CN107266924A - Antiskid insulation rubber covers and preparation method and the rocking arm condenser discharge welder using gum cover - Google Patents
Antiskid insulation rubber covers and preparation method and the rocking arm condenser discharge welder using gum cover Download PDFInfo
- Publication number
- CN107266924A CN107266924A CN201710640387.0A CN201710640387A CN107266924A CN 107266924 A CN107266924 A CN 107266924A CN 201710640387 A CN201710640387 A CN 201710640387A CN 107266924 A CN107266924 A CN 107266924A
- Authority
- CN
- China
- Prior art keywords
- parts
- rocking arm
- gum cover
- fiber net
- workbench
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to a kind of antiskid insulation rubber set and preparation method and the rocking arm condenser discharge welder using gum cover；Including workbench, the top of workbench is provided with the first rocking arm and the first clamping seat, and the top of the first rocking arm is connected with one end of the second rocking arm, the other end of second rocking arm is provided with supporting plate, supporting plate is provided with handle provided with electric welding head, the outside of supporting plate, and the outer cover of handle is equipped with antiskid insulation rubber set；The bottom of the workbench is provided with rotating seat；The side on workbench top is connected by hinged seat with the first rocking arm, is provided with the first retractor device on the first clamping seat of workbench top opposite side, the telescopic end of the first retractor device is connected with the first U-shaped crotch that the first rocking arm middle and lower part is set；Second clamping seat of the middle and upper part of first rocking arm provided with the retractor device of band second, the telescopic end of the second retractor device is connected with the second U-shaped crotch that the second rocking arm middle and lower part is set；Have the advantages that high temperature resistant, insulation and frictional force are big.
Description
Technical field
The invention belongs to electric welding machine technical field, and in particular to a kind of antiskid insulation rubber set of corrosion resistance and good and preparation
Method and the rocking arm condenser discharge welder using gum cover.
Background technology
Welded steel structure part is widely used in the shell of various plant equipment, cover plate, beam etc., and steel plate completes assembled spot welding
Afterwards, it is necessary to formally be welded, during welding, workpiece generally requires to arrange one by one, and region when so welding also increases therewith, often
Often need from one of platform to carry welder head to other end, the speed so welded will be very slow, carries to carry work
Intensity is also very high, and the consumption of the consumable accessory such as welder head and insulation sleeve, protection mouth, ignition tip is also very big.Moreover, wire feed
Machine, welding cable are all on ground, if placed more structural member to be welded in welding region, then welder must pull welding electricity
Cable gets around other workpiece, in addition it is also necessary to note cable avoid firm welding zone domain, one do not look cable broken thing scalded by high temperature weld seam
Happen occasionally, the distance that cable walks around sometimes also have to go to move wire-feed motor, wire-feed motor weight equipped with dishful welding wire
It is heavier, usually also need to drive a vehicle and moved to coordinate to remove, it is seen that welding changes a little cumbersome and time consuming, it is also possible to cause to a whole set of wire feed line
The damage consumption on road.
Technical scheme disclosed in a kind of location structure of rocker-arm movement electric welding head head of Publication No. 203390425 is
Through being solved to above mentioned problem, still, the technical scheme of the patent, which remains unchanged, to be had the following disadvantages：Due to being provided with support frame,
Cause when in use, and machine can not rotate adjustment position, therefore, be merely able to that the welding object in a direction weld to add
Work, its limitation is larger, be unfavorable for rapid welding processing, further, since welding and its for electric welding head, user operation when
Electric welding head is approached, the fenders such as gum cover are easily safe to the human body to be damaged without being provided with.
The content of the invention
The purpose of the present invention be that provided to solve the above problems it is a kind of it is easy to use, can 360 ° of rotations when using
Turn, and by rocking arm can convenient use person adjust station, welding article is carried out rapid welding its gum cover have high temperature resistant,
Insulation and frictional force big antiskid insulation rubber set and preparation method and the rocking arm condenser discharge welder using gum cover.
The present invention is achieved through the following technical solutions above-mentioned purpose：
(1) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 40-
56 parts, 35-47 parts of silicon rubber, 34-42 parts of phenolic resin, 30-40 parts of ethylene propylene diene rubber, cresyl diphenyl phosphoester 37-
41 parts, 16-28 parts of chlorinated paraffin, 30-50 parts of asbestos fibre, 14-18 parts of zinc oxide, 13-17 parts of magnesia, blanc fixe 20-
36 parts, 26-38 parts of bamboo charcoal powder, N ' -8-10 parts of a penylene BMI vulcanizing agent, 6-8 parts of stannous chloride accelerator, trichlorine
Change 10-14 parts of 4-6 parts of iron accelerator, 4-6 parts of silane coupler and platinum complex catalyst.
(2) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 56
Part, 35 parts of silicon rubber, 34 parts of phenolic resin, 30 parts of ethylene propylene diene rubber, 37 parts of cresyl diphenyl phosphoester, chlorinated paraffin 16
Part, 30 parts of asbestos fibre, 14 parts of zinc oxide, 13 parts of magnesia, 20 parts of blanc fixe, 26 parts of bamboo charcoal powder, N '-a penylene span come
8 parts of acid imide vulcanizing agent, 6 parts of stannous chloride accelerator, 4 parts of ferric trichloride accelerator, 4 parts of silane coupler and platinum complex are urged
10 parts of agent.
(3) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 40
Part, 47 parts of silicon rubber, 42 parts of phenolic resin, 40 parts of ethylene propylene diene rubber, 41 parts of cresyl diphenyl phosphoester, chlorinated paraffin 28
Part, 50 parts of asbestos fibre, 18 parts of zinc oxide, 17 parts of magnesia, 36 parts of blanc fixe, 38 parts of bamboo charcoal powder, N '-a penylene span come
10 parts of acid imide vulcanizing agent, 8 parts of stannous chloride accelerator, 6 parts of ferric trichloride accelerator, 6 parts of silane coupler and platinum complex
14 parts of catalyst.
(4) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 48
Part, 41 parts of silicon rubber, 38 parts of phenolic resin, 35 parts of ethylene propylene diene rubber, 39 parts of cresyl diphenyl phosphoester, chlorinated paraffin 22
Part, 40 parts of asbestos fibre, 16 parts of zinc oxide, 15 parts of magnesia, 28 parts of blanc fixe, 32 parts of bamboo charcoal powder, N '-a penylene span come
9 parts of acid imide vulcanizing agent, 7 parts of stannous chloride accelerator, 5 parts of ferric trichloride accelerator, 5 parts of silane coupler and platinum complex are urged
12 parts of agent.
