CN107235680A - One kind insulation abrasion-resistant hollow is laid bricks and preparation method thereof - Google Patents
One kind insulation abrasion-resistant hollow is laid bricks and preparation method thereof Download PDFInfo
- Publication number
- CN107235680A CN107235680A CN201710443886.0A CN201710443886A CN107235680A CN 107235680 A CN107235680 A CN 107235680A CN 201710443886 A CN201710443886 A CN 201710443886A CN 107235680 A CN107235680 A CN 107235680A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- laid bricks
- resistant hollow
- bauxite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Laid bricks the invention discloses one kind insulation abrasion-resistant hollow, it is made up of the component of following parts by weight：5 25 parts of lime stone, 5 20 parts of dolomite, 20 40 parts of portland cement; 3 15 parts of zircon sand, 10 20 parts of rock phosphate in powder, 15 30 parts of bauxite; 8 15 parts of glass bead, 5 15 parts of granular polystyrene, 12 24 parts of expanded perlite; 5 20 parts of organosilicon microballoon, 3 10 parts of aluminium powder, 8 16 parts of Chinese honey locust powder; 6 15 parts of haloflex, 6 11 parts of silane coupler, 38 parts of tall oil-asphalt sodium sulfonate; 5 10 parts of butyl titanate, appropriate amount of water.Compared with prior art, the present invention is added with glass bead, granular polystyrene, thus can improve the heat-insulating property that the insulation abrasion-resistant hollow is laid bricks, while being additionally added organosilicon microballoon, aluminium powder to improve anti-wear performance, makes its performance more preferable.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of insulation abrasion-resistant hollow is laid bricks and preparation method thereof.
Background technology
Traditional lays bricks using clay as raw material, in order to obtain the clay required for production of laying bricks, it is necessary to cut out top layer farming
Layer soil, after depths argillic horizon is exposed, takes out clay mineral reserve, this method, which needs to take, damages a large amount of arable lands, and to ring
Cause considerable damage in border.
The energy-saving heat preserving method of prior art building masonry wall in outer wall pasting, paving extension insulation material mainly by making to build
Build the heat inside thing scatter and disappear maintain certain level.The drawbacks of this way has very big, on the one hand carries to a certain extent
High quantities, adds construction period and cost；On the other hand, the excellent of insulation material directly determines building heat preserving
The quality of energy, and also have strict requirements for barbola work, if work progress is not careful, it is likely that cause thermal insulating material
Expect the phenomenon that drops, injure pedestrian by a crashing object or damage is caused to ground article.
The content of the invention
Laid bricks it is an object of the invention to provide one kind insulation abrasion-resistant hollow, the hollow block need not expend clay, favorably
In environmental protection, while having good heat-insulating property and anti-wear performance.
To achieve the above object, the present invention provides following technical scheme：
One kind insulation abrasion-resistant hollow is laid bricks, and it is made up of the component of following parts by weight：5-25 parts of lime stone, dolomite
5-20 parts, 20-40 parts of portland cement, 3-15 parts of zircon sand, 10-20 parts of rock phosphate in powder, 15-30 parts of bauxite, glass bead 8-
15 parts, 5-15 parts of granular polystyrene, 12-24 parts of expanded perlite, 5-20 parts of organosilicon microballoon, 3-10 parts of aluminium powder, Chinese honey locust powder 8-16
Part, 6-15 parts of haloflex, 6-11 parts of silane coupler, 3-8 parts of tall oil-asphalt sodium sulfonate, 5-10 parts of butyl titanate,
Appropriate amount of water.
Preferably, described insulation abrasion-resistant hollow is laid bricks is made up of the component of following parts by weight：13 parts of lime stone, in vain
10 parts of marble, 25 parts of portland cement, 9 parts of zircon sand, 15 parts of rock phosphate in powder, 22 parts of bauxite, 12 parts of glass bead, granular polystyrene
10 parts, 18 parts of expanded perlite, 8 parts of organosilicon microballoon, 6 parts of aluminium powder, 11 parts of Chinese honey locust powder, 10 parts of haloflex is silane coupled
7 parts of agent, 3 parts of tall oil-asphalt sodium sulfonate, 6 parts of butyl titanate, appropriate amount of water.
Preferably, described insulation abrasion-resistant hollow is laid bricks is made up of the component of following parts by weight：15 parts of lime stone, in vain
15 parts of marble, 32 parts of portland cement, 12 parts of zircon sand, 14 parts of rock phosphate in powder, 24 parts of bauxite, 10 parts of glass bead, polyphenyl
12 parts of grain, 20 parts of expanded perlite, 12 parts of organosilicon microballoon, 5 parts of aluminium powder, 10 parts of Chinese honey locust powder, 12 parts of haloflex, silane is even
Join 9 parts of agent, 5 parts of tall oil-asphalt sodium sulfonate, 8 parts of butyl titanate, appropriate amount of water.
