CN107254348A - A kind of strong repairing agent for automobile - Google Patents
A kind of strong repairing agent for automobile Download PDFInfo
- Publication number
- CN107254348A CN107254348A CN201710614949.4A CN201710614949A CN107254348A CN 107254348 A CN107254348 A CN 107254348A CN 201710614949 A CN201710614949 A CN 201710614949A CN 107254348 A CN107254348 A CN 107254348A
- Authority
- CN
- China
- Prior art keywords
- parts
- automobile
- additive
- repairing agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of strong repairing agent for automobile, the renovation agent includes the raw material of following parts by weight：5~9 parts of filler, 0.01~0.06 part of Nano diamond, 4~8 parts of ionic liquid, 60~80 parts of base oil, 0.5~1.2 part of thickener, 0.5~1.2 part of oxidation and corrosion inhibitor, 2~4 parts of polyisobutylene-bis-succinimide, 1~1.6 part of additive；Its preparation method is：1) Nano diamond 1) is added in dispersant polyisobutylene-bis-succinimide, stirred, precipitation is filtrated to get clear liquid；2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, grinding is stirred and evenly mixed after mixing；3) thickener is added, stirring obtains strong repairing agent for automobile；Simple production process of the present invention, production cost are low, can fill irregular surface part, metal surface can be made more smooth again, cold start-up partial loss are reduced, available for restoring automobile engine, it is adaptable to tackle the protection under urgent emergency case.
Description
Technical field
The present invention relates to a kind of renovation agent, more specifically, more particularly to a kind of strong repairing agent for automobile.
Background technology
Engine does work in operation process mainly leans on piston constantly to move back and forth to complete in cylinder, they
Constitute the main secondary friction of engine.The gap of the engine of long-term use, piston and cylinder wall can be increasing, causes gas
Cylinder sealing is deteriorated, and compression pressure and explosion pressure decline, and combustion gas scurries into crankcase, makes machine oil thinning, and accelerated oxidation is rotten.
Machine oil scurries into combustion chamber, causes burn oil, emits blue smoke, so that a series of serious consequences are caused, such as engine overheat, fuel oil and machine
Oilconsumption increase, leaving momentum reduction, cold start-up difficulty etc..Simultaneously because lubricating condition is deteriorated, each friction pair of engine
Friction level is aggravated, and wear extent is increased sharply, and fit clearance is further increased, and fit clearance is further increased, matching relationship
Not normal, engine noise is increased, and stable working deteriorates, serious to cause engine overhaul.Engine repair agent is exactly pin
To the automobile maintenance product of above mentioned problem.
Engine repair agent properties of product depend on used repair materials, and product currently on the market is also because using
Repair materials are different, are generally divided into three types：Nano-solid particle renovation agent, Ceramic gel renovation agent, fluorocarbon surface are repaiied
Multiple agent, occupies the share in engine repair agent market more than 80%, but all there are some shortcomings.
1st, nano-solid particle renovation agent：One is due to the nanometer agglomeration traits as generality problem.Work as metal particle
Because molecular force is reunited again be combined together after, this aggregate can turn into the new source of wear of engine, be repaiied which results in nanometer
Multiple agent had both been improved piece surface finish, and abrasion is exacerbated again while reducing friction；Two be the reality of nano-solid renovation agent
Matter is that solia particle renovation agent is added on lubricating base.It is too short that the maximum feature of solid renovation agent is to maintain the time, existing
10000~20000km can only be kept in the effect of general nanometer renovation agent on the market.
2nd, Ceramic gel renovation agent：It is to have certain effect to the part for producing trench abrasion (such as slight scuffing of cylinder bore), but to going out
The part of the larger abrasion of existing area, repairing effect is not obvious, and the abrasion of engine is generally trench abrasion and surface wear mixing
Occur, so the repairing effect of this cermet is limited.
3rd, fluorocarbon surface is modified renovation agent：This renovation agent has good reparation to the cylinder for surface wear to a certain degree occur
Effect, to there is the cylinder of trench abrasion, repairing effect is just bad.This is due to have no solid particle, film forming in fluorine carbon reparation
Thickness only has 4~8 nanometers, it is impossible to which deep hook-shaped abrasion is filled and led up, and its repairing effect to surface wear is fine.
Ionic liquid turns into one of forward position and study hotspot of contemporary chemical science with the advantage of its own.It has a lot
Advantage not available for molecular solvent, such as nonflammable explosive, fusing point is low, volatility is low, good in oxidation resistance and heat endurance height
Feature, these features are extremely coincide with the desired performance of preferable renovation agent, with excellent anti-wear and wear-resistant performance.
The content of the invention
It is an object of the invention to for above-mentioned the deficiencies in the prior art, there is provided a kind of strong repairing agent for automobile.
