CN107244883A - A kind of environment-friendly type inner wall coating material and its production technology - Google Patents
A kind of environment-friendly type inner wall coating material and its production technology Download PDFInfo
- Publication number
- CN107244883A CN107244883A CN201710479594.2A CN201710479594A CN107244883A CN 107244883 A CN107244883 A CN 107244883A CN 201710479594 A CN201710479594 A CN 201710479594A CN 107244883 A CN107244883 A CN 107244883A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating material
- wall coating
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-friendly type inner wall coating material and its production technology, the coating material includes the raw material of following parts by weight：100~120 parts of diatomite, 50~70 parts of bentonite, 15~30 parts of sepiolite, 20~30 parts of calcined kaolin, 8~20 parts of calcium hydroxide powder, 5~10 parts of bamboo-carbon fibre, 1~5 part of polyester fiber, 0.6~2 part of sodium perborate, 1~3 part of nano zine oxide, 0.2~0.6 part of calcium perborate, 0.1~0.5 part of dispersant, 0.2~0.8 part of wetting agent, 0.1~0.3 part of defoamer.The production technology of the coating material includes diatomaceous purifying, mixing, ball-milling technology.The environment-friendly type inner wall coating material of the present invention, each composition safety and environmental protection, heat-insulating and fire-proof function admirable, antibacterial bacteriostatic, waterproof, mould proof, corrosion-resistant, simple production process save the energy, are adapted to large-scale production.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of environment-friendly type inner wall coating material and its production work
Skill.
Background technology
With the development and growth in the living standard of society, the awareness of environment protection and health of people is remarkably reinforced, to inhabitation ring
The comfort level and security requirement more and more higher in border.Indoor temperature, relative air humidity, air quality are the weights of residence comfort
Want ambient parameter.Diatom ooze is a kind of indoor coating material based on diatomite, and diatomite was lived in before millions of years
A kind of unicellular aquatic class of swimming is biological.Diatomaceous main component is protein, and quality is light and soft, porous, porosity up to 90% with
On, specific surface area reaches 65m2/ g, determines that it has extremely strong physical absorption performance and ion-exchange performance.
In existing diatomaceous earth products, often there is function phase in most advantages just with diatomite in itself
To relatively simple and narrower purposes situation.Therefore, study it is a kind of have improve air quality, it is adjusting air humidity, mould proof, anti-
The functions such as fire, the multi-functional interior wall coating material limited with technical requirements is not limited by water source and is had great importance.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of environment-friendly type inner wall coating material and its production
Technique, the coating material safety and environmental protection, heat-insulating and fire-proof, antibacterial bacteriostatic, waterproof, mould proof, fine corrosion resistance, production technology letter
It is single, it is adapted to large-scale production.
The present invention solves technical problem and adopted the following technical scheme that：
A kind of environment-friendly type inner wall coating material, includes the raw material of following parts by weight：100~120 parts of diatomite, bentonite 50~70
Part, 15~30 parts of sepiolite, 20~30 parts of calcined kaolin, 8~20 parts of calcium hydroxide powder, 5~10 parts of bamboo-carbon fibre, polyester are fine
1~5 part of dimension, 0.6~2 part of sodium perborate, 1~3 part of nano zine oxide, 0.2~0.6 part of calcium perborate, dispersant 0.1~0.5
Part, 0.2~0.8 part of wetting agent, 0.1~0.3 part of defoamer.
Preferably, the coating material includes the raw material of following parts by weight：116 parts of diatomite, 62 parts of bentonite, sepiolite
25 parts, 26 parts of calcined kaolin, 14 parts of calcium hydroxide powder, 7 parts of bamboo-carbon fibre, 3 parts of polyester fiber, sodium perborate 1.3 part, nanometer
2 parts of zinc oxide, 0.3 part of calcium perborate, 0.2 part of dispersant, 0.5 part of wetting agent, 0.1 part of defoamer.
Preferably, the dispersant is one or more in sodium polyphosphate, calgon, PEG400,5040
Combination.
