CN107267042A - A kind of antirust paint for power equipment - Google Patents
A kind of antirust paint for power equipment Download PDFInfo
- Publication number
- CN107267042A CN107267042A CN201710656658.1A CN201710656658A CN107267042A CN 107267042 A CN107267042 A CN 107267042A CN 201710656658 A CN201710656658 A CN 201710656658A CN 107267042 A CN107267042 A CN 107267042A
- Authority
- CN
- China
- Prior art keywords
- parts
- power equipment
- antirust
- modified
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of antirust paint for power equipment, is made up of the component of following weight：20 30 parts of modified alkyd resin, 8 15 parts of polyurethane-modified acrylic acid emulsion, 10 15 parts of polyether modified siloxane, 5 10 parts of petroleum sulfonate, 48 parts of dimethylbenzene, 7 15 parts of oiliness wax, 8 12 parts of Quadrafos, 24 parts of chliorinated polyvinyl chloride, 5 10 parts of C5 hydrogenated petroleum resins, 3 parts of silica 1,46 parts of antirust agent.The beneficial effects of the invention are as follows：The present invention is using modified alkyd resin, polyurethane-modified acrylic acid emulsion, polyether modified siloxane as main material, and dimethylbenzene, oiliness wax, Quadrafos, C5 hydrogenated petroleum resins, silica, antirust agent are with the addition of as modifying agent, antioxidant, stability are enhanced, rust-preventing characteristic is enhanced.
Description
Technical field
The present invention relates to technical field of chemical paint, and in particular to a kind of antirust paint for power equipment.
Background technology
Power equipment mainly includes with generating equipment and the major class of power supply unit two, and generating equipment is mainly station boiler, steaming
Steam turbine, gas turbine, the hydraulic turbine, generator, transformer etc., power supply unit are mainly the power transmission line of various voltage class
Road, transformer, contactor etc..
The metal shell of power equipment by the chemical attacks such as water, acid, salt and other environmental conditions when being influenceed, electricity
The metal shell of power equipment can occur corrosion and produce rust stain, can have a strong impact on the operation of power equipment in shell, not only result in
The damage of power equipment, the waste of electric power resource, it is also possible to cause danger.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of antirust paint for power equipment.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of antirust paint for power equipment, is made up of the component of following weight：20-30 parts of modified alkyd resin, gathers
8-15 parts of urethane modified acrylate emulsion, 10-15 parts of polyether modified siloxane, 5-10 parts of petroleum sulfonate, 4-8 parts of dimethylbenzene,
7-15 parts of oiliness wax, 8-12 parts of Quadrafos, 2-4 parts of chliorinated polyvinyl chloride, 5-10 parts of C5 hydrogenated petroleum resins, silica 1-
3 parts, 4-6 parts of antirust agent.
The above-mentioned antirust paint for power equipment, the component of preferably following weight is made：25 parts of modified alkyd resin, poly- ammonia
Ester modified 13 parts of acrylic emulsion, 12 parts of polyether modified siloxane, 8 parts of petroleum sulfonate, 6 parts of dimethylbenzene is 11 parts of oiliness wax, poly-
10 parts of phosphate, 3 parts of chliorinated polyvinyl chloride, 7 parts of C5 hydrogenated petroleum resins, 2 parts of silica, 5 parts of antirust agent.
The antirust agent is made up of the component of following weight：5-10 parts of dicyclohexyl amine, 3-6 parts of soda ash, ceramic 2-4
Part, 1-2 parts of nano zine oxide, 2-3 parts of nano-calcium carbonate, 3-5 parts of Vitamin C palmitate.
The component of the antirust agent preferably following weight is made：8 parts of dicyclohexyl amine, 5 parts of soda ash, 3 parts of ceramic, nanometer
2 parts of zinc oxide, 2 parts of nano-calcium carbonate, 4 parts of Vitamin C palmitate.