The technical proposal of the invention is realized in this way：
A kind of strong repairing agent for automobile, the renovation agent includes the raw material of following parts by weight：5~9 parts of filler, nanogold
0.01~0.06 part of hard rock, 4~8 parts of ionic liquid, 60~80 parts of base oil, 0.5~1.2 part of thickener, oxidation and corrosion inhibitor 0.5
~1.2 parts, 2~4 parts of polyisobutylene-bis-succinimide, 1~1.6 part of additive.
Preferably, the renovation agent includes the raw material of following parts by weight：6~8 parts of filler, Nano diamond 0.03~0.05
Part, 5~7 parts of ionic liquid, 65~75 parts of base oil, 0.7~0.9 part of thickener, 0.7~0.9 part of oxidation and corrosion inhibitor, poly- isobutyl
Alkene double 2.5~3.5 parts of succimide, 1.2~1.4 parts of additives.
Preferably, the renovation agent includes the raw material of following parts by weight：7 parts of filler, 0.04 part of Nano diamond, ionic liquid
6 parts of body, 70 parts of base oil, 0.8 part of thickener, 0.8 part of oxidation and corrosion inhibitor, 3 parts of polyisobutylene-bis-succinimide, additive
1.3 part.
Further, the filler includes crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, two
The weight ratio of molybdenum sulfide is 1.7：1.
Further, the cation of the ionic liquid is 1- alkyl-3-methylimidazole ionic liquids, and anion is
At least one of tetrafluoroborate ion, salicylic acid borate anion.
Further, the additive is (S) -3- amino -4- (3- benzothienyls)-butyrate hydrochlorate.
A kind of preparation method of strong repairing agent for automobile, comprises the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirred
15min, stands after bubble is wholly absent, black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, ground after mixing
Mill is stirred and evenly mixed, and rotating speed is 150r/min, stirs 10~20min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.
Wherein, the particle diameter of Nano diamond is 1-3nm, and crystallite boron nitride ceramics is laminar hexagonal boron nitride particles,
Particle diameter is less than 0.3um, and thickener uses T603A polyisobutene viscosity index improvers, and oxidation and corrosion inhibitor uses diisooctyl two
Aniline oxidation and corrosion inhibitor.
The invention provides a kind of strong repairing agent for automobile, simple production process, production cost are low, crystallite boron nitride pottery
The laminar similar graphite-structure of porcelain reduces friction and surface abrasion, and prevents intermetallic direct contact, less than 0.3um
Particle diameter ensure optimum filter flowing, and prevent the deposition of kollag, molybdenum disulfide and crystallite boron nitride ceramics
Particle is polished in engine wall by chemistry and forms protective layer, can compensate engine cylinder wall scrambling rough surface,
Ionic liquid adds (S) -3- amino -4- (3- benzothienyls)-butyrate hydrochlorate amino-acid salt as additive and improves ion
Carboxyl in the abrasion-resistance of liquid, additive can very strong absorption on surface, so as to form diaphragm, wherein solion
Long alkyl group can improve frictional behaviour on middle alkyl imidazolium cation, but on the other hand also result in thermo oxidative stability
Reduction, and antifriction antiwear ability and thermo oxidative stability can be improved by adding tetrafluoroborate ion, salicylic acid borate anion,
Both, which coordinate, can fill irregular surface part, metal surface can be made more smooth again, reduce cold start-up partial loss, ball shaped nano
Diamond surface body so that sliding friction is changed into rolling friction, more conducively lubricates, after particulate boron nitride ceramic layer is formed, originally
Metal friction in engine movements will become the particulate rolling friction of boron nitride ceramics layer, coefficient of friction reduction, frictional heat
Reduce, the high-temperature work environment temperature reduction of machine oil extends the damped cycle of machine oil, no precipitation, with all common filter systems
Compatibility, will not increase the p and ses content in oil, available for restoring automobile engine, it is adaptable to tackle under urgent emergency case
Protection, repairing effect effect can keep 100000~200000km, and more existing automobile engine healer properties are significantly carried
Rise.
Embodiment
With reference to specific embodiment, the present invention is described in further detail, but does not constitute to any of the present invention
Limitation.
Portion of material is originated：Polyisobutylene-bis-succinimide is purchased from Jinan Gu Ruite Chemical Co., Ltd.s, (S) -3- ammonia
Base -4- (3- benzothienyls)-butyrate hydrochlorate is purchased from Shanghai Mai Ruier chemical technologies Co., Ltd, di-iso-octyldiphenylamine purchase
From Hengshun Chemical Co., Ltd., Chuzhou.