Preferably, the wetting agent is one or both of Dynol 960 or Dynol 980.
Preferably, the defoamer is silicone emulsion, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether or poly- two
One or more combinations in methylsiloxane.
The production technology of above-mentioned environment-friendly type inner wall coating material, comprises the following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours at 50~60 DEG C；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, flute profile is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~2 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.
Preferably, the step（1）Diatomite moisture after purification is maintained at less than 5%.
Preferably, the step（3）Ball mill barrel rotating speed is 30-50rpm/min, power of motor 22Kw.
Wherein, diatomite has loose structure, when indoor humidity is high, diatomite can by Vapor adsorption, when indoor humidity is low,
Steam can be desorbed by diatomite to be discharged, and the relative humidity of the interior space is automatically adjusted in 40%~70%, and this exactly body-sensing is relaxed
Suitable humidity is interval, will not also produce the bait mould of acarid, can anti-mite.Diatomaceous loose structure so that in space
Dry air has preferable heat-proof quality.
Bentonite is the broken quartz particles processed of quartz warp, is a kind of hard, wear-resisting, stable chemical performance
Silicate mineral, its main mineral constituent is SiO2, safety non-toxic, be widely used in glass, casting, ceramics and fire proofing material, smelting
Refine the industry such as ferrosilicon, flux for metallurgy.
Sepiolite is a kind of clay mineral of magnesium silicate containing Shuifu County for having layer chain structure, and shrinkage factor is low, and plasticity is good, matter
Gently, bigger than surface, adsorptivity is strong, with decolourizing, heat-insulated, insulation, anticorrosive, radioresistance and the performance such as thermally-stabilised.
Calcined kaolin is white or off-white color, powder fine, without grittiness, have lubrication, help stream, it is fire resisting, antiacid, exhausted
The good characteristic such as edge, covering power are good, soft, absorption affinity is strong.
Bamboo-carbon fibre takes mao bamboon to be raw material, employs the calcining new technology and new skill of pure oxygen high temperature and nitrogen barrier delay
Art so that the micropore that bamboo charcoal innately has more refine with honeycomb, with moisture absorption is ventilative, bacteriostasis antibiosis, cool in summer and warm in winter, green ring
The features such as guarantor.
Polyester fiber is the synthetic fibers as obtained by organic dibasic acid and the polyester of dihydric alcohol polycondensation through spinning, crease-resistant
Property and conformality very well, with higher intensity and elastic recovery capability.
Sodium perborate, calcium perborate are white monoclinic system crystal particle or powder, can be used as oxidant, bleaching agent, kill
Additive in microbial inoculum, deodorant, detergent etc., and fiber will not be damaged.
Nano zine oxide can make blood flow increase in subcutis, stimulate circulation outer, can also cover infrared
Line, reduces thermal loss, the effect with heat storing and heat preserving.
Compared with prior art, the present invention has following beneficial effect：
（1）The environment-friendly type inner wall coating material and its production technology of the present invention, coating material safety and environmental protection, heat-insulating and fire-proof, antibacterial
Antibacterial, waterproof, mould proof, fine corrosion resistance, simple production process are adapted to large-scale production.
（2）The environment-friendly type inner wall coating material of the present invention, diatomite, bentonite, sepiolite light weight, adsorptivity are strong and compare table
Area is big, improves heat-insulating flame-retardant performance, anti-chemical reagent, the corrosion resistant performance of the coating material；Diatomaceous porous knot
The honeycomb microcellular structure of structure and bamboo-carbon fibre so that the coating material moisture absorption is breathed freely, and antibacterial bacteriostatic, texture is refrigerant pleasant；Receive
Rice zinc oxide reduces the loss of heat, improves heat storing and heat preserving ability.
（3）The production technology of the coating material of the present invention has used the technique of ball mill grinding, efficiently converts mechanical energy
For heat energy, promote molecules strike and the mixing of each composition, greatly save electric energy and heating cost, provided for energy conservation standard non-
Chang Youyue condition.