The preparation method of the above-mentioned antirust paint for power equipment is as follows：
A, by modified alkyd resin, polyether modified siloxane, oiliness wax, C5 hydrogenated petroleum resins mix, be heated to melting
State, is stirred reaction, and mixing time is 20-30 minutes；
B, polyurethane-modified acrylic acid emulsion, dimethylbenzene, petroleum sulfonate, Quadrafos, chliorinated polyvinyl chloride, titanium dioxide
Silicon is added in reactor, and temperature setting is reacted in 120-150 degree, and the reaction time is 30-40 minutes；
C, will step a mixtures and b mixture add mixer in be stirred, mixing speed is 800-1000r/
Min, temperature setting is 80-90, and mixing time is 20-30 minutes；
D, antirust agent is added in step c mixer, continues to stir, mixing speed is 1200-1400r/min, temperature
Degree is set to 40-60, and mixing time is 30-40 minutes；
E, the mixture for handling step d well, carry out five segmentation grindings, that is, obtain finished product.
It is described five times segmentation grinding speed be respectively：40-50/rpm, 60-80/rpm, 90-100/rpm, 100-120/
rpm。
The beneficial effects of the invention are as follows：The present invention is with modified alkyd resin, polyurethane-modified acrylic acid emulsion, polyether-modified
Siloxanes is main material, and with the addition of dimethylbenzene, oiliness wax, Quadrafos, C5 hydrogenated petroleum resins, silica, antirust agent
As modifying agent, antioxidant, stability are enhanced, rust-preventing characteristic is enhanced.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of antirust paint for power equipment, is made up of the component of following weight：20 parts of modified alkyd resin, polyurethane
8 parts of modified acrylic acid emulsion, 10 parts of polyether modified siloxane, 5 parts of petroleum sulfonate, 4 parts of dimethylbenzene, 7 parts of oiliness wax, polyphosphoric acid
8 parts of salt, 2 parts of chliorinated polyvinyl chloride, 5 parts of C5 hydrogenated petroleum resins, silica 1 part, 4 parts of antirust agent.
The antirust agent is made up of the component of following weight：5 parts of dicyclohexyl amine, 3 parts of soda ash, 2 parts of ceramic, nano oxygen
Change 1 part of zinc, 2 parts of nano-calcium carbonate, 3 parts of Vitamin C palmitate.
The preparation method of the above-mentioned antirust paint for power equipment is as follows：
A, by modified alkyd resin, polyether modified siloxane, petroleum sulfonate mix, be heated to molten condition, stirred
Reaction is mixed, mixing time is 20 minutes；
B, polyurethane-modified acrylic acid emulsion, dimethylbenzene, oiliness wax, Quadrafos, chliorinated polyvinyl chloride, C5 hydrotreated petroleums
Resin, silica are added in reactor, and temperature setting is reacted at 120 degree, and the reaction time is 30 minutes；
C, will step a mixtures and b mixture add mixer in be stirred, mixing speed is 800r/min, temperature
Degree is set to 80, and mixing time is 20 minutes；
D, antirust agent is added in step c mixer, continues to stir, mixing speed is 1200r/min, temperature setting
For 40, mixing time is 30 minutes；
E, the mixture for handling step d well, carry out five segmentation grindings, and the speed of five segmentation grindings is respectively：40/
Rpm, 60/rpm, 90/rpm, 100/rpm, that is, obtain finished product.
Embodiment 2
A kind of antirust paint for power equipment, is made up of the component of following weight：30 parts of modified alkyd resin, polyurethane
15 parts of modified acrylic acid emulsion, 15 parts of polyether modified siloxane, 10 parts of petroleum sulfonate, 8 parts of dimethylbenzene is 15 parts of oiliness wax, poly-
12 parts of phosphate, 4 parts of chliorinated polyvinyl chloride, 10 parts of C5 hydrogenated petroleum resins, 3 parts of silica, 6 parts of antirust agent.
