CN105504970B - A kind of rub resistance oil polish and preparation method thereof - Google Patents
A kind of rub resistance oil polish and preparation method thereof Download PDFInfo
- Publication number
- CN105504970B CN105504970B CN201511015808.8A CN201511015808A CN105504970B CN 105504970 B CN105504970 B CN 105504970B CN 201511015808 A CN201511015808 A CN 201511015808A CN 105504970 B CN105504970 B CN 105504970B
- Authority
- CN
- China
- Prior art keywords
- varniss
- rub resistance
- siccative
- oil
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to oil polish technical fields, and in particular to a kind of rub resistance oil polish and preparation method thereof.A kind of rub resistance oil polish, including：Make siccative varniss, slack wax, PE waxes, microwax, mineral oil and drier by oneself；Wherein, self-control siccative varniss includes：Modified rosin resin, semi-drying vegetable oils, dry vegetable oil and gelling agent；Slack wax includes：Fischer-Tropsch wax and vegetable oil.The rub resistance oil polish has the advantages that rapid draing after printing, so as to shorten the production time, improves production efficiency.The ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, the frictional force that printing ink pellet surface is subject to can be effectively reduced, even if making printed article in the transportational process of long range, friction is small between printed article, so as to effectively prevent the case where printed article is easy friction scumming, and then the quality of printed article can be improved, avoid the generation of the important problems such as the return of goods, claim.
Description
Technical field
The present invention relates to oil polish technical fields, and in particular to a kind of rub resistance oil polish and preparation method thereof.
Background technology
In offset printing industry, in recent years, the use of solid matte paper and art paper increases.And due to calcium carbonate and grinding agent
Usually as the raw material of manufacture solid matte paper and art paper, therefore, the surface of manufactured solid matte paper and art paper is contained largely
Calcium carbonate and grinding agent.
The printed article printed using solid matte paper or art paper, since a large amount of calcium carbonate is also contained on the surface of these printed articles
And grinding agent, in post-processing or when transporting these printed articles, since these printed articles stack, these printings
It is easy to appear frictions between object, and the calcium carbonate and grinding agent that its surface is contained so that the friction between these printed articles is made
It with bigger, thus be easy to cause these printed articles and the case where friction scumming occurs, and then seriously affected these printed articles
Quality, and cause the important problem such as return goods, claim damages.In addition, if the transportation range and haulage time of these printed articles are long,
Friction scumming situation can be made more serious.
In order to prevent the case where above-mentioned this printed article is easy friction scumming, rub resistance is carried out to the ink formulations of printing
Improvement is relatively difficult, and therefore, it is urgent to provide a kind of rub resistance oil polishes, are gone bail for the ink on offset printing surface with it
Shield.However, oil polish in the prior art haves the shortcomings that crocking resistance is bad, making it difficult to prevent printed article and be easy friction
The case where scumming, and the drying property of oil polish in the prior art is bad so that the drying time needed for after printing is longer, into
And the production time is extended, reduce production efficiency.
Invention content
It is an object of the present invention in view of the deficiencies of the prior art, provide a kind of rub resistance glazing that drying property is good
Oil.
The second object of the present invention is to provide a kind of rub resistance glazing that drying property is good in view of the deficiencies of the prior art
The preparation method of oil.
One of to achieve the goals above, the present invention adopts the following technical scheme that：
A kind of rub resistance oil polish is provided, it includes the component of following weight percent：
Make siccative varniss 45% ~ 80% by oneself
Alkyd resin 1% ~ 10%
Slack wax 5% ~ 15%
PE waxes 5%~15%
Microwax 1%~4%
Mineral oil 5%~20%
Drier 2%~5%；
The self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 30%~45%
Semi-drying vegetable oils 10%~20%
Dry vegetable oil 40%~55%
Gelling agent 0.5%~2%.
The slack wax includes the component of following weight percent：
Fischer-Tropsch wax 35%~65%
Vegetable oil 35%~65%.
In the self-control siccative varniss, the gelling agent is alkyl aluminum.
Preferably, a kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 45% ~ 70% by oneself
Alkyd resin 1% ~ 7%
Slack wax 5% ~ 12%
PE waxes 8%~15%
Microwax 1%~4%
Mineral oil 10%~20%
Drier 2%~5%；
The self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 30%~40%
Semi-drying vegetable oils 15%~20%
Dry vegetable oil 40%~50%
Gelling agent 0.5%~2%.
More preferably, a kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 55% by oneself
Alkyd resin 5%
Slack wax 10%
PE waxes 15%
Microwax 2%
Mineral oil 10%
Drier 3%；
The self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 40%
Semi-drying vegetable oils 15%
Dry vegetable oil 44%
Gelling agent 1%.