A kind of preparation method of antiskid insulation rubber set, comprises the following steps：
1) thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorine are taken
Fossil waxes are added in reactor, by the way that reactor is heated into 180-220 DEG C, while stirred 3 hours with 50r/pm speed,
So that thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorinated paraffin by
To after high-temperature heating, mixed glue solution is made in melting, standby；
2) take zinc oxide, magnesia, blanc fixe and bamboo charcoal powder to carry out grinding 3 times repeatedly by grinder, powder is made
The filler of shape, then use the screen cloth of 50 mesh that powdered filler sub-sieve is removed into coarse grain, the mixed-powder below 50 mesh is collected, so
Obtained mixed-powder is added in mixer afterwards and water is added, the weight ratio of mixed-powder weight and water weight is 1:2, open
Dynamic mixer is rotated with 60r/pm rotating speed, and mixed-powder is mixed with water, and slurries are made, standby；
3) by step 1) made from mixed glue solution, step 2) made from slurries and take a N '-penylene BMI
Vulcanizing agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are added to banbury
It is interior, then drive banbury inversely to plasticate, the temperature for controlling banbury is 200-220 DEG C, the rotating speed of banbury is 25r/pm, warp
Cross high temperature to refine 30 minutes so that mixed glue solution is well mixed with slurries, while the additive added is modified to glue,
Mixing glue is made, it is standby；
4) by asbestos fibre according to part by weight 3:4:3 be respectively classified into first part of asbestos fibre, second part of asbestos fibre and
3rd part of asbestos fibre, braider is passed through by first part of asbestos fibre, second part of asbestos fibre and the 3rd part of asbestos fibre respectively
It is woven into bottom fiber net, mean fiber net and surface layer web, and by obtained bottom fiber net, mean fiber net and surface layer
Web is transported on injection moulding machine and deposited, standby；
5) by step 3) the obtained mixing glue of banbury be transported in injection machine, and by standby bottom fiber net,
Mean fiber net and surface layer web are rolled into tubular successively, and bottom fiber net is located at the inner ring of mean fiber net, mean fiber net
Between the inner ring of surface layer web, three layers of web at intervals of 5mm, and be placed in mould, be then injected into mixed
After refining glue liquid covering bottom fiber net, mean fiber net and surface layer web, glue cooling and solidifying to be mixed, it is made and contains three layers
The gum cover blank of fiber, it is standby；
6) by step 5) made from gum cover blank take out, by skin grinder on gum cover blank surface frosted process, enhancing
The roughness on gum cover surface, it is standby；
7) by step 6) in the good gum cover of working process be enclosed on handle, you can.
A kind of rocking arm condenser discharge welder of use gum cover, including workbench, the top of workbench are provided with the first rocking arm and first
Clamping seat, the top of the first rocking arm is connected with one end of the second rocking arm, and the other end of the second rocking arm is provided with supporting plate, and supporting plate is provided with
Head is welded, the outside of supporting plate is provided with handle, and the outer cover of handle is equipped with using anti-skidding exhausted described in any one of above-mentioned (one)-(four)
Edge gum cover；The bottom of the workbench is provided with rotating seat；The side on the workbench top passes through hinged seat and the first rocking arm
Be connected, the first retractor device be installed on the first clamping of workbench top opposite side seat, the telescopic end of the first retractor device with
The first U-shaped crotch that first rocking arm middle and lower part is set is connected；The middle and upper part of first rocking arm is provided with the retractor device of band second
Second clamping seat, the telescopic end of the second retractor device is connected with the second U-shaped crotch that the second rocking arm middle and lower part is set；Described second
The other end of rocking arm is connected by connecting seat with supporting plate.
Preferably, described rotating seat includes base, and the top of base is connected by thrust bearing with spill spin block, spill spin block
Upper surface sidepiece be provided with the first bearing pin for being connected with workbench.
Preferably, the first described retractor device and the second retractor device pass through each corresponding magnetic valve and storage respectively
Gas tank is connected, and magnetic valve is connected with programmable PLC controller.
Preferably, the top of the first described rocking arm is the cylindrical-shaped structure being folded upward at, and cylindrical-shaped structure is sleeved on U-shaped
Inside the through hole of fixture, U-shaped fixture is connected with one end of the second rocking arm.
Preferably, described U-shaped fixture includes offering in U-shaped fixture body, the closed end of U-shaped fixture body
Through hole, the openend both sides of U-shaped fixture body are respectively equipped between pinned hole, the openend of U-shaped fixture body internal set
There is one end of the second rocking arm, the openend of U-shaped fixture body is connected with one end of the second rocking arm by the second bearing pin.
The invention has the advantages that：Heretofore described workbench bottom is provided with rotating seat, can be when in use
By rotating adjustment direction, and the first rocking arm and the second rocking arm are fixed by being provided with retractor device, are conducive to it to make
With stable, its gum cover by thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester,
Chlorinated paraffin, asbestos fibre, zinc oxide, magnesia, blanc fixe, bamboo charcoal powder, N '-a penylene BMI vulcanizing agent,
Stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are made by the above method, have
High temperature resistant, insulation and the big advantage of frictional force.
Brief description of the drawings
Fig. 1 is structural representation of the invention.
Fig. 2 is the schematic diagram of rotating seat of the present invention.
Fig. 3 is the schematic diagram of U-shaped fixture of the present invention.
Embodiment
In order to which technical characteristic, purpose and effect to the present invention are more clearly understood from, now control illustrates this hair
Bright embodiment, in the various figures identical label represent identical part.It is only schematic in simplified form, each figure to make
Ground indicates the part related to invention, and they do not represent it as the practical structures of product.
The present invention covers and preparation method and the rocking arm condenser discharge welder using gum cover for antiskid insulation rubber；The rocking arm condenser discharge welder
Including antiskid insulation rubber set 331, wherein, antiskid insulation rubber set includes：
(1) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 40-
56 parts, 35-47 parts of silicon rubber, 34-42 parts of phenolic resin, 30-40 parts of ethylene propylene diene rubber, cresyl diphenyl phosphoester 37-
41 parts, 16-28 parts of chlorinated paraffin, 30-50 parts of asbestos fibre, 14-18 parts of zinc oxide, 13-17 parts of magnesia, blanc fixe 20-
36 parts, 26-38 parts of bamboo charcoal powder, N ' -8-10 parts of a penylene BMI vulcanizing agent, 6-8 parts of stannous chloride accelerator, trichlorine
Change 10-14 parts of 4-6 parts of iron accelerator, 4-6 parts of silane coupler and platinum complex catalyst.
