CN107311602A - A kind of formaldehydeless ecological ornamental plate - Google Patents
A kind of formaldehydeless ecological ornamental plate Download PDFInfo
- Publication number
- CN107311602A CN107311602A CN201710461728.8A CN201710461728A CN107311602A CN 107311602 A CN107311602 A CN 107311602A CN 201710461728 A CN201710461728 A CN 201710461728A CN 107311602 A CN107311602 A CN 107311602A
- Authority
- CN
- China
- Prior art keywords
- parts
- formaldehydeless
- ornamental plate
- ecological ornamental
- wood powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of formaldehydeless ecological ornamental plate, its raw material is according to mass ratio, wood powder is the 50 96% of gross mass, remaining is 50 parts of the epsom salt solution that Baume degrees is 24 30 °, 35 45 parts and 0.05 0.15 parts additive normal temperature of light-magnesite powder are well mixed, and are molded with by steam pressure.A kind of formaldehydeless ecological ornamental plate of the present invention, with formaldehydeless, halogenation, do not get damp, intensity height, long lifespan, A grades prevent fires the features such as, be with a wide range of applications as the construction material of safety and environmental protection.
Description
Technical field
The invention belongs to the technical field of building material field, specifically a kind of formaldehydeless ecological ornamental plate.
Background technology
House is used as an important indicator for weighing a national economy and living standards of the people, the safety of its construction material
Property, durability, heat insulating ability, easy act etc. is to improve housing quality, improve the important means of living environment.It is lightweight, high-strength
Magnesian is increasingly widely applied in the building in the present age.
Though current magnesian is commercially widely used, exist and get damp, return halogen phenomenon, metal is corrosive；
After the moisture absorption, mechanical strength is decreased obviously, the problems such as influenceing service life, urgent raising performance to be solved, not so will face influence
Development is used, or even has the crisis being eliminated.
The content of the invention
The invention provides following technical scheme:
A kind of formaldehydeless ecological ornamental plate, it is characterized in that, its raw material is that wood powder is the 50-96% of gross mass according to mass ratio,
Remaining is 50 parts of the epsom salt solution that Baume degrees is 24-30 °, and 35-45 parts and 0.05-0.15 parts of light-magnesite powder adds
Plus agent normal temperature is well mixed, is molded with by steam pressure.
Preferably, the additive according to quality proportioning be 3-5 parts of sodium lignin sulfonate, seven 40-60 parts of water alums,
2000-2500 parts of compositions of 100-120 parts of sodium dihydrogen phosphate and water.
Preferably, the wood powder moisture control is in 15-17%.
Preferably, the granular size of the wood powder is 0.1-3mm.
The advantage of the invention is that replace magnesium chloride using magnesium sulfate, from source prevented sheet material in chlorion intake,
It is that original sheet material moisture absorption, cracking, deformation, the phenomenon of corroding screw are improved, makes that magnesia board performance is more stable, product is used
Life-span is longer；Other inorganic adding materials are replaced using wood powder, renewable resource is rationally utilized, turned waste into wealth, energy-conservation and ring
Protect, while improving the heat-insulating property of sheet material.
Embodiment
The technical scheme provided below with reference to specific embodiment the present invention is described in detail, subordinate's specific embodiment party
Formula is only illustrative of the invention and is not intended to limit the scope of the invention.
Embodiment 1
A kind of formaldehydeless ecological ornamental plate, its raw material is that wood powder is the 50% of gross mass, and remaining is Baume degrees according to mass ratio
For 28 ° of 50 parts of epsom salt solution, 43 parts and 0.15 part additive normal temperature of light-magnesite powder is well mixed, by steaming
It is molded to form.The additive is 5 parts of sodium lignin sulfonate, seven 60 parts of water alums, biphosphate according to quality proportioning
2000 parts of compositions of 120 parts of sodium and water.
The wood powder moisture control is 17%.
The granular size of the wood powder is 3mm.
The formaldehydeless ecological ornamental plate dynamics of this example is strong, use JC688-2006 technical requirements standard detection dynamics for
10.5MPa, not oxidizable, dynamics is long lasting, and burst size of methanal is not detected, is examined using GB8624-2012 technical requirements
Drafting board material has reached A2 grades of standards.
Embodiment 2
A kind of formaldehydeless ecological ornamental plate, its raw material is that wood powder is the 73% of gross mass, and remaining is Baume degrees according to mass ratio
For 26 ° of 50 parts of epsom salt solution, 40 parts and 0.1 part additive normal temperature of light-magnesite powder is well mixed, by steaming
It is molded to form.The additive is 4 parts of sodium lignin sulfonate, seven 50 parts of water alums, biphosphate according to quality proportioning
2200 parts of compositions of 110 parts of sodium and water.
The wood powder moisture control is 16%.
The granular size of the wood powder is 1mm.
The formaldehydeless ecological ornamental plate dynamics of this example is strong, use JC688-2006 technical requirements standard detection dynamics for
10.5MPa, not oxidizable, dynamics is long lasting, and burst size of methanal is not detected, is examined using GB8624-2012 technical requirements
Drafting board material has reached A2 grades of standards.
Embodiment 3
A kind of formaldehydeless ecological ornamental plate, its raw material is that wood powder is the 96% of gross mass, and remaining is Baume degrees according to mass ratio
For 24 ° of 50 parts of epsom salt solution, 35 parts and 0.05 part additive normal temperature of light-magnesite powder is well mixed, by steaming
It is molded to form.The additive is 3 parts of sodium lignin sulfonate, seven 40 parts of water alums, biphosphate according to quality proportioning
2500 parts of compositions of 100 parts of sodium and water.
The wood powder moisture control is 15%.
The granular size of the wood powder is 0.2mm.
The formaldehydeless ecological ornamental plate dynamics of this example is strong, use JC688-2006 technical requirements standard detection dynamics for
10.5MPa, not oxidizable, dynamics is long lasting, and burst size of methanal is not detected, is examined using GB8624-2012 technical requirements
Drafting board material has reached A2 grades of standards.
Claims (4)
1. a kind of formaldehydeless ecological ornamental plate, it is characterized in that, its raw material is that wood powder is the 50- of gross mass according to mass ratio
96%, remaining is 50 parts of the epsom salt solution that Baume degrees is 24-30 °, 35-45 parts of light-magnesite powder and 0.05-0.15
Part additive normal temperature is well mixed, and is molded with by steam pressure.
2. additive according to claim 1, it is characterised in that：The additive is lignin sulfonic acid according to quality proportioning
3-5 parts of sodium, seven 40-60 parts of water alums, 2000-2500 parts of compositions of 100-120 parts of sodium dihydrogen phosphate and water.
3. a kind of formaldehydeless ecological ornamental plate according to claim 1, it is characterised in that：The wood powder moisture control exists
15-17%。
4. a kind of formaldehydeless ecological ornamental plate according to claim 1, it is characterised in that：The granular size of the wood powder
For 0.1-3mm.