Preferably, the slack wax includes the component of following weight percent：
Fischer-Tropsch wax 40%~60%
Vegetable oil 40%~60%.
More preferably, the slack wax includes the component of following weight percent：
Fischer-Tropsch wax 50%
Vegetable oil 50%.
To achieve the goals above two, the present invention adopts the following technical scheme that：
A kind of preparation method of rub resistance oil polish described above is provided, it is characterised in that：It includes the following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are thrown
Enter blender, be uniformly mixed, obtain the first mixture, the gelling agent of formula ratio is then added into the first mixture, stirring is mixed
It closes uniformly, obtains self-control siccative varniss；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2 by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and is done
Drying prescription is uniformly mixed, and obtains rub resistance oil polish.
In above-mentioned technical proposal, the step 1 prepares self-control siccative varniss：By the modified rosin resin of formula ratio, half
Dry vegetable oil and dry vegetable oil put into blender, mixing 3min ~ 7min are first mixed slowly at 50 DEG C ~ 70 DEG C, then again
210 DEG C ~ 230 DEG C are warming up to, is filled with nitrogen toward blender, then high-speed stirred mixes 50min ~ 70min, obtains the first mixture,
Then 30 DEG C ~ 100 DEG C are cooled to, the gelling agent of formula ratio is added into the first mixture, is uniformly mixed, obtains self-control
Siccative varniss；
Wherein, the speed mixed slowly is 200rpm ~ 400rpm, the speed of the high-speed stirred be 900rpm ~
1100rpm。
Compared with prior art, advantageous effect is the present invention：
（1）A kind of rub resistance oil polish provided by the invention, containing self-control siccative varniss, and since self-control quick-drying is all vertical
The component of water includes modified rosin resin, semi-drying vegetable oils, dry vegetable oil and gelling agent, wherein semi-drying vegetable oils are done
Property vegetable oil and gelling agent three between can generate well synergistic effect so that the self-control siccative varniss have it is very strong
Drying property enables to a kind of rub resistance oil polish of the present invention to have the advantages that rapid draing after printing, so as to contract
The short production time improves production efficiency.
（2）A kind of rub resistance oil polish provided by the invention, due to making the semi-drying vegetable oils in siccative varniss by oneself, doing
Good synergistic effect can be generated between property vegetable oil and gelling agent, with slack wax, PE waxes, microwax, mineral oil and drier
So that the ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, printing can be effectively reduced
The frictional force that ink pellet surface is subject to so that though printed article in the transportational process of long range, frictional force between printed article compared with
It is small, so as to effectively prevent the case where printed article is easy friction scumming, and then the quality of printed article can be improved, avoid moving back
The generation of the important problem such as goods, claim.
（3）A kind of rub resistance oil polish provided by the invention has formula simple, and production cost is low, and can be suitable for
The characteristics of large-scale production.
A kind of preparation method of rub resistance oil polish provided by the invention prepares the step of making siccative varniss by oneself, can
So that obtained self-control siccative varniss has very strong drying property.
（5）A kind of preparation method of rub resistance oil polish provided by the invention has preparation method simple, production cost
It is low, and the characteristics of person mass produces can be suitable for.
Specific implementation mode
In order to make the technical problems, technical solutions and beneficial effects solved by the present invention be more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only used to explain
The present invention is not intended to limit the present invention.
Wherein, the alkyl aluminum that the present invention refers to is alkyl bound directly with aluminium and the major class metallic aluminium organic compound that is formed
Object.
Embodiment 1.
A kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 55% by oneself
Alkyd resin 5%
Slack wax 10%
PE waxes 15%
Microwax 2%
Mineral oil 10%
Drier 3%；
In the present embodiment, self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 40%
Semi-drying vegetable oils 15%
Dry vegetable oil 44%
Gelling agent 1%.
In the present embodiment, make by oneself in siccative varniss, gelling agent is gelling agent.
In the present embodiment, slack wax includes the component of following weight percent：
Fischer-Tropsch wax 50%
Vegetable oil 50%.
A kind of preparation method of above-mentioned rub resistance oil polish, it includes the following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are thrown
Enter blender, mixing 5min is first mixed slowly at 60 DEG C, is then warming up to 220 DEG C again, nitrogen, then high speed are filled with toward blender
It is stirred 60min, obtains the first mixture, is then cooled to 90 DEG C, the gelling agent of formula ratio is added into the first mixture,
It is uniformly mixed, obtains self-control siccative varniss；
Wherein, the speed mixed slowly is 300rpm, and the speed of the high-speed stirred is 1000rpm；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2 by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and is done
Drying prescription is uniformly mixed, and obtains rub resistance oil polish.