Embodiment
Invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1.
A kind of environment-friendly type inner wall coating material, includes the raw material of following weight：Diatomite 225g, bentonite 120g, sepiolite
It is 50g, calcined kaolin 52g, calcium hydroxide powder 28g, bamboo-carbon fibre 14g, polyester fiber 6g, sodium perborate 2.6g, nano oxidized
Zinc 4g, calcium perborate 0.6g, sodium hexametaphosphate dispersant 0.4g, the 1g of wetting agent Dynol 960, defoamer polydimethylsiloxanes
Alkane 0.2g.
The production technology of above-mentioned environment-friendly type inner wall coating material, comprises the following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours, moisture at 50~60 DEG C
Content is maintained at less than 5%；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, taper is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~1.6 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.Wherein, ball mill barrel rotating speed is 38r/min, power of motor 22Kw.
Embodiment 2.
A kind of environment-friendly type inner wall coating material, includes the raw material of following weight：Diatomite 230g, bentonite 124g, sepiolite
It is 36g, calcined kaolin 44g, calcium hydroxide powder 30g, bamboo-carbon fibre 12g, polyester fiber 10g, sodium perborate 3.2g, nano oxidized
Zinc 4g, calcium perborate 1g, dispersant PEG400 0.8g, the 1.4g of wetting agent Dynol 980, defoamer polyoxyethylene polyoxy propyl alcohol
Amidogen ether 0.4g.
The production technology of above-mentioned environment-friendly type inner wall coating material, comprises the following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours, moisture at 50~60 DEG C
Content is maintained at less than 5%；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, taper is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~1.6 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.Wherein, ball mill barrel rotating speed is 38r/min, power of motor 22Kw.
Embodiment 3.
A kind of environment-friendly type inner wall coating material, includes the raw material of following weight：Diatomite 218g, bentonite 127g, sepiolite
50g, calcined kaolin 52g, calcium hydroxide powder 28g, bamboo-carbon fibre 16g, polyester fiber 10g, sodium perborate 3g, nano zine oxide
6g, calcium perborate 0.4g, the 0.6g of dispersant 5040, the 1.2g of wetting agent Dynol 960, defoamer polypropylene glycerol aether
0.6g。
The production technology of above-mentioned environment-friendly type inner wall coating material, comprises the following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours, moisture at 50~60 DEG C
Content is maintained at less than 5%；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, taper is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~1.6 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.Wherein, ball mill barrel rotating speed is 38r/min, power of motor 22Kw.
Embodiment 4.
A kind of environment-friendly type inner wall coating material, includes the raw material of following weight：Diatomite 237g, bentonite 124g, sepiolite
It is 48g, calcined kaolin 52g, calcium hydroxide powder 36g, bamboo-carbon fibre 16g, polyester fiber 6g, sodium perborate 3.6g, nano oxidized
Zinc 4g, calcium perborate 1.2g, sodium hexametaphosphate dispersant 1g, the 1g of wetting agent Dynol 980, defoamer silicone emulsion 0.4g.
The production technology of above-mentioned environment-friendly type inner wall coating material, comprises the following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours, moisture at 50~60 DEG C
Content is maintained at less than 5%；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, taper is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~1.6 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.Wherein, ball mill barrel rotating speed is 38r/min, power of motor 22Kw.
Embodiment 5.
A kind of environment-friendly type inner wall coating material, includes the raw material of following weight：Diatomite 240g, bentonite 140g, sepiolite
52g, calcined kaolin 60g, calcium hydroxide powder 36g, bamboo-carbon fibre 18g, polyester fiber 6g, sodium perborate 3g, nano zine oxide
4g, calcium perborate 1.2g, the 1g of dispersant 5040, the 1.6g of wetting agent Dynol 980, defoamer polyoxyethylene polyoxy propyl alcohol amidogen ether
0.4g。
The production technology of above-mentioned environment-friendly type inner wall coating material, comprises the following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours, moisture at 50~60 DEG C
Content is maintained at less than 5%；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, taper is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~1.6 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.Wherein, ball mill barrel rotating speed is 38r/min, power of motor 22Kw.
