CN107235698A - A kind of municipal sludge processing curing agent and preparation method thereof - Google Patents
A kind of municipal sludge processing curing agent and preparation method thereof Download PDFInfo
- Publication number
- CN107235698A CN107235698A CN201710583371.0A CN201710583371A CN107235698A CN 107235698 A CN107235698 A CN 107235698A CN 201710583371 A CN201710583371 A CN 201710583371A CN 107235698 A CN107235698 A CN 107235698A
- Authority
- CN
- China
- Prior art keywords
- parts
- curing agent
- raw material
- municipal sludge
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of municipal sludge processing curing agent and preparation method thereof, it is prepared from by gypsum, crude salt, bauxite, plant ash, sodium carboxymethylcellulose, silica, ferrous sulfate, sodium lignin sulfonate, sepiolite powder, triethanolamine and soda ash, above-mentioned each raw material is taken by proportioning, at ambient temperature, above-mentioned each raw material is mixed, add water mixing, heating stirring, is cooled to room temperature, dries, grinding, you can.Curing agent of the present invention has the advantages that penetration is strong, speed is fast, dosing is few, and solidification effect is good, while ensureing that later strength will not be reduced;It can remove sludge stink;Reduce release of the heavy metal into environment.
Description
The application is application number 2016100628838, the applying date 2016 year 01 month 30, " a kind of city is dirty for denomination of invention
The divisional application of mud processing curing agent and preparation method thereof ".
Technical field
The present invention relates to sludge treatment field, specifically a kind of municipal sludge processing curing agent and preparation method thereof.
Background technology
Municipal sludge complicated component, contains a large amount of microorganisms, pathogen, heavy metal and organic pollution etc..With the whole world
Expanding economy and the increase of improving earth geographical environment activity, the workload of the dredging operation of city water channel are increasing.By
In these sludge or sludge granules it is small, be difficult dehydration, low bearing capacity, the reason such as content of organics is high, mobility is big, it is impossible to directly
Banketed as the engineering in reclamation, dyke building, road engineering.Sludge is subjected to the utilization of resources by solidification technology
A series of problems in Treatment of Sludge are can solve the problem that as earth working material or as the preprocessing means of landfill stabilization.Exploitation is efficient
Sludge solidifying agent is the key of the processing procedure.
Domestic and international Normal practice is that the inserts such as substantial amounts of sand are added during Sludge landfill, but such do not only makes
Sludge landfill cost is greatly increased, while also reducing the effective rate of utilization of landfill yard.For the curing process of sludge, mud, mesh
It is preceding that curing agent is generally used as using cement, lime etc..Ordinary cement, lime condense hardening slowly, and they are in the case of high water-solid ratio
Non-condensing forward part sedimentation is will appear from, and mud organic substance content is high, can hinder the hydration reaction of cement, solidification effect is poor,
It can not even carry out.
The content of the invention
It is an object of the invention to provide a kind of municipal sludge processing curing agent and preparation method thereof, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides following technical scheme:
A kind of municipal sludge handles curing agent, is prepared from by the raw material of following parts by weight:30~36 parts of gypsum, crude salt 24
~30 parts, 21~25 parts of bauxite, 27~29 parts of plant ash, 19~21 parts of sodium carboxymethylcellulose, 9~13 parts of silica,
8~10 parts of ferrous sulfate, 7~9 parts of sodium lignin sulfonate, 23~25 parts of sepiolite powder, 5~7 parts of triethanolamine, soda ash 21~23
Part.
A kind of described municipal sludge handles the preparation method of curing agent, and specific preparation process is as follows:
(1) above-mentioned each raw material is taken by proportioning, it is standby;
(2) at ambient temperature, above-mentioned each raw material is mixed, adds the water of 4~6 times of raw material, be heated to 110~120 DEG C,
Stir 3~4h;
(3) room temperature is cooled to, 6~7h is dried at a temperature of 65~67 DEG C, and is ground to particle diameter for 240~300 mesh, i.e.,
Can.
Compared with prior art, the beneficial effects of the invention are as follows:Curing agent of the present invention has that penetration is strong, speed fast, medicine
The few advantage of agent consumption, solidification effect is good, while ensureing that later strength will not be reduced;It can remove sludge stink;Reduce heavy metal
Release into environment.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
Municipal sludge handles curing agent, is prepared from by the raw material of following parts by weight:30 parts of gypsum, 30 parts of crude salt, aluminium alum
21 parts of soil, 29 parts of plant ash, 19 parts of sodium carboxymethylcellulose, 3 parts of silica 1,8 parts of ferrous sulfate, sodium lignin sulfonate 9
Part, 23 parts of sepiolite powder, 7 parts of triethanolamine, 21 parts of soda ash.
The preparation process of municipal sludge processing curing agent is as follows in above-described embodiment:
(1) above-mentioned each raw material is taken by proportioning, it is standby;
(2) at ambient temperature, above-mentioned each raw material is mixed, adds the water of 4 times of raw material, be heated to 110 DEG C, stir 4h;
(3) room temperature is cooled to, 7h is dried at a temperature of 65 DEG C, and be ground to particle diameter for 300 mesh, you can.