A kind of rub resistance oil polish of the present embodiment has the advantages that rapid draing after printing, when so as to shorten production
Between, improve production efficiency.The ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, can
Effectively reduce the frictional force that is subject to of printing ink pellet surface so that though printed article in the transportational process of long range, printed article it
Between friction is small, so as to effectively prevent the case where printed article is easy friction scumming, and then printed article can be improved
Quality avoids the generation of the important problems such as the return of goods, claim.
Embodiment 2.
A kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 45% by oneself
Alkyd resin 1%
Slack wax 15%
PE waxes 13%
Microwax 1%
Mineral oil 20%
Drier 5%；
In the present embodiment, self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 30%
Semi-drying vegetable oils 20%
Dry vegetable oil 48%
Gelling agent 2%.
In the present embodiment, make by oneself in siccative varniss, gelling agent is.
In the present embodiment, slack wax includes the component of following weight percent：
Fischer-Tropsch wax 35%
Vegetable oil 65%.
A kind of preparation method of above-mentioned rub resistance oil polish, it includes the following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are thrown
Enter blender, mixing 7min is first mixed slowly at 50 DEG C, is then warming up to 210 DEG C again, nitrogen, then high speed are filled with toward blender
It is stirred 70min, obtains the first mixture, is then cooled to 100 DEG C, the gel of formula ratio is added into the first mixture
Agent is uniformly mixed, and obtains self-control siccative varniss；
Wherein, the speed mixed slowly is 200rpm, and the speed of the high-speed stirred is 900rpm；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2 by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and is done
Drying prescription is uniformly mixed, and obtains rub resistance oil polish.
A kind of rub resistance oil polish of the present embodiment has the advantages that rapid draing after printing, when so as to shorten production
Between, improve production efficiency.The ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, can
Effectively reduce the frictional force that is subject to of printing ink pellet surface so that though printed article in the transportational process of long range, printed article it
Between friction is small, so as to effectively prevent the case where printed article is easy friction scumming, and then printed article can be improved
Quality avoids the generation of the important problems such as the return of goods, claim.
Embodiment 3.
A kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 80% by oneself
Alkyd resin 1%
Slack wax 5%
PE waxes 5%
Microwax 2%
Mineral oil 5%
Drier 2%；
In the present embodiment, self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 45%
Semi-drying vegetable oils 10%
Dry vegetable oil 44.5%
Gelling agent 0.5%.
In the present embodiment, make by oneself in siccative varniss, gelling agent is alkyl aluminum.
In the present embodiment, slack wax includes the component of following weight percent：
Fischer-Tropsch wax 65%
Vegetable oil 35%.
A kind of preparation method of above-mentioned rub resistance oil polish, it includes the following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are thrown
Enter blender, mixing 3min is first mixed slowly at 70 DEG C, is then warming up to 230 DEG C again, nitrogen, then high speed are filled with toward blender
It is stirred 50min, obtains the first mixture, is then cooled to 60 DEG C, the gelling agent of formula ratio is added into the first mixture,
It is uniformly mixed, obtains self-control siccative varniss；
Wherein, the speed mixed slowly is 400rpm, and the speed of the high-speed stirred is 1100rpm；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2 by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and is done
Drying prescription is uniformly mixed, and obtains rub resistance oil polish.
A kind of rub resistance oil polish of the present embodiment has the advantages that rapid draing after printing, when so as to shorten production
Between, improve production efficiency.The ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, can
Effectively reduce the frictional force that is subject to of printing ink pellet surface so that though printed article in the transportational process of long range, printed article it
Between friction is small, so as to effectively prevent the case where printed article is easy friction scumming, and then printed article can be improved
Quality avoids the generation of the important problems such as the return of goods, claim.
Embodiment 4.
A kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 47% by oneself
Alkyd resin 3%
Slack wax 12%
PE waxes 15%
Microwax 4%
Mineral oil 15%
Drier 4%；
In the present embodiment, self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 43%
Semi-drying vegetable oils 15.5%
Dry vegetable oil 40%
Gelling agent 1.5%.
In the present embodiment, make by oneself in siccative varniss, gelling agent is alkyl aluminum.
In the present embodiment, slack wax includes the component of following weight percent：
Fischer-Tropsch wax 40%
Vegetable oil 60%.