Embodiment 1
A kind of strong repairing agent for automobile is present embodiments provided, the renovation agent includes the raw material of following parts by weight：Filling
It is 5 parts of agent, 0.01 part of Nano diamond, 4 parts of ionic liquid, 60 parts of base oil, 0.5 part of thickener, 0.5 part of oxidation and corrosion inhibitor, poly-
Isobutene double 2 parts of succimide, 1 part of additives.
The filler includes crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, molybdenum disulfide
Weight ratio is 1.7：1, the cation of the ionic liquid is 1- alkyl-3-methylimidazole ionic liquids, and anion is water
Poplar acid borate anion, the additive is (S) -3- amino -4- (3- benzothienyls)-butyrate hydrochlorate, nanometer Buddha's warrior attendant
The particle diameter of stone is 1nm, and crystallite boron nitride ceramics is laminar hexagonal boron nitride particles, and particle diameter is 0.3um, and thickener is used
T603A polyisobutene viscosity index improvers, oxidation and corrosion inhibitor uses di-iso-octyldiphenylamine oxidation and corrosion inhibitor.
A kind of preparation method of strong repairing agent for automobile, comprises the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirred
15min, stands after bubble is wholly absent, black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, ground after mixing
Mill is stirred and evenly mixed, and rotating speed is 150r/min, stirs 10min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.
Embodiment 2
A kind of strong repairing agent for automobile is present embodiments provided, the renovation agent includes the raw material of following parts by weight：Filling
It is 6 parts of agent, 0.03 part of Nano diamond, 5 parts of ionic liquid, 65 parts of base oil, 0.7 part of thickener, 0.7 part of oxidation and corrosion inhibitor, poly-
Isobutene double 2.5 parts of succimide, 1.2 parts of additives.
The filler includes crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, molybdenum disulfide
Weight ratio is 1.7：1, the cation of the ionic liquid is 1- alkyl-3-methylimidazole ionic liquids, and anion is four
Fluoro boron acid ion, the additive is (S) -3- amino -4- (3- benzothienyls)-butyrate hydrochlorate, Nano diamond
Particle diameter is 1.5nm, and crystallite boron nitride ceramics is laminar hexagonal boron nitride particles, and particle diameter is 0.25um, and thickener is used
T603A polyisobutene viscosity index improvers, oxidation and corrosion inhibitor uses di-iso-octyldiphenylamine oxidation and corrosion inhibitor.
A kind of preparation method of strong repairing agent for automobile, comprises the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirred
15min, stands after bubble is wholly absent, black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, ground after mixing
Mill is stirred and evenly mixed, and rotating speed is 150r/min, stirs 13min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.
Embodiment 3
A kind of strong repairing agent for automobile is present embodiments provided, the renovation agent includes the raw material of following parts by weight：Filling
It is 7 parts of agent, 0.04 part of Nano diamond, 6 parts of ionic liquid, 70 parts of base oil, 0.8 part of thickener, 0.8 part of oxidation and corrosion inhibitor, poly-
Isobutene double 3 parts of succimide, 1.3 parts of additives.
The filler includes crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, molybdenum disulfide
Weight ratio is 1.7：1, the cation of the ionic liquid is 1- alkyl-3-methylimidazole ionic liquids, and anion is four
Fluoro boron acid ion and salicylic acid borate anion, the additive are (S) -3- amino -4- (3- benzothienyls)-butyric acid
Hydrochloride, the particle diameter of Nano diamond is 2nm, and crystallite boron nitride ceramics is laminar hexagonal boron nitride particles, and particle diameter is
1.2um, thickener uses T603A polyisobutene viscosity index improvers, and oxidation and corrosion inhibitor uses di-iso-octyldiphenylamine antioxygen
Anti-corrosion additive.
A kind of preparation method of strong repairing agent for automobile, comprises the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirred
15min, stands after bubble is wholly absent, black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, ground after mixing
Mill is stirred and evenly mixed, and rotating speed is 150r/min, stirs 15min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.
Embodiment 4
A kind of strong repairing agent for automobile is present embodiments provided, the renovation agent includes the raw material of following parts by weight：Filling
It is 8 parts of agent, 0.05 part of Nano diamond, 7 parts of ionic liquid, 75 parts of base oil, 0.9 part of thickener, 0.9 part of oxidation and corrosion inhibitor, poly-
Isobutene double 3.5 parts of succimide, 1.4 parts of additives.
The filler includes crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, molybdenum disulfide
Weight ratio is 1.7：1, the cation of the ionic liquid is 1- alkyl-3-methylimidazole ionic liquids, and anion is four
At least one of fluoro boron acid ion, salicylic acid borate anion, the additive are (S) -3- amino -4- (3- benzos
Thienyl)-butyrate hydrochlorate, the particle diameter of Nano diamond is 2.5nm, and crystallite boron nitride ceramics is laminar hexagonal boron nitride
Particle, particle diameter is 0.15um, and thickener uses T603A polyisobutene viscosity index improvers, and oxidation and corrosion inhibitor is different pungent using two
Base diphenylamines oxidation and corrosion inhibitor.