(2) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 56
Part, 35 parts of silicon rubber, 34 parts of phenolic resin, 30 parts of ethylene propylene diene rubber, 37 parts of cresyl diphenyl phosphoester, chlorinated paraffin 16
Part, 30 parts of asbestos fibre, 14 parts of zinc oxide, 13 parts of magnesia, 20 parts of blanc fixe, 26 parts of bamboo charcoal powder, N '-a penylene span come
8 parts of acid imide vulcanizing agent, 6 parts of stannous chloride accelerator, 4 parts of ferric trichloride accelerator, 4 parts of silane coupler and platinum complex are urged
10 parts of agent.
(3) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 40
Part, 47 parts of silicon rubber, 42 parts of phenolic resin, 40 parts of ethylene propylene diene rubber, 41 parts of cresyl diphenyl phosphoester, chlorinated paraffin 28
Part, 50 parts of asbestos fibre, 18 parts of zinc oxide, 17 parts of magnesia, 36 parts of blanc fixe, 38 parts of bamboo charcoal powder, N '-a penylene span come
10 parts of acid imide vulcanizing agent, 8 parts of stannous chloride accelerator, 6 parts of ferric trichloride accelerator, 6 parts of silane coupler and platinum complex
14 parts of catalyst.
(4) a kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：Thermoplastic elastomer (TPE) 48
Part, 41 parts of silicon rubber, 38 parts of phenolic resin, 35 parts of ethylene propylene diene rubber, 39 parts of cresyl diphenyl phosphoester, chlorinated paraffin 22
Part, 40 parts of asbestos fibre, 16 parts of zinc oxide, 15 parts of magnesia, 28 parts of blanc fixe, 32 parts of bamboo charcoal powder, N '-a penylene span come
9 parts of acid imide vulcanizing agent, 7 parts of stannous chloride accelerator, 5 parts of ferric trichloride accelerator, 5 parts of silane coupler and platinum complex are urged
12 parts of agent.
A kind of preparation method of antiskid insulation rubber set, comprises the following steps：
1) thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorine are taken
Fossil waxes are added in reactor, by the way that reactor is heated into 180-220 DEG C, while stirred 3 hours with 50r/pm speed,
So that thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorinated paraffin by
To after high-temperature heating, mixed glue solution is made in melting, standby；
2) take zinc oxide, magnesia, blanc fixe and bamboo charcoal powder to carry out grinding 3 times repeatedly by grinder, powder is made
The filler of shape, then use the screen cloth of 50 mesh that powdered filler sub-sieve is removed into coarse grain, the mixed-powder below 50 mesh is collected, so
Obtained mixed-powder is added in mixer afterwards and water is added, the weight ratio of mixed-powder weight and water weight is 1:2, open
Dynamic mixer is rotated with 60r/pm rotating speed, and mixed-powder is mixed with water, and slurries are made, standby；
3) by step 1) made from mixed glue solution, step 2) made from slurries and take a N '-penylene BMI
Vulcanizing agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are added to banbury
It is interior, then drive banbury inversely to plasticate, the temperature for controlling banbury is 200-220 DEG C, the rotating speed of banbury is 25r/pm, warp
Cross high temperature to refine 30 minutes so that mixed glue solution is well mixed with slurries, while the additive added is modified to glue,
Mixing glue is made, it is standby；
4) by asbestos fibre according to part by weight 3:4:3 be respectively classified into first part of asbestos fibre, second part of asbestos fibre and
3rd part of asbestos fibre, braider is passed through by first part of asbestos fibre, second part of asbestos fibre and the 3rd part of asbestos fibre respectively
It is woven into bottom fiber net, mean fiber net and surface layer web, and by obtained bottom fiber net, mean fiber net and surface layer
Web is transported on injection moulding machine and deposited, standby；
5) by step 3) the obtained mixing glue of banbury be transported in injection machine, and by standby bottom fiber net,
Mean fiber net and surface layer web are rolled into tubular successively, and bottom fiber net is located at the inner ring of mean fiber net, mean fiber net
Between the inner ring of surface layer web, three layers of web at intervals of 5mm, and be placed in mould, be then injected into mixed
After refining glue liquid covering bottom fiber net, mean fiber net and surface layer web, glue cooling and solidifying to be mixed, it is made and contains three layers
The gum cover blank of fiber, it is standby；
6) by step 5) made from gum cover blank take out, by skin grinder on gum cover blank surface frosted process, enhancing
The roughness on gum cover surface, it is standby；
7) by step 6) in the good gum cover of working process be enclosed on handle, you can.
As shown in Figure 1, 2, 3, a kind of rocking arm condenser discharge welder of use gum cover, including workbench 1, the top of workbench 1 is set
Have the first rocking arm 2 and the first clamping seat 14, the top of the first rocking arm 2 is connected with one end of the second rocking arm 3, the second rocking arm 3 it is another
One end is provided with supporting plate 31, and supporting plate 31 is provided with handle 33 provided with electric welding first 4, the outside of supporting plate 31, and the outer cover of handle 33 is equipped with
Use the antiskid insulation rubber set 331 described in any one of above-mentioned (one)-(four)；The bottom of the workbench 1 is provided with rotating seat 6；
The side on the top of workbench 1 is connected by hinged seat 12 with the first rocking arm 2, the first clamping of the top opposite side of workbench 1
First retractor device 13, the first U that the telescopic end of the first retractor device 13 and the middle and lower part of the first rocking arm 2 are set are installed on seat 14
Shape crotch 24 is connected；Second clamping seat 22 of the middle and upper part of first rocking arm 2 provided with the second retractor device of band 21, second stretches
The telescopic end of device 21 is connected with the second U-shaped crotch 34 that the middle and lower part of the second rocking arm 3 is set；The other end of second rocking arm 3
It is connected by connecting seat 32 with supporting plate 31.Described rotating seat 6 includes base 61, the top of base 61 by thrust bearing 62 with
Spill spin block 63 is connected, and the upper surface sidepiece of spill spin block 63 is provided with the first bearing pin 64 being connected with workbench 1.Described first stretches
The retractor device 21 of device 13 and second is connected by each corresponding magnetic valve 8 with air accumulator 7 respectively, and magnetic valve 8 is with that can compile
Journey PLC 5 is connected.The top of the first described rocking arm 2 is the cylindrical-shaped structure being folded upward at, and cylindrical-shaped structure is sleeved on
Inside the through hole 232 of U-shaped fixture 23, U-shaped fixture 23 is connected with one end of the second rocking arm 3.Described U-shaped fixture includes
Offer through hole 232 in U-shaped fixture body 231, the closed end of U-shaped fixture body 231, U-shaped fixture body 231 is opened
Mouth end both sides are respectively equipped with inside between pinned hole 233, the openend of U-shaped fixture body 231 and are provided with the one of the second rocking arm 3
End, the openend of U-shaped fixture body 231 is connected with one end of the second rocking arm 3 by the second bearing pin 234.