The preparation method that described insulation abrasion-resistant hollow is laid bricks, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed
Close uniform, crush, cross 200-250 mesh sieves, then add mixture into mixer, add water and the water content control of compound is existed
60-70%, is stirred twice afterwards, first time mixing time be 3-6 minute, static 1 minute after, addition portland cement,
Zircon sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 4-8 minutes, obtains mixing slurry
Material；
(3) haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate are added in step (2)
In mixed slurry, foam 20-25min after stirring at a temperature of 65-72 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 25-30h, form removal obtains the insulation
Abrasion-resistant hollow is laid bricks.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention is added with glass bead, granular polystyrene, thus can improve the heat insulating ability that the insulation abrasion-resistant hollow is laid bricks
Can, while being additionally added organosilicon microballoon, aluminium powder to improve anti-wear performance, make its performance more preferable；In addition, the sky in the present invention
The heart is laid bricks other plurality of raw materials compositions of also arranging in pairs or groups, it is to avoid tradition aniseed in production and processing of laying bricks uses clay, so as to cause environment
Pollution.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
One kind insulation abrasion-resistant hollow is laid bricks, and it is made up of the component of following parts by weight：5 parts of lime stone, dolomite 5
Part, 20 parts of portland cement, 3 parts of zircon sand, 10 parts of rock phosphate in powder, 15 parts of bauxite, 8 parts of glass bead, 5 parts of granular polystyrene is swollen
Swollen 12 parts of perlite, 5 parts of organosilicon microballoon, 3 parts of aluminium powder, 8 parts of Chinese honey locust powder, 6 parts of haloflex, 6 parts of silane coupler, appropriate that
3 parts of oil asphalt sodium sulfonate, 5 parts of butyl titanate, appropriate amount of water.
The preparation method that described insulation abrasion-resistant hollow is laid bricks, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed
Close uniform, crush, cross 200-250 mesh sieves, then add mixture into mixer, add water and the water content control of compound is existed
60-70%, is stirred twice afterwards, first time mixing time be 3-6 minute, static 1 minute after, addition portland cement,
Zircon sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 4-8 minutes, obtains mixing slurry
Material；
(3) haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate are added in step (2)
In mixed slurry, foam 20-25min after stirring at a temperature of 65-72 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 25-30h, form removal obtains the insulation
Abrasion-resistant hollow is laid bricks.
Embodiment two：
One kind insulation abrasion-resistant hollow is laid bricks, and it is made up of the component of following parts by weight：25 parts of lime stone, dolomite 20
Part, 40 parts of portland cement, 15 parts of zircon sand, 20 parts of rock phosphate in powder, 30 parts of bauxite, 15 parts of glass bead, 15 parts of granular polystyrene,
24 parts of expanded perlite, 20 parts of organosilicon microballoon, 10 parts of aluminium powder, 16 parts of Chinese honey locust powder, 15 parts of haloflex, silane coupler 11
Part, 8 parts of tall oil-asphalt sodium sulfonate, 10 parts of butyl titanate, appropriate amount of water.
The preparation method that described insulation abrasion-resistant hollow is laid bricks, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed
Close uniform, crush, cross 220-250 mesh sieves, then add mixture into mixer, add water and the water content control of compound is existed
65%, stirred twice afterwards, first time mixing time is after 5 minutes, static 1 minute, to add portland cement, zirconium English
Sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 6 minutes, obtains mixed slurry；
(3) haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate are added in step (2)
In mixed slurry, foam 20-25min after stirring at a temperature of 65-72 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 30h, form removal obtains the insulation resistance to
Grind hollow block.
Embodiment three：
One kind insulation abrasion-resistant hollow is laid bricks, and it is made up of the component of following parts by weight：13 parts of lime stone, dolomite 10
Part, 25 parts of portland cement, 9 parts of zircon sand, 15 parts of rock phosphate in powder, 22 parts of bauxite, 12 parts of glass bead, 10 parts of granular polystyrene,
18 parts of expanded perlite, 8 parts of organosilicon microballoon, 6 parts of aluminium powder, 11 parts of Chinese honey locust powder, 10 parts of haloflex, 7 parts of silane coupler,
3 parts of tall oil-asphalt sodium sulfonate, 6 parts of butyl titanate, appropriate amount of water.
The preparation method that described insulation abrasion-resistant hollow is laid bricks, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed
Close uniform, crush, cross 200-230 mesh sieves, then add mixture into mixer, add water and the water content control of compound is existed
60-66%, is stirred twice afterwards, and first time mixing time is after 4 minutes, static 1 minute, to add portland cement, zirconium
Sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 6-8 minutes, obtains mixed slurry；
(3) haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate are added in step (2)
In mixed slurry, foam 20min after stirring at a temperature of 65-72 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 28h, form removal obtains the insulation resistance to
Grind hollow block.
Example IV:
One kind insulation abrasion-resistant hollow is laid bricks, and it is made up of the component of following parts by weight：15 parts of lime stone, dolomite 15
Part, 32 parts of portland cement, 12 parts of zircon sand, 14 parts of rock phosphate in powder, 24 parts of bauxite, 10 parts of glass bead, 12 parts of granular polystyrene,
20 parts of expanded perlite, 12 parts of organosilicon microballoon, 5 parts of aluminium powder, 10 parts of Chinese honey locust powder, 12 parts of haloflex, silane coupler 9
Part, 5 parts of tall oil-asphalt sodium sulfonate, 8 parts of butyl titanate, appropriate amount of water.