The antirust agent is made up of the component of following weight：10 parts of dicyclohexyl amine, 6 parts of soda ash, 4 parts of ceramic, nanometer
2 parts of zinc oxide, 3 parts of nano-calcium carbonate, 5 parts of Vitamin C palmitate.
The preparation method of the above-mentioned antirust paint for power equipment is as follows：
A, by modified alkyd resin, polyether modified siloxane, petroleum sulfonate mix, be heated to molten condition, stirred
Reaction is mixed, mixing time is 30 minutes；
B, polyurethane-modified acrylic acid emulsion, dimethylbenzene, oiliness wax, Quadrafos, chliorinated polyvinyl chloride, C5 hydrotreated petroleums
Resin, silica are added in reactor, and temperature setting is reacted at 150 degree, and the reaction time is 40 minutes；
C, will step a mixtures and b mixture add mixer in be stirred, mixing speed is 1000r/min, temperature
Degree is set to 90, and mixing time is 30 minutes；
D, antirust agent is added in step c mixer, continues to stir, mixing speed is 1400r/min, temperature setting
For 60, mixing time is 40 minutes；
E, the mixture for handling step d well, carry out five segmentation grindings, and the speed of five segmentation grindings is respectively：50/
Rpm, 80/rpm, 100/rpm, 120/rpm, that is, obtain finished product.
Control group 1
A kind of antirust paint for power equipment, is made up of the component of following weight：20 parts of modified alkyd resin, polyurethane
8 parts of modified acrylic acid emulsion, 10 parts of polyether modified siloxane, 5 parts of petroleum sulfonate, 4 parts of dimethylbenzene, 7 parts of oiliness wax, polyphosphoric acid
8 parts of salt, 2 parts of chliorinated polyvinyl chloride, 5 parts of C5 hydrogenated petroleum resins, silica 1 part, 4 parts of antirust agent.
The antirust agent is common antirust agent.
The preparation method of the above-mentioned antirust paint for power equipment is as follows：
A, by modified alkyd resin, polyether modified siloxane, petroleum sulfonate mix, be heated to molten condition, stirred
Reaction is mixed, mixing time is 20 minutes；
B, polyurethane-modified acrylic acid emulsion, dimethylbenzene, oiliness wax, Quadrafos, chliorinated polyvinyl chloride, C5 hydrotreated petroleums
Resin, silica are added in reactor, and temperature setting is reacted at 120 degree, and the reaction time is 30 minutes；
C, will step a mixtures and b mixture add mixer in be stirred, mixing speed is 800r/min, temperature
Degree is set to 80, and mixing time is 20 minutes；
D, antirust agent is added in step c mixer, continues to stir, mixing speed is 1200r/min, temperature setting
For 40, mixing time is 30 minutes；
E, the mixture for handling step d well, carry out five segmentation grindings, and the speed of five segmentation grindings is respectively：40/
Rpm, 60/rpm, 90/rpm, 100/rpm, that is, obtain finished product.
Control group 2
A kind of antirust paint for power equipment, is made up of the component of following weight：30 parts of modified alkyd resin, polyurethane
15 parts of modified acrylic acid emulsion, 15 parts of polyether modified siloxane, 10 parts of petroleum sulfonate, 8 parts of dimethylbenzene is 15 parts of oiliness wax, poly-
12 parts of phosphate, 4 parts of chliorinated polyvinyl chloride, 10 parts of C5 hydrogenated petroleum resins, 3 parts of silica, 6 parts of antirust agent.
The antirust agent is made up of the component of following weight：5 parts of dicyclohexyl amine, 3 parts of soda ash, 2 parts of ceramic, nano oxygen
Change 1 part of zinc, 2 parts of nano-calcium carbonate, 3 parts of Vitamin C palmitate.
