CN107311515A - 一种朱砂工艺品及其制备方法 - Google Patents

一种朱砂工艺品及其制备方法 Download PDF

Info

Publication number
CN107311515A
CN107311515A CN201710591525.0A CN201710591525A CN107311515A CN 107311515 A CN107311515 A CN 107311515A CN 201710591525 A CN201710591525 A CN 201710591525A CN 107311515 A CN107311515 A CN 107311515A
Authority
CN
China
Prior art keywords
cinnabar
parts
weight
resin
handicraft
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710591525.0A
Other languages
English (en)
Inventor
柴亚琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongren Testing Center City Wanshanqu Danfeng Vermilion Crafts Development Co Ltd
Original Assignee
Tongren Testing Center City Wanshanqu Danfeng Vermilion Crafts Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongren Testing Center City Wanshanqu Danfeng Vermilion Crafts Development Co Ltd filed Critical Tongren Testing Center City Wanshanqu Danfeng Vermilion Crafts Development Co Ltd
Priority to CN201710591525.0A priority Critical patent/CN107311515A/zh
Publication of CN107311515A publication Critical patent/CN107311515A/zh
Pending legal-status Critical Current

Abstract

本发明属于工艺品制备技术领域，尤其是一种朱砂工艺品及其制备方法，通过采用朱砂、树脂和香料为原料，通过合理的搭配，在结合工艺参数的调控制备成工艺品，使得产品的色泽亮丽，表面光滑；同时也保留朱砂原有的颜色，并且通过香料的加入，使得产品具有淡淡的香味，提升产品的品质。