A kind of preparation method of above-mentioned rub resistance oil polish, it includes the following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are thrown
Enter blender, mixing 6min is first mixed slowly at 55 DEG C, is then warming up to 215 DEG C again, nitrogen, then high speed are filled with toward blender
It is stirred 65min, obtains the first mixture, is then cooled to 30 DEG C, the gelling agent of formula ratio is added into the first mixture,
It is uniformly mixed, obtains self-control siccative varniss；
Wherein, the speed mixed slowly is 250rpm, and the speed of the high-speed stirred is 950rpm；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2 by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and is done
Drying prescription is uniformly mixed, and obtains rub resistance oil polish.
A kind of rub resistance oil polish of the present embodiment has the advantages that rapid draing after printing, when so as to shorten production
Between, improve production efficiency.The ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, can
Effectively reduce the frictional force that is subject to of printing ink pellet surface so that though printed article in the transportational process of long range, printed article it
Between friction is small, so as to effectively prevent the case where printed article is easy friction scumming, and then printed article can be improved
Quality avoids the generation of the important problems such as the return of goods, claim.
Embodiment 5.
A kind of rub resistance oil polish, it includes the component of following weight percent：
Make siccative varniss 60% by oneself
Alkyd resin 10%
Slack wax 8%
PE waxes 10%
Microwax 2%
Mineral oil 8%
Drier 2%；
In the present embodiment, self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 34%
Semi-drying vegetable oils 10%
Dry vegetable oil 55%
Gelling agent 1%.
In the present embodiment, make by oneself in siccative varniss, gelling agent is alkyl aluminum.
In the present embodiment, slack wax includes the component of following weight percent：
Fischer-Tropsch wax 60%
Vegetable oil 40%.
A kind of preparation method of above-mentioned rub resistance oil polish, it includes the following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are thrown
Enter blender, mixing 4min is first mixed slowly at 65 DEG C, is then warming up to 225 DEG C again, nitrogen, then high speed are filled with toward blender
It is stirred 55min, obtains the first mixture, is then cooled to 50 DEG C, the gelling agent of formula ratio is added into the first mixture,
It is uniformly mixed, obtains self-control siccative varniss；
Wherein, the speed mixed slowly is 350rpm, and the speed of the high-speed stirred is 1050rpm；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2 by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and is done
Drying prescription is uniformly mixed, and obtains rub resistance oil polish.
A kind of rub resistance oil polish of the present embodiment has the advantages that rapid draing after printing, when so as to shorten production
Between, improve production efficiency.The ink conjunctiva that the rub resistance oil polish is formed after printing ink dry tack free is more smooth, can
Effectively reduce the frictional force that is subject to of printing ink pellet surface so that though printed article in the transportational process of long range, printed article it
Between friction is small, so as to effectively prevent the case where printed article is easy friction scumming, and then printed article can be improved
Quality avoids the generation of the important problems such as the return of goods, claim.
Performance test：
By above-described embodiment 1 to embodiment 5, rub resistance oil polish obtained carries out test crocking resistance, drying property respectively
Energy and glossiness, and compared with the oil polish of the prior art, test data is shown in Table 1.
The performance test table of rub resistance oil polish made from 1 embodiment 1 of table to the difference of embodiment 5
| Test event | Prior art oil polish | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
| Learn vibration shape rub resistance (swinging up and down) | 3 grades | 4 grades | 4.5 grade | 5 grades | 4.8 grade | 4.5 grade |
| Swing abrasion resistance（It swings） | 3 grades | 5 grades | 5 grades | 5 grades | 5 grades | 5 grades |
| Vibration-type abrasion resistance | 3 grades | 5 grades | 5 grades | 5 grades | 5 grades | 5 grades |
| Drying time（h） | 8.6 | 4.2 | 4.0 | 4.0 | 4.1 | 4.1 |
| The just dry time (min) | 28 | 13 | 10 | 11 | 11 | 10 |
| Glossiness | 73 | 74 | 75 | 75 | 74 | 76 |
Wherein, it is to make to learn vibration shape abrasion-resistant tester measurement, test by Japan to learn vibration shape rub resistance (swinging up and down)
Condition is：Back and forth, as a result rank judges 500g/10：（Difference）1-3-5 (excellent).
Wherein, swing abrasion resistance（It swings）It is to be measured by swing abrasion-resistant tester, test condition is：
4 pounds/50 back and forth, and as a result rank judges：（Difference）1-3-5 (excellent).
Wherein, vibration-type abrasion resistance is measured by vibration-type abrasion-resistant tester, and as a result rank judges：（Difference）1-3-
5 (excellent).
Wherein, drying time is to dry analyzer by Japan's swinging to measure, and test condition is：Temperature：It is 25 DEG C, wet
Degree 50%.