The present invention is including workbench 1 and is arranged on for the first rocking arm 2 for carrying out first time position adjustment on workbench 1,
And be arranged on and be used for the second rocking arm 3 for carrying out second of position adjustment on the first rocking arm 2, and be arranged on the second rocking arm 3 and be used for
The electric welding first 4 of object is welded, and is arranged on the PLC that the outside of workbench 1 is used to control the first rocking arm 2 and the second rocking arm 3
5；The upper right side of workbench 1 is provided with the hinged seat 12 fixed with workbench 1 and for being hinged the first rocking arm 2, the bottom of workbench 1
It is provided with the rotating seat 6 for rotary table 1 fixed with workbench 1；The rotating seat 6 includes spill spin block 63, and sets
The first bearing pin 64 for being used to be connected with workbench 1 in the avris of spill spin block 63, and it is arranged on being revolved for supporting for the bottom of spill spin block 63
The base 61 of switch block 63, and the thrust bearing 62 that spill spin block 63 rotates that is used for being arranged between base 61 and spill spin block 63；Institute
The upper left side for stating workbench 1 is additionally provided with the first retractor device 13 for being connected to drive the activity of the first rocking arm 2 with workbench 1.
First retractor device 13 is provided with the first clamping seat 14 for being used to fix the first retractor device 13 being connected with workbench 1；
The telescopic end of first retractor device 13 is connected with the first U-shaped crotch 24 that the middle and lower part of the first rocking arm 2 is set, the first flexible dress
Put 13 and second retractor device 21 be telescopic cylinder, it is preferable that the model SC50-25 of telescopic cylinder, the second retractor device
21 structure is consistent with the structure of the first retractor device 13, and the bottom of the second retractor device 21 is provided with the second retractor device of clamping 21
And consolidate for firmly installing to be provided with first rocking arm 2 described in the second clamping seat 22 of the second retractor device 21 with the first rocking arm 2
Fixed the second retractor device 21 for being used to drive the activity of the second rocking arm 3；First rocking arm 2 includes the circle that left end is folded upward at
Post, and the U-shaped fixture 23 for connecting the second rocking arm 3 being arranged on cylinder.The U-shaped fixture 23 is fixed including U-shaped
The through hole that cylinder is folded upward at for the above-mentioned left end that is locked is offered in part body 231, the closed end of U-shaped fixture body 231
232, the openend both sides of U-shaped fixture body 231 are respectively equipped with pinned hole 233, the openend of U-shaped fixture body 231 it
Between be provided with one end of the second rocking arm 3, one end of the openend of U-shaped fixture body 231 and the second rocking arm 3 passes through the second bearing pin
234 are connected；The end of second rocking arm 3 is provided with the supporting plate 31 for support electric welding first 4；The rocking arm of supporting plate 31 and second
One end of 3 connections is provided with connecting seat 32, and one end of the connecting seat 32 is fixed with the second rocking arm 3, and the other end is cut with scissors with supporting plate 31
Connect, the other end of the supporting plate 31, which is provided with the hand-held handle 33 of acclivitous, convenient use person, the handle 33, to be set
Have for anti-skidding and insulation gum cover 331.
In order to more clearly explain the present invention, it is further described in conjunction with specific embodiment.It is specific real
Under applying for example：
Embodiment one
A kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：56 parts of thermoplastic elastomer (TPE), silicon
35 parts of rubber, 34 parts of phenolic resin, 30 parts of ethylene propylene diene rubber, 37 parts of cresyl diphenyl phosphoester, 16 parts of chlorinated paraffin, stone
30 parts of cotton fiber, 14 parts of zinc oxide, 13 parts of magnesia, 20 parts of blanc fixe, 26 parts of bamboo charcoal powder, N '-a penylene bismaleimide
8 parts of amine vulcanizing agent, 6 parts of stannous chloride accelerator, 4 parts of ferric trichloride accelerator, 4 parts of silane coupler and platinum complex catalyst
10 parts.
A kind of preparation method of antiskid insulation rubber set, comprises the following steps：
1) thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorine are taken
Fossil waxes are added in reactor, by the way that reactor is heated into 180-220 DEG C, while stirred 3 hours with 50r/pm speed,
So that thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorinated paraffin by
To after high-temperature heating, mixed glue solution is made in melting, standby；
2) take zinc oxide, magnesia, blanc fixe and bamboo charcoal powder to carry out grinding 3 times repeatedly by grinder, powder is made
The filler of shape, then use the screen cloth of 50 mesh that powdered filler sub-sieve is removed into coarse grain, the mixed-powder below 50 mesh is collected, so
Obtained mixed-powder is added in mixer afterwards and water is added, the weight ratio of mixed-powder weight and water weight is 1:2, open
Dynamic mixer is rotated with 60r/pm rotating speed, and mixed-powder is mixed with water, and slurries are made, standby；
3) by step 1) made from mixed glue solution, step 2) made from slurries and take a N '-penylene BMI
Vulcanizing agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are added to banbury
It is interior, then drive banbury inversely to plasticate, the temperature for controlling banbury is 200-220 DEG C, the rotating speed of banbury is 25r/pm, warp
Cross high temperature to refine 30 minutes so that mixed glue solution is well mixed with slurries, while the additive added is modified to glue,
Mixing glue is made, it is standby；
4) by asbestos fibre according to part by weight 3:4:3 be respectively classified into first part of asbestos fibre, second part of asbestos fibre and
3rd part of asbestos fibre, braider is passed through by first part of asbestos fibre, second part of asbestos fibre and the 3rd part of asbestos fibre respectively
It is woven into bottom fiber net, mean fiber net and surface layer web, and by obtained bottom fiber net, mean fiber net and surface layer
Web is transported on injection moulding machine and deposited, standby；
5) by step 3) the obtained mixing glue of banbury be transported in injection machine, and by standby bottom fiber net,
Mean fiber net and surface layer web are rolled into tubular successively, and bottom fiber net is located at the inner ring of mean fiber net, mean fiber net
Between the inner ring of surface layer web, three layers of web at intervals of 5mm, and be placed in mould, be then injected into mixed
After refining glue liquid covering bottom fiber net, mean fiber net and surface layer web, glue cooling and solidifying to be mixed, it is made and contains three layers
The gum cover blank of fiber, it is standby；
6) by step 5) made from gum cover blank take out, by skin grinder on gum cover blank surface frosted process, enhancing
The roughness on gum cover surface, it is standby；
7) by step 6) in the good gum cover of working process be enclosed on handle, you can.
