CN107286536A - A kind of fire protection flame retarding polyvinyl chloride cable sheath - Google Patents
A kind of fire protection flame retarding polyvinyl chloride cable sheath Download PDFInfo
- Publication number
- CN107286536A CN107286536A CN201710675120.5A CN201710675120A CN107286536A CN 107286536 A CN107286536 A CN 107286536A CN 201710675120 A CN201710675120 A CN 201710675120A CN 107286536 A CN107286536 A CN 107286536A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- fire protection
- flame retarding
- protection flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire protection flame retarding polyvinyl chloride cable sheath, it is constituted according to the parts by weight of following raw material：50 100 parts of polyvinyl chloride, 10 20 parts of modified epoxy, 15 parts of silicon rubber, 10 15 parts of zinc oxide, 10 20 parts of magnesium hydroxide, 35 parts of calcium carbonate, 5 10 parts of aluminium hydroxide, 13 parts of Firebrake ZB, 0.5 1 parts of 1,2 dihyaroquinoline, 12 parts of stabilizer, 15 parts of vulcanizing agent, 0.1 0.5 parts of vulcanization accelerator, 0.3 0.5 parts of magnesia, 0.1 0.2 parts of TRA antiscorching agent, 0.3 1.5 parts of preservative, 12 parts of repefral, 12 parts of DL171 coupling agents.The fire protection flame retarding polyvinyl chloride cable sheath of the present invention has very strong weather resisteant, reduces influence of the environment to cable cover(ing), and good insulation preformance, softness is good, and impact resistance is strong, while tensile strength is high, stability is excellent, and high mechanical strength and fire resistance are good.
Description
Technical field
The present invention relates to a kind of cable cover(ing), more particularly to a kind of fire protection flame retarding polyvinyl chloride cable sheath.
Background technology
At present, with the development of the social economy, China constantly expands to cable market demand and the scientific research of cable is thrown
What is entered deepens continuously, while also constantly being improved to the quality requirement of cable, the particularly requirement to cable cover(ing) is higher, it is desirable to
The side such as its insulating properties, high and low temperature resistance, fatigue durability, anti-broken string ability, antijamming capability, mechanical resistant damage, water proofing property
Face requires all especially high.
The content of the invention
The purpose of the present invention is that to solve the above problems and provide a kind of fire protection flame retarding polychlorostyrene second of fire protection flame retarding
Alkene cable cover(ing).
To achieve these goals, the present invention is achieved by the following technical solutions, and a kind of fire protection flame retarding polyvinyl chloride is electric
Cable sheath, it is constituted according to the parts by weight of following raw material：50-100 parts of polyvinyl chloride, 10-20 parts of modified epoxy, silicon rubber
1-5 parts of glue, 10-15 parts of zinc oxide, 10-20 parts of magnesium hydroxide, 3-5 parts of calcium carbonate, 5-10 parts of aluminium hydroxide, 1-3 parts of Firebrake ZB,
0.5-1 parts of 1,2- dihyaroquinolines, 1-2 parts of stabilizer, 1-5 parts of vulcanizing agent, 0.1-0.5 parts of vulcanization accelerator, magnesia 0.3-
0.5 part, 0.1-0.2 parts of TRA antiscorching agent, 0.3-1.5 parts of preservative, 1-2 parts of repefral, DL171 coupling agents 1-2
Part.
Further, a kind of fire protection flame retarding polyvinyl chloride cable sheath, it is constituted according to the parts by weight of following raw material：It is poly-
70-90 parts of vinyl chloride, 15-18 parts of modified epoxy, 3-5 parts of silicon rubber, 11-13 parts of zinc oxide, 15-18 parts of magnesium hydroxide,
3-5 parts of calcium carbonate, 6-9 parts of aluminium hydroxide, 1-3 parts of Firebrake ZB, 0.5-1 parts of 1,2- dihyaroquinolines, 1-2 parts of stabilizer, vulcanization
1-5 parts of agent, 0.1-0.5 parts of vulcanization accelerator, 0.3-0.5 parts of magnesia, 0.1-0.2 parts of TRA antiscorching agent, preservative 0.3-1.5
Part, 1-2 parts of repefral, 1-2 parts of DL171 coupling agents.
Further, a kind of fire protection flame retarding polyvinyl chloride cable sheath, it is constituted according to the parts by weight of following raw material：
80 parts of polyvinyl chloride, 16 parts of modified epoxy, 4 parts of silicon rubber, 12 parts of zinc oxide, 16 parts of magnesium hydroxide, 4 parts of calcium carbonate, hydrogen
8 parts of aluminum oxide, 2 parts of Firebrake ZB, 0.5 part of 1,2- dihyaroquinolines, 2 parts of stabilizer, 3 parts of vulcanizing agent, 0.3 part of vulcanization accelerator,
0.4 part of magnesia, 0.1 part of TRA antiscorching agent, 0.8 part of preservative, 2 parts of repefral, 1 part of DL171 coupling agents.
Particularly, the modified epoxy is that epoxy resin immersion phenol resin solution modification is formed.
The beneficial effects of the invention are as follows：The fire protection flame retarding polyvinyl chloride cable sheath of the present invention has very strong weather resisteant,
Influence of the environment to cable cover(ing), and good insulation preformance are reduced, softness is good, impact resistance is strong, while tensile strength
Height, stability is excellent, and high mechanical strength and fire resistance are good.