A kind of preparation method of strong repairing agent for automobile, comprises the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirred
15min, stands after bubble is wholly absent, black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, ground after mixing
Mill is stirred and evenly mixed, and rotating speed is 150r/min, stirs 18min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.
Embodiment 5
A kind of strong repairing agent for automobile is present embodiments provided, the renovation agent includes the raw material of following parts by weight：Filling
It is 9 parts of agent, 0.06 part of Nano diamond, 8 parts of ionic liquid, 80 parts of base oil, 1.2 parts of thickener, 1.2 parts of oxidation and corrosion inhibitor, poly-
Isobutene double 4 parts of succimide, 1.6 parts of additives.
The filler includes crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, molybdenum disulfide
Weight ratio is 1.7：1, the cation of the ionic liquid is 1- alkyl-3-methylimidazole ionic liquids, and anion is four
At least one of fluoro boron acid ion, salicylic acid borate anion, the additive are (S) -3- amino -4- (3- benzos
Thienyl)-butyrate hydrochlorate, the particle diameter of Nano diamond is 3nm, and crystallite boron nitride ceramics is laminar hexagonal boron nitride
Grain, particle diameter is 0.1um, and thickener uses T603A polyisobutene viscosity index improvers, and oxidation and corrosion inhibitor uses diisooctyl two
Aniline oxidation and corrosion inhibitor.
A kind of preparation method of strong repairing agent for automobile, comprises the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirred
15min, stands after bubble is wholly absent, black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, ground after mixing
Mill is stirred and evenly mixed, and rotating speed is 150r/min, stirs 20min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.
More than, it is only the present invention preferably embodiment, but protection scope of the present invention is not limited thereto, and it is any
Those familiar with the art the invention discloses technical scope in, technique according to the invention scheme and its invention
Design is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (7)
1. a kind of strong repairing agent for automobile, it is characterised in that the renovation agent includes the raw material of following parts by weight：Filler 5~9
Part, 0.01~0.06 part of Nano diamond, 4~8 parts of ionic liquid, 60~80 parts of base oil, 0.5~1.2 part of thickener, antioxygen
0.5~1.2 part of anti-corrosion additive, 2~4 parts of polyisobutylene-bis-succinimide, 1~1.6 part of additive.
2. a kind of strong repairing agent for automobile according to claim 1, it is characterised in that the renovation agent includes following weight
The raw material of part：6~8 parts of filler, 0.03~0.05 part of Nano diamond, 5~7 parts of ionic liquid, 65~75 parts of base oil, increasing
Thick dose 0.7~0.9 part, 0.7~0.9 part of oxidation and corrosion inhibitor, 2.5~3.5 parts of polyisobutylene-bis-succinimide, additive 1.2
~1.4 parts.
3. a kind of strong repairing agent for automobile according to claim 1, it is characterised in that the renovation agent includes following weight
The raw material of part：7 parts of filler, 0.04 part of Nano diamond, 6 parts of ionic liquid, 70 parts of base oil, 0.8 part of thickener, antioxygen resist
Rotten 0.8 part of agent, 3 parts of polyisobutylene-bis-succinimide, 1.3 parts of additive.
4. a kind of strong repairing agent for automobile according to claim 1 or 2 or 3, it is characterised in that the filler includes
Crystallite boron nitride ceramics and molybdenum disulfide, the crystallite boron nitride ceramics, the weight ratio of molybdenum disulfide are 1.7：1.
5. a kind of strong repairing agent for automobile according to claim 1 or 2 or 3, it is characterised in that the ionic liquid
Cation is 1- alkyl-3-methylimidazole ionic liquids, anion be tetrafluoroborate ion, salicylic acid borate it is cloudy from
At least one of son.
6. a kind of strong repairing agent for automobile according to claim 1 or 2 or 3, it is characterised in that the additive is
(S) -3- amino -4- (3- benzothienyls)-butyrate hydrochlorate.
7. a kind of preparation method of strong repairing agent for automobile according to any one of claim 1~6, it is characterised in that
Comprise the following steps：
1) Nano diamond is added in dispersant polyisobutylene-bis-succinimide, rotating speed is 100r/min, stirs 15min,
Standing is after bubble is wholly absent, and black precipitate occurs in bottom, is filtered to remove precipitation, obtains clear liquid standby；
2) above-mentioned clear liquid and filler, ionic liquid, oxidation and corrosion inhibitor, additive are added in base oil, grinding is stirred after mixing
Mixing is mixed, rotating speed is 150r/min, stirs 10~20min,；
3) thickener is added, rotating speed is 200r/min, stirs 10min, obtain strong repairing agent for automobile.