Embodiment 6
Bulk density, thermal conductivity factor, anti-microbial property, absorb-discharge humid have been carried out to the embodiment 1-5 interior wall coating materials produced
It can be measured, the results are shown in Table 1.
The interior wall coating material properties test result of table 1.
As can be seen from the above table, interior wall coating material bulk density of the invention is very small, and light weight is breathed freely, and thermal conductivity factor is small,
Heat-insulating and fire-proof, with excellent antibacterial bacteriostatic performance, the ability for being absorbed from air and discharging moisture is strong, and breathable properties are good, no
Easy alice, do not fall off, colour-fast resistance to oxidation, extend service life.
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, also should be regarded as the present invention
Protection domain.
Claims (8)
1. a kind of environment-friendly type inner wall coating material, it is characterised in that include the raw material of following parts by weight：Diatomite 100~120
Part, 50~70 parts of bentonite, 15~30 parts of sepiolite, 20~30 parts of calcined kaolin, 8~20 parts of calcium hydroxide powder, bamboo charcoal are fine
5~10 parts of dimension, 1~5 part of polyester fiber, 0.6~2 part of sodium perborate, 1~3 part of nano zine oxide, calcium perborate 0.2~0.6
Part, 0.1~0.5 part of dispersant, 0.2~0.8 part of wetting agent, 0.1~0.3 part of defoamer.
2. environment-friendly type inner wall coating material according to claim 1, it is characterised in that the coating material includes following weight
Measure the raw material of part：116 parts of diatomite, 62 parts of bentonite, 25 parts of sepiolite, 26 parts of calcined kaolin, 14 parts of calcium hydroxide powder, bamboo
7 parts of Carbon fibe, 3 parts of polyester fiber, 1.3 parts of sodium perborate, 2 parts of nano zine oxide, 0.3 part of calcium perborate, 0.2 part of dispersant,
0.5 part of wetting agent, 0.1 part of defoamer.
3. environment-friendly type inner wall coating material according to claim 1, it is characterised in that the dispersant is polyphosphoric acids
One or more combinations in sodium, calgon, PEG400,5040.
4. environment-friendly type inner wall coating material according to claim 1, it is characterised in that the wetting agent is Dynol 960
One or both of or Dynol 980.
5. environment-friendly type inner wall coating material according to claim 1, it is characterised in that the defoamer be silicone emulsion,
One or more combinations in polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether or dimethyl silicone polymer.
6. the production technology of the environment-friendly type inner wall coating material according to claim 1-5 any one, it is characterised in that bag
Include following steps：
（1）By diatomite through natural drying, weathering, crushing, soaked 30~40 minutes using deionized water, centrifuge 5~10
After minute, using 20~40 mesh filter-cloth filterings, filtrate dries the diatomite obtained after purification for 6~8 hours at 50~60 DEG C；
（2）Diatomite after purification, calcined kaolin, calcium hydroxide powder, bamboo-carbon fibre, polyester fiber are mixed, flute profile is used
After mixer is stirred 20~30 minutes, 100~200 mesh sieves are crossed, mixed-powder a is obtained；
（3）Mixed-powder a, bentonite, sepiolite, sodium perborate, nano zine oxide, calcium perborate, dispersant, wetting agent, disappear
After infusion mixing, feeding ball mill ball mill grinding 1~2 hour, after 200~300 mesh sieves, packaging produces the interior wall coating material
Material.
7. the production technology of environment-friendly type inner wall coating material according to claim 6, it is characterised in that the step（1）
Diatomite moisture after purification is maintained at less than 5%.
8. the production technology of environment-friendly type inner wall coating material according to claim 6, it is characterised in that the step（3）
Ball mill barrel rotating speed is 30-50rpm/min, power of motor 22Kw.