A kind of rocking arm condenser discharge welder of use gum cover, including workbench 1, the top of workbench 1 is provided with the first rocking arm 2 and the
One clamping seat 14, the top of the first rocking arm 2 is connected with one end of the second rocking arm 3, and the other end of the second rocking arm 3 is provided with supporting plate 31,
Supporting plate 31 is provided with handle 33 provided with electric welding first 4, the outside of supporting plate 31, and the outer cover of handle 33, which is equipped with, uses above-mentioned anti-skidding insulation
Gum cover 331；The bottom of the workbench 1 is provided with rotating seat 6；The side on the top of workbench 1 passes through hinged seat 12 and
One rocking arm 2 is connected, and the first retractor device 13, the first flexible dress are provided with the first clamping seat 14 of the top opposite side of workbench 1
The first U-shaped crotch 24 that the telescopic end and the middle and lower part of the first rocking arm 2 for putting 13 are set is connected；The middle and upper part of first rocking arm 2 is set
There is the second clamping seat 22 of the second retractor device of band 21, the telescopic end of the second retractor device 21 and the middle and lower part of the second rocking arm 3 are set
The second U-shaped crotch 34 be connected；The other end of second rocking arm 3 is connected by connecting seat 32 with supporting plate 31.Described rotation
Seat 6 includes base 61, and the top of base 61 is connected by thrust bearing 62 with spill spin block 63, and the upper surface sidepiece of spill spin block 63 is set
There is the first bearing pin 64 being connected with workbench 1.The first described retractor device 13 and the second retractor device 21 are respectively by respective
Corresponding magnetic valve 8 is connected with air accumulator 7, and magnetic valve 8 is connected with programmable PLC controller 5.The first described rocking arm 2
Top is the cylindrical-shaped structure being folded upward at, and cylindrical-shaped structure is sleeved on inside the through hole 232 of U-shaped fixture 23, U-shaped fixture
23 are connected with one end of the second rocking arm 3.Described U-shaped fixture includes U-shaped fixture body 231, U-shaped fixture body 231
Closed end on offer through hole 232, the openend both sides of U-shaped fixture body 231 are respectively equipped with pinned hole 233, and U-shaped is fixed
Internal one end for being provided with the second rocking arm 3 between the openend of part body 231, the openend of U-shaped fixture body 231 and second is shaken
One end of arm 3 is connected by the second bearing pin 234.
Embodiment two
A kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：40 parts of thermoplastic elastomer (TPE), silicon
47 parts of rubber, 42 parts of phenolic resin, 40 parts of ethylene propylene diene rubber, 41 parts of cresyl diphenyl phosphoester, 28 parts of chlorinated paraffin, stone
50 parts of cotton fiber, 18 parts of zinc oxide, 17 parts of magnesia, 36 parts of blanc fixe, 38 parts of bamboo charcoal powder, N '-a penylene bismaleimide
10 parts of amine vulcanizing agent, 8 parts of stannous chloride accelerator, 6 parts of ferric trichloride accelerator, 6 parts of silane coupler and platinum complex catalysis
14 parts of agent.
A kind of preparation method of antiskid insulation rubber set, comprises the following steps：
1) thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorine are taken
Fossil waxes are added in reactor, by the way that reactor is heated into 180-220 DEG C, while stirred 3 hours with 50r/pm speed,
So that thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorinated paraffin by
To after high-temperature heating, mixed glue solution is made in melting, standby；
2) take zinc oxide, magnesia, blanc fixe and bamboo charcoal powder to carry out grinding 3 times repeatedly by grinder, powder is made
The filler of shape, then use the screen cloth of 50 mesh that powdered filler sub-sieve is removed into coarse grain, the mixed-powder below 50 mesh is collected, so
Obtained mixed-powder is added in mixer afterwards and water is added, the weight ratio of mixed-powder weight and water weight is 1:2, open
Dynamic mixer is rotated with 60r/pm rotating speed, and mixed-powder is mixed with water, and slurries are made, standby；
3) by step 1) made from mixed glue solution, step 2) made from slurries and take a N '-penylene BMI
Vulcanizing agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are added to banbury
It is interior, then drive banbury inversely to plasticate, the temperature for controlling banbury is 200-220 DEG C, the rotating speed of banbury is 25r/pm, warp
Cross high temperature to refine 30 minutes so that mixed glue solution is well mixed with slurries, while the additive added is modified to glue,
Mixing glue is made, it is standby；
4) by asbestos fibre according to part by weight 3:4:3 be respectively classified into first part of asbestos fibre, second part of asbestos fibre and
3rd part of asbestos fibre, braider is passed through by first part of asbestos fibre, second part of asbestos fibre and the 3rd part of asbestos fibre respectively
It is woven into bottom fiber net, mean fiber net and surface layer web, and by obtained bottom fiber net, mean fiber net and surface layer
Web is transported on injection moulding machine and deposited, standby；
5) by step 3) the obtained mixing glue of banbury be transported in injection machine, and by standby bottom fiber net,
Mean fiber net and surface layer web are rolled into tubular successively, and bottom fiber net is located at the inner ring of mean fiber net, mean fiber net
Between the inner ring of surface layer web, three layers of web at intervals of 5mm, and be placed in mould, be then injected into mixed
After refining glue liquid covering bottom fiber net, mean fiber net and surface layer web, glue cooling and solidifying to be mixed, it is made and contains three layers
The gum cover blank of fiber, it is standby；
6) by step 5) made from gum cover blank take out, by skin grinder on gum cover blank surface frosted process, enhancing
The roughness on gum cover surface, it is standby；
7) by step 6) in the good gum cover of working process be enclosed on handle, you can.