Mud is dug out from river course or lake, block therein and club class debris is removed.Determine mud moisture content be
47.4%.500g mud is put into agitator, 30g curing agent is added, mechanical agitation makes it uniformly mix, after stirring 2min
Sludge is gradually hardened, and stops stirring.After granulation 2 days, its moisture content is reduced to 17.6%, and it is strong to test its with an axle compression test
Spend for 586KN/m2, and sludge odorless after solidification, it disclosure satisfy that landfill and building are banketed requirement, can also be made using grinding tool
Variously-shaped brick is used to build.
Embodiment 2
Municipal sludge handles curing agent, is prepared from by the raw material of following parts by weight:33 parts of gypsum, 27 parts of crude salt, aluminium alum
24 parts of soil, 28 parts of plant ash, 20 parts of sodium carboxymethylcellulose, 1 part of silica 1,9 parts of ferrous sulfate, sodium lignin sulfonate 8
Part, 24 parts of sepiolite powder, 6 parts of triethanolamine, 22 parts of soda ash.
The preparation process of municipal sludge processing curing agent is as follows in above-described embodiment:
(1) above-mentioned each raw material is taken by proportioning, it is standby;
(2) at ambient temperature, above-mentioned each raw material is mixed, adds the water of 5 times of raw material, be heated to 115 DEG C, stirring 3~
4h;
(3) room temperature is cooled to, 6.5h is dried at a temperature of 66 DEG C, and be ground to particle diameter for 270 mesh, you can.
Mud is dug out from river course or lake, block therein and club class debris is removed.Determine mud moisture content be
50.8%.500g mud is put into agitator, 30g curing agent is added, mechanical agitation makes it uniformly mix, 1.5min is stirred
Sludge is gradually hardened afterwards, stops stirring.After granulation 2 days, its moisture content is reduced to 12.8%, and it is test with an axle compression test
Intensity is 635KN/m2, and sludge odorless after solidification, it disclosure satisfy that landfill and building are banketed requirement, grinding tool system can also be utilized
It is used to build into variously-shaped brick.
Embodiment 3
Municipal sludge handles curing agent, is prepared from by the raw material of following parts by weight:36 parts of gypsum, 24 parts of crude salt, aluminium alum
25 parts of soil, 27 parts of plant ash, 21 parts of sodium carboxymethylcellulose, 9 parts of silica, 10 parts of ferrous sulfate, sodium lignin sulfonate 7
Part, 25 parts of sepiolite powder, 5 parts of triethanolamine, 23 parts of soda ash.
The preparation process of municipal sludge processing curing agent is as follows in above-described embodiment:
(1) above-mentioned each raw material is taken by proportioning, it is standby;
(2) at ambient temperature, above-mentioned each raw material is mixed, adds the water of 6 times of raw material, be heated to 120 DEG C, stir 3h;
(3) room temperature is cooled to, 6h is dried at a temperature of 67 DEG C, and be ground to particle diameter for 240 mesh, you can.
Mud is dug out from river course or lake, block therein and club class debris is removed.Determine mud moisture content be
48.3%.500g mud is put into agitator, 30g curing agent is added, mechanical agitation makes it uniformly mix, after stirring 2min
Sludge is gradually hardened, and stops stirring.After granulation 2 days, its moisture content is reduced to 18.2%, and it is strong to test its with an axle compression test
Spend for 510KN/m2, and sludge odorless after solidification, it disclosure satisfy that landfill and building are banketed requirement, can also be made using grinding tool
Variously-shaped brick is used to build.
Solidification sludge after crushing contain the nutrients such as abundant organic matter and nitrogen, phosphorus, potassium and calcium, magnesium, copper, iron,
The trace elements such as zinc, can play change soil texture, increase soil fertility, promote the effect of plant growth, can be used as gardens
The fertilizer in greenery patches, realizes the recycling of sludge.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Claims (1)
1. a kind of municipal sludge handles the preparation method of curing agent, it is characterised in that described municipal sludge processing curing agent, by
The raw material of following parts by weight is prepared from:30~36 parts of gypsum, 24~30 parts of crude salt, 21~25 parts of bauxite, plant ash 27~
29 parts, 19~21 parts of sodium carboxymethylcellulose, 9~13 parts of silica, 8~10 parts of ferrous sulfate, sodium lignin sulfonate 7~9
Part, 23~25 parts of sepiolite powder, 5~7 parts of triethanolamine, 21~23 parts of soda ash;
Described municipal sludge handles the preparation method of curing agent, and specific preparation process is as follows:
(1) above-mentioned each raw material is taken by proportioning, it is standby;
(2) at ambient temperature, above-mentioned each raw material is mixed, adds the water of 4~6 times of raw material, be heated to 110~120 DEG C, stirring
3~4h;
(3) room temperature is cooled to, 6~7h is dried at a temperature of 65~67 DEG C, and be ground to particle diameter for 240~300 mesh, you can.