Description

一种朱砂工艺品及其制备方法
技术领域
本发明属于工艺品制备技术领域，尤其是一种朱砂工艺品及其制备方法。
背景技术
朱砂、原名“辰砂”，是炼汞的主要原料，亦称“汞砂”；又因呈红色，俗称“丹砂”、“丹栗”、“赤丹”、“朱砂石”；它的化学成分为硫化汞，为三方晶系，晶体呈板块状或土状，晶簇常呈菱形双晶、大颗粒单晶体，半透明或不透明，鲜红、朱红、浅红、暗红色或红色，性脆，对光敏感，有很高的折射率，硬度2～2.5，比重8.09～8.2，体重，质脆，片状者易破碎，粉末状者有闪烁的光泽，无味。朱砂有“软红宝石”之美名；目前，朱砂用于工艺品的制作屡见不鲜，大部分朱砂工艺品表面较为粗糙，并且还有微小的气泡，严重影响到产品的触感和美观。
发明内容
为解决上述技术问题，本发明提供一种朱砂工艺品及其制备方法。
具体是通过以下技术方案得以实现的：
一种朱砂工艺品，原料以重量份计为朱砂60～80份、树脂20～30份、香料1～5份。
进一步优选原料以重量份计为朱砂74份、树脂28份、香料3份。
所述树脂为环氧树脂、聚氯乙烯树脂、聚苯乙烯树脂、聚丙烯树脂、松香树脂中任一种，两种及以上重量配比相等。
所述香料是将植物香料5～10重量份、薄荷脑4～9重量份和无水乙醇15～20重量份混合均匀即可。
所述植物香料为玫瑰、薰衣草、百合、沉香、檀香中至少一种，两种及以上重量配比相等。
本发明的另一个目的是提供该工艺品的制备方法，包括以下步骤：
(1)按照配方量取朱砂与树脂混匀，常温下放入转速为200～300r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用320～360r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂或，置于温度为65～75℃环境中进行固化30～40min；
(4)脱模后，在表面刷上一层透明料即可。
所述朱砂经过粉碎至100～200目。
所述固化剂由三乙醇胺和二甲基苯胺按照30～50：1的重量配比制备而成。
所述透明料是将有机硅改性苯丙乳液10～15重量份、无水乙醇25～40重量份、氧化锌5～10重量份、多官能团聚氨酯10～15份和无色透明纳米银溶液0.5～1重量份混合均匀即可。
有益效果
本发明通过加入香料，使得产品的带有淡淡的清香味，品质得到提高；通过采用三乙醇胺和二甲基苯胺为固化剂，提高固化效果，缩短固化时间，促使产品表面光滑，减少产品表面出现细小气泡；本发明通过对原料的配比进行合理的调整，提高产品的可塑性，进而可以加工成各种形状，并且使其色泽光鲜亮丽，并保留了朱砂的原有颜色；通过使用透明料，防止原料中的有害物质对人体皮肤产生不利的影响，同时对工艺品起到保护的作用，并且还具有驱虫杀菌的功效。
本发明通过采用朱砂、树脂和香料为原料，通过合理的搭配，在结合工艺参数的调控制备成工艺品，使得产品的色泽亮丽，表面光滑；同时也保留朱砂原有的颜色，并且通过香料的加入，使得产品具有淡淡的清香味，提升产品的品质。
具体实施方式
实施例1
配方：朱砂6kg、树脂2kg、香料0.1kg；
制备方法：(1)按照配方量取朱砂与树脂混匀，常温下放入转速为200r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用320r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂或，置于温度为65℃环境中进行固化30min；
(4)脱模后，在表面刷上一层透明料即可。
所述树脂为环氧树脂、聚氯乙烯树脂、聚苯乙烯树脂和聚丙烯树脂、用量均为0.5kg。
所述香料是将植物香料50g、薄荷脑40g和无水乙醇15g重量份混合均匀即可。
所述植物香料为玫瑰。
所述朱砂经过粉碎至100目。
所述固化剂由三乙醇胺和二甲基苯胺按照30：1的重量配比制备而成。
所述透明料是将有机硅改性苯丙乳液100g、无水乙醇250g、氧化锌50g、多官能团聚氨酯100g和无色透明纳米银溶液5g混合均匀即可。
实施例2
配方：朱砂8kg、环氧树脂3kg、香料0.5kg；
制备方法：(1)按照配方量取朱砂与树脂混匀，常温下放入转速为300r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用360r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂或，置于温度为75℃环境中进行固化40min；
(4)脱模后，在表面刷上一层透明料即可。
所述树脂为环氧树脂。
所述香料是将植物香料200g、薄荷脑180g和无水乙醇400g混合均匀即可。
所述植物香料为薰衣草。
所述朱砂经过粉碎至200目。
所述固化剂由三乙醇胺和二甲基苯胺按照50：1的重量配比制备而成。
所述透明料是将有机硅改性苯丙乳液150g、无水乙醇400g、氧化锌100g、多官能团聚氨酯150g和无色透明纳米银溶液10g混合均匀即可。
实施例3
配方：朱砂7.4kg、树脂2.8kg、香料0.3kg；
制备方法：(1)按照配方量取朱砂与树脂混匀，常温下放入转速为240r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用340r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂或，置于温度为70℃环境中进行固化35min；
(4)脱模后，在表面刷上一层透明料即可。
所述树脂为聚丙烯树脂。
所述香料是将植物香料70g、薄荷脑60g和无水乙醇170g混合均匀即可。
所述植物香料为百合35g、檀香35g。
所述朱砂经过粉碎至180目。
所述固化剂由三乙醇胺和二甲基苯胺按照38：1的重量配比制备而成。
所述透明料是将有机硅改性苯丙乳液130g、无水乙醇320g、氧化锌70g、多官能团聚氨酯110g和无色透明纳米银溶液6g混合均匀即可。
实施例4
配方：朱砂6kg、环氧树脂3kg、香料0.1kg；
制备方法：(1)按照配方量取朱砂与树脂混匀，常温下放入转速为220r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用350r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂或，置于温度为72℃环境中进行固化38min；
(4)脱模后，在表面刷上一层透明料即可。
所述树脂为聚氯乙烯树脂、聚丙烯树脂和松香树脂，用量均为0.5kg。
所述香料是将植物香料20g、薄荷脑36g和无水乙醇60g混合均匀即可。
所述植物香料为檀香。
所述朱砂经过粉碎至120目。
所述固化剂由三乙醇胺和二甲基苯胺按照45：1的重量配比制备而成。
所述透明料是将有机硅改性苯丙乳液150g、无水乙醇250g、氧化锌50g、多官能团聚氨酯150g和无色透明纳米银溶液5g混合均匀即可。
实施例5
配方：朱砂8kg、环氧树脂2kg、香料0.3kg；
制备方法：(1)按照配方量取朱砂与树脂混匀，常温下放入转速为280r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用330r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂或，置于温度为68℃环境中进行固化32min；
(4)脱模后，在表面刷上一层透明料即可。
所述树脂为聚苯乙烯树脂和聚丙烯树脂，用量均为1kg。。
所述香料是将植物香料80g、薄荷脑70g和无水乙醇190g混合均匀即可。
所述植物香料为沉香。
所述朱砂经过粉碎至170目。
所述固化剂由三乙醇胺和二甲基苯胺按照42：1的重量配比制备而成。
所述透明料是将有机硅改性苯丙乳液130g、无水乙醇280g、氧化锌60g、多官能团聚氨酯140g和无色透明纳米银溶液9g混合均匀即可。
在此有必要指出的是，以上实施例仅限于对本发明的技术方案做进一步的阐述和理解，不能理解为对本发明的技术方案做进一步的限定，本领域技术人员作出的非突出实质性特征和显著进步的发明创造，仍然属于本发明的保护范畴。