A kind of rocking arm condenser discharge welder of use gum cover, including workbench 1, the top of workbench 1 is provided with the first rocking arm 2 and the
One clamping seat 14, the top of the first rocking arm 2 is connected with one end of the second rocking arm 3, and the other end of the second rocking arm 3 is provided with supporting plate 31,
Supporting plate 31 is provided with handle 33 provided with electric welding first 4, the outside of supporting plate 31, and the outer cover of handle 33, which is equipped with, uses above-mentioned anti-skidding insulation
Gum cover 331；The bottom of the workbench 1 is provided with rotating seat 6；The side on the top of workbench 1 passes through hinged seat 12 and
One rocking arm 2 is connected, and the first retractor device 13, the first flexible dress are provided with the first clamping seat 14 of the top opposite side of workbench 1
The first U-shaped crotch 24 that the telescopic end and the middle and lower part of the first rocking arm 2 for putting 13 are set is connected；The middle and upper part of first rocking arm 2 is set
There is the second clamping seat 22 of the second retractor device of band 21, the telescopic end of the second retractor device 21 and the middle and lower part of the second rocking arm 3 are set
The second U-shaped crotch 34 be connected；The other end of second rocking arm 3 is connected by connecting seat 32 with supporting plate 31.Described rotation
Seat 6 includes base 61, and the top of base 61 is connected by thrust bearing 62 with spill spin block 63, and the upper surface sidepiece of spill spin block 63 is set
There is the first bearing pin 64 being connected with workbench 1.The first described retractor device 13 and the second retractor device 21 are respectively by respective
Corresponding magnetic valve 8 is connected with air accumulator 7, and magnetic valve 8 is connected with programmable PLC controller 5.The first described rocking arm 2
Top is the cylindrical-shaped structure being folded upward at, and cylindrical-shaped structure is sleeved on inside the through hole 232 of U-shaped fixture 23, U-shaped fixture
23 are connected with one end of the second rocking arm 3.Described U-shaped fixture includes U-shaped fixture body 231, U-shaped fixture body 231
Closed end on offer through hole 232, the openend both sides of U-shaped fixture body 231 are respectively equipped with pinned hole 233, and U-shaped is fixed
Internal one end for being provided with the second rocking arm 3 between the openend of part body 231, the openend of U-shaped fixture body 231 and second is shaken
One end of arm 3 is connected by the second bearing pin 234.
Embodiment three
A kind of antiskid insulation rubber set, the raw material that the gum cover includes following parts by weight is made：48 parts of thermoplastic elastomer (TPE), silicon
41 parts of rubber, 38 parts of phenolic resin, 35 parts of ethylene propylene diene rubber, 39 parts of cresyl diphenyl phosphoester, 22 parts of chlorinated paraffin, stone
40 parts of cotton fiber, 16 parts of zinc oxide, 15 parts of magnesia, 28 parts of blanc fixe, 32 parts of bamboo charcoal powder, N '-a penylene bismaleimide
9 parts of amine vulcanizing agent, 7 parts of stannous chloride accelerator, 5 parts of ferric trichloride accelerator, 5 parts of silane coupler and platinum complex catalyst
12 parts.
A kind of preparation method of antiskid insulation rubber set, comprises the following steps：
1) thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorine are taken
Fossil waxes are added in reactor, by the way that reactor is heated into 180-220 DEG C, while stirred 3 hours with 50r/pm speed,
So that thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorinated paraffin by
To after high-temperature heating, mixed glue solution is made in melting, standby；
2) take zinc oxide, magnesia, blanc fixe and bamboo charcoal powder to carry out grinding 3 times repeatedly by grinder, powder is made
The filler of shape, then use the screen cloth of 50 mesh that powdered filler sub-sieve is removed into coarse grain, the mixed-powder below 50 mesh is collected, so
Obtained mixed-powder is added in mixer afterwards and water is added, the weight ratio of mixed-powder weight and water weight is 1:2, open
Dynamic mixer is rotated with 60r/pm rotating speed, and mixed-powder is mixed with water, and slurries are made, standby；
3) by step 1) made from mixed glue solution, step 2) made from slurries and take a N '-penylene BMI
Vulcanizing agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are added to banbury
It is interior, then drive banbury inversely to plasticate, the temperature for controlling banbury is 200-220 DEG C, the rotating speed of banbury is 25r/pm, warp
Cross high temperature to refine 30 minutes so that mixed glue solution is well mixed with slurries, while the additive added is modified to glue,
Mixing glue is made, it is standby；
4) by asbestos fibre according to part by weight 3:4:3 be respectively classified into first part of asbestos fibre, second part of asbestos fibre and
3rd part of asbestos fibre, braider is passed through by first part of asbestos fibre, second part of asbestos fibre and the 3rd part of asbestos fibre respectively
It is woven into bottom fiber net, mean fiber net and surface layer web, and by obtained bottom fiber net, mean fiber net and surface layer
Web is transported on injection moulding machine and deposited, standby；
5) by step 3) the obtained mixing glue of banbury be transported in injection machine, and by standby bottom fiber net,
Mean fiber net and surface layer web are rolled into tubular successively, and bottom fiber net is located at the inner ring of mean fiber net, mean fiber net
Between the inner ring of surface layer web, three layers of web at intervals of 5mm, and be placed in mould, be then injected into mixed
After refining glue liquid covering bottom fiber net, mean fiber net and surface layer web, glue cooling and solidifying to be mixed, it is made and contains three layers
The gum cover blank of fiber, it is standby；
6) by step 5) made from gum cover blank take out, by skin grinder on gum cover blank surface frosted process, enhancing
The roughness on gum cover surface, it is standby；
7) by step 6) in the good gum cover of working process be enclosed on handle, you can.