Wherein, just the dry time is measured by the automatic just dry analyzer of Japan's system.
Wherein, glossiness is measured by WGG-60E4 Grossmeters.
The data tested by table 1 are it is found that rub resistance oil polish produced by the present invention has good crocking resistance, preferably
Glossiness, and have the advantages that printing after rapid draing, so as to shorten the production time, improve production efficiency.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of range is protected, although being explained in detail to the present invention with reference to preferred embodiment, those skilled in the art answer
Work as understanding, technical scheme of the present invention can be modified or replaced equivalently, without departing from the reality of technical solution of the present invention
Matter and range.
Claims (9)
1. a kind of rub resistance oil polish, it is characterised in that：It includes the component of following weight percent：
Make siccative varniss 45% ~ 80% by oneself
Alkyd resin 1% ~ 10%
Slack wax 5% ~ 15%
PE waxes 5%~15%
Microwax 1%~4%
Mineral oil 5%~20%
Drier 2%~5%；
The self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 30%~45%
Semi-drying vegetable oils 10%~20%
Dry vegetable oil 40%~55%
Gelling agent 0.5%~2%.
2. a kind of rub resistance oil polish according to claim 1, it is characterised in that：The slack wax includes following weight percent
The component of ratio：
Fischer-Tropsch wax 35%~65%
Vegetable oil 35%~65%.
3. a kind of rub resistance oil polish according to claim 1, it is characterised in that：In the self-control siccative varniss, institute
It is alkyl aluminum to state gelling agent.
4. a kind of rub resistance oil polish according to claim 1, it is characterised in that：It includes the group of following weight percent
Part：
Make siccative varniss 45% ~ 70% by oneself
Alkyd resin 1% ~ 7%
Slack wax 5% ~ 12%
PE waxes 8%~15%
Microwax 1%~4%
Mineral oil 10%~20%
Drier 2%~5%；
The self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 30%~40%
Semi-drying vegetable oils 15%~20%
Dry vegetable oil 40%~50%
Gelling agent 0.5%~2%.
5. a kind of rub resistance oil polish according to claim 1, it is characterised in that：It includes the group of following weight percent
Part：
Make siccative varniss 55% by oneself
Alkyd resin 5%
Slack wax 10%
PE waxes 15%
Microwax 2%
Mineral oil 10%
Drier 3%；
The self-control siccative varniss includes the component of following weight percent：
Modified rosin resin 40%
Semi-drying vegetable oils 15%
Dry vegetable oil 44%
Gelling agent 1%.
6. a kind of rub resistance oil polish according to claim 2, it is characterised in that：The slack wax includes following weight percent
The component of ratio：
Fischer-Tropsch wax 40%~60%
Vegetable oil 40%~60%.
7. a kind of rub resistance oil polish according to claim 2, it is characterised in that：The slack wax includes following weight percent
The component of ratio：
Fischer-Tropsch wax 50%
Vegetable oil 50%.
8. a kind of preparation method of rub resistance oil polish described in claim 1 to 7 any one, it is characterised in that：It includes
Following steps：
Step 1 prepares self-control siccative varniss and slack wax：
Prepare self-control siccative varniss：Modified rosin resin, semi-drying vegetable oils and the dry vegetable oil input of formula ratio are stirred
Device is mixed, is uniformly mixed, obtains the first mixture, the gelling agent of formula ratio is then added into the first mixture, is stirred
It is even, obtain self-control siccative varniss；
Prepare slack wax：The Fischer-Tropsch wax of formula ratio and vegetable oil are uniformly mixed, slack wax is obtained；
Step 2, by the self-control siccative varniss of formula ratio, alkyd resin, slack wax, PE waxes, microwax, mineral oil and drier
It is uniformly mixed, obtains rub resistance oil polish.
9. a kind of preparation method of rub resistance oil polish according to claim 8, it is characterised in that：It is prepared by the step 1
Make siccative varniss by oneself：The modified rosin resin, semi-drying vegetable oils and dry vegetable oil of formula ratio are put into blender, 50
DEG C ~ 70 DEG C at first mix slowly mixing 3min ~ 7min, be then warming up to 210 DEG C ~ 230 DEG C again, be filled with nitrogen toward blender, then
High-speed stirred mixes 50min ~ 70min, obtains the first mixture, is then cooled to 30 DEG C ~ 100 DEG C, adds into the first mixture
The gelling agent for entering formula ratio, is uniformly mixed, and obtains self-control siccative varniss；
Wherein, the speed mixed slowly is 200rpm ~ 400rpm, the speed of the high-speed stirred be 900rpm ~
1100rpm。