The preparation method that described insulation abrasion-resistant hollow is laid bricks, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed
Close uniform, crush, cross 250 mesh sieves, then add mixture into mixer, add water and the water content control of compound is existed
70%, stirred twice afterwards, first time mixing time is after 3 minutes, static 1 minute, to add portland cement, zirconium English
Sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 5 minutes, obtains mixed slurry；
(3) haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate are added in step (2)
In mixed slurry, foam 22min after stirring at a temperature of 66 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 25h, form removal obtains the insulation resistance to
Grind hollow block.
Embodiment five:
One kind insulation abrasion-resistant hollow is laid bricks, and it is made up of the component of following parts by weight：18 parts of lime stone, dolomite 12
Part, 30 parts of portland cement, 8 parts of zircon sand, 15 parts of rock phosphate in powder, 23 parts of bauxite, 12 parts of glass bead, 10 parts of granular polystyrene,
18 parts of expanded perlite, 12 parts of organosilicon microballoon, 6 parts of aluminium powder, 12 parts of Chinese honey locust powder, 10 parts of haloflex, silane coupler 9
Part, 6 parts of tall oil-asphalt sodium sulfonate, 8 parts of butyl titanate, appropriate amount of water.
The preparation method that described insulation abrasion-resistant hollow is laid bricks, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed
Close uniform, crush, cross 250 mesh sieves, then add mixture into mixer, add water and the water content control of compound is existed
70%, stirred twice afterwards, first time mixing time is after 3 minutes, static 1 minute, to add portland cement, zirconium English
Sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 5 minutes, obtains mixed slurry；
(3) haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate are added in step (2)
In mixed slurry, foam 22min after stirring at a temperature of 66 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 25h, form removal obtains the insulation resistance to
Grind hollow block.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to skill of the invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (4)
1. one kind insulation abrasion-resistant hollow is laid bricks, it is characterised in that it is made up of the component of following parts by weight：Lime stone 5-25
Part, 5-20 parts of dolomite, 20-40 parts of portland cement, 3-15 parts of zircon sand, 10-20 parts of rock phosphate in powder, 15-30 parts of bauxite, glass
Change 8-15 parts of microballon, 5-15 parts of granular polystyrene, 12-24 parts of expanded perlite, 5-20 parts of organosilicon microballoon, 3-10 parts of aluminium powder, soap
8-16 parts of pod powder, 6-15 parts of haloflex, 6-11 parts of silane coupler, 3-8 parts of tall oil-asphalt sodium sulfonate, butyl titanate
5-10 parts, appropriate amount of water.
2. a kind of insulation abrasion-resistant hollow according to claim 1 is laid bricks, it is characterised in that it is by following parts by weight
Component is made：13 parts of lime stone, 10 parts of dolomite, 25 parts of portland cement, 9 parts of zircon sand, 15 parts of rock phosphate in powder, bauxite 22
Part, 12 parts of glass bead, 10 parts of granular polystyrene, 18 parts of expanded perlite, 8 parts of organosilicon microballoon, 6 parts of aluminium powder, 11 parts of Chinese honey locust powder,
10 parts of haloflex, 7 parts of silane coupler, 3 parts of tall oil-asphalt sodium sulfonate, 6 parts of butyl titanate, appropriate amount of water.
3. a kind of insulation abrasion-resistant hollow according to claim 1 is laid bricks, it is characterised in that it is by following parts by weight
Component is made：15 parts of lime stone, 15 parts of dolomite, 32 parts of portland cement, 12 parts of zircon sand, 14 parts of rock phosphate in powder, bauxite 24
Part, 10 parts of glass bead, 12 parts of granular polystyrene, 20 parts of expanded perlite, 12 parts of organosilicon microballoon, 5 parts of aluminium powder, Chinese honey locust powder 10
Part, 12 parts of haloflex, 9 parts of silane coupler, 5 parts of tall oil-asphalt sodium sulfonate, 8 parts of butyl titanate, appropriate amount of water.
4. the preparation method that a kind of insulation abrasion-resistant hollow according to any one of claim 1-3 is laid bricks, it is characterised in that
Comprise the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) lime stone, dolomite, rock phosphate in powder, glass bead, granular polystyrene, expanded perlite and organosilicon microballoon are mixed equal
It is even, crush, cross 200-250 mesh sieves, then mixer is added mixture into, add water and cause the water content control of compound in 60-
70%, stirred twice afterwards, first time mixing time is after 3-6 minutes, static 1 minute, to add portland cement, zirconium English
Sand, bauxite, aluminium powder and Chinese honey locust powder, carry out second and stir, and second of mixing time is 4-8 minutes, obtains mixed slurry；
(3) mixing for adding haloflex, silane coupler, tall oil-asphalt sodium sulfonate, butyl titanate in step (2)
In slurry, foam 20-25min after stirring at a temperature of 65-72 DEG C, obtains foamed slurry；
(4) by the foamed slurry injection moulding mould in step (3), natural curing 25-30h, form removal obtains the insulation wear-resisting
Hollow block.