A kind of rocking arm condenser discharge welder of use gum cover, including workbench 1, the top of workbench 1 is provided with the first rocking arm 2 and the
One clamping seat 14, the top of the first rocking arm 2 is connected with one end of the second rocking arm 3, and the other end of the second rocking arm 3 is provided with supporting plate 31,
Supporting plate 31 is provided with handle 33 provided with electric welding first 4, the outside of supporting plate 31, and the outer cover of handle 33, which is equipped with, uses above-mentioned anti-skidding insulation
Gum cover 331；The bottom of the workbench 1 is provided with rotating seat 6；The side on the top of workbench 1 passes through hinged seat 12 and
One rocking arm 2 is connected, and the first retractor device 13, the first flexible dress are provided with the first clamping seat 14 of the top opposite side of workbench 1
The first U-shaped crotch 24 that the telescopic end and the middle and lower part of the first rocking arm 2 for putting 13 are set is connected；The middle and upper part of first rocking arm 2 is set
There is the second clamping seat 22 of the second retractor device of band 21, the telescopic end of the second retractor device 21 and the middle and lower part of the second rocking arm 3 are set
The second U-shaped crotch 34 be connected；The other end of second rocking arm 3 is connected by connecting seat 32 with supporting plate 31.Described rotation
Seat 6 includes base 61, and the top of base 61 is connected by thrust bearing 62 with spill spin block 63, and the upper surface sidepiece of spill spin block 63 is set
There is the first bearing pin 64 being connected with workbench 1.The first described retractor device 13 and the second retractor device 21 are respectively by respective
Corresponding magnetic valve 8 is connected with air accumulator 7, and magnetic valve 8 is connected with programmable PLC controller 5.The first described rocking arm 2
Top is the cylindrical-shaped structure being folded upward at, and cylindrical-shaped structure is sleeved on inside the through hole 232 of U-shaped fixture 23, U-shaped fixture
23 are connected with one end of the second rocking arm 3.Described U-shaped fixture includes U-shaped fixture body 231, U-shaped fixture body 231
Closed end on offer through hole 232, the openend both sides of U-shaped fixture body 231 are respectively equipped with pinned hole 233, and U-shaped is fixed
Internal one end for being provided with the second rocking arm 3 between the openend of part body 231, the openend of U-shaped fixture body 231 and second is shaken
One end of arm 3 is connected by the second bearing pin 234.
Experimental example
Experimental subjects：Using the fine rubber sleeve of common propylene as a control group one, special polytetrafluoroethylene (PTFE) gum cover is as right
According to group two, the gum cover that is made of the embodiment of the present invention one as experimental group.
Requirement of experiment：Above-mentioned control group one, control group two are in the same size with the embodiment of the present invention one.
Experimental method：Carried out by the gum cover to control group one, the gum cover of control group two and the embodiment of the present invention one durable
Degree test, in this experimental example, durability degree test includes shrinkage factor, resistance to elevated temperatures, thermal conductivity and weatherability test.
Table one is the durability degree test result physical record of three groups of gum covers：
With reference to table one, the data as obtained by by three groups of gum covers under identical experimental method, the receipts of the gum cover of experimental group
Shrinkage is less than control group one and control group two, and weatherability, resistance to elevated temperatures are better than control group one and control group two, heat conduction system
Number is significantly lower than control group one and control group two.
The technology of the present invention effect major embodiment is in the following areas：The heretofore described bottom of workbench 1 is provided with rotation
Seat 6, can be when in use by rotating adjustment direction, and the first rocking arm 2 and the second rocking arm 3 are entered by being provided with retractor device
Row is fixed, and is conducive to it using stabilization, its gum cover is by thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, first
Phenolic group diphenyl phosphoester, chlorinated paraffin, asbestos fibre, zinc oxide, magnesia, blanc fixe, bamboo charcoal powder, N '-penylene are double
Maleimide vulcanizing agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst pass through
The above method is made, and has the advantages that high temperature resistant, insulation and frictional force are big.
The basic principles, principal features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, the original for simply illustrating the present invention described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its Xiao Wu circle
It is fixed.
Claims (10)
1. a kind of antiskid insulation rubber set, it is characterised in that：The raw material that the gum cover includes following parts by weight is made：Thermoplastic elastic
40-56 parts of body, 35-47 parts of silicon rubber, 34-42 parts of phenolic resin, 30-40 parts of ethylene propylene diene rubber, cresyl diphenylphosphoric acid
37-41 parts of ester, 16-28 parts of chlorinated paraffin, 30-50 parts of asbestos fibre, 14-18 parts of zinc oxide, 13-17 parts of magnesia, barite
20-36 parts of powder, 26-38 parts of bamboo charcoal powder, N ' -8-10 parts of a penylene BMI vulcanizing agent, stannous chloride accelerator 6-8
10-14 parts of part, 4-6 parts of ferric trichloride accelerator, 4-6 parts of silane coupler and platinum complex catalyst.
2. antiskid insulation rubber set according to claim 1, it is characterised in that：The gum cover includes the raw material of following parts by weight
It is made：56 parts of thermoplastic elastomer (TPE), 35 parts of silicon rubber, 34 parts of phenolic resin, 30 parts of ethylene propylene diene rubber, cresyl diphenylphosphine
37 parts of acid esters, 16 parts of chlorinated paraffin, 30 parts of asbestos fibre, 14 parts of zinc oxide, 13 parts of magnesia, 20 parts of blanc fixe, bamboo charcoal powder
26 parts, N ' -8 parts of a penylene BMI vulcanizing agent, 6 parts of stannous chloride accelerator, 4 parts of ferric trichloride accelerator, silane
10 parts of 4 parts of coupling agent and platinum complex catalyst.
3. antiskid insulation rubber set according to claim 1, it is characterised in that：The gum cover includes the raw material of following parts by weight
It is made：40 parts of thermoplastic elastomer (TPE), 47 parts of silicon rubber, 42 parts of phenolic resin, 40 parts of ethylene propylene diene rubber, cresyl diphenylphosphine
41 parts of acid esters, 28 parts of chlorinated paraffin, 50 parts of asbestos fibre, 18 parts of zinc oxide, 17 parts of magnesia, 36 parts of blanc fixe, bamboo charcoal powder
38 parts, N ' -10 parts of a penylene BMI vulcanizing agent, 8 parts of stannous chloride accelerator, 6 parts of ferric trichloride accelerator, silane
14 parts of 6 parts of coupling agent and platinum complex catalyst.
