CN107266998A - 一种环保型路面防滑涂料 - Google Patents

一种环保型路面防滑涂料 Download PDF

Info

Publication number
CN107266998A
CN107266998A CN201611204302.6A CN201611204302A CN107266998A CN 107266998 A CN107266998 A CN 107266998A CN 201611204302 A CN201611204302 A CN 201611204302A CN 107266998 A CN107266998 A CN 107266998A
Authority
CN
China
Prior art keywords
parts
environment
friendly type
type pavement
pavement antiskid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611204302.6A
Other languages
English (en)
Inventor
兰细平
柳湘平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huizhou Xinxing Coating Chemical Co Ltd
Original Assignee
Huizhou Xinxing Coating Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huizhou Xinxing Coating Chemical Co Ltd filed Critical Huizhou Xinxing Coating Chemical Co Ltd
Priority to CN201611204302.6A priority Critical patent/CN107266998A/zh
Publication of CN107266998A publication Critical patent/CN107266998A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保型路面防滑涂料。本发明的环保型路面防滑涂料包括以下质量配比的组分组成：水性丙烯酸树脂50‑100份、二甲苯15‑35份、苯乙烯化苯酚4‑10份、固化剂10‑24份、邻苯二甲酸二辛酯10‑20份、骨料80‑180份。本发明的环保型路面防滑涂料结合强度高，防滑性、耐磨性能突出，采用环保材料降低环境污染。

Description

一种环保型路面防滑涂料
技术领域
本发明属于化工涂料技术领域，具体是一种环保型路面防滑涂料。
背景技术
在一些城市道路、机场、港口、厂矿、学校等地区，需要涂铺的防滑标线或设置具有防滑作用的路面，以提高安全性。现有的路面防滑涂料，存在容易结块或干燥时间较长、耐磨性较差的不足。
发明内容
本发明的目的是提供一种环保型路面防滑涂料。
本发明的技术方案如下：一种环保型路面防滑涂料，由以下质量配比的组分组成：水性丙烯酸树脂50-100份、二甲苯15-35份、苯乙烯化苯酚4-10份、固化剂10-24份、邻苯二甲酸二辛酯10-20份、骨料80-180份。
优选的，所述环保型路面防滑涂料质量配比的组成，包括以下质量配比的组分：水性丙烯酸树脂70份、二甲苯25份、苯乙烯化苯酚6份、固化剂18份、邻苯二甲酸二辛酯15份、骨料90份。
优选的，所述环保型路面防滑涂料质量配比的组成，包括以下质量配比的组分：水性丙烯酸树脂85份、二甲苯16份、苯乙烯化苯酚10份、固化剂12份、邻苯二甲酸二辛酯17份、骨料110份。
优选的，所述环保型路面防滑涂料质量配比的组成，包括以下质量配比的组分：水性丙烯酸树脂90份、二甲苯33份、苯乙烯化苯酚4份、固化剂20份、邻苯二甲酸二辛酯14份、骨料138份。
进一步的，所述骨料为将废橡胶回收再处理制备得到的废橡胶纳米颗粒骨料。
更进一步的，所述固化剂是以烯丙基缩水甘油醚改性三乙撑甲胺得到的固化剂或常用胺类固化剂。
本发明环保型路面防滑涂料本发明的环保型路面防滑涂料结合强度高、防滑性能好、耐磨性能突出，采用环保材料降低环境污染。
具体实施方式
下面通过实施例对本发明做进一步详细说明，这些实施例仅用来说明本发明，并不限制本发明的范围。
实施例1 一种环保型路面防滑涂料，由以下质量配比的组分组成：水性丙烯酸树脂70份、二甲苯25份、苯乙烯化苯酚6份、以烯丙基缩水甘油醚改性三乙撑甲胺得到的固化剂18份、邻苯二甲酸二辛酯15份、废橡胶纳米颗粒骨料90份、溶剂（水、醇）28份。
实施例2 一种环保型路面防滑涂料，由以下质量配比的组分组成：水性丙烯酸树脂85份、二甲苯16份、苯乙烯化苯酚10份、以烯丙基缩水甘油醚改性三乙撑甲胺得到的固化剂12份、邻苯二甲酸二辛酯17份、铝矾土颗粒骨料80份、废橡胶纳米颗粒骨料110份。
实施例3 一种环保型路面防滑涂料，由以下质量配比的组分组成：水性丙烯酸树脂90份、二甲苯33份、苯乙烯化苯酚4份、改性芳香胺固化剂20份、邻苯二甲酸二辛酯14份、废橡胶纳米颗粒骨料138份。

Claims (6)

1.一种环保型路面防滑涂料，其特征在于：包括以下质量配比的组分：水性丙烯酸树脂50-100份、二甲苯15-35份、苯乙烯化苯酚4-10份、固化剂10-24份、邻苯二甲酸二辛酯10-20份、骨料80-180份。
2.根据权利要求1所述的环保型路面防滑涂料，其特征在于：包括以下质量配比的组分：水性丙烯酸树脂70份、二甲苯25份、苯乙烯化苯酚6份、固化剂18份、邻苯二甲酸二辛酯15份、骨料90份。
3.根据权利要求1所述的环保型路面防滑涂料，其特征在于：包括以下质量配比的组分： 水性丙烯酸树脂85份、二甲苯16份、苯乙烯化苯酚10份、固化剂12份、邻苯二甲酸二辛酯17份、骨料110份。
4.根据权利要求1所述的环保型路面防滑涂料，其特征在于：包括以下质量配比的组分：水性丙烯酸树脂90份、二甲苯33份、苯乙烯化苯酚4份、固化剂20份、邻苯二甲酸二辛酯14份、骨料138份。
5.根据权利要求1-4任一项所述的环保型路面防滑涂料，其特征在于：骨料为废橡胶纳米颗粒骨料。
6.根据权利要求1-4任一项所述的环保型路面防滑涂料，其特征在于：所述固化剂是以烯丙基缩水甘油醚改性三乙撑甲胺得到的固化剂。
CN201611204302.6A 2016-12-23 2016-12-23 一种环保型路面防滑涂料 Pending CN107266998A (zh)