Claims (9)

1.一种朱砂工艺品，其特征在于，原料以重量份计为朱砂60～80份、树脂20～30份、香料1～5份。
2.如权利要求1所述朱砂工艺品，其特征在于，原料以重量份计为朱砂74份、树脂28份、香料3份。
3.如权利要求1或2所述朱砂工艺品，其特征在于，所述树脂为环氧树脂、聚氯乙烯树脂、聚苯乙烯树脂、聚丙烯树脂、松香树脂中至少一种，两种及以上重量配比相等。
4.如权利要求1或2所述朱砂工艺品，其特征在于，所述香料是将植物香料5～10重量份、薄荷脑4～9重量份和无水乙醇15～20重量份混合均匀即可。
5.如权利要求4所述朱砂工艺品，其特征在于，所述植物香料为玫瑰、薰衣草、百合、沉香、檀香中至少一种，两种及以上重量配比相等。
6.如权利要求1或2所述朱砂工艺品的制备方法，其特征在于，包括以下步骤：
(1)按照配方量取朱砂与树脂混匀，常温下放入转速为200～300r/min的搅拌机中混匀，备用：
(2)步骤1)结束后添加香料，采用320～360r/min转速搅拌均匀，得到混合物；
(3)将混合物倒入模具中，并添加固化剂置于温度为65～75℃环境中进行固化30～40min；
(4)脱模后，在表面刷上一层透明料即可。
7.如权利要求6所述朱砂工艺品的制备方法，其特征在于，所述朱砂经过粉碎至100～200目。
8.如权利要求6所述朱砂工艺品的制备方法，其特征在于，所述固化剂由三乙醇胺和二甲基苯胺按照30～50：1的重量配比制备而成。
9.如权利要求6所述所述朱砂工艺品的制备方法，其特征在于，所述透明料是将有机硅改性苯丙乳液10～15重量份、无水乙醇25～40重量份、氧化锌5～10重量份、多官能团聚氨酯10～15份和无色透明纳米银溶液0.5～1重量份混合均匀即可。
CN201710591525.0A 2017-07-19 2017-07-19 一种朱砂工艺品及其制备方法 Pending CN107311515A (zh)