Uniformly punched on person's aluminium foil cloth, aperture is 2 ~ 3mm.
CN201710566174.8A 2017-07-12 2017-07-12 A kind of environmental-protection decorative warming plate and preparation method thereof Withdrawn CN107323032A (en)