Embodiment
Specific embodiment 1：A kind of fire protection flame retarding polyvinyl chloride cable sheath, its according to following raw material parts by weight array
Into：50 parts of polyvinyl chloride, 10 parts of modified epoxy, 1 part of silicon rubber, 10 parts of zinc oxide, 10 parts of magnesium hydroxide, 3 parts of calcium carbonate,
5 parts of aluminium hydroxide, 1 part of Firebrake ZB, 0.5 part of 1,2- dihyaroquinolines, 1 part of stabilizer, 1 part of vulcanizing agent, vulcanization accelerator 0.1
Part, 0.3 part of magnesia, 0.1 part of TRA antiscorching agent, 0.3 part of preservative, 1 part of repefral, 1 part of DL171 coupling agents.
Wherein modified epoxy is that epoxy resin immersion phenol resin solution modification is formed.
Specific embodiment 2：A kind of fire protection flame retarding polyvinyl chloride cable sheath, its according to following raw material parts by weight array
Into：80 parts of polyvinyl chloride, 16 parts of modified epoxy, 4 parts of silicon rubber, 12 parts of zinc oxide, 16 parts of magnesium hydroxide, 4 parts of calcium carbonate,
8 parts of aluminium hydroxide, 2 parts of Firebrake ZB, 0.5 part of 1,2- dihyaroquinolines, 2 parts of stabilizer, 3 parts of vulcanizing agent, vulcanization accelerator 0.3
Part, 0.4 part of magnesia, 0.1 part of TRA antiscorching agent, 0.8 part of preservative, 2 parts of repefral, 1 part of DL171 coupling agents.
Wherein modified epoxy is that epoxy resin immersion phenol resin solution modification is formed.
Specific embodiment 3：A kind of fire protection flame retarding polyvinyl chloride cable sheath, its according to following raw material parts by weight array
Into：100 parts of polyvinyl chloride, 20 parts of modified epoxy, 5 parts of silicon rubber, 15 parts of zinc oxide, 20 parts of magnesium hydroxide, calcium carbonate 5
Part, 10 parts of aluminium hydroxide, 3 parts of Firebrake ZB, 1 part of 1,2- dihyaroquinolines, 2 parts of stabilizer, 5 parts of vulcanizing agent, vulcanization accelerator 0.5
Part, 0.5 part of magnesia, 0.2 part of TRA antiscorching agent, 1.5 parts of preservative, 2 parts of repefral, 2 parts of DL171 coupling agents.
Wherein modified epoxy is that epoxy resin immersion phenol resin solution modification is formed.
Embodiment provided above is the better embodiment of the present invention, only illustrates the present invention for convenient, not to this hair
It is bright to make any formal limitation, any those of ordinary skill in the art, if putting forward skill not departing from the present invention
In the range of art feature, using the equivalent embodiment for locally changing or modifying made by disclosed technology contents, and
Without departing from the technical characteristic content of the present invention, in the range of still falling within the technology of the present invention feature.
Claims (4)
1. a kind of fire protection flame retarding polyvinyl chloride cable sheath, it is characterised in that：Constituted according to the parts by weight of following raw material：Polychlorostyrene
50-100 parts of ethene, 10-20 parts of modified epoxy, 1-5 parts of silicon rubber, 10-15 parts of zinc oxide, 10-20 parts of magnesium hydroxide, carbon
Sour calcium 3-5 parts, 5-10 parts of aluminium hydroxide, 1-3 parts of Firebrake ZB, 0.5-1 parts of 1,2- dihyaroquinolines, 1-2 parts of stabilizer, vulcanizing agent
1-5 parts, 0.1-0.5 parts of vulcanization accelerator, 0.3-0.5 parts of magnesia, 0.1-0.2 parts of TRA antiscorching agent, 0.3-1.5 parts of preservative,
1-2 parts of repefral, 1-2 parts of DL171 coupling agents.
2. a kind of fire protection flame retarding polyvinyl chloride cable sheath according to claim 1, it is characterised in that：According to following raw material
Parts by weight composition：70-90 parts of polyvinyl chloride, 15-18 parts of modified epoxy, 3-5 parts of silicon rubber, 11-13 parts of zinc oxide,
15-18 parts of magnesium hydroxide, 3-5 parts of calcium carbonate, 6-9 parts of aluminium hydroxide, 1-3 parts of Firebrake ZB, 0.5-1 parts of 1,2- dihyaroquinolines,
1-2 parts of stabilizer, 1-5 parts of vulcanizing agent, 0.1-0.5 parts of vulcanization accelerator, 0.3-0.5 parts of magnesia, TRA antiscorching agent 0.1-0.2
Part, 0.3-1.5 parts of preservative, 1-2 parts of repefral, 1-2 parts of DL171 coupling agents.
3. a kind of fire protection flame retarding polyvinyl chloride cable sheath according to claim 1, it is characterised in that：According to following raw material
Parts by weight composition：80 parts of polyvinyl chloride, 16 parts of modified epoxy, 4 parts of silicon rubber, 12 parts of zinc oxide, magnesium hydroxide 16
Part, 4 parts of calcium carbonate, 8 parts of aluminium hydroxide, 2 parts of Firebrake ZB, 0.5 part of 1,2- dihyaroquinolines, 2 parts of stabilizer, 3 parts of vulcanizing agent, sulphur
Change 0.3 part of accelerator, 0.4 part of magnesia, 0.1 part of TRA antiscorching agent, 0.8 part of preservative, 2 parts of repefral,
1 part of DL171 coupling agents.
4. a kind of fire protection flame retarding polyvinyl chloride cable sheath according to claim 1 or 2 or 3, it is characterised in that：It is described to change
Property epoxy resin be epoxy resin immersion phenol resin solution be modified form.