4. antiskid insulation rubber set according to claim 1, it is characterised in that：The gum cover includes the raw material of following parts by weight
It is made：48 parts of thermoplastic elastomer (TPE), 41 parts of silicon rubber, 38 parts of phenolic resin, 35 parts of ethylene propylene diene rubber, cresyl diphenylphosphine
39 parts of acid esters, 22 parts of chlorinated paraffin, 40 parts of asbestos fibre, 16 parts of zinc oxide, 15 parts of magnesia, 28 parts of blanc fixe, bamboo charcoal powder
32 parts, N ' -9 parts of a penylene BMI vulcanizing agent, 7 parts of stannous chloride accelerator, 5 parts of ferric trichloride accelerator, silane
12 parts of 5 parts of coupling agent and platinum complex catalyst.
5. a kind of preparation method of the set of the antiskid insulation rubber as described in claim any one of 1-4, it is characterised in that：Including following step
Suddenly：
1) thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorination stone are taken
Wax is added in reactor, by the way that reactor is heated into 180-220 DEG C, while being stirred 3 hours with 50r/pm speed so that
Thermoplastic elastomer (TPE), silicon rubber, phenolic resin, ethylene propylene diene rubber, cresyl diphenyl phosphoester and chlorinated paraffin are by height
After temperature heating, mixed glue solution is made in melting, standby；
2) take zinc oxide, magnesia, blanc fixe and bamboo charcoal powder to carry out grinding 3 times repeatedly by grinder, be made powdered
Filler, then use the screen cloth of 50 mesh that powdered filler sub-sieve is removed into coarse grain, the mixed-powder below 50 mesh is collected, then will
Obtained mixed-powder is added in mixer and adds water, and the weight ratio of mixed-powder weight and water weight is 1:2, startup is stirred
Mix machine to rotate with 60r/pm rotating speed, mixed-powder is mixed with water, slurries are made, it is standby；
3) by step 1) made from mixed glue solution, step 2) made from slurries and take N '-penylene BMI vulcanization
Agent, stannous chloride accelerator, ferric trichloride accelerator, silane coupler and platinum complex catalyst are added in banbury, so
Driving banbury is inversely plasticated afterwards, and the temperature for controlling banbury is 200-220 DEG C, and the rotating speed of banbury is 25r/pm, through too high
Temperature refining 30 minutes so that mixed glue solution is well mixed with slurries, while the additive added is modified to glue, is made
Glue is kneaded, it is standby；
4) by asbestos fibre according to part by weight 3:4:3 are respectively classified into first part of asbestos fibre, second part of asbestos fibre and the 3rd
Part asbestos fibre, first part of asbestos fibre, second part of asbestos fibre and the 3rd part of asbestos fibre are woven by braider respectively
Into bottom fiber net, mean fiber net and surface layer web, and by obtained bottom fiber net, mean fiber net and surface layer fiber
Net is transported on injection moulding machine and deposited, standby；
5) by step 3) the obtained mixing glue of banbury be transported in injection machine, and by standby bottom fiber net, middle level
Web and surface layer web are rolled into tubular successively, and bottom fiber net is located at the inner ring of mean fiber net, and mean fiber net is located at
Between the inner ring of surface layer web, three layers of web at intervals of 5mm, and be placed in mould, be then injected into elastomeric compound
After liquid covering bottom fiber net, mean fiber net and surface layer web, glue cooling and solidifying to be mixed, it is made containing three layers of fiber
Gum cover blank, it is standby；
6) by step 5) made from gum cover blank take out, by skin grinder on gum cover blank surface frosted process, strengthen gum cover
The roughness on surface, it is standby；
7) by step 6) in the good gum cover of working process be enclosed on handle, you can.
6. a kind of rocking arm condenser discharge welder of use gum cover, it is characterised in that：Including workbench (1), the top of workbench (1) is provided with
First rocking arm (2) and the first clamping seat (14), the top of the first rocking arm (2) are connected with one end of the second rocking arm (3), the second rocking arm
(3) the other end is provided with supporting plate (31), and supporting plate (31) is provided with handle (33), hand provided with electric welding head (4), the outside of supporting plate (31)
The outer cover of handle (33) requires the antiskid insulation rubber set (331) described in any one of 1-4 equipped with usage right；The workbench (1)
Bottom rotating seat (6) is installed；
The side on workbench (1) top is connected by hinged seat (12) with the first rocking arm (2), and workbench (1) top is another
The first retractor device (13), the telescopic end and the first rocking arm of the first retractor device (13) are installed on the first clamping seat (14) of side
(2) the first U-shaped crotch (24) that middle and lower part is set is connected；
Second clamping seat (22) of the middle and upper part of first rocking arm (2) provided with the retractor device of band second (21), the second flexible dress
The second U-shaped crotch (34) that the telescopic end and the second rocking arm (3) middle and lower part for putting (21) are set is connected；
The other end of second rocking arm (3) is connected by connecting seat (32) with supporting plate (31).
7. the rocking arm condenser discharge welder of gum cover is used according to claim 6, it is characterised in that：Described rotating seat (6) includes
Base (61), the top of base (61) is connected by thrust bearing (62) with spill spin block (63), the upper surface side of spill spin block (63)
Portion is provided with the first bearing pin (64) being connected with workbench (1).
8. the rocking arm condenser discharge welder of gum cover is used according to claim 6, it is characterised in that：The first described retractor device
(13) it is connected respectively by each corresponding magnetic valve (8) with air accumulator (7) with the second retractor device (21), magnetic valve (8)
It is connected with programmable PLC controller (5).
9. the rocking arm condenser discharge welder of gum cover is used according to claim 6, it is characterised in that：Described the first rocking arm (2)
Top is the cylindrical-shaped structure being folded upward at, and the through hole (232) that cylindrical-shaped structure is sleeved on U-shaped fixture (23) is internal, and U-shaped is solid
The one end for determining part (23) with the second rocking arm (3) is connected.
10. the rocking arm condenser discharge welder of gum cover is used according to claim 9, it is characterised in that：Described U-shaped fixture (23)
Including U-shaped fixture body (231), through hole (232), U-shaped fixture are offered in the closed end of U-shaped fixture body (231)
The openend both sides of body (231) are respectively equipped between pinned hole (233), the openend of U-shaped fixture body (231) internal set
There is one end of the second rocking arm (3), the openend of U-shaped fixture body (231) and one end of the second rocking arm (3) pass through the second bearing pin
(234) it is connected.