The preparation method of the above-mentioned antirust paint for power equipment is as follows：
A, by modified alkyd resin, polyether modified siloxane, petroleum sulfonate mix, be heated to molten condition, stirred
Reaction is mixed, mixing time is 30 minutes；
B, polyurethane-modified acrylic acid emulsion, dimethylbenzene, oiliness wax, Quadrafos, chliorinated polyvinyl chloride, C5 hydrotreated petroleums
Resin, silica are added in reactor, and temperature setting is reacted at 100 degree, and the reaction time is 40 minutes；
C, will step a mixtures and b mixture add mixer in be stirred, mixing speed is 600r/min, temperature
Degree is set to 90, and mixing time is 30 minutes；
D, antirust agent is added in step c mixer, continues to stir, mixing speed is 800r/min, temperature setting
For 60, mixing time is 40 minutes；
E, the mixture for handling step d well, are ground, that is, obtain finished product.
Table 1 is the present invention and control group performance test
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
1. a kind of antirust paint for power equipment, is made up of the component of following weight：20-30 parts of modified alkyd resin, poly- ammonia
Ester modified acrylic emulsion 8-15 parts, 10-15 parts of polyether modified siloxane, 5-10 parts of petroleum sulfonate, 4-8 parts of dimethylbenzene, oil
7-15 parts of wax of property, 8-12 parts of Quadrafos, 2-4 parts of chliorinated polyvinyl chloride, 5-10 parts of C5 hydrogenated petroleum resins, silica 1-3
Part, 4-6 parts of antirust agent.
2. the antirust paint according to claim 1 for power equipment, it is characterised in that the component system of preferred following weight
Into：25 parts of modified alkyd resin, 13 parts of polyurethane-modified acrylic acid emulsion, 12 parts of polyether modified siloxane, petroleum sulfonate 8
Part, 6 parts of dimethylbenzene, 11 parts of oiliness wax, 10 parts of Quadrafos, 3 parts of chliorinated polyvinyl chloride, 7 parts of C5 hydrogenated petroleum resins, titanium dioxide
2 parts of silicon, 5 parts of antirust agent.
3. the antirust paint according to claim 1 for power equipment, it is characterised in that the antirust agent is by following weight
Component be made：5-10 parts of dicyclohexyl amine, 3-6 parts of soda ash, 2-4 parts of ceramic, 1-2 parts of nano zine oxide, nano-calcium carbonate
2-3 parts, 3-5 parts of Vitamin C palmitate.
4. the antirust paint according to claim 3 for power equipment, it is characterised in that the preferably following weight of the antirust agent
The component of amount is made：8 parts of dicyclohexyl amine, 5 parts of soda ash, 3 parts of ceramic, 2 parts of nano zine oxide, 2 parts of nano-calcium carbonate are anti-bad
4 parts of blood palmitate.
5. a kind of any one of claim 1-2 for preparing is used for the antirust paint of power equipment, it is characterised in that as follows including step：
A, by modified alkyd resin, polyether modified siloxane, oiliness wax, C5 hydrogenated petroleum resins mix, be heated to molten condition,
Reaction is stirred, mixing time is 20-30 minutes；
B, polyurethane-modified acrylic acid emulsion, dimethylbenzene, petroleum sulfonate, Quadrafos, chliorinated polyvinyl chloride, silica add
Enter into reactor, temperature setting is reacted in 120-150 degree, the reaction time is 30-40 minutes；
C, will step a mixtures and b mixture add mixer in be stirred, mixing speed is 800-1000r/min, temperature
Degree is set to 80-90, and mixing time is 20-30 minutes；
D, antirust agent is added in step c mixer, continues to stir, mixing speed is 1200-1400r/min, and temperature is set
40-60 is set to, mixing time is 30-40 minutes；
E, the mixture for handling step d well, carry out five segmentation grindings, that is, obtain finished product.
6. method according to claim 5, it is characterised in that the speed of five segmentations grinding is respectively：40-50/
Rpm, 60-80/rpm, 90-100/rpm, 100-120/rpm.